Textbook Question
Chapter 6.13, Problem 28KCP
Describe the microstructure of a heavily cold-worked metal of an Al–0.8% Mg alloy as observed with an optical microscope at 100× (see Fig. 6.46a). Describe the micro-structure of the same material at 20,000× (see Fig. 6.47a).
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
To put lattice defects in perspective, consider a metal blank that has a dislocation density of 10^3 mm^-2 suppose all the dislocations in 1000 mm^3 are linked together as a chain.How long will this chain be in km? Now suppose that dislocation density increases to (10^10) mm^-2 with cold deformation. How long will the chain be now?
The yield strength for an alloy that has an average grain diameter of 4.7 × 102 mm is 134 MPa.
At a grain diameter of 7.4 x 103 mm, the yield strength increases to 236 MPa. At what grain
diameter, in mm, will the yield strength be 249 MPa?
Schottky Defect
Frenkel Defect
Name four methods used for strengthening of metals. What is the common principle that these
methods rely on to make a metal stronger.
2. For the data given below
a) Calculate the number-average molecular weight of polypropyl
carbon are 1.008 and
ns? Atomic weights of hydrogen and
Chapter 6 Solutions
Foundations of Materials Science and Engineering
Ch. 6.13 - (a) How are metal alloys made by the casting...Ch. 6.13 - Why are cast metal sheet ingots hot-rolled first...Ch. 6.13 - What type of heat treatment is given to the rolled...Ch. 6.13 - Describe and illustrate the following types of...Ch. 6.13 - Describe the forging process. What is the...Ch. 6.13 - What is the difference between open-die and...Ch. 6.13 - Describe the wire-drawing process. Why is it...Ch. 6.13 - Distinguish between elastic and plastic...Ch. 6.13 - Define (a) engineering stress and strain and (b)...Ch. 6.13 - Define (a) modulus of elasticity, (b) yield...
Ch. 6.13 - (a) Define the hardness of a metal. (b) How is the...Ch. 6.13 - What types of indenters are used in (a) the...Ch. 6.13 - What are slipbands and slip lines? What causes the...Ch. 6.13 - Describe the slip mechanism that enables a metal...Ch. 6.13 - (a) Why does slip in metals usually take place on...Ch. 6.13 - Prob. 16KCPCh. 6.13 - What other types of slip planes are important...Ch. 6.13 - Define the critical resolved shear stress for a...Ch. 6.13 - Describe the deformation twinning process that...Ch. 6.13 - What is the difference between the slip and...Ch. 6.13 - Prob. 21KCPCh. 6.13 - Prob. 22KCPCh. 6.13 - What experimental evidence shows that grain...Ch. 6.13 - (a) Describe the grain shape changes that occur...Ch. 6.13 - How is the ductility of a metal normally affected...Ch. 6.13 - (a) What is solid-solution strengthening? Describe...Ch. 6.13 - What are the three main metallurgical stages that...Ch. 6.13 - Describe the microstructure of a heavily...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Prob. 33KCPCh. 6.13 - Prob. 34KCPCh. 6.13 - Prob. 35KCPCh. 6.13 - Prob. 36KCPCh. 6.13 - Prob. 37KCPCh. 6.13 - Why are nanocrystalline materials stronger? Answer...Ch. 6.13 - A 70% Cu30% Zn brass sheet is 0.0955 cm thick and...Ch. 6.13 - A sheet of aluminum alloy is cold-rolled 30% to a...Ch. 6.13 - Calculate the percent cold reduction when an...Ch. 6.13 - Prob. 42AAPCh. 6.13 - What is the relationship between engineering...Ch. 6.13 - A tensile specimen of cartridge brass sheet has a...Ch. 6.13 - A 0.505-in.-diameter rod of an aluminum alloy is...Ch. 6.13 - In Figure 6.23, estimate the toughness of SAE 1340...Ch. 6.13 - The following engineering stress-strain data were...Ch. 6.13 - Prob. 49AAPCh. 6.13 - A 0.505-in.-diameter aluminum alloy test bar is...Ch. 6.13 - A 20-cm-long rod with a diameter of 0.250 cm is...Ch. 6.13 - Prob. 52AAPCh. 6.13 - Prob. 53AAPCh. 6.13 - Prob. 54AAPCh. 6.13 - Prob. 55AAPCh. 6.13 - Prob. 56AAPCh. 6.13 - A specimen of commercially pure titanium has a...Ch. 6.13 - Prob. 58AAPCh. 6.13 - Prob. 59AAPCh. 6.13 - Prob. 60AAPCh. 6.13 - Prob. 61AAPCh. 6.13 - Prob. 62AAPCh. 6.13 - Prob. 63AAPCh. 6.13 - Prob. 64AAPCh. 6.13 - Prob. 65SEPCh. 6.13 - Prob. 66SEPCh. 6.13 - A 20-mm-diameter, 350-mm-long rod made of an...Ch. 6.13 - Prob. 68SEPCh. 6.13 - Prob. 69SEPCh. 6.13 - Consider casting a cube and a sphere on the same...Ch. 6.13 - When manufacturing complex shapes using cold...Ch. 6.13 - Prob. 74SEPCh. 6.13 - Draw a generic engineering stress-strain diagram...Ch. 6.13 - (a) Draw a generic engineering stress-strain...Ch. 6.13 - Prob. 77SEPCh. 6.13 - Prob. 78SEPCh. 6.13 - Prob. 79SEPCh. 6.13 - The material for a rod of cross-sectional area...Ch. 6.13 - What do E, G, v, Ur, and toughness tell you about...Ch. 6.13 - A cylindrical component is loaded in tension until...Ch. 6.13 - Referring to Figures 6.20 and 6.21 (read the...Ch. 6.13 - (a) Show, using the definition of the Poissons...Ch. 6.13 - A one-inch cube of tempered stainless steel (alloy...Ch. 6.13 - Prob. 87SEPCh. 6.13 - Prob. 88SEPCh. 6.13 - Prob. 89SEPCh. 6.13 - Prob. 90SEPCh. 6.13 - Prob. 91SEPCh. 6.13 - Prob. 92SEPCh. 6.13 - Prob. 93SEPCh. 6.13 - Prob. 94SEPCh. 6.13 - Starting with a 2-in.-diameter rod of brass, we...Ch. 6.13 - Prob. 96SEPCh. 6.13 - Prob. 97SEPCh. 6.13 - Prob. 98SEPCh. 6.13 - The cupro-nickel substitutional solid solution...Ch. 6.13 - Prob. 100SEP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
The moment of inertia Iy for the slender rod in terms of the rod’s total mass m .
Engineering Mechanics: Statics & Dynamics (14th Edition)
What is the importance of modeling in engineering? How are the mathematical models for engineering processes pr...
HEAT+MASS TRANSFER:FUND.+APPL.
What is the weight in newtons of an object that has a mass of (a) 8 kg, (b) 0.04 kg, (c) 760 Mg?
Statics and Mechanics of Materials (5th Edition)
What types of polymers are most commonly blow molded?
Degarmo's Materials And Processes In Manufacturing
Comprehension Check 7-14
The power absorbed by a resistor can be given by P = I2R, where P is power in units of...
Thinking Like an Engineer: An Active Learning Approach (3rd Edition)
Repeat Problem 4-6 except solve by the vector loop method.
DESIGN OF MACHINERY
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Consider an aluminum polycrystal with a grain size of 10 μm. If a dislocationsource at the center of a grain emits dislocations under an appliedshear stress of 50 MPa that pile up at the grain boundaries, what is the stressexperienced by a grain boundary? Take G = 26 GPa and b = 0.3 nm.arrow_forwardHelp me pleasearrow_forwardQuestion The yield strength for an aluminum alloy that has an average grain diameter of 10 um is 400 MPa. As the grain diameter is increased to 80 um, the yield strength decreases to 260 MPa. When the grain diameter is 2 um, its yield strength is close to 760 MPa 668 MPa 566 MPa 419 MPaarrow_forward
- Calculate the dislocation spacing in a symmetrical tilt boundary (θ = 0.5◦) in a copper crystal.arrow_forwardExplain the differences in grain structure for a metal that has been cold worked and one that has been cold worked and then recrystallized.arrow_forwardConsider a single crystal of some hypothetical metal that has the FCC crystal structure and is oriented such that a tensile stress is applied along a [11 2] direction. If slip occurs on a ( 111) plane and in a [0 11] direction, and the crystal yields at a stress of 5.12 MPa, compute the critical resolved shear stress. CRITICAL RESOLVED SHEAR STRESS • CRITICAL RESOLVED SHEAR STRESS (T, THE MOST FAVORABLY ORIENTED SLIP SYSTEM WHEN SHEAR STRESS IS AT J: SLIP IN A SYSTEM STARTS ON CRSS THIS CRITICAL VALUE • MINIMUM SHEAR STRESS REQUIRED TO INITIATE SLIP • SINGLE CRYSTAL PLASTICALLY DEFORMS WHEN: T, > T, CRSS OR TR(max) =T CRSS 'R Tcrss (cos o cos A)maxarrow_forward
- The yield strength for an alloy that has an average grain diameter of 5.2 x 102 mm is 110 MPa. At a grain diameter of 6.3 x 103 mm, the yield strength increases to 251 MPa. At what grain diameter, in mm, will the yield strength be 222 MPa? d = mmarrow_forward(6) For an aluminum alloy under constant load, the creep rate increased by a factor of 2 when the temperature was increased from 71°C to 77°C. Find the activation energy and express it in Joule/mole.arrow_forwardA single crystal of a metal that has the FCC crystal structure is oriented such that a tensile stress is applied parallel to the [100] direction. If the critical resolved shear stress for this material is 1.18 MPa, calculate the magnitude of applied stress necessary to cause slip to occur on the (111) plane in the [1-10] direction.arrow_forward
- To provide some perspective on the dimensions of atomic defects, consider a metal specimen that has a dislocation density of 104 mm-2. Suppose that all the dislocations in 1000 mm3 (1 cm3) were somehow removed and linked end to end. How far (in miles) would this chain extend? Now suppose that the density is increased to 1010 mm-2 by cold working. What would be the chain length of dislocations in 1000 mm3 of material?arrow_forwardHelp me pleasearrow_forwardA copper-zinc alloy has the following properties: Grain Diameter (mm) Strength (MPa) 0.015 170 MPa 0.025 158 MPa 0.035 151 MPa 0.050 145 MPa Determine (a) the constants in the Hall-Petch equation; and (b) the grain size required to obtain a strength of 200 MPa.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Explanation of Solidification of Metals & Alloys | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=G5z9KknF_s8;License: Standard Youtube License