Question
Chapter 6, Problem 6.110P
To determine
Theexpression for the tension required in Steckel rolling of a flat sheet.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Wire is drawn through a draw die with entrance angle a= 17°. Starting
diameter is 3.0 mm and final diameter = 2.4 mm. The coefficient of friction at
the work-die interface = 0.08. The metal has a strength coefficient K = 205
MPa and a strain-hardening exponent n =
draw force in this operation.
Why are multiple passes usually required to achieve the desired reduction?
(Hint: Observe the draw stress value found in this question)
0.20. Determine the draw stress and
Lubricant box
Initial wire stock (in coil form)
Multiple
pass/draft
drawing
Draw die
V2, F
V3, F
shown in
figure.
Capstan drum (holds multiple loops of wire)
(1)
(2)
(3)
5) A steel specimen of rectangular cross section with 120 mm width, 180 mm
thickness and 90 mm height was upset at room temperature by open-die forging to
a height of 55 mm. If the strength coefficient and strain hardening exponent of this
material were 1015 MPa and 0.17 respectively, the coefficient of friction is 0.2, and
assuming that the thickness would not change during forging; determine the
required upsetting force at the end of stroke.
During a direct extrusion process for a billet with 5 in long and diameter
2.5 in to 1.6 in. For the work metal, strength coefficient is 75000 Ib/in,
and strain hardening exponent is 0.4, also the die angle of extrusion is
90. In Johnson extrusion strain equation a = 0.8, and b= 1.5. Determine:
(a) extrusion ratio (b) true strain (c) extrusion strain, and (d) ram pressure
at length 5, 4.2, 2.3,1.5,and 0 in.
Chapter 6 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
Ch. 6 - Prob. 6.1QCh. 6 - Prob. 6.2QCh. 6 - Prob. 6.3QCh. 6 - Prob. 6.4QCh. 6 - Prob. 6.5QCh. 6 - Prob. 6.6QCh. 6 - Prob. 6.7QCh. 6 - Prob. 6.8QCh. 6 - Prob. 6.9QCh. 6 - Prob. 6.10Q
Ch. 6 - Prob. 6.11QCh. 6 - Prob. 6.12QCh. 6 - Prob. 6.13QCh. 6 - Prob. 6.14QCh. 6 - Prob. 6.15QCh. 6 - Prob. 6.16QCh. 6 - Prob. 6.17QCh. 6 - Prob. 6.18QCh. 6 - Prob. 6.19QCh. 6 - Prob. 6.20QCh. 6 - Prob. 6.21QCh. 6 - Prob. 6.22QCh. 6 - Prob. 6.23QCh. 6 - Prob. 6.24QCh. 6 - Prob. 6.25QCh. 6 - Prob. 6.26QCh. 6 - Prob. 6.27QCh. 6 - Prob. 6.28QCh. 6 - Prob. 6.29QCh. 6 - Prob. 6.30QCh. 6 - Prob. 6.31QCh. 6 - Prob. 6.32QCh. 6 - Prob. 6.33QCh. 6 - Prob. 6.34QCh. 6 - Prob. 6.35QCh. 6 - Prob. 6.36QCh. 6 - Prob. 6.37QCh. 6 - Prob. 6.38QCh. 6 - Prob. 6.39QCh. 6 - Prob. 6.40QCh. 6 - Prob. 6.41QCh. 6 - Prob. 6.42QCh. 6 - Prob. 6.43QCh. 6 - Prob. 6.44QCh. 6 - Prob. 6.45QCh. 6 - Prob. 6.46QCh. 6 - Prob. 6.47QCh. 6 - Prob. 6.48QCh. 6 - Prob. 6.49QCh. 6 - Prob. 6.50QCh. 6 - Prob. 6.51QCh. 6 - Prob. 6.52QCh. 6 - Prob. 6.53QCh. 6 - Prob. 6.54QCh. 6 - Prob. 6.55QCh. 6 - Prob. 6.56QCh. 6 - Prob. 6.57QCh. 6 - Prob. 6.58QCh. 6 - Prob. 6.59QCh. 6 - Prob. 6.60QCh. 6 - Prob. 6.61QCh. 6 - Prob. 6.62QCh. 6 - Prob. 6.63QCh. 6 - Prob. 6.64QCh. 6 - Prob. 6.65QCh. 6 - Prob. 6.66QCh. 6 - Prob. 6.67QCh. 6 - Prob. 6.68QCh. 6 - Prob. 6.69QCh. 6 - Prob. 6.70QCh. 6 - Prob. 6.71QCh. 6 - Prob. 6.72QCh. 6 - Prob. 6.73PCh. 6 - Prob. 6.74PCh. 6 - Prob. 6.75PCh. 6 - Prob. 6.76PCh. 6 - Prob. 6.77PCh. 6 - Prob. 6.78PCh. 6 - Prob. 6.79PCh. 6 - Prob. 6.80PCh. 6 - Prob. 6.81PCh. 6 - Prob. 6.82PCh. 6 - Prob. 6.83PCh. 6 - Prob. 6.84PCh. 6 - Prob. 6.85PCh. 6 - Prob. 6.86PCh. 6 - Prob. 6.87PCh. 6 - Prob. 6.88PCh. 6 - Prob. 6.89PCh. 6 - Prob. 6.90PCh. 6 - Prob. 6.91PCh. 6 - Prob. 6.92PCh. 6 - Prob. 6.93PCh. 6 - Prob. 6.94PCh. 6 - Prob. 6.95PCh. 6 - Prob. 6.96PCh. 6 - Prob. 6.97PCh. 6 - Prob. 6.98PCh. 6 - Prob. 6.99PCh. 6 - Prob. 6.100PCh. 6 - Prob. 6.101PCh. 6 - Prob. 6.102PCh. 6 - Prob. 6.103PCh. 6 - Prob. 6.104PCh. 6 - Prob. 6.105PCh. 6 - Prob. 6.106PCh. 6 - Prob. 6.107PCh. 6 - Prob. 6.108PCh. 6 - Prob. 6.109PCh. 6 - Prob. 6.110PCh. 6 - Prob. 6.111PCh. 6 - Prob. 6.112PCh. 6 - Prob. 6.113PCh. 6 - Prob. 6.114PCh. 6 - Prob. 6.115PCh. 6 - Prob. 6.116PCh. 6 - Prob. 6.117PCh. 6 - Prob. 6.118PCh. 6 - Prob. 6.119PCh. 6 - Prob. 6.120PCh. 6 - Prob. 6.121PCh. 6 - Prob. 6.122PCh. 6 - Prob. 6.123PCh. 6 - Prob. 6.124PCh. 6 - Prob. 6.125PCh. 6 - Prob. 6.126PCh. 6 - Prob. 6.127PCh. 6 - Prob. 6.128PCh. 6 - Prob. 6.129PCh. 6 - Prob. 6.130PCh. 6 - Prob. 6.131PCh. 6 - Prob. 6.132PCh. 6 - Prob. 6.133PCh. 6 - Prob. 6.134PCh. 6 - Prob. 6.135PCh. 6 - Prob. 6.136PCh. 6 - Prob. 6.137PCh. 6 - Prob. 6.138PCh. 6 - Prob. 6.139PCh. 6 - Prob. 6.140PCh. 6 - Prob. 6.142DCh. 6 - Prob. 6.143DCh. 6 - Prob. 6.144DCh. 6 - Prob. 6.145DCh. 6 - Prob. 6.146DCh. 6 - Prob. 6.147DCh. 6 - Prob. 6.149D
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A spool of copper wire has a starting diameter of 2.5 mm. It is drawn through a die with an opening that is 2.1 mm. The entrance angle of the die = 18°. Coefficient of friction at the work die interface is 0.08. The pure copper has a strength coefficient = 300 MPa and a strain hardening coefficient = 0.50. The operation is performed at room temperature. Determine (a) area reduction, (b) draw stress, and (c) draw force required for the operation.arrow_forwardIn a slab rolling operation, the maximum thickness reduction (del hmax) is given by del hmax = μ²R, where R is the radius of the roll and u is the coefficient of friction between the roll and the sheet. If µ = 0.1, find the maximum angle subtended by the deformation zone at the centre of the roll.arrow_forwardPlease give me full explanation in 1hour do it fast A 4-in-thick aluminum slab is 10 in wide and 100 in long. It is reduced in one pass in a two-high rolling mill to a thickness = 3.5 in. The roll rotates at a speed = 12 rev/min and has a radius = 20 in. The aluminum has a strength coefficient = 25,000 lb/in2 and a strain hardening exponent = 0.20. Determine the (a) roll force, (b) roll torque, and (c) power required to accomplish this operation, d) Estimate the GHG emission in an hour for the rolling operation.arrow_forward
- A rectangufar workpiece has the following original dimensions: 2a = 120 mm, h = 40 mm and width = 25 mm (see Fig. 6.5). The metal has a strength coefficient of 530 MPa and a strain hardening exponent of 0.26. It is being forged in-plane strain with u = 0.25. Calculate the force required at a reduction of 25%. Use the average- Question 2 Not yet answered Marked out of 5 pressure formula. P Flag questionarrow_forwardA plate that is 250 mm wide and 25 mm thick is to be reduced in a single pass in a two-high rolling mill to a thickness of 20 mm. The roll has a radius = 500 mm, and its speed = 30 m/min. The work material has a strength coefficient = 240 MPa and a strain hardening exponent = 0.2. Determine (a)roll force, (b) roll torque, and (c) power required to accomplish this .operation 1365 N & 529865 N-m & 452 W O 500250 N & 12005 N-m & 2456 W O 71254632 N & 135674 N-m & 12053 W O 1851829 N & 46296 N-m & 92,591 W Oarrow_forwardA 3in long and 1in diameter billet is extruded in a direct extrusion operation with an rx = 4.0. The extrusion has a cross section. The angle of the die (half angle) is 90o. The work metal has a resistance coefficient of 60ksi and a strain hardening exponent of 0.18. Use Johnston's formula with a = 0.8 and b = 1.5 to estimate the extrusion stress. Determine the pressure applied to the end of the billet when the piston moves forward.arrow_forward
- A cylindrical part with initial diameter of 45 mm and the initial height of 40 mm is upset forged in an open die to a height = 25 mm. The strength coefficient is 650 MPa and strain- hardening exponent is 0.12. Qa =1.11 (Qa takes into account both friction and workpiece geometry). Calculate the force required for upsetting this part at room temperature. O 1786 kN O 1648 kN O 1247 kN O 1109 kN O none of themarrow_forwardA steel billet with a rectangular cross section is being forged using a die with a width of 84.5 mm. The billet has an original thickness of 46.0 mm and a width of 273 mm. The billet is upset to a thickness of 28.0 mm and the coefficient of friction for the workpiece-die interface is 0.234. Take the strength coefficient (K) as 526 MPa and the strain-hardening exponent (n) as 0.225. a) Determine the maximum die pressure (do not use average pressure formula). Expected answer: 1050 MPa b) Determine the required forging force (use average pressure). Expected answer: 16200000 Narrow_forwardA plate that is 260 mm wide and 27 mm thick is to be reduced in a single pass in a two‑high rolling mill to a thickness of 22 mm. The roll has a radius = 510 mm, and its speed = 25 m/min. The work material has a strength coefficient = 235 MPa and a strain hardening exponent = 0.21. Determine (a) roll force, (b) roll torque, and (c) power required to accomplish this operationarrow_forward
- A compound die will be used to blank and punch a large washer out of 6061ST aluminum alloy sheet stock 3.50 mm thick. The outside diameter of the washer is 50.0 mm and the inside diameter is 15.0 mm. if The aluminum sheet metal has a tensile strength = 310 MPa, a strength coefficient of 350 MPa, and a strain-hardening exponent of 0.12. (a) Assume that blanking and punching occur simultaneously. (b) Assume the punches are staggered so that punching occurs first, then blanking. Determine (1) the punch and die sizes for the blanking operation, and (2) the punch and die sizes for the punching operation.(3) the minimum tonnage press to perform the blanking and punching operationarrow_forwardTwo high rolling mill setup has been used to reduce the thickness of a plate from 40 mm at the maximum draft per pass to become 34 mm after the last pass. The width of the rolled material is 560 mm and the roll diameter is 560 mm. The material has a strength coefficient of 260 MPa and a strain hardening exponent of 0.18. The coefficient of friction during the process was 0.085. Determine the following: 1- Number of passes required to perform the reduction process = 2- Strain of the last pass = 3- Average flow stress of the last pass = MPa 4- The rolling force to roll the last pass =arrow_forwardA metal strip is to be rolled from an initial wrought thickness of 3.5 mm to a final rolled thickness of 2.5 mm in a single pass rolling mill having rolls of 250 mm diameter. The strip is 450 mm wide. The average coefficient of friction in the roll gap is 0.08. Taking plane strain low stress of 140 MPa, for the metal and assuming negligible spreading, the roll separating force is.....arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Types of Manufacturing Process | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=koULXptaBTs;License: Standard Youtube License