Question
Chapter 9.13, Problem 103SEP
(a)
To determine
Why austenitic stainless steel is more resistant to corrosion than ferritic and martensitic.
(b)
To determine
Martensitic stainless steel be heat treated to higher strengths than ferritic and austenitic.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
1.
a) Explain why plain carbon steel has a numbers of application as engineering materials, even though it does not have a corrosion resistance.
b) Explain the reasons why aluminum is used as the material for vessel in cryogenic applications.
A material is required as heating elements for an electrical resistance furnace for heat treating steels. Make and list appropriate assumptions for temperature and furnace environment. List what you would judge to be the design-limiting properties. Name three candidate heating element materials.
Of the following alloys, pick the one(s) thatmay be strengthened by heat treatment,cold work, or both: R50250 titanium, AZ31Bmagnesium, 6061 aluminum, C51000 phos-phor bronze, lead, 6150 steel, 304 stainlesssteel, and C17200 beryllium copper.
Chapter 9 Solutions
Foundations of Materials Science and Engineering
Ch. 9.13 - (a) How is raw pig iron extracted from iron oxide...Ch. 9.13 - (a) Why is the FeFe3C phase diagram a metastable...Ch. 9.13 - (a) What is the structure of pearlite? (b) Draw a...Ch. 9.13 - Distinguish between the following three types of...Ch. 9.13 - Prob. 5KCPCh. 9.13 - (a) Define an FeC martensite. (b) Describe the...Ch. 9.13 - (a) What is an isothermal transformation in the...Ch. 9.13 - How does the isothermal transformation diagram for...Ch. 9.13 - Draw a continuous-cooling transformation diagram...Ch. 9.13 - (a) Describe the full-annealing heat treatment for...
Ch. 9.13 - Describe the process-annealing heat treatment for...Ch. 9.13 - What is the normalizing heat treatment for steel...Ch. 9.13 - Describe the tempering process for a plain-carbon...Ch. 9.13 - (a) Describe the martempering (marquenching)...Ch. 9.13 - (a) Describe the austempering process for a...Ch. 9.13 - (a) Explain the numbering system used by the AISI...Ch. 9.13 - (a) What arc some of the limitations of...Ch. 9.13 - (a) What compounds docs aluminum form in steels?...Ch. 9.13 - Prob. 19KCPCh. 9.13 - (a) Define the hardenability of a steel. (b)...Ch. 9.13 - Prob. 21KCPCh. 9.13 - Prob. 22KCPCh. 9.13 - Prob. 23KCPCh. 9.13 - What is the difference between a coherent...Ch. 9.13 - Prob. 25KCPCh. 9.13 - Prob. 26KCPCh. 9.13 - Prob. 27KCPCh. 9.13 - (a) Describe the three principal casting processes...Ch. 9.13 - Prob. 29KCPCh. 9.13 - Prob. 30KCPCh. 9.13 - Prob. 31KCPCh. 9.13 - Prob. 32KCPCh. 9.13 - Prob. 33KCPCh. 9.13 - Prob. 34KCPCh. 9.13 - Prob. 35KCPCh. 9.13 - (a) What are the cast irons? (b) What is their...Ch. 9.13 - Prob. 37KCPCh. 9.13 - Prob. 38KCPCh. 9.13 - Prob. 39KCPCh. 9.13 - Prob. 40KCPCh. 9.13 - Prob. 41KCPCh. 9.13 - Prob. 42KCPCh. 9.13 - Prob. 43KCPCh. 9.13 - Prob. 44KCPCh. 9.13 - Prob. 45KCPCh. 9.13 - (a) Why arc titanium and its alloys of special...Ch. 9.13 - Prob. 47KCPCh. 9.13 - Prob. 48KCPCh. 9.13 - Prob. 49KCPCh. 9.13 - Prob. 50KCPCh. 9.13 - Prob. 51KCPCh. 9.13 - Prob. 52KCPCh. 9.13 - Describe the structural changes that take place...Ch. 9.13 - Describe the structural changes that take place...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - If a thin sample of a eutectoid plain-carbon steel...Ch. 9.13 - (a) What types of microstructures arc produced by...Ch. 9.13 - A 0.65 % C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A 0.25% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A plain-carbon steel contains 93 wt % ferrite7 wt%...Ch. 9.13 - A plain-carbon steel contains 45 wt% proeutectoid...Ch. 9.13 - A plain-carbon steel contains 5.9 wt%...Ch. 9.13 - A 0.90% C hypereutectoid plain-carbon steel is...Ch. 9.13 - A 1.10% C hypereutectoid plain-carbon steel is...Ch. 9.13 - If a hypereutectoid plain-carbon steel contains...Ch. 9.13 - A hypereutectoid plain-carbon steel contains 10.7...Ch. 9.13 - A plain-carbon steel contains 20.0 wt%...Ch. 9.13 - A 0.55% C hypoeutectoid plain-carbon steel is...Ch. 9.13 - A hypoeutectoid steel contains 44.0 wt% eutectoid...Ch. 9.13 - A hypoeutectoid steel contains 24.0 wt% eutectoid...Ch. 9.13 - A 1.10 % C hypereutectoid plain-carbon steel is...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Draw timetemperature cooling paths for a 1080...Ch. 9.13 - Thin pieces of 0.3-mm-thick hot-rolled strips of...Ch. 9.13 - Prob. 75AAPCh. 9.13 - Prob. 76AAPCh. 9.13 - Prob. 77AAPCh. 9.13 - Prob. 78AAPCh. 9.13 - Prob. 79AAPCh. 9.13 - Prob. 80AAPCh. 9.13 - Prob. 81AAPCh. 9.13 - Prob. 82AAPCh. 9.13 - An austenitized 40-mm-diameter 4340 steel bar is...Ch. 9.13 - Prob. 84AAPCh. 9.13 - Prob. 85AAPCh. 9.13 - Prob. 86AAPCh. 9.13 - Prob. 87AAPCh. 9.13 - Prob. 88AAPCh. 9.13 - Prob. 89AAPCh. 9.13 - Prob. 90AAPCh. 9.13 - Prob. 91AAPCh. 9.13 - Prob. 92AAPCh. 9.13 - (a) For a plain-carbon steel with 1 wt % carbon...Ch. 9.13 - Prob. 94SEPCh. 9.13 - Prob. 95SEPCh. 9.13 - Prob. 96SEPCh. 9.13 - Prob. 97SEPCh. 9.13 - Prob. 98SEPCh. 9.13 - Prob. 99SEPCh. 9.13 - Prob. 100SEPCh. 9.13 - Prob. 101SEPCh. 9.13 - Prob. 102SEPCh. 9.13 - Prob. 103SEPCh. 9.13 - Both 4140 and 4340 steel alloys may be tempered to...Ch. 9.13 - Prob. 105SEPCh. 9.13 - Aircraft fuselage is made of aluminum alloys 2024...Ch. 9.13 - Prob. 107SEPCh. 9.13 - Prob. 108SEPCh. 9.13 - Prob. 109SEPCh. 9.13 - (a) What makes austenitic stainless steels that...Ch. 9.13 - Prob. 111SEPCh. 9.13 - Prob. 112SEPCh. 9.13 - Prob. 113SEPCh. 9.13 - (a) Give examples of components or products that...Ch. 9.13 - Prob. 115SEPCh. 9.13 - Prob. 116SEPCh. 9.13 - Prob. 117SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Explain how intergranular precipitation leads to intergranular Stress corrosion cracking (IG Stress corrosion cracking) in austenitic stainless steel? ( explain deeply with step by step and type the answer.)arrow_forwardProblem 1 A 0.65 percent C hypoeutectoid plain-carbon steel is slowly cooled from about 950°C to a temperature just slightly above 723°C. Calculate the weight percent austenite and weight percent proeutectoid ferrite in this steel. a +y a a 0.02% C 0.65% C 0.80% Carrow_forward1 Plastic Deformation Occurs Through Dislocation Motion... ...so in order to make a material stronger, we should prevent dislocations from moving. For each of the following alloys, identify the strengthening mechanism and explain how it impedes dislocation motion: A. An aluminum alloy "inoculated" with TiB2 during solidification, producing a large number of small grains. B. Monel, a corrosion-resistant solid solution of Ni and Cu. C. An aluminum-lithium aerospace alloy containing precipitates of Al3Li. D. Wrought iron, which is often worked into complex shapes such as railings or furniture.arrow_forward
- Explain the phases shown in the attached image of a stress strain cureve for 0.15% carbon steelarrow_forwardWhy does chromium in stainless steel make them more corrosion resistant in many environments than plain carbon steelarrow_forward(a) Using sketches, describe the carburisation process for steel components.(b) The yield stress for a metal changes from 450 Nmm-2to 610 Nmm-2 when the average grain diameter decrease from 0.043 mm to 0.022 mm. Determine the yield stressfor the same metal with an average grain diameter of 0.030 mm.(c) From the point of view of corrosion, Describe and discuss, using sketches andexamples the use of metallic coatings.(d) Discuss the advantages and disadvantages of hot and cold working of metals.(e) Describe and discuss the ionic bonding process.2. (a) A polypropylene specimen has a mass of 28 kg and density of 1.65x103 kgm-3.Determine the crystallinity by weight of the specimen.Use the following information,Density of the crystalline phase = 1.77x103 kgm-3Density of the amorphous phase = 1.43x103 kgm-3(b) A standard Vickers Hardness test was conducted on a metal specimen. Determine theVicker’s hardness number and the tensile stress of the specimen. The applied loadwas 10 kgf, and the…arrow_forward
- 1. Determine working stresses for the two alloys that have the stress–strain behaviors shown in Figures 6.22.arrow_forwardExplain what should be corrosion potential of galvanized steel which zinc layer has been removed and polished in 0.5M NaCl solution?arrow_forwardA steel contains 18% pearlite and 82% primary ferrite at room temperature. Estimate the carbon content of the steel. Is the steel hypoeutectoid or hypereutectoid?arrow_forward
- 4. Which surface property is crucial for the corrosion resistance of metallic biomaterials? has 6. What is the significant advantage of 316L stainless steel over other grades of stainless steel? Explain your answer.arrow_forwardThe chemical composition of X38CrMoV5-3 steel is given in the table below. b) This steel is austenitized at 1050 ° C and hardened by giving water in oil (completely martensite structure has been formed and has a hardness of 57 HRC) and tempered at 510 ° C to reduce its hardness (54 HRC) and gain toughness. In addition, it is desired to harden the surface by nitration. In order to achieve the desired surface hardness, liquid nitration should be done at 600 ° C, gas nitration at 510 ° C and plasma nitration at 450 ° C. Which nitration method do you prefer? Why is that?arrow_forwardAt room temperature, the steel contains 18% cementite and 82% ferrite. Calculate the amount of carbon in the steel and determine whether it is hypo-eutectoid or hyper-eutectoid.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Materials Science Mechanical Engineering - Part 3 Corrosion Explained; Author: Mega Mechatronics;https://www.youtube.com/watch?v=Il-abRhrzFY;License: Standard Youtube License