Q2) Cylindrical rod with original diameter (12mm) and original length (70 mm) made of 1020 Hot-rolled steel alloy which their yield stress (207 MPa) and Young modulus (210 GPa). Tensile test was carried on this rod and it's broken under (27.5 KN) force with final diameter (10mm) and final length (84 mm). Calculate: (A) 1- Engineering fracture stress 2- True fracture stress. (B) If you know that the Brinell hardness for this alloy (HB=111). Estimate the tensile strength of this alloy in (MPa).

Q2) Cylindrical rod with original diameter (12mm) and original length (70 mm) made of 1020 Hot-rolled steel alloy which their yield stress (207 MPa) and Young modulus (210 GPa). Tensile test was carried on this rod and it's broken under (27.5 KN) force with final diameter (10mm) and final length (84 mm). Calculate: (A) 1- Engineering fracture stress 2- True fracture stress. (B) If you know that the Brinell hardness for this alloy (HB=111). Estimate the tensile strength of this alloy in (MPa).

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 35.5 mm - Final Diameter after fracture = 3.6 mm & - Ultimate stress = 396 MPa SOLUTION: iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
Problem: A tensile test specimen of stainless steel alloy having a with a diameter of 12.6 mm and a 50 mm gage length was tested to fracture. Load and deformation data obtained during the test are given: Determine: (a) the modulus of elasticity. (b) the proportional limit. Load (kN) 0.00 Change in length (mm) (c) the ultimate strength. 0.00 (d) the yield strength (0.20% offset). 0.00 25.79 0.00 (e) the fracture stress. 0.05 51.59 0.10 (f) the true fracture stress if the final diameter 66.55 73.36 80.18 87.77 0.20 of the specimen at the location of the fracture 0.30 0.45 was 8.89 mm 0.63 95.35 0.81 101.42 105.98 112.05 1.01 1,18 1.41 only solve d, e,f 118.13 123.46 128.03 131.85 133.39 134.95 135.73 1.66 1.94 2.27 2.60 2,82 3.15 3.35 3.68 136.53 136.56 3.93 135.84 4.26 135.14 4,66 133.66 4.94 130.67 5.22 5.47 128.44 124.69 5.70 120.92 5.82 117.91 5.95 fracture 116.52
3. A rod-shaped MgO specimen with round cross section is tested with the three-point bend method. What is the calculated minimum radius without fracture if the applied load is 5560 N, the flexural strength is 105 MPa, and the separation between the two support pins is 45 mm?
A material with an Ultimate Tensile Strength (UTS) of 400 Mpa is loaded cyclically about mean stress of 80 MPa. If the stress range that will cause fatigue fracture in 100 000 cycles under zero mean stress is (+,- )60 MPa, what stress range (in MPa) about the mean of 70 MPa will give the same life
A bar made of carbon-steel of size 12mm x 20mm has a yield stress of 400 MPa and ultimate tensile strength of550 MPa. Tha gauge length of the specimen tested under tension loading is 350mm. a. Determine its elongation when a tension load of 75 KN is applied. b. Determine the maximum load the bar can take before it fractures. Take Youngs Modulus of steel as 200,000 MPa
Q6:1f the rod fracture at 35% elongation find the percentage difference between engineering and true stress at fracture point?
A mild steel tensile specimen of initial length 44 mm and initial diameter 6.4 mm is subjected to a tensile test and the following data are obtained. - Yield Strength as 88 MPa - Maximum Strength as 212 MPa - Fracture Strength as 152 MPa - Percentage of Elongation as 63 % - Percentage of Reduction in area as 39% Determine the Final length, Final area, Yield load, Ultimate load
What’s the answer for this please ?
Tensile and fully reversed loading fatigue tests were conducted for a certain steelalloy and revealed the tensile strength and endurance limit to be 1200 and 550 MPa,respectively. If a rod of this material supply were subjected to a static stress of 600MPa and fully-reversed oscillating stresses whose total range was 700 MPa. Assuming garber relationship will this rod fail by fatigue failure
An unknown specimen having a rectangular cross section of dimensions 5 mm × 20 mm isdeformed in tension. Using the load-elongation data shown in the below table, answer thefollowing questions.(d) Determine the tensile strength.(e) Compute the modulus of resilience.(f) What is the ductility, in percent elongation? only d,e,and f
MECH.ENG. DESIGN 1
Qu2. (A) What is fatigue? Mention the sequence of steps involved in fatigue of a smooth specimen. Mention Four (4) factors that affect fatigue of smooth specimens, stating how each affects fatigue life (B) A very wide panel made of a material of plane-strain fracture toughness of Kic=55MPaVm was found to have a central crack of size 2.5mm. It is subjected to cyclic loading at a design (or working) stress of 690MPA and stress ratio of zero. (a) Sketch the stress-time graph of the loading cycle and determine (i) Stress Range, (ii) maximum cycle stress, (iii) stress amplitude and (iv) mean stress (b) Will the initial loading cycle cause the panel to fracture? Why or whynot? Compute the maximum allowable fatigue flaw size that can fracture the panel during the cyclic loading. (Assume that plain strain condition prevails). (c)