Mechanics of Materials, 7th Edition
7th Edition
ISBN: 9780073398235
Author: Ferdinand P. Beer, E. Russell Johnston Jr., John T. DeWolf, David F. Mazurek
Publisher: McGraw-Hill Education
expand_more
expand_more
format_list_bulleted
Concept explainers
Videos
Textbook Question
Chapter 11.3, Problem 3P
Determine the modulus of resilience for each of the following metals:
- (a) Stainless steel
AISI 302 (annealed): E = 190 GPa σY = 260 MPa
- (b) Stainless steel
AISI 302 (cold-rolled): E = 190 GPa σY = 520 MPa
- (c) Malleable cast iron: E = 165 GPa σY = 230 MPa
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A tensile test was conducted on a mild steel& the following data was obtained as follows. Diameter of the steel bar = 3 cm,Gauge length of the bar = 20 cm. Load at elastic limit = 250 kN . Extension at a load of 150kN = 0.21 mm . Maximum load = 380 kN . Total extension = 60 mm . Diameter of the rod at failure = 2. 25 cm
Determine: (a) Young’s modulus (b) stress at elastic limit (c)the percentage of elongation (d) Percentage decrease in area.
A square bar of wrought iron 2.6-in on each side is raised to a temperature of 94 deg F above its normal. If held so that it cannot expand, what stress (in bars) will be induced in it? Normal temperature of wrought iron is 32°F. Thermal expansion coefficient, α = 6.8 x 10-6 per deg F. Modulus of Elasticity of wrought iron is 28 x10^3 ksi.
Consider a 1 m-long bar of 2024-T81 aluminum alloy with a 20mm-diameter and the following property data:
E=70 GPa
Y.S = 410 MPa
T.S. = 480 MPa
% Elongation at failure = 8 %
What is the maximum tensile load that can be permitted without producing extensive plastic deformation of the bar? Your answer should be in units of Newtons (N).
Chapter 11 Solutions
Mechanics of Materials, 7th Edition
Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - The stress-strain diagram shown has been drawn...Ch. 11.3 - The stress-strain diagram shown has been drawn...Ch. 11.3 - Prob. 7PCh. 11.3 - Prob. 8PCh. 11.3 - Using E = 29 106 psi, determine (a) the strain...Ch. 11.3 - Using E = 200 GPa, determine (a) the strain energy...
Ch. 11.3 - A 30-in. length of aluminum pipe of...Ch. 11.3 - A single 6-mm-diameter steel pin B is used to...Ch. 11.3 - Prob. 13PCh. 11.3 - Prob. 14PCh. 11.3 - The assembly ABC is made of a steel for which E =...Ch. 11.3 - Show by integration that the strain energy of the...Ch. 11.3 - Prob. 17PCh. 11.3 - Prob. 18PCh. 11.3 - Prob. 19PCh. 11.3 - 11.18 through 11.21 In the truss shown, all...Ch. 11.3 - Prob. 21PCh. 11.3 - Each member of the truss shown is made of aluminum...Ch. 11.3 - Each member of the truss shown is made of aluminum...Ch. 11.3 - 11.24 through 11.27 Taking into account only the...Ch. 11.3 - Prob. 25PCh. 11.3 - 11.24 through 11.27 Taking into account only the...Ch. 11.3 - 11.24 through 11.27 Taking into account only the...Ch. 11.3 - Prob. 28PCh. 11.3 - Prob. 29PCh. 11.3 - Prob. 30PCh. 11.3 - 11.30 and 11.31 Using E = 200 GPa, determine the...Ch. 11.3 - Assuming that the prismatic beam AB has a...Ch. 11.3 - Prob. 33PCh. 11.3 - The design specifications for the steel shaft AB...Ch. 11.3 - Show by integration that the strain energy in the...Ch. 11.3 - The state of stress shown occurs in a machine...Ch. 11.3 - Prob. 37PCh. 11.3 - The state of stress shown occurs in a machine...Ch. 11.3 - Prob. 39PCh. 11.3 - Prob. 40PCh. 11.3 - Prob. 41PCh. 11.5 - A 5-kg collar D moves along the uniform rod AB and...Ch. 11.5 - The 18-lb cylindrical block E has a horizontal...Ch. 11.5 - The cylindrical block E has a speed v0 =16 ft/s...Ch. 11.5 - Prob. 45PCh. 11.5 - Prob. 46PCh. 11.5 - The 48-kg collar G is released from rest in the...Ch. 11.5 - Prob. 48PCh. 11.5 - Prob. 49PCh. 11.5 - Prob. 50PCh. 11.5 - Prob. 51PCh. 11.5 - The 2-kg block D is dropped from the position...Ch. 11.5 - The 10-kg block D is dropped from a height h = 450...Ch. 11.5 - Prob. 54PCh. 11.5 - A 160-lb diver jumps from a height of 20 in. onto...Ch. 11.5 - Prob. 56PCh. 11.5 - A block of weight W is dropped from a height h...Ch. 11.5 - 11.58 and 11.59 Using the method of work and...Ch. 11.5 - 11.58 and 11.59 Using the method of work and...Ch. 11.5 - 11.60 and 11.61 Using the method of work and...Ch. 11.5 - 11.60 and 11.61 Using the method of work and...Ch. 11.5 - 11.62 and 11.63 Using the method of work and...Ch. 11.5 - 11.62 and 11.63 Using the method of work and...Ch. 11.5 - Using the method of work and energy, determine the...Ch. 11.5 - Using the method of work and energy, determine the...Ch. 11.5 - The 20-mm diameter steel rod BC is attached to the...Ch. 11.5 - Torques of the same magnitude T are applied to the...Ch. 11.5 - Prob. 68PCh. 11.5 - The 20-mm-diameter steel rod CD is welded to the...Ch. 11.5 - The thin-walled hollow cylindrical member AB has a...Ch. 11.5 - 11.71 and 11.72 Each member of the truss shown has...Ch. 11.5 - 11.71 and 11.72 Each member of the truss shown has...Ch. 11.5 - Each member of the truss shown is made of steel...Ch. 11.5 - Each member of the truss shown is made of steel....Ch. 11.5 - Each member of the truss shown is made of steel...Ch. 11.5 - The steel rod BC has a 24-mm diameter and the...Ch. 11.9 - 11.77 and 11.78 Using the information in Appendix...Ch. 11.9 - 11.77 and 11.78 Using the information in Appendix...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.83 through 11.85 For the prismatic beam shown,...Ch. 11.9 - 11.83 through 11.85 For the prismatic beam shown,...Ch. 11.9 - 11.83 through 11.85 For the prismatic beam shown,...Ch. 11.9 - 11.86 through 11.88 For the prismatic beam shown,...Ch. 11.9 - 11.86 through 11.88 For the prismatic beam shown,...Ch. 11.9 - 11.86 through 11.88 For the prismatic beam shown,...Ch. 11.9 - For the prismatic beam shown, determine the slope...Ch. 11.9 - For the prismatic beam shown, determine the slope...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - 11.93 and 11.94 For the beam and loading shown,...Ch. 11.9 - 11.93 and 11.94 For the beam and loading shown,...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - Prob. 97PCh. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - 11.99 and 11.100 For the truss and loading shown,...Ch. 11.9 - 11.99 and 11.100 For the truss and loading shown,...Ch. 11.9 - 11.101 and 11.102 Each member of the truss shown...Ch. 11.9 - 11.101 and 11.102 Each member of the truss shown...Ch. 11.9 - 11.103 and 11.104 Each member of the truss shown...Ch. 11.9 - 11.103 and 11 104 Each member of the truss shown...Ch. 11.9 - A uniform rod of flexural rigidity EI is bent and...Ch. 11.9 - For the uniform rod and loading shown and using...Ch. 11.9 - For the beam and loading shown and using...Ch. 11.9 - Two rods AB and BC of the same flexural rigidity...Ch. 11.9 - Three rods, each of the same flexural rigidity EI,...Ch. 11.9 - Three rods, each of the same flexural rigidity EI,...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - For the uniform beam and loading shown, determine...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.121 and 11.122 Knowing that the eight members...Ch. 11.9 - 11.121 and 11.122 Knowing that the eight members...Ch. 11 - Rod AB is made of a steel for which the yield...Ch. 11 - Each member of the truss shown is made of steel...Ch. 11 - The ship at A has just started to drill for oil on...Ch. 11 - Collar D is released from rest in the position...Ch. 11 - Each member of the truss shown is made of steel...Ch. 11 - A block of weight W is placed in contact with a...Ch. 11 - Two solid steel shafts are connected by the gears...Ch. 11 - A 160-lb diver jumps from a height of 20 in. onto...Ch. 11 - For the prismatic beam shown, determine the slope...Ch. 11 - A disk of radius a has been welded to end B of the...Ch. 11 - A uniform rod of flexural rigidity EI is bent and...Ch. 11 - The steel bar ABC has a square cross section of...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- O 0.5% O20% 35% If an isotropic material has a shear modulus of 21 Gpa and a Poisson's ratio of 0.4, calculate its Young's modulus. Select one: O E= 60 Gpa O E= 80 Gpa OE=450 Gpa O E= 30 Gpa OE= 300 Gpa 9:15 PM EN 4/15/202 TOSHIBAarrow_forwardCompare the torsional rigidities of the following sections: (a) a hollow tube 30 mm outside diameter and 1.5 mm thick (b) the same tube split along its length with a 1 mm gap (c) an equal leg angle section having the same perimeter and thickness as (b) (d) a square box section with side length 30 mm and I .5 mm wall thickness (e) a rectangular solid bar, side ratio 2.5 to I. having the same metal cross-sectional area as the hollow tube. Compare also the maximum stresses arising in each case.arrow_forward3. Two brass rods (one square, one circular) are extruded; initial and final dimensions are provided below. Which part is expected to have the greater tensile strength? Which part is expected to have the greater ductility? Part Initial Dimensions Final Dimensions Cylindrical D=2.5 in D = 2.35 in. Square 4 × 4 in. 3.9 × 3.9 in.arrow_forward
- Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.arrow_forwardb) A composite bar is shown in figure Qlb. Determine. The thermal stresses in copper tube and steel bar i. ii. Reaction in the steel bar. Copper tube (a1, E1) Steel bar (a2, E2) L = 500mm Fig Qlb Given: di = 100mm, L = 500mm d2 = 200mm, AT = 100°C Соррer Steel E (GPa) 100 200 al°C 16х 10-6 12 x 10-6arrow_forwardA steel disk with a 150 mm outer diameter is to be press fit to a hollow steel tube whose outer diameter is 90 mm and inner diameter is 45 mm. The maximum tangential stress in the disk is to be 180 MPa. What diametral interference is required between the shaft and the disk to cause this stress? The modulus of the steel is 207 GPa.arrow_forward
- The figure below shows the tensile engineering stress-strain behavior for a steel alloy. (a) What is the modulus of elasticity? (b) What is the yield strength at a strain offset of 0.002? (c) What is the tensile strength? Stress (MPa) 600 500 400 300 200 100 T I 0.00 Stress (MPa) 0.04 500 400 300 200 100 0.000 0.08 0.002 Strain 0.004 Strain 0.12 I 0.006 0.16 0.20 In the previous problem, A load of 85,000 N (19,100 lbf) is applied to a cylindrical specimen of the steel alloy that has a cross-sectional diameter of 15 mm (0.59 in.). (a) Will the specimen experience elastic and/or plastic deformation? Why? (b) If the original specimen length is 250 mm (10 in.), how much will it increase in length when this load is applied?arrow_forward– The weight is suspended from structural A–36 steel alloy and 2014-T6 aluminum alloy wires, eachhaving the same initial length of 10 ft and cross-sectional area of 7×10–3 in2 (Figure Q1). If the weight is increasedgradually, determine which wire yields first? Explain which material model and yield criterion you will use? Justifyyour choicesarrow_forwardA steel rod with a cross-sectional area of 180 mm2 is stretched between two fixed points. The tensile load at 25°C is 3,600N. Assume thermal coefficient equal to 11.7 x 10-6 mm/ (mm°C) and E = 200 GPa. Which of the following most nearly gives the temperature at which the compressive stress will be 48 MPa? Which of the following most nearly gives the temperature at which the tensile stress will be 48 MPa? Which of the following most nearly gives the temperature at which the stress will be zero?arrow_forward
- Problem 4. The stress strain curve for an elastic perfectly plastic material is shown. (This material behaves in a linear elastic manner until the proportion limit. Beyond the proportional limit (PL) the material yields until fracture (fr). = 450 MPa Determine: E = 0.0015 E = 0.250 a. The Modulus of Elasticity (E): b. The Modulus of Resilience (ur): c. The Modulus of Toughness (ut): d. The Strain when o = 240 MPa:arrow_forwardThe shear stress-strain diagram for an alloy is shown in the figure below (Figure 1). Take ✓ = 0.3 This is the info Figure T (ksi) || provided 0.004 y (rad) 1 of 2 Part A If a bolt having a diameter of 0.27 in. is made of this material and used in the lap joint, determine the modulus of elasticity E. (Figure 2) Express your answer to three significant figures and include appropriate units. Submit Part B HÅ Value Request Answer 3 μA P= 3.5.104 Provide Feedback Determine the force P required to cause the material to yield. Express your answer Units 3 o three significant figures and include appropriate units. ? ksi Submit Previous Answers Request Answer ? X Incorrect; Try Again; 5 attempts remaining Enter your answer using units of US customary force. Pearsonarrow_forwardProblem 4 The attached figure shows, for a gray cast iron, the tensile engineering stress-strain curve in the elastic region. Determine (a) the tangent modulus at 25 MPa and (b) the secant modulus taken to 35 MPa. Stress (MPa) 60 50 40 30 20 10 0.0002 0.0004 Strain 0.0006 T 8 6 ★ 2 0.0008 Stress (10³ psi)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Understanding Conduction and the Heat Equation; Author: The Efficient Engineer;https://www.youtube.com/watch?v=6jQsLAqrZGQ;License: Standard youtube license