(a) How is raw pig iron extracted from iron oxide ores? (b) Write a typical chemical reaction for the reduction of iron oxide (Fe2O3) by carbon monoxide to produce iron. (c) Describe the basic oxygen process for converting pig iron into steel.
(a)
How is raw pig iron extracted from iron oxide ores?
Explanation of Solution
Raw pig iron is usually extracted from ores of iron oxide in a blast furnace in the presence of reducing agent. The typical reducing agent used in the blast furnace is coke. The produced pig iron contains nearly 4% of carbon.
(b)
Write a typical chemical reaction for the reduction of iron oxide by carbon monoxide to produce iron.
Explanation of Solution
Write chemical reaction for the reduction of iron oxide by carbon monoxide.
Here, iron oxide is
(c)
Describe the basic oxygen process for converting pig iron into steel.
Explanation of Solution
In the basic oxygen process, pig iron is changed into steel by the process of oxidation in a convertor of refractory-lined type. A lance of oxygen insert gives pure oxygen to perform a bathing of molten pig iron and scrapping of steel.
The formed iron oxide then reacts with the carbon in the steel to produce carbon monoxide.
Want to see more full solutions like this?
Chapter 9 Solutions
Foundations of Materials Science and Engineering
- For an Fe-0.35% C alloy, determine the composition and amount of each phase present at 726 ° C; and the composition and amount of each microconstituent present at 726 °C.arrow_forward1. What temperature does a Fe-C metal with less than 4 weight percent C melt at? 2. What temperature does a Fe-C metal with less than two weight percent C melt at? 3. What climate causes delta-Fe to change into gamma-Fe? 4. What percentage of proeutectoid Fe 3C is present in a steel with 1.15 wt% carbon at 727.1 o C?arrow_forwardA 80%Sn-20%Pb alloy is melted fully at 300°C and then slowly cooled down to 182°C. Sketch the microstructures at 300°C, 200°C, and 182°C, respectively. Label all phases and indicate their approximate compositions. Also, determine the follows for this alloy at 182°C. (1) The weight fractions of α and β phases.(2) The weight fractions of primary β and eutectic structure.(3) The weight fraction of eutectic β .arrow_forward
- 5 During decommissioning work, in order to determine the number of radionuclides deposited in a section of iron pipe, you grind up a small section of the pipe into a fine powder to carry out a reaction at 400 0C. Preliminary analysis shows that the predominant iron species are FeO and Fe2O3 Is it safe to use an aluminum crucible for heating your sample? What about a graphite crucible? Provide a short but detailed explanation referencing Ellingham diagrams, calculating Gibbs Free Energy, as well as provide any relevant reactions.arrow_forwardWhy are Ni3Al (γ') precipitates particularly effective at strengthening nickel-based superalloys?arrow_forward1)What is types of cast iron? Explain detail with;a)Elemental compositionb)Production methodc)Properties (Characteristic)d)Microstructersarrow_forward
- You are assured that a Pb-98.5%Sn alloy is good for a treatment of Aging, if we take that information as correct, will it be possible that an alloy Is Pb-10%Sn also very good for that treatment? Justify your answer.arrow_forwardCalculate the percentage of C and other alloying elements of the steel given the short designations 10CrMo910 and 45CrVMoW58arrow_forwardAnswer all the questions briefly 1. Define the term alloy and give an example. 2. Why is aluminum useful for aeroplane wings? 3. Why is cast iron useful for manhole covers? 4. Name the element that is added to iron to make mild steel. 5. Explain why copper might be suitable for the roof of a building.arrow_forward
- Is it possible to produce and iron-carbon alloy of eutectoid composition that has a minimum hardness of 200HRB and a minimum ductility of 25% RA? If so, describe the continuous cooling heat treatment to which the alloy would be subjected to achieve these properties. If it is not possible, explain why.arrow_forwardMake use of drawings of segments of the Fe-Cr phase diagram to illustrate the reason for theexistence of ferritic, martensitic and austenitic stainless steels by also noting the influence ofspecific alloying elements where applicable.arrow_forwardBriefly describe how precipitation hardening happens in Al alloys (how the microstructure evolves as annealing time increases). Why it first forms q” then q’ before q is finally formed? How does the alloy’s strength change during this process? What are the strengthening mechanisms?arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY