Question
Chapter 8.15, Problem 55SEP
(a)
To determine
Design a Pb-Sn alloy with 50 solid and 50 liquid phase fraction at given temperature.
(b)
To determine
Refer Figure 8.12 and find the amount of each component should be used to produce 100g of the entire alloy.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Your friend in the lab has been working with a 90% Dc, 10% Vr alloy and developed the time-temperature transformation (TTT) diagram below, including the formation of a martensite (M) phase.
You have 3 pieces of this alloy in your furnace currently held at 800 °C. State the steps that you would need to obtain this alloy with the following phase fractions at room temperature:
i. 100 % eta (η) phase
ii. 100 % beta (β) phase
iii. 50% martensite (M), 50% beta (β) phase
A 50 wt% Pb–50 wt% Mg alloy is slowly cooled from 700°C to 400°C. (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? (c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase?
Problem 4
A 50 wt% Ni-50 wt% Cu alloy is slowly
cooled from 1400°C (2550°F) to 1200°C
(2190°F).
(a) At what temperature does the first solid
phase form?
(b) What is the composition of this solid
phase?
(c) At what temperature does the liquid
solidify?
(d) What is the composition of this last
remaining liquid phase?
Chapter 8 Solutions
Foundations of Materials Science and Engineering
Ch. 8.15 - Define (a) a phase in a material and (b) a phase...Ch. 8.15 - In the pure water pressure-temperature equilibrium...Ch. 8.15 - How many triple points are there in the pure iron...Ch. 8.15 - Write the equation for the Gibbs phase rule and...Ch. 8.15 - Refer to the pressuretemperature equilibrium phase...Ch. 8.15 - (a) What is a cooling curve? (b) What type of...Ch. 8.15 - Prob. 7KCPCh. 8.15 - What is an alloy? What is the difference between...Ch. 8.15 - Prob. 9KCPCh. 8.15 - What is the significance of the liquidus curve?...
Ch. 8.15 - Prob. 11KCPCh. 8.15 - Prob. 12KCPCh. 8.15 - Prob. 13KCPCh. 8.15 - Describe the mechanism that produces the...Ch. 8.15 - Can coring and surrounding occur in a...Ch. 8.15 - What is a monotectic invariant reaction? How is...Ch. 8.15 - Write equations for the following invariant...Ch. 8.15 - How are eutectic and eutectoid reactions similar?...Ch. 8.15 - Distinguish between (a) a terminal phase and (b)...Ch. 8.15 - Distinguish between (a) an intermediate phase and...Ch. 8.15 - What is the difference between a congruently...Ch. 8.15 - Consider an alloy containing 70 wt% Ni and 30 wt%...Ch. 8.15 - Consider the binary eutectic coppersilver phase...Ch. 8.15 - If 500 g of a 40 wt% Ag60 wt% Cu alloy is slowly...Ch. 8.15 - A lead-tin (PbSn) alloy consists of 60 wt%...Ch. 8.15 - A PbSn alloy (Fig. 8.12) contains 40 wt% and 60...Ch. 8.15 - An alloy of 30 wt% Pb70 wt% Sn is slowly cooled...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - In the copperlead (CuPb) system (Fig. 8.24) for an...Ch. 8.15 - For an alloy of Cu70 wt% Pb (Fig. 8.24), determine...Ch. 8.15 - What is the average composition (weight percent)...Ch. 8.15 - Consider an Fe4.2 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Consider an Fe5.0 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Determine the weight percent and composition in...Ch. 8.15 - Determine the composition in weight percent of the...Ch. 8.15 - Draw, schematically, the liquidus and the solidus...Ch. 8.15 - Consider the CuZn phase diagram of Figure 8.26. a....Ch. 8.15 - Consider the nickelvanadium phase diagram of...Ch. 8.15 - Consider the titaniumaluminum phase diagram of...Ch. 8.15 - What is the composition of point y in Figure...Ch. 8.15 - In Figure 8.12, determine the degree of freedom,...Ch. 8.15 - The cooling curve of an unknown metal shows a...Ch. 8.15 - In the PbSn phase diagram (Fig. 8.12), answer the...Ch. 8.15 - Based on the CuAg phase diagram in Figure P8.23,...Ch. 8.15 - Based on the PdAg phase diagram in Figure EP 8.3,...Ch. 8.15 - Prob. 49SEPCh. 8.15 - Derive the lever rule for the amount in weight...Ch. 8.15 - Based on the AlNi phase diagram given in Figure...Ch. 8.15 - Prob. 52SEPCh. 8.15 - Based on the Al2O3SiO2 phase diagram in Figure...Ch. 8.15 - (a) Design a CuNi alloy that will be completely...Ch. 8.15 - Prob. 55SEPCh. 8.15 - Given that Pb and Sn have similar tensile...Ch. 8.15 - Consider the sugarwater phase diagram shown in...Ch. 8.15 - In Figure P8.57, if 60 g of water and 140 g of...Ch. 8.15 - In Figure P8.57, if 30 g of water and 170 g of...Ch. 8.15 - At 80C, if the wt% of sugar is 80%, (a) what...Ch. 8.15 - (a) Based on the phase diagram in Figure P8.61,...Ch. 8.15 - Referring to Figure P8.61. explain what happens as...Ch. 8.15 - Referring to Figure P8.61, (a) explain what...Ch. 8.15 - Using Figure P8.40, explain what the phase diagram...Ch. 8.15 - Using Figure P8.40. explain why, according to the...Ch. 8.15 - (a) In the TiAl phase diagram. Figure P8.42, what...Ch. 8.15 - Draw an approximate hypothetical phase diagram for...Ch. 8.15 - Draw the hypothetical phase diagram for a binary...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- For a 64 wt% Zn-36 wt% Cu alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 900°C (1650 F), 820°C (1510 F), 750°C (1380°F), and 600°C (1100 F). Label all phases and indicate their approximate compositions.arrow_forwardFor a 76 wt% Pb–24 wt% Mg alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 575°C, 500°C, 450°C, and 300°C. Label all phases and indicate their approximate compositions.arrow_forwardReferring to Figure 1, answer the following: What are the liquidus and solidus temperatures for an 80%Pb20%Tl alloy? What is the composition of the solid solution phase for the aforementioned alloy once we hit the liquidus temperature upon cooling? For the same alloy above, use the inverse lever rule to calculate the %solid and %liquid at 325Carrow_forward
- a. Your friend in the lab has been working with a 90% Dc, 10% Vr alloy and developed the time-temperature transformation (TTT) diagram below, including the formation of a martensite (M) phase. You have 3 pieces of this alloy in your furnace currently held at 800 °C. State the steps that you would need to obtain this alloy with the following phase fractions at room temperature: i. 100 % eta (η) phase ii. 100 % beta (β) phase iii. 50% martensite (M), 50% beta (β) phase Which of the microstructures formed in part a would you expect to have the highest tensile strength? Would this microstructure also be expected to have the highest elongation? Explain.arrow_forwardA lead-tin (Pb-Sn) alloy of composition 50 wt % Sn and 50 wt % Pb is slowly heated from a temperature of 100 °C. Refer to the phase diagram provided in Figure 1 and answer the following. (i) At what temperature does the first liquid phase form? (ii) What is the composition of this liquid phase? (iii) At what temperature does complete melting of the alloy occur? (iv) What is the composition of the last solid remaining prior to complete melting? Composition (at% Sn) 20 40 60 80 100 327°C 600 300 Liquid 500 232°C a + L 200 B+L 1400 183°C 18.3 61.9 97.8 300 100 a + B 200 H100 20 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Figure 1. Lead (Pb) and Tin (Sn) Phase diagram Temperature (°C) Temperature (°F)arrow_forward3. For a Pb-10% Sn alloy Determine (a) composition of the first solid to form; (b) liquidus temperature, solidus temperature, solvus temperature (as a pplicable), and freezing range of the alloy; (c) amounts and compositions of each phase at 300° C; (d) amounts and compositions of each phase at 200° C; and (e) amounts and compositions of cach phase at 100° C. 400 300 Liquidus Solidus Liquidus Sohdus a+ L 200 19 1831 619 97.5 Solvus Solvus 100 a + B Pb 20 40 60 80 Sn Weight percent tin Temperature ('C)arrow_forward
- Consider the magnesium oxide-aluminum oxide phase diagram; ss indicates a solid solution. The radii of Mg2 + and Al3 + are 0.072 and 0.053 nm, respectively. (a) There are two eutectic reactions on the diagram; describe them (temperatures, compositions and phases). (b) Spinel, at temperatures below 1000 °C, is a compound with a composition of 50 mol% Al2O3-50 mol% MgO. For higher temperatures, spinel is stable for a range of compositions. What is the temperature of the congruent fusion? (c) What are the main reasons for the low solubility of Al2O3 in MgO below 1400 °C? (d) Maximum non-stoichiometry on the Al2O3-rich side, in the spinel phase field, occurs approximately 2000 °C and corresponds to approximately 82 mol% (92% w) of Al2O3. Determine the type of gaps defect that is produced and the percentage of gaps that exists in this composition.arrow_forward1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13 wt. % C steel with no alloying elements. calculate the amount of pro eutectoid product, where applicable (at the bottom) A) quenched in cold water to 650 C in 0.1 seconds, then held at 650 C for 5 seconds, then quenched to 400 C, held at 400C for 60 seconds, and finally quenched to room temperature B. Necessary Steel Phase Diagram Calculations to determine the amount of pro eutectoid product:arrow_forwardA lead-tin (Pb-Sn) alloy of composition 30 wt % Sn and 70 wt % Pb is slowly heated from a temperature of 140 OC. Refer to the phase diagram provided in Figure 1 and answer the following. (i) At what temperature does the first liquid phase form? (ii) What is the composition of this liquid phase? (iii) At what temperature does complete melting of the alloy occur? (iv) What is the composition of the last solid remaining prior to complete melting?arrow_forward
- find the relative amounts (in terms of mass fractions) of the phases for the following alloys and temperature: 90 wt% Zn-10 wt% Cu at 400°C.arrow_forwardBINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…arrow_forward5. For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, ii. Calculate the composition(s) of the phase(s) present. iii. Calculate the amount of each phase present in terms of mass fraction. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 80 100 (Pb) (Sn) Composition (wt% Sn) Temperature ("C) Temperat ure ("F)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
How to balance a see saw using moments example problem; Author: Engineer4Free;https://www.youtube.com/watch?v=d7tX37j-iHU;License: Standard Youtube License