Whether the percentage elongations of materials are calculated on the basis of Figure 2.6 or not and also explain the reason
Answer to Problem 2.1Q
The percentage elongations of materials cannot be calculated on the basis of Figure 2.6.
Explanation of Solution
Given:
The Figure 2.6 represents the graph between true strain and true stress.
Concept used:
Write the expression for percentage elongation.
Here, E is percentage elongation,
Calculation:
From Figure 2.6 the value of fracture strain and necking strain can be calculated but the original gage length cannot be calculated from Figure 2.6.
Equation (1) represented that elongation is function of the gage length, and gage length cannot be calculated from Figure 2.6. Therefore, the percentage elongations of materials cannot be calculated by Figure 2.6.
Conclusion:
Thus, the percentage elongations of materials cannot be calculated on the basis of Figure 2.6.
Want to see more full solutions like this?
Chapter 2 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
- Pls. Answer thank you? If the moduli of rigidity and elasticity of a material are 15,000 ksi and 40,000 ksi, respectively, its Poisson’s ratio is __________?arrow_forwardBuild a table with all the mechanical properties presented and discussed in Callister and in the video classes. In the first column, indicate the properties (examples: Modulus of Elasticity, Poisson's Ratio, Tenacity, Ductility, Fracture Tenacity, Flow Stress, etc.) and in the second column explain each one. (maximum one page)arrow_forwardtensile test is performed on metal specimen and it found that a true plastic strain of 0.02 is produced when a true stress of 345 MPa is applied. How much will a specimen of this material elongate when a true stress of 415 MPa is applied if the original length is 500 mm. Assume that the value of 0.22 for strain hardening exponent.arrow_forward
- Given the stress plot, how do you make strain plots for each of the models/materials given (Maxwell and Kelvin-Voigt)?arrow_forwardPlease use all the given information and solve the question by using a mechanical properties.arrow_forwardStress can be related to strain. Explain by using experimental methods?arrow_forward
- Explain what the meaning of strain hardening is, how it happens in the materials. Do you think strain hardening is useful? Explain your answerarrow_forwardcylindrical bar of aluminum 20 mm in diameter is to be deformed elastically in tension. Aforce of 17,000 N. produces a reduction in specimen diameter of 3*10-3 mm if its elastic modulus is100 GPa. Draw the deformation situation and Compute Poisson’s ratio for this material if its elasticmodulus is 100 GPa?arrow_forwardA steel rod is subjected to a force of 5 kN. The initial length of the rod is 690 mm and after elongation its length is equal to 700 mm. Estimate engineering and true strain.arrow_forward
- Calculate the amount of elongation in cm when a mass of 1000 g is suspended on the tip of the spring with a spring constant of 700 N/m.arrow_forwardTaking E=200GPa, A 200 × 100 × 50 mm steel block is subjected to a hydrostatic pressure of 15 MPa. The Poisson's ratio of the material 0.3, Calculate the change in volume of the block?arrow_forwardBy looking at these graphs, answer the following answer: 1/ Is the material is ductile or brittle? explain by using information from the graphs. 2/ What are the differences between these two graphs?arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY