Textbook Question
Chapter 9.13, Problem 63AAP
A 0.90% C hypereutectoid plain-carbon steel is slowly cooled from 900°C to a temperature just slightly above 727°C. Calculate the weight percent proeutectoid cementite and weight percent austenite present in the steel.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A 0.25% C hypoeutectoid plain-carbon steel is slowly cooled from 950°C to a temperature just slightly below 723°C.(a) Calculate the weight percent proeutectoid ferrite in the steel.(b) Calculate the weight percent eutectoid ferrite and weight percent eutectoid cementite in the steel.
The chemical composition of X38CrMoV5-3 steel is given in the table below.
b) This steel is austenitized at 1050 ° C and hardened by giving water in oil (completely martensite structure has been formed and has a hardness of 57 HRC) and tempered at 510 ° C to reduce its hardness (54 HRC) and gain toughness. In addition, it is desired to harden the surface by nitration. In order to achieve the desired surface hardness, liquid nitration should be done at 600 ° C, gas nitration at 510 ° C and plasma nitration at 450 ° C. Which nitration method do you prefer? Why is that?
If a eutectoid steel sample is heated to 800°C and then quenched in a cold-water bath then
what would be the possible microstructure? Draw the microstructure and label it.
Chapter 9 Solutions
Foundations of Materials Science and Engineering
Ch. 9.13 - (a) How is raw pig iron extracted from iron oxide...Ch. 9.13 - (a) Why is the FeFe3C phase diagram a metastable...Ch. 9.13 - (a) What is the structure of pearlite? (b) Draw a...Ch. 9.13 - Distinguish between the following three types of...Ch. 9.13 - Prob. 5KCPCh. 9.13 - (a) Define an FeC martensite. (b) Describe the...Ch. 9.13 - (a) What is an isothermal transformation in the...Ch. 9.13 - How does the isothermal transformation diagram for...Ch. 9.13 - Draw a continuous-cooling transformation diagram...Ch. 9.13 - (a) Describe the full-annealing heat treatment for...
Ch. 9.13 - Describe the process-annealing heat treatment for...Ch. 9.13 - What is the normalizing heat treatment for steel...Ch. 9.13 - Describe the tempering process for a plain-carbon...Ch. 9.13 - (a) Describe the martempering (marquenching)...Ch. 9.13 - (a) Describe the austempering process for a...Ch. 9.13 - (a) Explain the numbering system used by the AISI...Ch. 9.13 - (a) What arc some of the limitations of...Ch. 9.13 - (a) What compounds docs aluminum form in steels?...Ch. 9.13 - Prob. 19KCPCh. 9.13 - (a) Define the hardenability of a steel. (b)...Ch. 9.13 - Prob. 21KCPCh. 9.13 - Prob. 22KCPCh. 9.13 - Prob. 23KCPCh. 9.13 - What is the difference between a coherent...Ch. 9.13 - Prob. 25KCPCh. 9.13 - Prob. 26KCPCh. 9.13 - Prob. 27KCPCh. 9.13 - (a) Describe the three principal casting processes...Ch. 9.13 - Prob. 29KCPCh. 9.13 - Prob. 30KCPCh. 9.13 - Prob. 31KCPCh. 9.13 - Prob. 32KCPCh. 9.13 - Prob. 33KCPCh. 9.13 - Prob. 34KCPCh. 9.13 - Prob. 35KCPCh. 9.13 - (a) What are the cast irons? (b) What is their...Ch. 9.13 - Prob. 37KCPCh. 9.13 - Prob. 38KCPCh. 9.13 - Prob. 39KCPCh. 9.13 - Prob. 40KCPCh. 9.13 - Prob. 41KCPCh. 9.13 - Prob. 42KCPCh. 9.13 - Prob. 43KCPCh. 9.13 - Prob. 44KCPCh. 9.13 - Prob. 45KCPCh. 9.13 - (a) Why arc titanium and its alloys of special...Ch. 9.13 - Prob. 47KCPCh. 9.13 - Prob. 48KCPCh. 9.13 - Prob. 49KCPCh. 9.13 - Prob. 50KCPCh. 9.13 - Prob. 51KCPCh. 9.13 - Prob. 52KCPCh. 9.13 - Describe the structural changes that take place...Ch. 9.13 - Describe the structural changes that take place...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - (a) What types of microstructures arc produced by...Ch. 9.13 - A 0.65 % C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A 0.25% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A plain-carbon steel contains 93 wt % ferrite7 wt%...Ch. 9.13 - A plain-carbon steel contains 45 wt% proeutectoid...Ch. 9.13 - A plain-carbon steel contains 5.9 wt%...Ch. 9.13 - A 0.90% C hypereutectoid plain-carbon steel is...Ch. 9.13 - A 1.10% C hypereutectoid plain-carbon steel is...Ch. 9.13 - If a hypereutectoid plain-carbon steel contains...Ch. 9.13 - A hypereutectoid plain-carbon steel contains 10.7...Ch. 9.13 - A plain-carbon steel contains 20.0 wt%...Ch. 9.13 - A 0.55% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A hypoeutectoid steel contains 44.0 wt% eutectoid...Ch. 9.13 - A hypoeutectoid steel contains 24.0 wt% eutectoid...Ch. 9.13 - A 1.10 % C hypereutectoid plain-carbon steel is...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Thin pieces of 0.3-mm-thick hot-rolled strips of...Ch. 9.13 - Prob. 75AAPCh. 9.13 - Prob. 76AAPCh. 9.13 - Prob. 77AAPCh. 9.13 - Prob. 78AAPCh. 9.13 - Prob. 79AAPCh. 9.13 - Prob. 80AAPCh. 9.13 - Prob. 81AAPCh. 9.13 - Prob. 82AAPCh. 9.13 - An austenitized 40-mm-diameter 4340 steel bar is...Ch. 9.13 - Prob. 84AAPCh. 9.13 - Prob. 85AAPCh. 9.13 - Prob. 86AAPCh. 9.13 - Prob. 87AAPCh. 9.13 - Prob. 88AAPCh. 9.13 - Prob. 89AAPCh. 9.13 - Prob. 90AAPCh. 9.13 - Prob. 91AAPCh. 9.13 - Prob. 92AAPCh. 9.13 - (a) For a plain-carbon steel with 1 wt % carbon...Ch. 9.13 - Prob. 94SEPCh. 9.13 - Prob. 95SEPCh. 9.13 - Prob. 96SEPCh. 9.13 - Prob. 97SEPCh. 9.13 - Prob. 98SEPCh. 9.13 - Prob. 99SEPCh. 9.13 - Prob. 100SEPCh. 9.13 - Prob. 101SEPCh. 9.13 - Prob. 102SEPCh. 9.13 - Prob. 103SEPCh. 9.13 - Both 4140 and 4340 steel alloys may be tempered to...Ch. 9.13 - Prob. 105SEPCh. 9.13 - Aircraft fuselage is made of aluminum alloys 2024...Ch. 9.13 - Prob. 107SEPCh. 9.13 - Prob. 108SEPCh. 9.13 - Prob. 109SEPCh. 9.13 - (a) What makes austenitic stainless steels that...Ch. 9.13 - Prob. 111SEPCh. 9.13 - Prob. 112SEPCh. 9.13 - Prob. 113SEPCh. 9.13 - (a) Give examples of components or products that...Ch. 9.13 - Prob. 115SEPCh. 9.13 - Prob. 116SEPCh. 9.13 - Prob. 117SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- 3.The TTT diagram of a plain carbon steel is given in Fig. 1. Identify whether this steel is a hypoeutectoid, eutectoid or hypereutectoid steel. Explain why the transformation happens slowly at 850°C as well as at 300°C. Determine the microstructures expected in this type of steel after the following heat treatment processes. a) Austenize at 900°C, quench to 400°C and hold for 1000 s and quench to 25°C. b) Austenize at 900°C, quench to 25°C. c) Austenize at 900°C, quench to 675°C and hold for 1 s, quench to 400°C and hold for 900 s and slowly cool to 25°C. 900 Acm Cs 800 A1 FezC + Y 33 Fe3C + pearlite 45 700 Ps 600 ++ Fe3C + pearlite Y+ bainite Bs 500 46 Bainite 400 Yu Bf 300 57 Ms 200 60 Mf Y+ martensite 100 62 Martensite 102 65 103 104 105 106 0.1 1 10 Time (s) Fig. 1 Temperature (°C) Rockwell C hardnessarrow_forwardExplain the phases shown in the attached image of a stress strain cureve for 0.15% carbon steelarrow_forwardIf a 0.80 percent plain carbon steel is austenitized (heated to a read heat) and quenched in water to room temperatures so that the cooling curve does not cut into the “nose” of the I-T diagram, what will the resultant microstructure be?arrow_forward
- A 1.05% C steel is slowly cooled from 900 °C to temperature just slightly above 723 °C. Calculate the weight percent of cementite and the weight percent of austenite presents in the steelarrow_forwardDescribe the final microstructure obtained in a 1050 steel after heat at 8200C, cooled to 7000C and hold for 5 s, cooled to room temperature. 900- a+y 800 A, 700 A1 F, Pr a+ pearlite 23 600 -y+a+pearlite 30 500 B1 y+ bainite Bainite 39 F=Ferrite B, M, 400 49 P=Pearlite 300 Y+ martensite B=Bainite 200 Martensite M=Martensite 62 100- 102 10 10 10 10 0.1 1 10 Time (s) TTT curve for carbon steel AISI 1050 Temperature (°C) Rockwell C hardnessarrow_forwardDetermine the tensile strength, yield strength and percentage elongation (% ductility) for an iron- carbon alloy with 0.76 wt % carbon composition. O Yield strength - 60000 psi : Tensile strength - 110000 psi: Ductility - 15% O Yield strength - 130000 psi : Tensile strength - 68000 psi;: Ductility - 10% O Yield strength - 68000 psi : Tensile strength - 130000 psi; Ductility - 10% O Yield strength 50000 psi: Tensile strength - 100000 psi: Ductility - 20% O Yield strength - 86000 psi : Tensile strength 150000 psi: Ductility 25%arrow_forward
- A steel contains 18% pearlite and 82%primary ferrite at room temperature. Esti-mate the carbon content of the steel. Is thesteel hypoeutectoid or hypereutectoid?arrow_forwardA 609 g eutectoid steel ( about 0.8%C) is heated to 1,002 C and cooled slowly through the eutectorid temperature. This results in the formation of cementite Fe3C (6.67%C) and ferrite (0.025%C). Calculate the number of grams of cementite that form in the steel.arrow_forwardThis equilibrium phase of steel only occurs at temperatures above 723° C: martensite ferrite austenite O cementitearrow_forward
- What is the% C ratio of two different steels with 80% and equal austenite content at 724 Celsius?arrow_forwardDetermine the quenching and normalizing process temperatures of 2 different steels containing 0.6% C and 1.3% C (Ac3 and Acm will be considered linear)arrow_forward2 By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- Find the Eutectic, Eutectoid temperature of cast iron with 4.3% C 2- The microstructure of Cast iron with 3.5% C. 3- Find the melting point and microstructure of steel with 0.83% C 4- Define the temperature range for Acm temperature. 5- Find the AC3, Ac¡ temperature of steel with 0.45% C 6- The Liquid and Austinite percent with chemical composition for cast iron with 2.3% C at 1300°Carrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Relationship Between Elastic Constants and Connecting Equations; Author: Engineers Academy;https://www.youtube.com/watch?v=whW5PnM7Pug;License: Standard Youtube License