Textbook Question
Chapter 8.15, Problem 63SEP
Referring to Figure P8.61, (a) explain what happens as 23 wt% salt solution is cooled from room temperature to −30°C. Give information regarding phases available and the compositional changes in each phase, (b) What would you call this reaction? Can you write a transformation equation for this reaction?
Figure P8.61
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
What is degree of reaction? Give expressions of reaction rate
equations by degree of reaction.
A) Calculate the differences in the chemical potentials
of ice and super-cooled water at -5.00 C and 1.00 atm
pressure
B) Calculate the differences in the chemical potentials
of super heated ice and water at 100 C and 1.00 atm
pressure
For this problem, the molar entropics for each phase of
water are S (G48.0Jmol K S()700J mol
and S (E)= 18S.8 J mol K
Develop a general equation for the standard heat of reaction as a function of temperature for one of the reactions given in the picture:
Chapter 8 Solutions
Foundations of Materials Science and Engineering
Ch. 8.15 - Define (a) a phase in a material and (b) a phase...Ch. 8.15 - In the pure water pressure-temperature equilibrium...Ch. 8.15 - How many triple points are there in the pure iron...Ch. 8.15 - Write the equation for the Gibbs phase rule and...Ch. 8.15 - Refer to the pressuretemperature equilibrium phase...Ch. 8.15 - (a) What is a cooling curve? (b) What type of...Ch. 8.15 - Prob. 7KCPCh. 8.15 - What is an alloy? What is the difference between...Ch. 8.15 - Prob. 9KCPCh. 8.15 - What is the significance of the liquidus curve?...
Ch. 8.15 - Prob. 11KCPCh. 8.15 - Prob. 12KCPCh. 8.15 - Prob. 13KCPCh. 8.15 - Describe the mechanism that produces the...Ch. 8.15 - Can coring and surrounding occur in a...Ch. 8.15 - What is a monotectic invariant reaction? How is...Ch. 8.15 - Write equations for the following invariant...Ch. 8.15 - How are eutectic and eutectoid reactions similar?...Ch. 8.15 - Distinguish between (a) a terminal phase and (b)...Ch. 8.15 - Distinguish between (a) an intermediate phase and...Ch. 8.15 - What is the difference between a congruently...Ch. 8.15 - Consider an alloy containing 70 wt% Ni and 30 wt%...Ch. 8.15 - Consider the binary eutectic coppersilver phase...Ch. 8.15 - If 500 g of a 40 wt% Ag60 wt% Cu alloy is slowly...Ch. 8.15 - A lead-tin (PbSn) alloy consists of 60 wt%...Ch. 8.15 - A PbSn alloy (Fig. 8.12) contains 40 wt% and 60...Ch. 8.15 - An alloy of 30 wt% Pb70 wt% Sn is slowly cooled...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - In the copperlead (CuPb) system (Fig. 8.24) for an...Ch. 8.15 - For an alloy of Cu70 wt% Pb (Fig. 8.24), determine...Ch. 8.15 - What is the average composition (weight percent)...Ch. 8.15 - Consider an Fe4.2 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Consider an Fe5.0 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Determine the weight percent and composition in...Ch. 8.15 - Determine the composition in weight percent of the...Ch. 8.15 - Draw, schematically, the liquidus and the solidus...Ch. 8.15 - Consider the CuZn phase diagram of Figure 8.26. a....Ch. 8.15 - Consider the nickelvanadium phase diagram of...Ch. 8.15 - Consider the titaniumaluminum phase diagram of...Ch. 8.15 - What is the composition of point y in Figure...Ch. 8.15 - In Figure 8.12, determine the degree of freedom,...Ch. 8.15 - The cooling curve of an unknown metal shows a...Ch. 8.15 - In the PbSn phase diagram (Fig. 8.12), answer the...Ch. 8.15 - Based on the CuAg phase diagram in Figure P8.23,...Ch. 8.15 - Based on the PdAg phase diagram in Figure EP 8.3,...Ch. 8.15 - Prob. 49SEPCh. 8.15 - Derive the lever rule for the amount in weight...Ch. 8.15 - Based on the AlNi phase diagram given in Figure...Ch. 8.15 - Prob. 52SEPCh. 8.15 - Based on the Al2O3SiO2 phase diagram in Figure...Ch. 8.15 - (a) Design a CuNi alloy that will be completely...Ch. 8.15 - Prob. 55SEPCh. 8.15 - Given that Pb and Sn have similar tensile...Ch. 8.15 - Consider the sugarwater phase diagram shown in...Ch. 8.15 - In Figure P8.57, if 60 g of water and 140 g of...Ch. 8.15 - In Figure P8.57, if 30 g of water and 170 g of...Ch. 8.15 - At 80C, if the wt% of sugar is 80%, (a) what...Ch. 8.15 - (a) Based on the phase diagram in Figure P8.61,...Ch. 8.15 - Referring to Figure P8.61. explain what happens as...Ch. 8.15 - Referring to Figure P8.61, (a) explain what...Ch. 8.15 - Using Figure P8.40, explain what the phase diagram...Ch. 8.15 - Using Figure P8.40. explain why, according to the...Ch. 8.15 - (a) In the TiAl phase diagram. Figure P8.42, what...Ch. 8.15 - Draw an approximate hypothetical phase diagram for...Ch. 8.15 - Draw the hypothetical phase diagram for a binary...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Using the Ti-Cu phase diagram, if you start with 100 kg of a Ti-Cu mixture at 3000C and 10 wt. % Cu and cool down very slowly to points A (1400 C), B (950 C), C (800 C), and D (500 C), determine what phases are present at each letter, determine the compositions for each phase, and determine the weight in each phase. Point A): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point B): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point C): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point D): Phase(s) present Weight % of Cu in each phaseWeight of each phasearrow_forwardIdentify the corresponding three-phase invariant reactions below:arrow_forwardQ4/ A sample of 0.676g of an unknown compound containing barium ions (Ba*) is dissolved in water and treated with an excess of NazSO4 If the mass of BaSO4precipitate formed is 0.4105g. What is the percent by mass of Ba in the original unknown compound?arrow_forward
- Using the Ti-Cu phase diagram, if you start with 100 kg of a Ti-Cu mixture at 3000C and 10 wt. % Cu and cool down very slowly to point D (500 C), determine what phases are present at each letter, determine the compositions for each phase, and determine theweight in each phase. Point D): Phase(s) present Weight % of Cu in each phaseWeight of each phasearrow_forwardThe given figure shows the pressure-temperature phase diagram for H2O. Apply the Gibbs phase rule at points A,B, and C, and specify the number of degrees of freedom at each of the points, that is, the number of externally controllable variables that need to be specified to completely define the system.arrow_forwardQuenching is a process used to preserve at room temperature a phase which exists in equilibrium at high temperature but which would decompose during equilibrium cooling. Explain the basis of this process in the precipitation process and martensitic transformation. Use phase diagrams when necessary.arrow_forward
- 1. Calculate the mass fraction fα of α of Fe-0.45% C at 750 °C by the lever rule. Draw the schematic of microstructure of Fe-0.45% C at 20°C which was gradually cooled from 750°C, and describe the name of each phase.arrow_forwardA 65%Ni-35%Cu alloy is heated to be partially melted at a specific temperature T. Here, we find that Cα=70%. Estimate (1) The temperature T,(2) The liquid composition CL ,(3) The weight fractions of the solid and liquid phases.Label the corresponding condition points used.arrow_forwardThe lead and tin are partially dissolved in each other in solid state although they completely dissolved in liquid state. They form eutectic from solid solutions alfa (a) and beta (B) at alloying composition 62% tin and 38% lead, the eutectic forming temperature is 184°C. Alfa contained 20% tin dissolved in 80% lead at 184°C while beta consist of lead dissolved in tin at 184°C. If the 100 g of eutectic contained 45.5 g of alfa at 184°C.Knowing that the melting temperatures of lead and tin are 329°C and 232°C respectively, and the solubility of tin and lead in each other's diminished to zero at room temperature. Answer the following a) Plot the phase diagram for lead-tin system label all phases and temperature. b) What is the composition of beta at eutectic temperature. c) For 40 % lead alloy calculate the phase amount and composition at 350°C, 170°C, and Trarrow_forward
- A 45 wt% Pb-55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high- temperature microstructure is preserved. This microstructure is found to consist of the a phase and Mg2Pb, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Use Animated Figure. °℃arrow_forwardCan you explain how to calculate the reactions step by step?arrow_forward(a) Sketch a Pressure-Temperature phase diagram for a pure substance X where liquid X is less dense than solid X. Insert an isobar at 1 atm and an isotherm at 300 K. Clearly label all physical states, triple point, critical temperature and any normal transition temperatures.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Science, Phase Diagrams, Part 1; Author: Welt der Werkstoffe;https://www.youtube.com/watch?v=G83ZaoB3XCc;License: Standard Youtube License