Textbook Question
Chapter 9.13, Problem 72AAP
Draw time–temperature cooling paths for a 1080 steel on an isothermal transformation diagram that will produce the following microstructures. Start with the steels in the austenitic condition at time = 0 and temperature = 850°C. (a) 100% martensite, (b) 50% martensite and 50% coarse pearlite, (c) 100% fine pearlite, (d) 50% martensite and 50% upper bainite, (e) 100% upper bainite, and (f) 100% lower bainite.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
With respect to the S-N diagram shown below, answer the following questions:(a) for Gray cast iron, what is the projected number of cycles to failure for an induced stress of 20,000 psi?(b) What is the endurance limit and associated stress for a 0.47% heat treated carbon steel? (c) What is the endurance limit for the Aluminum-copper alloy?(d) What is the endurance strength for heat treated Alloy Steel at 400,000 cycles?
Below is a continuous cooling transformation curve for steel (upper) and for a silicate melt (lower).
Describe the similarities and differences as follows.
a. What is the critical cooling rate in each case?
b. What phase(s) form in each case when the critical cooling rate is exceeded?
c. What phase(s) form in each case if the cooling rate is very slow?
800
1400
Ae lemperature
Austenite
*peorlite begins
10FI
700
1200
Austenitepearlite complete 1600
1000
5009
800
Tronsformation stops
400
600
300
400
Austenite -mortenstic structure
200
-Isathermal dogram
Continuous transformaton
diogrom
Constant rate coding curves - 100
200
Findl structure
Mortensite Morlensite
i peorlile
Peorite (softer, coorser-
0.1
10?
10
Tronsformation time, seconds
Continuous Cooling-Transformation (C-T)Diagram
(Derived from the isothermal-transformation diagram for a plain-carbon eutectoid steel)
1200
Glass
Crystallization
begins
1100
1000
Critical
cooling
rate
Glass-ceramic
900
Crystallization
ends
800
700
102
10…
Using the TTT diagram for eutectoid steel, draw the specified cooling path on the diagram.
Indicate what phases you expect in the final product with percentage of each phase. Assume the material has been fully austenitized before cooling.
a. Water cool to room temperature
b. Hot quench in molten salt to 690°C and then cooled isothermally for 2 hours:
c. Hot quench to 610°C hold 3 minutes and water quench
Chapter 9 Solutions
Foundations of Materials Science and Engineering
Ch. 9.13 - (a) How is raw pig iron extracted from iron oxide...Ch. 9.13 - (a) Why is the FeFe3C phase diagram a metastable...Ch. 9.13 - (a) What is the structure of pearlite? (b) Draw a...Ch. 9.13 - Distinguish between the following three types of...Ch. 9.13 - Prob. 5KCPCh. 9.13 - (a) Define an FeC martensite. (b) Describe the...Ch. 9.13 - (a) What is an isothermal transformation in the...Ch. 9.13 - How does the isothermal transformation diagram for...Ch. 9.13 - Draw a continuous-cooling transformation diagram...Ch. 9.13 - (a) Describe the full-annealing heat treatment for...
Ch. 9.13 - Describe the process-annealing heat treatment for...Ch. 9.13 - What is the normalizing heat treatment for steel...Ch. 9.13 - Describe the tempering process for a plain-carbon...Ch. 9.13 - (a) Describe the martempering (marquenching)...Ch. 9.13 - (a) Describe the austempering process for a...Ch. 9.13 - (a) Explain the numbering system used by the AISI...Ch. 9.13 - (a) What arc some of the limitations of...Ch. 9.13 - (a) What compounds docs aluminum form in steels?...Ch. 9.13 - Prob. 19KCPCh. 9.13 - (a) Define the hardenability of a steel. (b)...Ch. 9.13 - Prob. 21KCPCh. 9.13 - Prob. 22KCPCh. 9.13 - Prob. 23KCPCh. 9.13 - What is the difference between a coherent...Ch. 9.13 - Prob. 25KCPCh. 9.13 - Prob. 26KCPCh. 9.13 - Prob. 27KCPCh. 9.13 - (a) Describe the three principal casting processes...Ch. 9.13 - Prob. 29KCPCh. 9.13 - Prob. 30KCPCh. 9.13 - Prob. 31KCPCh. 9.13 - Prob. 32KCPCh. 9.13 - Prob. 33KCPCh. 9.13 - Prob. 34KCPCh. 9.13 - Prob. 35KCPCh. 9.13 - (a) What are the cast irons? (b) What is their...Ch. 9.13 - Prob. 37KCPCh. 9.13 - Prob. 38KCPCh. 9.13 - Prob. 39KCPCh. 9.13 - Prob. 40KCPCh. 9.13 - Prob. 41KCPCh. 9.13 - Prob. 42KCPCh. 9.13 - Prob. 43KCPCh. 9.13 - Prob. 44KCPCh. 9.13 - Prob. 45KCPCh. 9.13 - (a) Why arc titanium and its alloys of special...Ch. 9.13 - Prob. 47KCPCh. 9.13 - Prob. 48KCPCh. 9.13 - Prob. 49KCPCh. 9.13 - Prob. 50KCPCh. 9.13 - Prob. 51KCPCh. 9.13 - Prob. 52KCPCh. 9.13 - Describe the structural changes that take place...Ch. 9.13 - Describe the structural changes that take place...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - (a) What types of microstructures arc produced by...Ch. 9.13 - A 0.65 % C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A 0.25% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A plain-carbon steel contains 93 wt % ferrite7 wt%...Ch. 9.13 - A plain-carbon steel contains 45 wt% proeutectoid...Ch. 9.13 - A plain-carbon steel contains 5.9 wt%...Ch. 9.13 - A 0.90% C hypereutectoid plain-carbon steel is...Ch. 9.13 - A 1.10% C hypereutectoid plain-carbon steel is...Ch. 9.13 - If a hypereutectoid plain-carbon steel contains...Ch. 9.13 - A hypereutectoid plain-carbon steel contains 10.7...Ch. 9.13 - A plain-carbon steel contains 20.0 wt%...Ch. 9.13 - A 0.55% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A hypoeutectoid steel contains 44.0 wt% eutectoid...Ch. 9.13 - A hypoeutectoid steel contains 24.0 wt% eutectoid...Ch. 9.13 - A 1.10 % C hypereutectoid plain-carbon steel is...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Thin pieces of 0.3-mm-thick hot-rolled strips of...Ch. 9.13 - Prob. 75AAPCh. 9.13 - Prob. 76AAPCh. 9.13 - Prob. 77AAPCh. 9.13 - Prob. 78AAPCh. 9.13 - Prob. 79AAPCh. 9.13 - Prob. 80AAPCh. 9.13 - Prob. 81AAPCh. 9.13 - Prob. 82AAPCh. 9.13 - An austenitized 40-mm-diameter 4340 steel bar is...Ch. 9.13 - Prob. 84AAPCh. 9.13 - Prob. 85AAPCh. 9.13 - Prob. 86AAPCh. 9.13 - Prob. 87AAPCh. 9.13 - Prob. 88AAPCh. 9.13 - Prob. 89AAPCh. 9.13 - Prob. 90AAPCh. 9.13 - Prob. 91AAPCh. 9.13 - Prob. 92AAPCh. 9.13 - (a) For a plain-carbon steel with 1 wt % carbon...Ch. 9.13 - Prob. 94SEPCh. 9.13 - Prob. 95SEPCh. 9.13 - Prob. 96SEPCh. 9.13 - Prob. 97SEPCh. 9.13 - Prob. 98SEPCh. 9.13 - Prob. 99SEPCh. 9.13 - Prob. 100SEPCh. 9.13 - Prob. 101SEPCh. 9.13 - Prob. 102SEPCh. 9.13 - Prob. 103SEPCh. 9.13 - Both 4140 and 4340 steel alloys may be tempered to...Ch. 9.13 - Prob. 105SEPCh. 9.13 - Aircraft fuselage is made of aluminum alloys 2024...Ch. 9.13 - Prob. 107SEPCh. 9.13 - Prob. 108SEPCh. 9.13 - Prob. 109SEPCh. 9.13 - (a) What makes austenitic stainless steels that...Ch. 9.13 - Prob. 111SEPCh. 9.13 - Prob. 112SEPCh. 9.13 - Prob. 113SEPCh. 9.13 - (a) Give examples of components or products that...Ch. 9.13 - Prob. 115SEPCh. 9.13 - Prob. 116SEPCh. 9.13 - Prob. 117SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- In your own words describe the following heat treatment procedures for steels and, for each, the intended final microstructure: (a) full annealing (b) normalizing (c) quenching (d) tempering.arrow_forward3.The TTT diagram of a plain carbon steel is given in Fig. 1. Identify whether this steel is a hypoeutectoid, eutectoid or hypereutectoid steel. Explain why the transformation happens slowly at 850°C as well as at 300°C. Determine the microstructures expected in this type of steel after the following heat treatment processes. a) Austenize at 900°C, quench to 400°C and hold for 1000 s and quench to 25°C. b) Austenize at 900°C, quench to 25°C. c) Austenize at 900°C, quench to 675°C and hold for 1 s, quench to 400°C and hold for 900 s and slowly cool to 25°C. 900 Acm Cs 800 A1 FezC + Y 33 Fe3C + pearlite 45 700 Ps 600 ++ Fe3C + pearlite Y+ bainite Bs 500 46 Bainite 400 Yu Bf 300 57 Ms 200 60 Mf Y+ martensite 100 62 Martensite 102 65 103 104 105 106 0.1 1 10 Time (s) Fig. 1 Temperature (°C) Rockwell C hardnessarrow_forward1. Why does the tensile strength of steel, which contains only austenite at room temperature, differ fromsteel that shows only pearlite in its microstructure? Give two important reasons for the difference. 2. What general prerequ_isites exist for the formation of martensite in steel? 3. What is an isothermal transformation of a material in the solid state condition? 4. Draw a typical isothermal transformation diagram for plain .carbon eutectoid steel and indicate thevarious decomposition products expected by simple diagrammatic drawing.arrow_forward
- For the isothermal time-temperature-transformation diagram provided (next page) for an Fe-C steel, answer the following (show any work on the diagram):a. based on the phases depicted, what is the average composition for the Fe-C alloy depicted (be specific). Explain your answer. (Note: you do have the Fe-C phase diagram in your notes and in the text for reference.)b. in an isothermal heat-treatment of a pure austenite structure at 300 C, how long will it take for austenite to be completely converted to bainite after bainite first begins to form?c. A standard size, automobile engine block and a 1 mm diameter rod of the same steel composition are taken from a heat-treatment furnace and immersed in a water bath at the same temperature. Do you expect that the microstructure of both pieces will be the same or different? Justify your answer.d. note that the time required to initiate the transformation of the austenite phase tends to decrease as the isothermal treatment temperature is reduced…arrow_forwardThe TTT diagram for a 1076 eutectoid steel is given: What is the heat treatment process to form 50% Coarse Pearlite + 50% Martensite. 800 A 1400 Eutectoid temperature 700 A 1200 600 1000 500 800 400 A 600 300 M(start) 200 50% 400 M + A M(50%) M(90%) 100 200 10-1 1 10 102 103 104 105 Time (s) Temperature (°C) Temperature (°F)arrow_forwardDraw Iron - Iron Carbide Phase diagram and show the following: 1- Temperature, phases and carbon weight for Eutectic. 2- Temperature, phases and carbon weight for Eutectoid Thecementite, 3- austenite, ferrite, delta phases with their 4- Types of ferrous alloys on different carbon rates. 5- Draw the phase at T= 700 CD and 0.7 wt% C what is its name ? temperatures and carbon weight.arrow_forward
- How would the following heat treatment be conducted, quoting approximates temperatures, cooling rate and microstructure of:(i) Normalizing of a plain carbon steel containing 0.8 wt % C, (ii) Quenching of a plain carbon steel containing 0.8 wt % C in water (iii) Quenching of a plain carbon steel containing 0.8 wt % C in oil (iv) full annealing of a plain carbon steel containing 0.8 % C.arrow_forwardWhat is the% C ratio of two different steels with 80% and equal austenite content at 724 Celsius?arrow_forwardPart C. Which type of phase transformation is important in heat treatment of steels? (circle one)Peritectic Eutectic Eutectoid Incongruent meltingAt what temperature and overall composition wt% C, does it occur?Write the reaction equation for this transformation, and briefly describe the nature of each of the three important phases that are involved.arrow_forward
- 1. 1. Using the isothermal transformation diagram below, describe the microstructure present in a eutectoid carbon steel, after each of the following heat treatments. From 800 C: (a) Cool to 450 C and hold for 10 s, cool to 375 C hold for 100 s, quench to 25 C. (b) Cool to 650 C and hold for 300 s, and quench to 25 C. (c) Cool to 720 C and hold for 100 s, quench to 400 C and hold for 200 s, and quench to 25 C. Temperature (°C) 800 700 600 500 400 300 200 100 0 10-1 A A A M(start) M(50%) M(90%) 1 10 M+A Eutectoid temperature P 10² Time (s) B 50% 10³ 104 1400 1200 1000 800 600 400 200 105 Temperature (°F)arrow_forward(b) Figure Q4 (b) displays the time-temperature cooling paths for a 1080 steel on an isothermal transformation diagram. Start with the steels in the austenitic condition at time = 0 and 850°C. Interpret the final microstructures that will be obtained for paths (i, ii and iii) shown in the figure. 700 600 500 400 300 (iii) Ms 200 (i) (ii) Mf Figure Q4 (b)arrow_forwardQ1: Austenitized 40 mm diameter 5140 alloy steel bar is quenched in agitated oil. Predict what is the Rockwell hardness of this bar will be at (a) its surface and (b) its center (c) What do you think about the difference in hardness number between the center and surface (d) Differentiate between hardness and hardenability (e) Rank the steels in the figure below from lowest to highest hardenability and explain why. 600- Bar diameter (mm) 100 80 60 40 20 0 300 0 Cooling rate at 700°C (°C/sec). -150 55 0 تنا 25 ------- 5 S 10 12.5 8 M-R L 1/2 34-R Agitated oil 15 20 ¼ ¾ Distance from quenched end. De (Jominy distance) 5,5 54 Car Bar diameter (in.) 0 25 mm. 1 in. Hardness (Rockwell C) Where (C = center, S = surface, M-R = mid-radius) 2828 292 65 60- 55- 50 45 40 35 30 25 20 15 10 0 J 10 5140 30 20 Distance from quenched end (mm) 4340 2 4 6 8 10 12 14 16 18 20 22 24 26 28 30 32 Distance from quenched end (sixteenths of an inch) 40 9840 4140 8640 50arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Extent of Reaction; Author: LearnChemE;https://www.youtube.com/watch?v=__stMf3OLP4;License: Standard Youtube License