Chapter 6.13, Problem 95SEP
Starting with a 2-in.-diameter rod of brass, we would like to process 0.2-in.-diameter rods that possess minimum yield strength of 40 ksi and a minimum elongation to fracture of 40% (see Fig. 6.44). Design a process that achieves that. Hint: Reduction of the diameter directly from 2 in. to 0.6 in. is not possible; why?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A metallic rod with an initial diameter of 10 mm and an initial length of 50 mm is subjected to the tensile test. After the fracture, the final length was measured as 51.8 mm, and the final diameter was measured as 9.5 mm.(a) Calculate modulus of elasticity, ultimate tensile strength, elongation at fracture in %,reduction of area in %, true stress at maximum load, true strain at maximum load, strain hardening exponent, strength coefficient.?
Problem 5. Starting with a 2-inch diameter rod of
brass, we would like to process 0.2-inch diameter
rods that possess minimum yield strength of 40 ksi
and a minimum elongation to fracture of 40%, (see
the following figure). Design a process that achieves
that.
120
70% Cu-30% Zn
100
Tensile strength
80
60
60
Yield strength
40
40
20
20
Elongation
10
20
30
40
50
60
Percent cold work
Tensile strength and yield strength (ksi)
Elongation percent
3.
A rod-shaped MgO specimen with round cross section is tested with the
three-point bend method. What is the calculated minimum radius without
fracture if the applied load is 5560 N, the flexural strength is 105 MPa,
and the separation between the two support pins is 45 mm?
Chapter 6 Solutions
Foundations of Materials Science and Engineering
Ch. 6.13 - (a) How are metal alloys made by the casting...Ch. 6.13 - Why are cast metal sheet ingots hot-rolled first...Ch. 6.13 - What type of heat treatment is given to the rolled...Ch. 6.13 - Describe and illustrate the following types of...Ch. 6.13 - Describe the forging process. What is the...Ch. 6.13 - What is the difference between open-die and...Ch. 6.13 - Describe the wire-drawing process. Why is it...Ch. 6.13 - Distinguish between elastic and plastic...Ch. 6.13 - Define (a) engineering stress and strain and (b)...Ch. 6.13 - Define (a) modulus of elasticity, (b) yield...
Ch. 6.13 - (a) Define the hardness of a metal. (b) How is the...Ch. 6.13 - What types of indenters are used in (a) the...Ch. 6.13 - What are slipbands and slip lines? What causes the...Ch. 6.13 - Describe the slip mechanism that enables a metal...Ch. 6.13 - (a) Why does slip in metals usually take place on...Ch. 6.13 - Prob. 16KCPCh. 6.13 - What other types of slip planes are important...Ch. 6.13 - Define the critical resolved shear stress for a...Ch. 6.13 - Describe the deformation twinning process that...Ch. 6.13 - What is the difference between the slip and...Ch. 6.13 - Prob. 21KCPCh. 6.13 - Prob. 22KCPCh. 6.13 - What experimental evidence shows that grain...Ch. 6.13 - (a) Describe the grain shape changes that occur...Ch. 6.13 - How is the ductility of a metal normally affected...Ch. 6.13 - (a) What is solid-solution strengthening? Describe...Ch. 6.13 - What are the three main metallurgical stages that...Ch. 6.13 - Describe the microstructure of a heavily...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Prob. 33KCPCh. 6.13 - Prob. 34KCPCh. 6.13 - Prob. 35KCPCh. 6.13 - Prob. 36KCPCh. 6.13 - Prob. 37KCPCh. 6.13 - Why are nanocrystalline materials stronger? Answer...Ch. 6.13 - A 70% Cu30% Zn brass sheet is 0.0955 cm thick and...Ch. 6.13 - A sheet of aluminum alloy is cold-rolled 30% to a...Ch. 6.13 - Calculate the percent cold reduction when an...Ch. 6.13 - Prob. 42AAPCh. 6.13 - What is the relationship between engineering...Ch. 6.13 - A tensile specimen of cartridge brass sheet has a...Ch. 6.13 - A 0.505-in.-diameter rod of an aluminum alloy is...Ch. 6.13 - In Figure 6.23, estimate the toughness of SAE 1340...Ch. 6.13 - The following engineering stress-strain data were...Ch. 6.13 - Prob. 49AAPCh. 6.13 - A 0.505-in.-diameter aluminum alloy test bar is...Ch. 6.13 - A 20-cm-long rod with a diameter of 0.250 cm is...Ch. 6.13 - Prob. 52AAPCh. 6.13 - Prob. 53AAPCh. 6.13 - Prob. 54AAPCh. 6.13 - Prob. 55AAPCh. 6.13 - Prob. 56AAPCh. 6.13 - A specimen of commercially pure titanium has a...Ch. 6.13 - Prob. 58AAPCh. 6.13 - Prob. 59AAPCh. 6.13 - Prob. 60AAPCh. 6.13 - Prob. 61AAPCh. 6.13 - Prob. 62AAPCh. 6.13 - Prob. 63AAPCh. 6.13 - Prob. 64AAPCh. 6.13 - Prob. 65SEPCh. 6.13 - Prob. 66SEPCh. 6.13 - A 20-mm-diameter, 350-mm-long rod made of an...Ch. 6.13 - Prob. 68SEPCh. 6.13 - Prob. 69SEPCh. 6.13 - Consider casting a cube and a sphere on the same...Ch. 6.13 - When manufacturing complex shapes using cold...Ch. 6.13 - Prob. 74SEPCh. 6.13 - Draw a generic engineering stress-strain diagram...Ch. 6.13 - (a) Draw a generic engineering stress-strain...Ch. 6.13 - Prob. 77SEPCh. 6.13 - Prob. 78SEPCh. 6.13 - Prob. 79SEPCh. 6.13 - The material for a rod of cross-sectional area...Ch. 6.13 - What do E, G, v, Ur, and toughness tell you about...Ch. 6.13 - A cylindrical component is loaded in tension until...Ch. 6.13 - Referring to Figures 6.20 and 6.21 (read the...Ch. 6.13 - (a) Show, using the definition of the Poissons...Ch. 6.13 - A one-inch cube of tempered stainless steel (alloy...Ch. 6.13 - Prob. 87SEPCh. 6.13 - Prob. 88SEPCh. 6.13 - Prob. 89SEPCh. 6.13 - Prob. 90SEPCh. 6.13 - Prob. 91SEPCh. 6.13 - Prob. 92SEPCh. 6.13 - Prob. 93SEPCh. 6.13 - Prob. 94SEPCh. 6.13 - Starting with a 2-in.-diameter rod of brass, we...Ch. 6.13 - Prob. 96SEPCh. 6.13 - Prob. 97SEPCh. 6.13 - Prob. 98SEPCh. 6.13 - The cupro-nickel substitutional solid solution...Ch. 6.13 - Prob. 100SEP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
List several uses of the arbor press.
Machine Tool Practices (10th Edition)
Locate the centroid of the area. Prob. 9-17
Engineering Mechanics: Statics
3.3 It is known that a vertical force of 200 lb is required to remove the nail at C from the board. As the nail...
Vector Mechanics for Engineers: Statics
A windowmounted air conditioner removes 3.5kJ from the inside of a home using 1.75 kJ work input. How much ener...
EBK FUNDAMENTALS OF THERMODYNAMICS, ENH
A 20-lb force is applied to the control rod AB as shown. Knowing that the length of the rod is 9 in. and that t...
Statics and Mechanics of Materials
How is the hydrodynamic entry length defined for flow in a pipe? Is the entry length longer in laminar or turbu...
Fluid Mechanics Fundamentals And Applications
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A sample of giant reed is shaped into a beam with a square cross section of 15.5 mm by 15.5 mm. Two supports placed 22.1 mm apart support thesample and a load is applied halfway between the support points in order to test the force required to fracture the sample. If ultimate tensile strength is912 MPa, what would be the force F (newtons) required to cause failure?arrow_forwardA high-strength steel has yield strength of 1165 MPa and fracture toughness of 95 MPavm. Calculate the size of an internal crack that will lead to catastrophic failure at an applied stress of 80% yield strength. (Y = 1.00 for internal crack, and Y=1.12 for surface crack)arrow_forwardExample: Consider a metal whose strain hardening behavior follows: 25,000 0.25 psi. If an annealed bar of this metal is pulled in a tension test from a starting dia. of 12.7mm to a dia. of 11.5mm (uniform elongation, no friction, no distortion), what is the work per unit volume required? If the bar is reduced by extruding and the deformation efficiency is 70%, what is the extrusion pressure?arrow_forward
- A steel rod (initial diameter: 3.2 mm, initial length: 42 mm) is extended by auniaxial tensile load of 4800 N in 120 seconds. At this load, the length of therod is measured as 49,2 mm. Calculate the followings:(a) Stress and strain occurred on the rod at this load.(b) Initial strain rate.(c) Diameter of the rod at this load.(Yield strength : 380 MPa, Ultimate Tensile Strength: 670 MPa,Modulus of Elasticity: 210000 MPa were given for this material)arrow_forwardA metallic rod with an initial diameter of 10 mm and an initial length of 50 mm is subjected to the tensile test. After the fracture, the final length was measured as 51.8 mm, and the final diameter was measured as 9.5 mm. (a) Calculate modulus of elasticity, (b) Calculate ultimate tensile strength, (c) Calculate elongation at fracture in %, (d) Calculate reduction of area in %, (e) Calculate true stress at maximum load, Calculate true strain at maximum load, (f) (g) Calculate strain hardening exponent, (h) Calculate strength coefficient. Load, N 0 3300 9900 18000 23000 16000* 16000 21500 24000 Elongation, mm 0.01 0.03 0.05 0.10 0.50 1.0 1.4 2* Fracture pointarrow_forwardA gauge # 10 HSLA steel for an automotive application has a Young’s modulus of 200 GPa, a yield strength of 370 MPa and a ultimate tensile strength of 440 MPa. What is the punch force needed to punch a square hole with a side length of 20 mm on this HSLA steel? Show your work.arrow_forward
- (C) A plain sided specimen is subjected to 2 * 107 cycles at the applied stress range of 100 MPa. Estimate how many further cycles can be applied at a stress range of 400 MPa before failure is predicted to occur.arrow_forwardDiscussion : • Difficulties in testing brittle materials. • Advantages of stress - strain diagram. • Sources of error you expect in the experiment. • Define the term strain hardening and explain in which stage in the stress- strain diagram it occurs, what are its reasons, and its effects on material properties? • Compare between the brittle and ductile fracture. fr in tearrow_forwardExample (6): A tensile specimen with a 12 mm initial djameter and 50 gage Jength reaches maximum load at 90 kN and fractures at 70, kN. minimum diameter at fracture is 10 mm. Determine the engineering stre maximum load (the ultimate tensile strength) and the true frācture stress?. what is the value of true and engineering strain at fråcture?arrow_forward
- A three-point transverse bending test was performed on a glass specimen having a square cross-section of 18.5 mm length on each edge. The specimen fractured at a load of 4530 N when the distance between support points was 42 mm. A second test is to be performed on another specimen of this same glass material, but one that has a circular cross-section. What minimum specimen diameter is required to ensure that fracture will not occur when a load of 3480 N is applied? Assume that the support separation is maintained at 42 mm. mmarrow_forward(a) A three-point bending test is conducted on a cylindrical specimen of aluminum oxide having a reported flexural strength of 300 MPa. If the specimen radius is 5.0 mm and the support point separation distance is 15.0 mm, predict whether or not you would expect the specimen to fracture when a load of 7500 N is applied? Justify your prediction. (b) Would you be 100% certain of the prediction in part (a)? Why or why not?arrow_forwardA cylindrical brass rod with a minimum tensile strength of 450 MPa, a ductility of at least 13% EL (elongation), and a final diameter of 12.7mm is required. You have in your inventory some 19.0mm diameter brass stock that has been cold worked to 35%. Assuming that the cross section of the rod is still circular after being cold worked, and that brass experiences cracking at 65% CW, describe the necessary working steps in order to achieve the final product. Take the expression for % cold work to be = (Ao - Af)/ Ao x 100%, where Ao and Af are the original and final circular cross-sectional areas of the rod.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
EVERYTHING on Axial Loading Normal Stress in 10 MINUTES - Mechanics of Materials; Author: Less Boring Lectures;https://www.youtube.com/watch?v=jQ-fNqZWrNg;License: Standard YouTube License, CC-BY