Chapter 6.13, Problem 99SEP
The cupro-nickel substitutional solid solution alloys Cu–40 wt% Ni and Ni–10 wt% Cu have similar tensile strengths. For a given application in which only tensile strength is important, which one would you select?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A solid solution alloy of Cu containing 10% Ni has a yield strength of 200 MPa. What would
you expect the strength of an alloy with 40% Ni to be? Justify answer.
Animated Figure 9.41 is a plot of the logarithm stress versus the Larson-Miller parameter for an S-590 alloy. A component made of this alloy is subjected to a stress of 600 MPa. At what temperature will the rupture lifetime be 200 h?
Question 1
You are working on a design team at a small orthopaedic firm. You have been asked to select a cobalt-
chrome-molybdenum (CoCr) material that will not experience plastic deformation under a specific mechanical test, as follows...
A tensile stress is applied along the long axis of a solid cylindrical rod that has a diameter of 10 mm. An applied load of some
magnitude F produces a 7x10-³ mm change in diameter (see figure below, original shape is blue, elongated shape is unshaded).
Q1A-B: Calculate the transverse strain in the x-direction (Ex) associated with the reduction in diameter. Calculate the axial strain in
the z-direction (₂) associated with the length increase.
Chapter 6 Solutions
Foundations of Materials Science and Engineering
Ch. 6.13 - (a) How are metal alloys made by the casting...Ch. 6.13 - Why are cast metal sheet ingots hot-rolled first...Ch. 6.13 - What type of heat treatment is given to the rolled...Ch. 6.13 - Describe and illustrate the following types of...Ch. 6.13 - Describe the forging process. What is the...Ch. 6.13 - What is the difference between open-die and...Ch. 6.13 - Describe the wire-drawing process. Why is it...Ch. 6.13 - Distinguish between elastic and plastic...Ch. 6.13 - Define (a) engineering stress and strain and (b)...Ch. 6.13 - Define (a) modulus of elasticity, (b) yield...
Ch. 6.13 - (a) Define the hardness of a metal. (b) How is the...Ch. 6.13 - What types of indenters are used in (a) the...Ch. 6.13 - What are slipbands and slip lines? What causes the...Ch. 6.13 - Describe the slip mechanism that enables a metal...Ch. 6.13 - (a) Why does slip in metals usually take place on...Ch. 6.13 - Prob. 16KCPCh. 6.13 - What other types of slip planes are important...Ch. 6.13 - Define the critical resolved shear stress for a...Ch. 6.13 - Describe the deformation twinning process that...Ch. 6.13 - What is the difference between the slip and...Ch. 6.13 - Prob. 21KCPCh. 6.13 - Prob. 22KCPCh. 6.13 - What experimental evidence shows that grain...Ch. 6.13 - (a) Describe the grain shape changes that occur...Ch. 6.13 - How is the ductility of a metal normally affected...Ch. 6.13 - (a) What is solid-solution strengthening? Describe...Ch. 6.13 - What are the three main metallurgical stages that...Ch. 6.13 - Describe the microstructure of a heavily...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Prob. 33KCPCh. 6.13 - Prob. 34KCPCh. 6.13 - Prob. 35KCPCh. 6.13 - Prob. 36KCPCh. 6.13 - Prob. 37KCPCh. 6.13 - Why are nanocrystalline materials stronger? Answer...Ch. 6.13 - A 70% Cu30% Zn brass sheet is 0.0955 cm thick and...Ch. 6.13 - A sheet of aluminum alloy is cold-rolled 30% to a...Ch. 6.13 - Calculate the percent cold reduction when an...Ch. 6.13 - Prob. 42AAPCh. 6.13 - What is the relationship between engineering...Ch. 6.13 - A tensile specimen of cartridge brass sheet has a...Ch. 6.13 - A 0.505-in.-diameter rod of an aluminum alloy is...Ch. 6.13 - In Figure 6.23, estimate the toughness of SAE 1340...Ch. 6.13 - The following engineering stress-strain data were...Ch. 6.13 - Prob. 49AAPCh. 6.13 - A 0.505-in.-diameter aluminum alloy test bar is...Ch. 6.13 - A 20-cm-long rod with a diameter of 0.250 cm is...Ch. 6.13 - Prob. 52AAPCh. 6.13 - Prob. 53AAPCh. 6.13 - Prob. 54AAPCh. 6.13 - Prob. 55AAPCh. 6.13 - Prob. 56AAPCh. 6.13 - A specimen of commercially pure titanium has a...Ch. 6.13 - Prob. 58AAPCh. 6.13 - Prob. 59AAPCh. 6.13 - Prob. 60AAPCh. 6.13 - Prob. 61AAPCh. 6.13 - Prob. 62AAPCh. 6.13 - Prob. 63AAPCh. 6.13 - Prob. 64AAPCh. 6.13 - Prob. 65SEPCh. 6.13 - Prob. 66SEPCh. 6.13 - A 20-mm-diameter, 350-mm-long rod made of an...Ch. 6.13 - Prob. 68SEPCh. 6.13 - Prob. 69SEPCh. 6.13 - Consider casting a cube and a sphere on the same...Ch. 6.13 - When manufacturing complex shapes using cold...Ch. 6.13 - Prob. 74SEPCh. 6.13 - Draw a generic engineering stress-strain diagram...Ch. 6.13 - (a) Draw a generic engineering stress-strain...Ch. 6.13 - Prob. 77SEPCh. 6.13 - Prob. 78SEPCh. 6.13 - Prob. 79SEPCh. 6.13 - The material for a rod of cross-sectional area...Ch. 6.13 - What do E, G, v, Ur, and toughness tell you about...Ch. 6.13 - A cylindrical component is loaded in tension until...Ch. 6.13 - Referring to Figures 6.20 and 6.21 (read the...Ch. 6.13 - (a) Show, using the definition of the Poissons...Ch. 6.13 - A one-inch cube of tempered stainless steel (alloy...Ch. 6.13 - Prob. 87SEPCh. 6.13 - Prob. 88SEPCh. 6.13 - Prob. 89SEPCh. 6.13 - Prob. 90SEPCh. 6.13 - Prob. 91SEPCh. 6.13 - Prob. 92SEPCh. 6.13 - Prob. 93SEPCh. 6.13 - Prob. 94SEPCh. 6.13 - Starting with a 2-in.-diameter rod of brass, we...Ch. 6.13 - Prob. 96SEPCh. 6.13 - Prob. 97SEPCh. 6.13 - Prob. 98SEPCh. 6.13 - The cupro-nickel substitutional solid solution...Ch. 6.13 - Prob. 100SEP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
6–1C A mechanic claims to have developed a car engine that runs on water instead of gasoline. What is your resp...
Thermodynamics: An Engineering Approach
Find the change in length of side AB.
Mechanics of Materials, 7th Edition
Convert the following quantities from English to SI units: a. 98 Btu/(hr-ft-F) b. 0.24 Btu/(lbm-F) C. 0.04 Ibm/...
Heating Ventilating and Air Conditioning: Analysis and Design
A biological fluid moves at a flow rate of m=0.02kg/s through a coiled, thin-walled, 5-mm-diameter tube submerg...
Fundamentals of Heat and Mass Transfer
The triple jump is a track-and-field event in which an athlete gets a running start and tries to leap as far as...
Vector Mechanics For Engineers
Determine the velocity of block D if end A of the rope is pulled down with a speed of vA = 3 m/s.
Engineering Mechanics: Dynamics (14th Edition)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Determine the tensile strength, yield strength and percentage elongation (% ductility) for an iron- carbon alloy with 0.76 wt % carbon composition. O Yield strength - 60000 psi : Tensile strength - 110000 psi: Ductility - 15% O Yield strength - 130000 psi : Tensile strength - 68000 psi;: Ductility - 10% O Yield strength - 68000 psi : Tensile strength - 130000 psi; Ductility - 10% O Yield strength 50000 psi: Tensile strength - 100000 psi: Ductility - 20% O Yield strength - 86000 psi : Tensile strength 150000 psi: Ductility 25%arrow_forwardA low-nickel steel in the heat-treated condition had an 'engineering' tensile strength of 708 N/mm2. The reduction in area of cross-section at the fracture was 44%. What was the true tensile strength of the steel?arrow_forwardDetermine the modulus of resilience for each of the following alloys using modulus of elasticity given in the below tablearrow_forward
- A copper-zinc alloy has the following properties: Grain Diameter (mm) Strength (MPa) 0.015 170 MPa 0.025 158 MPa 0.035 151 MPa 0.050 145 MPa Determine (a) the constants in the Hall-Petch equation; and (b) the grain size required to obtain a strength of 200 MPa.arrow_forwardQuestion-7. Steady-state creep data taken for an alloy at a stress level of 160 MPa are given below. The stress exponent n for the alloy is 6.8. R is 8.3145 J/mol-K. Compute the steady-state creep rate at 1000 °C and a stress level of 68 MPa. Es (h-1) 6.8 × 10-5 T (°C) 800 8.6 x 10-3 900arrow_forwardHall-Petch Constants Material Y; (MPa) k (MPa.ma) Copper 25 0.12 Titanium 80 0.40 Mild Steel 70 0.74 Using Hall-Petch equation, determine the Yield Stress (MPa) for a Mild Steel piece of metal having a grain size of 100 um. O 115 MPa O 101 MPa O 144 MPa O 130 MPaarrow_forward
- HEY MAY YOU PLEASE HELP ME WITH THE FOLLOWING QUESTIONS Which one of the alloys given below will have the highest hardness. Give a brief explanation and illustrate your answer with an applicable calculation. 98% Pb + 2% Mg (RPb = 0.175nm, RMg = 0.160nm) 98% Pb + 2% Sn (RPb = 0.175nm, RSn = 0.151nm)arrow_forwardUsing the values found in the previous two questions, use the Hall-Petch equation and the graph below for a 70 Cu-30 Zn cartridge brass to predict the yield strength (in MPa) of this alloy when the average grain diameter is 1.0 x 10³ mm. Enter only the numerical value, do not include the unit. Grain size, d (mm) 10- 10-2 5 x 103 200 150 100 50 4 8. 12 16 d1/2 (mm-1/2) Yield strength (MPa)arrow_forwardDetermine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.arrow_forward
- 4. Compare between resilience and toughness. 5. Show by sketch only the creep strain-time (e-t) curve. 6. In Iron-Carbon System, compare between a-ferrite and y-austenite.arrow_forwardQ3 contd. (d) The yield strength values of pure aluminium (Al) and pure copper (Cu) are 25 MPa and 20 MPa, respectively; whereas the yield strength values of cold rolled Al-Mn-Mg alloy and cast 60-40 Brass (60% Cu, 40% Zn) are 200 MPa and 105 MPa, respectively. With aid of schematics, explain the main mechanisms account for the increases in the strengths. (e) A cylindrical tie rod with a diameter of 18.4 mm is subjected to cyclic loading. The stress range is +/- 200 kN. Figure Q3.3 shows the S-N curve of the material of which the rod is made, how many cycles will this rod survive? Stress amplitude O₂ (MPa) 1500 1400 1300 1200 1100 1000 900 800 700 600 500 400 10² 10³ 104 4340 low-alloy steel Stress ratio = -1 Fig. Q3.3 105 106 Number of cycles to failure, Nf 107 108arrow_forwardAn uncold-worked brass specimen of average grain size 0.006 mm has a yield strength of 178 MPa. Estimate the yield strength of this alloy (in MPa) after it has been heated to 600°C for 1000 s, if it is known that the value of ky is 11 MPa-mm1/2. The Animated Figure 7.25 may be helpful. Attached is the question and the figure referenced.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY