Question
Chapter 6.13, Problem 59AAP
a)
To determine
The percent of cold work to attain a tensile strength of 50 ksi has to be determined.
b)
To determine
The initial diameter of the rod has to be determined.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
3. A 30-cm long, 12-mm diameter carbon steel rod was
subjected to 15.5 kN of tension. Calculate (a) the stress and
strain in the rod, (b) the amount that it stretches, (c) its
change in diameter, and (d) its stiffness (k=EA/L). (e) If the
force was only 4.5 kN, by what amount would the rod have
stretched?
Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20).
If we use a 4340; 4140; 8640; 5140; 1040 steel, what would be the hardness
number at the center of the part?
1) How much stress will be generated in the 13mm diameter aluminum rod below with an increase in
temperature of 30 degress C?
- Look up the coefficient of thermal expansion and elastic modulus for aluminum (SI units) in the book.
- Calculate the temperature increase it would take for the aluminum rod to expand an contact the wall.
- Subtract that number from the temperature change given to see how much of our temperature change
will be after this contact and generate stress.
- Calculate the stress generated in that rod due to that excess temperature increase.
- Compare your answer: 13.89 MPa
0.5 mm-
L = 1 m
Chapter 6 Solutions
Foundations of Materials Science and Engineering
Ch. 6.13 - (a) How are metal alloys made by the casting...Ch. 6.13 - Why are cast metal sheet ingots hot-rolled first...Ch. 6.13 - What type of heat treatment is given to the rolled...Ch. 6.13 - Describe and illustrate the following types of...Ch. 6.13 - Describe the forging process. What is the...Ch. 6.13 - What is the difference between open-die and...Ch. 6.13 - Describe the wire-drawing process. Why is it...Ch. 6.13 - Distinguish between elastic and plastic...Ch. 6.13 - Define (a) engineering stress and strain and (b)...Ch. 6.13 - Define (a) modulus of elasticity, (b) yield...
Ch. 6.13 - (a) Define the hardness of a metal. (b) How is the...Ch. 6.13 - What types of indenters are used in (a) the...Ch. 6.13 - What are slipbands and slip lines? What causes the...Ch. 6.13 - Describe the slip mechanism that enables a metal...Ch. 6.13 - (a) Why does slip in metals usually take place on...Ch. 6.13 - Prob. 16KCPCh. 6.13 - What other types of slip planes are important...Ch. 6.13 - Define the critical resolved shear stress for a...Ch. 6.13 - Describe the deformation twinning process that...Ch. 6.13 - What is the difference between the slip and...Ch. 6.13 - Prob. 21KCPCh. 6.13 - Prob. 22KCPCh. 6.13 - What experimental evidence shows that grain...Ch. 6.13 - (a) Describe the grain shape changes that occur...Ch. 6.13 - How is the ductility of a metal normally affected...Ch. 6.13 - (a) What is solid-solution strengthening? Describe...Ch. 6.13 - What are the three main metallurgical stages that...Ch. 6.13 - Describe the microstructure of a heavily...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Prob. 33KCPCh. 6.13 - Prob. 34KCPCh. 6.13 - Prob. 35KCPCh. 6.13 - Prob. 36KCPCh. 6.13 - Prob. 37KCPCh. 6.13 - Why are nanocrystalline materials stronger? Answer...Ch. 6.13 - A 70% Cu30% Zn brass sheet is 0.0955 cm thick and...Ch. 6.13 - A sheet of aluminum alloy is cold-rolled 30% to a...Ch. 6.13 - Calculate the percent cold reduction when an...Ch. 6.13 - Prob. 42AAPCh. 6.13 - What is the relationship between engineering...Ch. 6.13 - A tensile specimen of cartridge brass sheet has a...Ch. 6.13 - A 0.505-in.-diameter rod of an aluminum alloy is...Ch. 6.13 - In Figure 6.23, estimate the toughness of SAE 1340...Ch. 6.13 - The following engineering stress-strain data were...Ch. 6.13 - Prob. 49AAPCh. 6.13 - A 0.505-in.-diameter aluminum alloy test bar is...Ch. 6.13 - A 20-cm-long rod with a diameter of 0.250 cm is...Ch. 6.13 - Prob. 52AAPCh. 6.13 - Prob. 53AAPCh. 6.13 - Prob. 54AAPCh. 6.13 - Prob. 55AAPCh. 6.13 - Prob. 56AAPCh. 6.13 - A specimen of commercially pure titanium has a...Ch. 6.13 - Prob. 58AAPCh. 6.13 - Prob. 59AAPCh. 6.13 - Prob. 60AAPCh. 6.13 - Prob. 61AAPCh. 6.13 - Prob. 62AAPCh. 6.13 - Prob. 63AAPCh. 6.13 - Prob. 64AAPCh. 6.13 - Prob. 65SEPCh. 6.13 - Prob. 66SEPCh. 6.13 - A 20-mm-diameter, 350-mm-long rod made of an...Ch. 6.13 - Prob. 68SEPCh. 6.13 - Prob. 69SEPCh. 6.13 - Consider casting a cube and a sphere on the same...Ch. 6.13 - When manufacturing complex shapes using cold...Ch. 6.13 - Prob. 74SEPCh. 6.13 - Draw a generic engineering stress-strain diagram...Ch. 6.13 - (a) Draw a generic engineering stress-strain...Ch. 6.13 - Prob. 77SEPCh. 6.13 - Prob. 78SEPCh. 6.13 - Prob. 79SEPCh. 6.13 - The material for a rod of cross-sectional area...Ch. 6.13 - What do E, G, v, Ur, and toughness tell you about...Ch. 6.13 - A cylindrical component is loaded in tension until...Ch. 6.13 - Referring to Figures 6.20 and 6.21 (read the...Ch. 6.13 - (a) Show, using the definition of the Poissons...Ch. 6.13 - A one-inch cube of tempered stainless steel (alloy...Ch. 6.13 - Prob. 87SEPCh. 6.13 - Prob. 88SEPCh. 6.13 - Prob. 89SEPCh. 6.13 - Prob. 90SEPCh. 6.13 - Prob. 91SEPCh. 6.13 - Prob. 92SEPCh. 6.13 - Prob. 93SEPCh. 6.13 - Prob. 94SEPCh. 6.13 - Starting with a 2-in.-diameter rod of brass, we...Ch. 6.13 - Prob. 96SEPCh. 6.13 - Prob. 97SEPCh. 6.13 - Prob. 98SEPCh. 6.13 - The cupro-nickel substitutional solid solution...Ch. 6.13 - Prob. 100SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A ductile cast-iron bar is to support a load of 178 kN in a heat-treating furnace used to make malleable cast iron. The bar is located in a spot that is continuously exposed to 500°C. Design the bar so that it can operate for at least 10 years without failing.arrow_forwardA non-cold-worked cylindrical rod with an initial length of 800 mm and diameter of 15 mm is to be deformed using a tensile load of 45 kN. Of the materials listed below, which are possible candidates if you assume that failure of the system occurs when the rod plastically deforms? Do the possible candidates change if you change your assumption to the system failing at the onset of necking in the rod? Justify your choice(s). Material Young’s Modulus (GPa) Yield Strength (MPa) 1040 Steel UTS (MPa) Elongation (%) 680 205 440 25 Brass 100 185 310 68 Сopper 125 160 220 44arrow_forwardA 0.013 m diameter, 0.5 m long cylindrical metal bar is subjected to a compressive force of 8,500 N. This load does not exceed the yield strength of the material. Determine its diameter under this load. You will need some of the following properties of the metal to solve the problem: modulus of elasticity = 207 GPa, Poisson’s ratio = 0.30, yield strength = 180 MPa, tensile strength = 380 MPa, ductility = 23% elongation.arrow_forward
- (a) If a rod of 368 steel 1.0m long is cooled from 20 to -80°C while its ends are maintained rigid, determine the type and magnitude of stress that develops. Assume that at 20°C the rod is stress free. (b) What will be the stress magnitude if a rod 2.0 m long is used? (c) If the rod in part (a) is heated from 20 to 80°C, what type and magnitude of stress will result? Assume that asteel = 16 x 10-6/°C ; E steel = 207 %3D GPaarrow_forwardPick the best soultion for the multiple choices. Modulus of resilience is: Slope of elastic portion of stress – strain curve Area under the elastic portion of the stress –strain curve Energy absorbed during fracture in a tension test Energy absorbed during fracture in an impact test Slope of the plastic portion of the stress- strain curve ( ) Fatigue failure occurs under the condition of: High elastic stress High corrosivity High stress fluctuations High temperature High rate of loading ( ) Creep failure of a material occurs most rapidly when the operating temperature is: Cryogenic temperature Equal to its melting point Grater than 0.4 times its melting point in K Greater than 200 oF Close to boiling point ( ) Young’s modulus of a material is indicative of its: Tensile strength Yield Strength Ductility Stiffness Corrosion Resistance…arrow_forwardA 30 cm long, 12 mm diameter carbon steel rod was subjected to 15.5 kN of tension. Calculate: (a) the stress and strain in the rod (b) the amount that it stretches, (c) its change in diameter and its stiffness (k= EA/L), (d) If the force was only 4.5 kN, by what amount would the rod have stretched?arrow_forward
- information: "When performing a tensile test of a metal, these values were found for stress and strain. the yield strength (YS) is stress at 0.2% plastic strain" The task: A 5 meter long rod of this material is loaded axially with a stress of 244 MPa.i. How long is the rod under load?ii. Then the bar is relieved, how long is it now?arrow_forwardQuestion-1 A 70% Cu-30% Zn brass wire is cold-drawn 20 percent to a diameter of 2.80 mm. The wire is then further cold- drawn to a diameter of 2.45 mm. (a) Calculate the total percent cold work that the wire undergoes. (b) Estimate the wire's tensile and yield strengths and elongation.arrow_forwardA 100 mm x 5 mm × 5 mm steel bar free to expand is heated from 15°C to 40°C. What shall be developed? (a) Tensile stress (b) Compressive stress (c) Shear stress (d) No stressarrow_forward
- We wish to produce a 0.3 inch thick plate of 3105 aluminum having a tensile strength of at least 25,000 psi and an elongation of at least 5%. The original thickness of the plate is 3 inches. The maximum cold work in each step is 85%. Which of the following procedures would achieve the correct final properties (more than one answer is possible!)? Group of answer choices Hot work from 3 in to 0.7 in; cold work from 0.7 in to 0.3 in Cold work from 3 in to 0.7 in; do an anneal to recrystallize the material; cold work from 0.7 in to 0.3 in Cold work from 3 inches to 0.3 inches Cold work from 3 in to 0.7 in; cold work from 0.7 to 0.5 in; do an anneal to recrystallize the material; cold work from 0.5 in to 0.3 in Hot work from 3 in to 0.5 in; do an anneal to recrystallize the material; hot work from 0.5 to 0.3 in Hot work from 3 in to 0.7 in; do an anneal to recrystallize the material; hot work from 0.7 to 0.3 in Cold work from 3 in to 0.5 in; do an anneal to recrystallize the…arrow_forwardQ2) Cylindrical rod with original diameter (12mm) and original length (70 mm) made of 1020 Hot-rolled steel alloy which their yield stress (207 MPa) and Young modulus (210 GPa). Tensile test was carried on this rod and it's broken under (27.5 KN) force with final diameter (10mm) and final length (84 mm). Calculate: (A) 1- Engineering fracture stress (B) If you know that the Brinell hardness for this alloy (HB=111). Estimate the tensile strength of this alloy in (MPa). 2- True fracture stress. (C) 1- Toughness gauge. 2- The percentage of elongation.arrow_forwardAn ordinary mild steel bar has been prestressed to a working stress of 200 MPa. If the Young's modulus of steel is 200 GPa and permanent negative strain due to shrinkage and creep is 0.0008, what is the effective stress left in the steel?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY