The yield strength for an alloy that has an averagegrain diameter of 5.2 x 102 mm is 110 MPa. At agrain diameter of 6.3 x 103 mm, the yield strengthincreases to 251 MPa. At what grain diameter, inmm, will the yield strength be 222 MPa?d =mm

Answered: Image /qna-images/answer/de7aa0be-9e62-4771-b0fc-0a43c2e14329.jpg

The yield strength for an alloy that has an average grain diameter of 5.2 × 10-2 mm is 110 MPa. At a grain diameter of 6.3 × 10³ mm, the yield strength increases to 251 MPa. At what grain diameter, in mm, will the yield strength be 222 MPa? d = mm

The yield strength for an alloy that has an average grain diameter of 5.2 × 10-2 mm is 110 MPa. At a grain diameter of 6.3 × 10³ mm, the yield strength increases to 251 MPa. At what grain diameter, in mm, will the yield strength be 222 MPa? d = mm

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Match the image with the material property depicted by the image. - 1.…

A: Ductile failure or fracture: When the tensile stress increase in a ductile material than it behaves…

Q: e yield strength for an alloy that has an average grain diameter of 4.1 × 10-2 mm is 131 MPa. At a…

A: Given:σ1=131 MPaD1=4.1*10-2 mmD2=7.6*10-3 mmσ2=246 MPaσ=236 MPa

Q: Identify the material as shown in the figure.,

Q: t as a separate question that has no relationship to previous parts of the question. 1 and 2 are…

Q: SHORT ANSWER Use the stress-strain figure below to answer the following questions: 1) In the…

A: The given graph in the question is the stress-strain diagram- There are various points in a…

Q: A graphene sheet with thickness t= 150 nm and u= 0.185 is subjected to a nanoindentation test. Based…

A: thcikness (t) =150 nm and poison's ratio (ν) = 0.185 poison' ratio (ν)= 0.25 young's modulus (Ei )=…

Q: The yield region for steel that has a normal grain diameter of 2.4x10-2 mm is 260 MPa. At a grain…

Q: The compressive strength of alumina quartz (Al2O3) is 2.1 GPa. A quartz tube is being used for a…

Q: Question The yield strength for an aluminum alloy that has an average grain diameter of 10 um is 400…

A: OPTION B -668MPa is the right answer. Detailed explanation and solution of the above problem…

Q: If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force…

Q: When λ=1.5Å and θ=30°, how much strain (Δd/d) is needed to cause a peak broadening same as that of…

A: This problem is related to Braggs law. if λ is the wavelength of X-ray,d is the distance between…

Q: V Use the engincering stress strain diagram provided below to answer parts (A) to (1) below (the…

Q: The fatigue life of a certain steel was found to be 10* cycles at + 70 MPa and 10 cycles at + 50…

Q: (6) For an aluminum alloy under constant load, the creep rate increased by a factor of 2 when the…

Q: (1) Compute the dislocation density in tungsten if the flow stress is controlled by the stress…

A: Since all the questions are different, according to our guidelines, we are supposed to answer 1st…

Q: There are three slip systems on a FCC octahedral plane, i.e. one of the {111} planes. Assume a 2 MPa…

A: "Since you have asked multiple questions, we will answer the first question for you. If you want any…

Q: 7- Calculate the tensile strength of steel: ou = 700 * c% + 340 N mm ( for hypo eutectoid steel)

Q: A sample is made of a făce-centered cubic (fcc) single crystal. The sample starts to have plastic…

A: Given: The stress along {012} direction = 100 MPa

Q: b) Estimate the yield stress of copper containing an array of equally spaced second phase…

A: Yield strength alludes to the pressure at which the event of a foreordained measure of super durable…

Q: The yield strength for an alloy that has an average grain diameter of 1.6 × 10² mm is 320 MPa. At a…

Q: le) Name four methods used for strengthening of metals. What is the common principle that these…

Q: Consider an undeformed, fully annealed copper sample which is loaded in uniaxial tension. Its yield…

A: Given data Yield strength = 3.800×10^1 Mpa Dislocation density = 3.200×10^12 m-2 and KWH= 3.430…

Q: You are given a 10-cm-diameter cylindrically shaped extruded bar (length = 50 cm) of an aluminum…

A: The anisotropic fracture toughness behavior should be an exhibit by the extruded bar with the lowest…

Q: Define Modulus of Rigidity: Word description: Sketch (example) : Equations: Units:

Q: 4- The following strength data were collected for silicon nitride ceramic (Sİ3N4). Calculate the…

Q: Please show how the value of b was calculated Calculate the dislocation density in tungsten if the…

A: The already calculated solution for the given problem is as below.The expression for the dislocation…

Q: An aircraft skin panel that is part of a commercial airline is to be made from aluminium alloy…

Q: An aircraft component, made of 7075-T6 aluminum alloy, can be represented as a bar of diameter 20 mm…

Q: Larger animals have sturdier bones that smaller animals. A mouse’s skeleton is only a few percent of…

A: Given data: Mass of man = 70 kg Cross-sectional area of femur = 4.8 x 10-4 m2 Compressive strength…

Q: 1. A piece of fully-annealed copper crystal has the orientation as shown. It is loaded under the…

A: For determination of resolved shear stress, we have to determine angles between stress direction…

Q: From the grain distribution curve, D60 = 1.45 mm, D30 = 0.75 mm and D10 = 0.45 mm. Determine the…

A: Write the formula for uniformity coefficient. Cu=D60D10 Here, Cu is the uniformity coefficient, D60…

Q: Calculate the tensile modulus (G) of a 1-cm poly(methyl methacrylate) (CAS# 9011-14-7) rod with a…

Q: Strain hardening aluminium increases the strength by reducing the number of dislocations True False

Q: You need to produce a Ci-Ni alloy having minimum yield strength of 20,000psi, a minimum tensile…

A: Required properties for Cu-Ni alloy:Minimum yield strength (σy) = 20,000 psiMinimum tensile strength…

Q: Figure below shows the grain boundaries of low-carbon steel under a microscope with 200X…

Q: Consider the following face-centered-cubic dislocation reaction: (110) [21]+(121) 2 (a) Given [b]= z…

A: The Initial dislocation is,u = 1, v= 1 and z =0.Therefore,

Q: A tensile force of 200 KN is applied on a 0.02-m diameter and.2-m long rod. After applying the load,…

Q: These questions are based on a high carbon stell with a composition of 1.5%C and 98.5%Fe 1)Name the…

A: Given 1.5 wt% C and 98.5 wt%Fe so Co=1.5 wt%C

Q: Use the E- of Chart to identify the metals and ceramics that have E > 10 GPa and of >100 MPa. ? 2-…

Q: The influence of grain size on the yield strength of metallic material is shown in the figure, what…

Q: According to Hall-Petch equation, the 1 point decreasing in grain size causes strengthening of…

A: Hall-Petch equation or Grain-boundary Strengthening predicts that when the grain size decreases…

Q: Stress (MPa) Consider the brass alloy for which the stress-strain behavior is shown in the Animated…

A: Consider the brass alloy for which the stress - strain behavior is shown in the Animated Figure…

Q: onsider the tensile stress-strain diagram in the figure below labeled 1 and 2. These diagrams are…

Q: To put lattice defects in perspective, consider a metal blank that has a dislocation density of 10^3…

A: Given DataDislocation Density=103mm-2Dislocation Volume=103mm3Increased Dislocation Density=1010mm-2…

Q: Tensile stress-strain diag 450 400 350 300 250 200 150 100

A: given:

Q: Column A Column B Increasing thickness of alumina Hardness Column A Column B Increase in atomic…

A: 1) increase in thickness of the lamina DECREASE the hardness. 2)Increase in atomic packing factor…

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

The yield strength for an alloy that has an average
grain diameter of 5.2 x 102 mm is 110 MPa. At a
grain diameter of 6.3 x 103 mm, the yield strength
increases to 251 MPa. At what grain diameter, in
mm, will the yield strength be 222 MPa?
d =
mm

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step 3

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 3 steps with 3 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Please do fast
Which one of the following materials would plastic deformation through twinning be the most likely to occur? O a material with a BCC crystal structure a material with an HCP crystal structure O an amorphous material (no crystal structure) none, twinning does not occur in regular materials Question 2 What is the resolved shear stress in the (111)[110] slip system due to a normal stress of 10 MPa applied in the [010] direction? O -2.31 MPa O -5.35 MPa -4.08 MPa -6.35 MPa
Figure 2 shows the stress versus strain curve of four engineering materials. Compare the ability of the materials to sustain stress without fracture and their ability to absorb the energy before fracture between Material A and D. A C В D Strain Figure 2. Stress versus strain curve of four engineering materials. Stress (MPa)
Calculate Vickers Hardness for a material if pyramid diamond (d)= 0.41mm and applied ?load (F)=30kgf 220 O 110 O 440 O 330 O
How does strain hardening and grain size reduction affect elastic modulus
4. The mechanical properties of a given titanium alloy (Ti-6Al-4V) are E = 114 GPa, σy = 880 MPa and Kic = 75 MPa√m. What is the approximate plastic zone size? How large must a part be made if we want to test its K₁ using LEFM?
0-10) Compare the equilibrium spacing of two partial dislocations between an Al alloy (G=28GPa bie 0.165nm, stacking fault energy 200MJM ) and Gold (G=38GPA, bpartial3D0.166nm, SFE- 9mJm).
When a cold-worked metal is heat-treated below its melting point over a period of time, which of the following phenomena occur? (This question has more than one correct answer) a. Strength is increased b. Dislocation density decreases c. Grain size increases d. Internal lattice strains decrease e. Ductility is reduced
N MPa = 10 2.2. When the Hall-Petch coefficient is 20 GPa nm/2, estimate the grain size of this alloy after recrystallization. -1/2 d O=O₂+ Kuda куба го вра има че app MPa = 150 MPa + 20 × 10 °MPant -150MPa 1
5. Consider a single crystal of some hypothetical metal that has the FCC crystal structure and is oriented such that a tensile stress is applied along a [102] direction. If slip occurs on a (111) plane and in a [101] direction, compute the stress at which the crystal yields if its critical resolved shear stress is 3.42 MPa.
Consider a dislocation condition as shown below. A) what is the strain state in the upper region and B) how would addition of small impurity atoms in the region indicated by "*"s change it? OOOOOO ooooooo OO OO O O O O O O O O O O O O Select one: a. Tensile, would increase tensile strain b. Shear, would increase compressive strain c. Tensile, would decrease tensile strain O d. Compressive, would reduce compressive strain e. Compressive, would increase compressive strain
Hall-Petch Constants Material Y; (MPa) k (MPa.ma) Copper 25 0.12 Titanium 80 0.40 Mild Steel 70 0.74 Using Hall-Petch equation, determine the Yield Stress (MPa) for a Mild Steel piece of metal having a grain size of 100 um. O 115 MPa O 101 MPa O 144 MPa O 130 MPa