The tensile stress that must be applied to the
Explanation of Solution
Write the expression to determine the angle
Here,
Write the expression for the Schmidt law using the equation 6.17.
Here, the applied stress is
Conclusion:
Substitute 1 for
Calculate the angle between
Substitute 1 for
Substitute 0.85 MPa for
Thus, the resolved shear stress for the 0.85 MPa is 2.08 MPa.
Want to see more full solutions like this?
Chapter 6 Solutions
Foundations of Materials Science and Engineering
- A single crystal of an FCC metal isoriented so that the [001] direction is parallel to an applied stress of 5000 psi. Calculate the resolved shear stress acting on the (111) slip plane in the [110] and [101] slip directions. Which slip system(s) will become active first?arrow_forwardIf a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions. Which of the following is the value of cos(lambda) for the angle lambda between the force direction and the slip direction? Group of answer choices 0.707 0.316 0.632 0.500arrow_forwardA single crystal of an FCC metal is oriented so that the [001] direction is parallel to an applied stress of 5000 psi. Calculate the resolved shear stress acting on the (111) slip plane in the [-110], and [10-1] slip directions. Which slip system(s) will become active first?arrow_forward
- (b) The yield stress for a metal changes from 450 Nmm-2to 610 Nmm-2 when the average grain diameter decrease from 0.043 mm to 0.022 mm. Determine the yield stressfor the same metal with an average grain diameter of 0.030 mm.arrow_forwardA single crystal of a metal that has the FCC crystal structure is oriented such that a tensile stress is applied parallel to the [100] direction. If the critical resolved shear stress for this material is 1.18 MPa, calculate the magnitude of applied stress necessary to cause slip to occur on the (111) plane in the [1-10] direction.arrow_forward1. There are three slip systems on a FCC octahedral plane, i.e. one of the {111} planes. Assume a2 MPa tensile stress is applied along the [100] direction of a gold single crystal, whose criticalresolved shear stress is 0.91 MPa at room temperature. Demonstrate quantitatively thatmeasurable slip will not occur on any of the three slip systems containing the (111) plane as aresult of this applied tensile stress. (Hint: Schmid’s law) 2. Identify the Burgers vector (using vector notation) of a screw dislocation that can cross-slipbetween (111) and (111) planes of an FCC crystal (Hint: Use Weiss zone law). 3. Why are dislocations not considered thermodynamic equilibrium defects like vacancies?Explain by describing the relative interplay between entropy and enthalpy affecting the Gibbsfree energy of the dislocations-containing material system.arrow_forward
- In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation? Select one: a.120.5 MPa, no b.140.5, no c.129.5, yes d.123.5 MPa, yes e.133.5 MPa, yesarrow_forwardIn an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation?arrow_forwardA single crystal of an FCC metal is oriented so that the [001] direction is parallel to an applied stress of 34.47MPa. Calculate the resolved shear stress acting on the (111) slip plane in the [-110], and [10-1] slip directions. Which slip system(s) will become active first?arrow_forward
- Consider a single crystal of a hypothetical metal that has the BCC crystal structure. A stress of 50 MPa is applied in the [101] direction of the BCC unit cell.a. Determine the most favourable slip direction for the (011) slip plane of the BCC unit cell. ⟨111⟩ is the family of directions with the highest linear density in the BCC unit cell.b. If τcrss = 27.5 MPa, determine if the single crystal yields. If not, what stress level is required?c. What is the minimum stress at which the BCC single crystal yields?arrow_forwardIf a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions. Which of the following is the critical resolved shear stress on the slip plane in the slip direction? Group of answer choices 24.49 MPa 34.65 MPa 12.25 MPa 102 MPaarrow_forwardIn order to find out the effects of the grain sizes on the mechanical strength of a metal, three different grain sizes of 10 µm, 500 nm and 10 nm were produced. What will be the yield stresses of these same metals at different average grain sizes? The yield strength for a grain or reference point is 78 MPa, while the material proportional constant is 29.2 MPa-mm1/2.arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY