Question
Chapter 9.13, Problem 82AAP
To determine
The cooling rate experienced by an austenitized and quenched 5140 steel bar and the bar has a Rockwell C hardness of 35 at a point on its surface.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Q1: Austenitized 40 mm diameter 5140 alloy steel bar is quenched in agitated oil. Predict what is the
Rockwell hardness of this bar will be at (a) its surface and (b) its center (c) What do you think about
the difference in hardness number between the center and surface (d) Differentiate between hardness
and hardenability (e) Rank the steels in the figure below from lowest to highest hardenability and
explain why.
600-
Bar diameter (mm)
100
80
60
40
20
0
300
0
Cooling rate at 700°C (°C/sec).
-150
55
0
تنا
25
-------
5
S
10
12.5 8
M-R
L
1/2
34-R
Agitated oil
15
20
¼
¾
Distance from quenched end. De
(Jominy distance)
5,5
54
Car
Bar diameter (in.)
0
25 mm.
1 in.
Hardness (Rockwell C)
Where (C = center, S = surface, M-R = mid-radius)
2828 292
65
60-
55-
50
45
40
35
30
25
20
15
10
0
J
10
5140
30
20
Distance from quenched end (mm)
4340
2 4 6 8 10 12 14 16 18 20 22 24 26 28 30 32
Distance from quenched end (sixteenths of an inch)
40
9840
4140
8640
50
Q3: With a moderately agitated water, a cylindrical piece of steel with 80 mm diameter is to be quenched. The
hardnesses of the surface and center must be at least 55 and 40 HRC, respectively. Which of these alloys will
satisfy the following requirements: 1040, 5140, 4340, 4140, 8620, 8630, 8640, and 8660?
Cooling rate at 700c
Cooling rate at 700°c
170 70 31 18
5.6
3.9 "C
270 170 70 31 18 9
60
2 "Os
5.6
3.9
2.8
100
100
50
4340
80
75
3
Surface
40
4140
Center
8640
30
5140
25
1040
20
10
20
30
40
50 mm
10
20
30 mm
Distance from quenched end
Equivalent distance from quenched end
Figure 3
Figure 4
Hardness, HRC
Percent martensite
Diameter of bar (mm)
A nitriding heat treatment of a BCC steel normally requires 2 h at 600 °C. What temperature would be required to reduce the heat treatment time to 1 h?(Q =76570 J/mol, Do =0.0047x10- 4 m2/s)
and the last one. thanks for ur helping.
Chapter 9 Solutions
Foundations of Materials Science and Engineering
Ch. 9.13 - (a) How is raw pig iron extracted from iron oxide...Ch. 9.13 - (a) Why is the FeFe3C phase diagram a metastable...Ch. 9.13 - (a) What is the structure of pearlite? (b) Draw a...Ch. 9.13 - Distinguish between the following three types of...Ch. 9.13 - Prob. 5KCPCh. 9.13 - (a) Define an FeC martensite. (b) Describe the...Ch. 9.13 - (a) What is an isothermal transformation in the...Ch. 9.13 - How does the isothermal transformation diagram for...Ch. 9.13 - Draw a continuous-cooling transformation diagram...Ch. 9.13 - (a) Describe the full-annealing heat treatment for...
Ch. 9.13 - Describe the process-annealing heat treatment for...Ch. 9.13 - What is the normalizing heat treatment for steel...Ch. 9.13 - Describe the tempering process for a plain-carbon...Ch. 9.13 - (a) Describe the martempering (marquenching)...Ch. 9.13 - (a) Describe the austempering process for a...Ch. 9.13 - (a) Explain the numbering system used by the AISI...Ch. 9.13 - (a) What arc some of the limitations of...Ch. 9.13 - (a) What compounds docs aluminum form in steels?...Ch. 9.13 - Prob. 19KCPCh. 9.13 - (a) Define the hardenability of a steel. (b)...Ch. 9.13 - Prob. 21KCPCh. 9.13 - Prob. 22KCPCh. 9.13 - Prob. 23KCPCh. 9.13 - What is the difference between a coherent...Ch. 9.13 - Prob. 25KCPCh. 9.13 - Prob. 26KCPCh. 9.13 - Prob. 27KCPCh. 9.13 - (a) Describe the three principal casting processes...Ch. 9.13 - Prob. 29KCPCh. 9.13 - Prob. 30KCPCh. 9.13 - Prob. 31KCPCh. 9.13 - Prob. 32KCPCh. 9.13 - Prob. 33KCPCh. 9.13 - Prob. 34KCPCh. 9.13 - Prob. 35KCPCh. 9.13 - (a) What are the cast irons? (b) What is their...Ch. 9.13 - Prob. 37KCPCh. 9.13 - Prob. 38KCPCh. 9.13 - Prob. 39KCPCh. 9.13 - Prob. 40KCPCh. 9.13 - Prob. 41KCPCh. 9.13 - Prob. 42KCPCh. 9.13 - Prob. 43KCPCh. 9.13 - Prob. 44KCPCh. 9.13 - Prob. 45KCPCh. 9.13 - (a) Why arc titanium and its alloys of special...Ch. 9.13 - Prob. 47KCPCh. 9.13 - Prob. 48KCPCh. 9.13 - Prob. 49KCPCh. 9.13 - Prob. 50KCPCh. 9.13 - Prob. 51KCPCh. 9.13 - Prob. 52KCPCh. 9.13 - Describe the structural changes that take place...Ch. 9.13 - Describe the structural changes that take place...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - (a) What types of microstructures arc produced by...Ch. 9.13 - A 0.65 % C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A 0.25% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A plain-carbon steel contains 93 wt % ferrite7 wt%...Ch. 9.13 - A plain-carbon steel contains 45 wt% proeutectoid...Ch. 9.13 - A plain-carbon steel contains 5.9 wt%...Ch. 9.13 - A 0.90% C hypereutectoid plain-carbon steel is...Ch. 9.13 - A 1.10% C hypereutectoid plain-carbon steel is...Ch. 9.13 - If a hypereutectoid plain-carbon steel contains...Ch. 9.13 - A hypereutectoid plain-carbon steel contains 10.7...Ch. 9.13 - A plain-carbon steel contains 20.0 wt%...Ch. 9.13 - A 0.55% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A hypoeutectoid steel contains 44.0 wt% eutectoid...Ch. 9.13 - A hypoeutectoid steel contains 24.0 wt% eutectoid...Ch. 9.13 - A 1.10 % C hypereutectoid plain-carbon steel is...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Thin pieces of 0.3-mm-thick hot-rolled strips of...Ch. 9.13 - Prob. 75AAPCh. 9.13 - Prob. 76AAPCh. 9.13 - Prob. 77AAPCh. 9.13 - Prob. 78AAPCh. 9.13 - Prob. 79AAPCh. 9.13 - Prob. 80AAPCh. 9.13 - Prob. 81AAPCh. 9.13 - Prob. 82AAPCh. 9.13 - An austenitized 40-mm-diameter 4340 steel bar is...Ch. 9.13 - Prob. 84AAPCh. 9.13 - Prob. 85AAPCh. 9.13 - Prob. 86AAPCh. 9.13 - Prob. 87AAPCh. 9.13 - Prob. 88AAPCh. 9.13 - Prob. 89AAPCh. 9.13 - Prob. 90AAPCh. 9.13 - Prob. 91AAPCh. 9.13 - Prob. 92AAPCh. 9.13 - (a) For a plain-carbon steel with 1 wt % carbon...Ch. 9.13 - Prob. 94SEPCh. 9.13 - Prob. 95SEPCh. 9.13 - Prob. 96SEPCh. 9.13 - Prob. 97SEPCh. 9.13 - Prob. 98SEPCh. 9.13 - Prob. 99SEPCh. 9.13 - Prob. 100SEPCh. 9.13 - Prob. 101SEPCh. 9.13 - Prob. 102SEPCh. 9.13 - Prob. 103SEPCh. 9.13 - Both 4140 and 4340 steel alloys may be tempered to...Ch. 9.13 - Prob. 105SEPCh. 9.13 - Aircraft fuselage is made of aluminum alloys 2024...Ch. 9.13 - Prob. 107SEPCh. 9.13 - Prob. 108SEPCh. 9.13 - Prob. 109SEPCh. 9.13 - (a) What makes austenitic stainless steels that...Ch. 9.13 - Prob. 111SEPCh. 9.13 - Prob. 112SEPCh. 9.13 - Prob. 113SEPCh. 9.13 - (a) Give examples of components or products that...Ch. 9.13 - Prob. 115SEPCh. 9.13 - Prob. 116SEPCh. 9.13 - Prob. 117SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A nitriding heat treatment of a BCC steel normally requires 2 h at 600 °C. What temperature would be required to reduce the heat treatment time to 1 h?(Q =76570 J/mol, Do =0.0047x10- 4 m2/s)arrow_forwardThe TTT diagram for a 1076 eutectoid steel is given: What is the heat treatment process to form 50% Coarse Pearlite + 50% Martensite. 800 A 1400 Eutectoid temperature 700 A 1200 600 1000 500 800 400 A 600 300 M(start) 200 50% 400 M + A M(50%) M(90%) 100 200 10-1 1 10 102 103 104 105 Time (s) Temperature (°C) Temperature (°F)arrow_forward36 Asiacell O Homework 4 -... -> 3 Class Materials Eng. Dep. Heat Treatment Ismail Ibrahim Marhoon Homework 4 Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20). If we use a 4340; 4140; 8640; 5140; 1040 steel, what would be the hardness number at the center of the part? Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a 3.75 cm diameter 4320 steel bar. Given Cingrate t 00c00 143 to 4340 50 40 8640 ab 9310 30 4320 1050 1040 10 20 it 1 1 2n 10 20 30 Jominy distance th of an inch) Die he eted e TABLE The N canticient, or seveity of the querch, far several guenehing sedla H Coefticient Coaling Rate at he Center of a l-in. Bar (CA) Medium Ol no taton) 04 anitation) 025 18 45 HyD inc agtation H0 fegiutont Brine Ino agtaton) Brine lapttiori 10 4.0 190 20 60 90 230 Ad DISTANCE FROM OUENCHED END IN) DIAMETER IN)arrow_forward
- Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20). If we use a 4340; 4140; 8640; 5140; 1040 steel, what would be the hardness number at the center of the part? Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a 3.75 cm diameter 4320 steel bar.arrow_forwardDescribe the final microstructure obtained in a 1050 steel after heat at 8200C, cooled to 7000C and hold for 5 s, cooled to room temperature. 900- a+y 800 A, 700 A1 F, Pr a+ pearlite 23 600 -y+a+pearlite 30 500 B1 y+ bainite Bainite 39 F=Ferrite B, M, 400 49 P=Pearlite 300 Y+ martensite B=Bainite 200 Martensite M=Martensite 62 100- 102 10 10 10 10 0.1 1 10 Time (s) TTT curve for carbon steel AISI 1050 Temperature (°C) Rockwell C hardnessarrow_forwardA sheet of a 70% Cu-30% Zn alloy is cold-rolled 20% to a thickness of 3.0mm. The sheet is then further coldrolledto 2.0 mm. What is the percentage cold work?arrow_forward
- If a eutectoid steel sample is heated to 800°C and then quenched in a cold-water bath then what would be the possible microstructure? Draw the microstructure and label it.arrow_forwardIf a 0.80 percent plain carbon steel is austenitized (heated to a read heat) and quenched in water to room temperatures so that the cooling curve does not cut into the “nose” of the I-T diagram, what will the resultant microstructure be?arrow_forwardSome alloys use a combination of strain hardening and precipitation hardening to achieve particularly high strength levels. The usual order of strengthening is solution treatment, quenching, cold working, and finally precipitation heat treatment. Why not reverse the order of the cold working and precipitation heat treatment steps?arrow_forward
- Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20). If we use a 4340; 4140; 8640; 5140; 1040 steel, what would be the hardness number at the center of the part? Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a 3.75 cm diameter 4320 steel bar, Given re n 4340 50 8640 9310 Sie 4320 1050 10 20 10 20 30 Jominy distance (th of an inch) TABLE Fhe N coeticiet ar severily af the quench, far several omehing med Cosling Ratethe Center Medium Coeicien O ne gato Otton 0 (re aghuion Ho laghatord Brire ne agtnoni tre agn 025 10 10 20 DIAMETER IN) HFACTOR Rockwell Channessarrow_forwardExcellent combinations of hardness, strength, and toughness are obtained from bainite. One heat treater austenitized a eutectoid steel at 750°C, quenched and held the steel at 250°C for 15 min, and finally permitted the steel to cool to room temperature. Did he produce the required bainitic structure? Use the diagram below in your answer 900 600 700 14 00 Y. 400 12 52 M. 00 57 M. 100 0.3 10 10 10 Answer: Time Temperature ("C) Rockwell Chardnensarrow_forward(b) Figure Q4 (b) displays the time-temperature cooling paths for a 1080 steel on an isothermal transformation diagram. Start with the steels in the austenitic condition at time = 0 and 850°C. Interpret the final microstructures that will be obtained for paths (i, ii and iii) shown in the figure. 700 600 500 400 300 (iii) Ms 200 (i) (ii) Mf Figure Q4 (b)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Introduction to Diffusion in Solids; Author: Engineering and Design Solutions;https://www.youtube.com/watch?v=K_1QmKJvNjc;License: Standard youtube license