Chapter 9.13, Problem 110SEP
(a) What makes austenitic stainless steels that are cooled slowly through the 870°C to 600°C range become susceptible to intergranular corrosion? (b) How can the intergranular susceptibility of slow-cooled austenitic stainless steels be prevented?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
The chemical composition of X38CrMoV5-3 steel is given in the table below.
b) This steel is austenitized at 1050 ° C and hardened by giving water in oil (completely martensite structure has been formed and has a hardness of 57 HRC) and tempered at 510 ° C to reduce its hardness (54 HRC) and gain toughness. In addition, it is desired to harden the surface by nitration. In order to achieve the desired surface hardness, liquid nitration should be done at 600 ° C, gas nitration at 510 ° C and plasma nitration at 450 ° C. Which nitration method do you prefer? Why is that?
Question: 4
A sheet of copper is exposed to oxygen at 1000°C. After 100 h, 0.245 g of copper are lost per
cm' of surface area; after 250 h, 0.385 g/ cm² are lost; and after 500 h, 0.560 g/ em are lost.
i. Determine whether oxidation is parabolic, linear, or logarithmic
ii. Calculate the time required for a 0.76-cm sheet of copper to be completely oxidized. The
sheet of copper is oxidized from both sides.
A 1.5-kg specimen of a 88 wt% Pb-12 wt% Sn alloy (Animated Figure 9.8) is heated to 220°C; at this temperature it is entirely an a-
phase solid solution. The alloy is to be melted to the extent that 50% of the specimen is liquid, the remainder being the a phase. This
may be accomplished either by heating the alloy or changing its composition while holding the temperature constant.
(a) To what temperature must the specimen be heated?
i
°C
(b) How much tin must be added to the 1.5-kg specimen at 220°C to achieve this state?
i
kg
Chapter 9 Solutions
Foundations of Materials Science and Engineering
Ch. 9.13 - (a) How is raw pig iron extracted from iron oxide...Ch. 9.13 - (a) Why is the FeFe3C phase diagram a metastable...Ch. 9.13 - (a) What is the structure of pearlite? (b) Draw a...Ch. 9.13 - Distinguish between the following three types of...Ch. 9.13 - Prob. 5KCPCh. 9.13 - (a) Define an FeC martensite. (b) Describe the...Ch. 9.13 - (a) What is an isothermal transformation in the...Ch. 9.13 - How does the isothermal transformation diagram for...Ch. 9.13 - Draw a continuous-cooling transformation diagram...Ch. 9.13 - (a) Describe the full-annealing heat treatment for...
Ch. 9.13 - Describe the process-annealing heat treatment for...Ch. 9.13 - What is the normalizing heat treatment for steel...Ch. 9.13 - Describe the tempering process for a plain-carbon...Ch. 9.13 - (a) Describe the martempering (marquenching)...Ch. 9.13 - (a) Describe the austempering process for a...Ch. 9.13 - (a) Explain the numbering system used by the AISI...Ch. 9.13 - (a) What arc some of the limitations of...Ch. 9.13 - (a) What compounds docs aluminum form in steels?...Ch. 9.13 - Prob. 19KCPCh. 9.13 - (a) Define the hardenability of a steel. (b)...Ch. 9.13 - Prob. 21KCPCh. 9.13 - Prob. 22KCPCh. 9.13 - Prob. 23KCPCh. 9.13 - What is the difference between a coherent...Ch. 9.13 - Prob. 25KCPCh. 9.13 - Prob. 26KCPCh. 9.13 - Prob. 27KCPCh. 9.13 - (a) Describe the three principal casting processes...Ch. 9.13 - Prob. 29KCPCh. 9.13 - Prob. 30KCPCh. 9.13 - Prob. 31KCPCh. 9.13 - Prob. 32KCPCh. 9.13 - Prob. 33KCPCh. 9.13 - Prob. 34KCPCh. 9.13 - Prob. 35KCPCh. 9.13 - (a) What are the cast irons? (b) What is their...Ch. 9.13 - Prob. 37KCPCh. 9.13 - Prob. 38KCPCh. 9.13 - Prob. 39KCPCh. 9.13 - Prob. 40KCPCh. 9.13 - Prob. 41KCPCh. 9.13 - Prob. 42KCPCh. 9.13 - Prob. 43KCPCh. 9.13 - Prob. 44KCPCh. 9.13 - Prob. 45KCPCh. 9.13 - (a) Why arc titanium and its alloys of special...Ch. 9.13 - Prob. 47KCPCh. 9.13 - Prob. 48KCPCh. 9.13 - Prob. 49KCPCh. 9.13 - Prob. 50KCPCh. 9.13 - Prob. 51KCPCh. 9.13 - Prob. 52KCPCh. 9.13 - Describe the structural changes that take place...Ch. 9.13 - Describe the structural changes that take place...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - (a) What types of microstructures arc produced by...Ch. 9.13 - A 0.65 % C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A 0.25% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A plain-carbon steel contains 93 wt % ferrite7 wt%...Ch. 9.13 - A plain-carbon steel contains 45 wt% proeutectoid...Ch. 9.13 - A plain-carbon steel contains 5.9 wt%...Ch. 9.13 - A 0.90% C hypereutectoid plain-carbon steel is...Ch. 9.13 - A 1.10% C hypereutectoid plain-carbon steel is...Ch. 9.13 - If a hypereutectoid plain-carbon steel contains...Ch. 9.13 - A hypereutectoid plain-carbon steel contains 10.7...Ch. 9.13 - A plain-carbon steel contains 20.0 wt%...Ch. 9.13 - A 0.55% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A hypoeutectoid steel contains 44.0 wt% eutectoid...Ch. 9.13 - A hypoeutectoid steel contains 24.0 wt% eutectoid...Ch. 9.13 - A 1.10 % C hypereutectoid plain-carbon steel is...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Thin pieces of 0.3-mm-thick hot-rolled strips of...Ch. 9.13 - Prob. 75AAPCh. 9.13 - Prob. 76AAPCh. 9.13 - Prob. 77AAPCh. 9.13 - Prob. 78AAPCh. 9.13 - Prob. 79AAPCh. 9.13 - Prob. 80AAPCh. 9.13 - Prob. 81AAPCh. 9.13 - Prob. 82AAPCh. 9.13 - An austenitized 40-mm-diameter 4340 steel bar is...Ch. 9.13 - Prob. 84AAPCh. 9.13 - Prob. 85AAPCh. 9.13 - Prob. 86AAPCh. 9.13 - Prob. 87AAPCh. 9.13 - Prob. 88AAPCh. 9.13 - Prob. 89AAPCh. 9.13 - Prob. 90AAPCh. 9.13 - Prob. 91AAPCh. 9.13 - Prob. 92AAPCh. 9.13 - (a) For a plain-carbon steel with 1 wt % carbon...Ch. 9.13 - Prob. 94SEPCh. 9.13 - Prob. 95SEPCh. 9.13 - Prob. 96SEPCh. 9.13 - Prob. 97SEPCh. 9.13 - Prob. 98SEPCh. 9.13 - Prob. 99SEPCh. 9.13 - Prob. 100SEPCh. 9.13 - Prob. 101SEPCh. 9.13 - Prob. 102SEPCh. 9.13 - Prob. 103SEPCh. 9.13 - Both 4140 and 4340 steel alloys may be tempered to...Ch. 9.13 - Prob. 105SEPCh. 9.13 - Aircraft fuselage is made of aluminum alloys 2024...Ch. 9.13 - Prob. 107SEPCh. 9.13 - Prob. 108SEPCh. 9.13 - Prob. 109SEPCh. 9.13 - (a) What makes austenitic stainless steels that...Ch. 9.13 - Prob. 111SEPCh. 9.13 - Prob. 112SEPCh. 9.13 - Prob. 113SEPCh. 9.13 - (a) Give examples of components or products that...Ch. 9.13 - Prob. 115SEPCh. 9.13 - Prob. 116SEPCh. 9.13 - Prob. 117SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- What factors determine the Debye temperature of a particular element? Provide comments,with sufficient details, on the choice of factors.arrow_forwardIn a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the total and partial phases? Given:Eutectoid temperature=723°C; Eutectoid concentration=0.76% C; Limit concentration of ferrite=0.022%; Limiting concentration of cementite: 6.7%.arrow_forwardA 609 g eutectoid steel ( about 0.8%C) is heated to 1,002 C and cooled slowly through the eutectorid temperature. This results in the formation of cementite Fe3C (6.67%C) and ferrite (0.025%C). Calculate the number of grams of cementite that form in the steel.arrow_forward
- Analyze the development of microstructure in Iron-Carbon alloys.arrow_forward4. Give the temperature range over which it is possible to austenitize each of the following Fe-C alloys during full anneal heat treatment (a) 0.20 wt% C (b) 0.60 wt% C (c) 0.95 wt% Carrow_forwardA 6061-T4 aluminum alloy is to be used to make a thin-walled cylindrical canister in which high-pressure chemical reactions will be performed. The design calls for a diameter of 50 cm, a length of 80 cm, and a maximum operating pressure of 5 MPa. Assume a safety factor of four is required (i.e., the maximum stress can never exceed onequarter of the alloy’s yield strength). a. What wall thickness is required to ensure safe operation? b. Is this wall thickness a maximum or a minimum? Explain. c. How do your answers change if the cylinder is made twice as long?arrow_forward
- What kinds of dispersion hardened alloys can retain their strength up to 1000 ° C?arrow_forwardQuestion 4 (a): The figure below shows the Pourbaix diagram of copper in water. Will copper corrode in deaerated water? Justify your answer using the diagram. 2.2 E(v) 2 7 8 9 10 11 12 13 14 15 16 2.2 2 o 2 4 6 4 2 1.8 1.8 1.6 1.6 1.4 1.4 (b} 1.2 Cuo 1.2 1 0.8 Cutt 0.8 0.6 0.6 0.4 HCUO2 0.4 0.2 0.2 CuO2 0 2 4 6 (a) Cu2O Cu* -0.2 Cu -0.2 -0.4 -0.4 -0.6 -0.6 -0.8 -0.8 -1 -1 -1.2 -1.2 -1.4 -1.4 -1.6 -1.6 -1.8 -2 -1 0 1 2 3 4 -1.8 9 10 11 12 13 14 15 16 pH 5 6 7 8 (e) Copperarrow_forward7. Consider 1.5 kg of a 99.6 wt% Fe-0.4 wt% C steel that is cooled to a temperature just below the eutectoid. (a) How many kilograms of ferrite (a) form? (b) How many kilograms of cementite (Fe;C) form? Include your tie line in the solution. 1600| L 1400 T(°C) 1200 (austenite) y+L 1148°C L+Fe;C 1000 Y + Fe;C 800 727°C 600 a + Fe;C 400 1 2 4 6 6.7 C, wt% C Fe;C (cementite)arrow_forward
- List the phase(s) that are present, the phase composition(s) and the weight fractions of the phase(s) for each of the following alloys:(a) 70 wt% Zn-30 wt% Cu at 300 C (b) 90 wt% Pb-10 wt% Sn at 325 C (c) 2.5 kg Cu and 5.0 kg Ag at 900 C (d) 37 lbm Pb and 6.5 lbm Mg at 500 Carrow_forwardFor an Fe-0.35% C alloy, determine (a) the temperature at which austenite first begins to transform on cooling; (b) the primary microconstituent that forms; (c) the composition and amount of each phase present at 728 °C; (d) the composition and amount of each phase present at 726 ° C; and (e) the composition and amount of each microconstituent present at 726 °C.arrow_forwardQuestion-3 If 500 g of a 40 wt % Ag - 60 wt % Cu alloy is slowly cooled from 1000°C to just below 780°C: (a) How many grams of liquid and proeutectic alpha are present at 850°C? (b) How many grams of liquid and proeutectic alpha are present at 780°C + AT ? (c) How many grams of alpha are present in the eutectic structure at 780°C - AT ? (d) How many grams of beta are present in the eutectic structure at 780°C - AT ? Atomic percent silver °C °F 10 20 30 40 50 60 70 80 90 1100 1084.5 1900 1000 961.93 1700 900 L+a 1600 L+B 800 780 1400 7.9 719 91.2 700 1200 600 a+B 1000 500 850 400 Cu 10 30 40 50 60 70 80 90 Ag Weight percent silver 20arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Materials Science Mechanical Engineering - Part 3 Corrosion Explained; Author: Mega Mechatronics;https://www.youtube.com/watch?v=Il-abRhrzFY;License: Standard Youtube License