Chapter 6.13, Problem 86SEP
A one-inch cube of tempered stainless steel (alloy 316) is loaded on the same face with a shear stress of 30.00 ksi. Draw a schematic of the cube before and after loading, showing any changes in the shape. (G = 11.01 × 106 psi; use Fig. 6.17c)
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
An ordinary mild steel bar has been prestressed to a working stress of 200 MPa. If the Young's modulus of steel is 200 GPa and permanent negative strain due to shrinkage and creep is 0.0008, what is the effective stress left in the steel?
The figure below shows the stress-strain behavior of a mild steel (the insert shows part of the same plot, but with
different scale). This steel is used to make a rod that is 6 mm in diameter and 400 mm long. The rod is loaded in
tension until an elongation of 1.2 mm is reached.
A. Estimate the Yield Stress for the Steel.
B. Estimate the Ultimate Tensile Stress for the Steel.
C. Estimate the Elastic Modulus for the Steel.
D. Estimate the %Elongation for the Steel.
E. Estimate the Force acting on the rod necessary to achieve an elongation of 1.2mm.
F. After an elongation of 1.2mm the load on the rod is removed. Estimate the length of the rod after the load is
released.
600
500
400
500
400
300
300
200
200
100
100
0.000
0.002
0.004
0.006
Strain
0.00
0.04
0.08
0.12
0.16
0.20
Strain
Stress (MPa)
Stress (MPa)
What is the maximum value of KIc as per LEFM that can be determined from experiments on a 20 mm thick plate? yield strength= 500 MPa, E= 210 GPa, poission ratio=0.3.
Chapter 6 Solutions
Foundations of Materials Science and Engineering
Ch. 6.13 - (a) How are metal alloys made by the casting...Ch. 6.13 - Why are cast metal sheet ingots hot-rolled first...Ch. 6.13 - What type of heat treatment is given to the rolled...Ch. 6.13 - Describe and illustrate the following types of...Ch. 6.13 - Describe the forging process. What is the...Ch. 6.13 - What is the difference between open-die and...Ch. 6.13 - Describe the wire-drawing process. Why is it...Ch. 6.13 - Distinguish between elastic and plastic...Ch. 6.13 - Define (a) engineering stress and strain and (b)...Ch. 6.13 - Define (a) modulus of elasticity, (b) yield...
Ch. 6.13 - (a) Define the hardness of a metal. (b) How is the...Ch. 6.13 - What types of indenters are used in (a) the...Ch. 6.13 - What are slipbands and slip lines? What causes the...Ch. 6.13 - Describe the slip mechanism that enables a metal...Ch. 6.13 - (a) Why does slip in metals usually take place on...Ch. 6.13 - Prob. 16KCPCh. 6.13 - What other types of slip planes are important...Ch. 6.13 - Define the critical resolved shear stress for a...Ch. 6.13 - Describe the deformation twinning process that...Ch. 6.13 - What is the difference between the slip and...Ch. 6.13 - Prob. 21KCPCh. 6.13 - Prob. 22KCPCh. 6.13 - What experimental evidence shows that grain...Ch. 6.13 - (a) Describe the grain shape changes that occur...Ch. 6.13 - How is the ductility of a metal normally affected...Ch. 6.13 - (a) What is solid-solution strengthening? Describe...Ch. 6.13 - What are the three main metallurgical stages that...Ch. 6.13 - Describe the microstructure of a heavily...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Prob. 33KCPCh. 6.13 - Prob. 34KCPCh. 6.13 - Prob. 35KCPCh. 6.13 - Prob. 36KCPCh. 6.13 - Prob. 37KCPCh. 6.13 - Why are nanocrystalline materials stronger? Answer...Ch. 6.13 - A 70% Cu30% Zn brass sheet is 0.0955 cm thick and...Ch. 6.13 - A sheet of aluminum alloy is cold-rolled 30% to a...Ch. 6.13 - Calculate the percent cold reduction when an...Ch. 6.13 - Prob. 42AAPCh. 6.13 - What is the relationship between engineering...Ch. 6.13 - A tensile specimen of cartridge brass sheet has a...Ch. 6.13 - A 0.505-in.-diameter rod of an aluminum alloy is...Ch. 6.13 - In Figure 6.23, estimate the toughness of SAE 1340...Ch. 6.13 - The following engineering stress-strain data were...Ch. 6.13 - Prob. 49AAPCh. 6.13 - A 0.505-in.-diameter aluminum alloy test bar is...Ch. 6.13 - A 20-cm-long rod with a diameter of 0.250 cm is...Ch. 6.13 - Prob. 52AAPCh. 6.13 - Prob. 53AAPCh. 6.13 - Prob. 54AAPCh. 6.13 - Prob. 55AAPCh. 6.13 - Prob. 56AAPCh. 6.13 - A specimen of commercially pure titanium has a...Ch. 6.13 - Prob. 58AAPCh. 6.13 - Prob. 59AAPCh. 6.13 - Prob. 60AAPCh. 6.13 - Prob. 61AAPCh. 6.13 - Prob. 62AAPCh. 6.13 - Prob. 63AAPCh. 6.13 - Prob. 64AAPCh. 6.13 - Prob. 65SEPCh. 6.13 - Prob. 66SEPCh. 6.13 - A 20-mm-diameter, 350-mm-long rod made of an...Ch. 6.13 - Prob. 68SEPCh. 6.13 - Prob. 69SEPCh. 6.13 - Consider casting a cube and a sphere on the same...Ch. 6.13 - When manufacturing complex shapes using cold...Ch. 6.13 - Prob. 74SEPCh. 6.13 - Draw a generic engineering stress-strain diagram...Ch. 6.13 - (a) Draw a generic engineering stress-strain...Ch. 6.13 - Prob. 77SEPCh. 6.13 - Prob. 78SEPCh. 6.13 - Prob. 79SEPCh. 6.13 - The material for a rod of cross-sectional area...Ch. 6.13 - What do E, G, v, Ur, and toughness tell you about...Ch. 6.13 - A cylindrical component is loaded in tension until...Ch. 6.13 - Referring to Figures 6.20 and 6.21 (read the...Ch. 6.13 - (a) Show, using the definition of the Poissons...Ch. 6.13 - A one-inch cube of tempered stainless steel (alloy...Ch. 6.13 - Prob. 87SEPCh. 6.13 - Prob. 88SEPCh. 6.13 - Prob. 89SEPCh. 6.13 - Prob. 90SEPCh. 6.13 - Prob. 91SEPCh. 6.13 - Prob. 92SEPCh. 6.13 - Prob. 93SEPCh. 6.13 - Prob. 94SEPCh. 6.13 - Starting with a 2-in.-diameter rod of brass, we...Ch. 6.13 - Prob. 96SEPCh. 6.13 - Prob. 97SEPCh. 6.13 - Prob. 98SEPCh. 6.13 - The cupro-nickel substitutional solid solution...Ch. 6.13 - Prob. 100SEP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
Assume the following vectors are already defined: V1=[302]V2=[214]V3=[5131]V4=[0.50.10.20.2] For each of the fo...
Thinking Like an Engineer: An Active Learning Approach (4th Edition)
Determine the velocity of block D if end A of the rope is pulled down with a speed of vA = 3 m/s.
Engineering Mechanics: Dynamics (14th Edition)
The spring of k and unstretched length 1.5R is attached to the disk at a radial distance of 0.75R from the cent...
Engineering Mechanics: Statics
What is the weight in newtons of an object that has a mass of (a) 8 kg, (b) 0.04 kg, (c) 760 Mg?
Statics and Mechanics of Materials (5th Edition)
Convert the following quantities from English to SI units: a. 98 Btu/(hr-ft-F) b. 0.24 Btu/(lbm-F) C. 0.04 Ibm/...
Heating Ventilating and Air Conditioning: Analysis and Design
A windowmounted air conditioner removes 3.5kJ from the inside of a home using 1.75 kJ work input. How much ener...
EBK FUNDAMENTALS OF THERMODYNAMICS, ENH
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A steel rod (initial diameter: 3.2 mm, initial length: 42 mm) is extended by auniaxial tensile load of 4800 N in 120 seconds. At this load, the length of therod is measured as 49,2 mm. Calculate the followings:(a) Stress and strain occurred on the rod at this load.(b) Initial strain rate.(c) Diameter of the rod at this load.(Yield strength : 380 MPa, Ultimate Tensile Strength: 670 MPa,Modulus of Elasticity: 210000 MPa were given for this material)arrow_forwardA high-strength steel has a yield strength of 1,460 MPa and a KIC of 98 MPa √m. Calculate the size of a surface crack that will lead to catastrophic failure at an applied stress of 3/4Y.S.arrow_forwardDetermine the indentation diameter of a mild steel material subjected to a Brinell hardness test with a test force of 8.1 kN using a hardened steel ball indentor of 10 mm. Take the Brinell Hardness Number as 926. Also, determine the surface area of indentation. (NOTE: Please Solve the problem in a paper and upload in the separate submission link provided and also fill the answers without the unit in the box below) i) Indentation Diameter (in mm) -- ii) Surface Area of Indentation (in mm?)arrow_forward
- Sketch a tensile member with (a) a rectangular crosssection, (b) a solid circular cross section, and (c) a circulartubecross section, and label the dimensions symbolically (e.g.,label the radius for the solid circular case). For each member, write out the definition of engineering stress in terms of the actual dimensions of the component. If therectangular member has dimensions of width and thicknessequal to 1 cm 0.3 cm, what would be the radius of a solidcircular member such that the stress is equal for an equaltensile load? If a tube has an outer radius equal to that ofthis same solid cylinder, what is the maximum inner radiussuch that the stress does not exceed 200% of the stress inthe solid cylinder?arrow_forwardAn application requires ultimate tensile strength and yield strength ofa steel at 110 ksi and 91 ksi, respectively. Answer the following 4 questions: Can SAE 1040 steel be selected for this application? If “no” is the answer in Part I, the following Part II, III, and IV can beignored. If “yes” is the answer in Part I, which condition of SAE 1040 shouldbe selected? Why is that steel with the condition in part II selected? Is the selected steel brittle or ductile? and Why?arrow_forwardThe Highest load sustained druing an uniaxial tensile testing experiment is 7,500lb. If the original cross section has a diamter of 0.25in, what is the ultimate tensile strength? (please also make a drawing)arrow_forward
- Suppose a 24 in. long round bar is to support a load of 400 lb. without any permanent deformation. Calculate the minium diameter of the bar if it is made of (a) AZ0A-T5 magnesium alloy and (b) 6061-T6 aluminum alloy. Calculate the wieght of the bar and the approximate cost based on pure Al and Mg in each case.arrow_forwarda)Draw the stress-strain curve of a ductile material such as that of a ductile steel and discuss the various regions of the curve. Explain the difference between a ductile and brittle material and the concept of ductility and its measurement. b)A machine part 10 mm thick, having the dimensions shown in the figure, is to be subjected to cyclic loading. If the maximum stress is limited to 60 MPa, determine the allowable force P. Approximate the stress concentration factors form the graph given. Where might a potential fracture occur?arrow_forwardDerive the following equation for computing shear stress in a solid bar along an oblique plane with angle B with respect to the vertical plane. The bar is subjected to centric axial loading. sin 0 cos 0 T = Aoarrow_forward
- A 3-mm-long gold alloy wire intended to electricallybond a computer chip to its package has an initial diameter of30 μm. During testing, it is pulled axially with a load of 15grams-force. If the wire diameter decreases uniformly to29 μm, compute the following:a. The final length of the wire.b. The true stress and true strain at this load.c. The engineering stress and strain at this load.arrow_forwardDraw a Stress/Strain graph of a mild tensile steel and identify the limit of proportionality and the yield pointarrow_forwardThe engineering stress-engineering strain tensile curve for a stainless steel type 304 alloy is shown. Calculate the constants K and n for the true stress and true strain curve before necking (or = K (&)"). Engineering Stress (MPa) 1000 900- 800- 700- 600- 500- 400- 300- 200- 100- of 0.0 02 0.4 Enginering Strain (mm/mm) 0.6 0.8 1.0arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY