Textbook Question
Chapter 11.3, Problem 2P
Determine the modulus of resilience for each of the following aluminum alloys:
- (a) 1100-H14: E = 70 GPa: σY = 55 MPa
- (b) 2014-T6: E = 72 GPa: σY = 220 MPa
- (c) 6061-T6: E = 69 GPa: σY = 150 MPa
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
– The weight is suspended from structural A–36 steel alloy and 2014-T6 aluminum alloy wires, eachhaving the same initial length of 10 ft and cross-sectional area of 7×10–3 in2 (Figure Q1). If the weight is increasedgradually, determine which wire yields first? Explain which material model and yield criterion you will use? Justifyyour choices
Question 1
The S-N diagram for a titanium alloy is shown
in the figure. Calculate the fraction of life
consumed by the following sequence of
loadings:
15,000 cycles at 80 MPa
120,000 cycles at 60 MPa
3,500,000 cycles at 50 MPa
Maximum stress (ksi)
160
140
120
100
80
60
40
20
I
10³
104
105
Cycles to failure
100
107
Consider a 1 m-long bar of 2024-T81 aluminum alloy with a 20mm-diameter and the following property data:
E=70 GPa
Y.S = 410 MPa
T.S. = 480 MPa
% Elongation at failure = 8 %
What is the maximum tensile load that can be permitted without producing extensive plastic deformation of the bar? Your answer should be in units of Newtons (N).
Chapter 11 Solutions
Mechanics of Materials, 7th Edition
Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - Determine the modulus of resilience for each of...Ch. 11.3 - The stress-strain diagram shown has been drawn...Ch. 11.3 - The stress-strain diagram shown has been drawn...Ch. 11.3 - Prob. 7PCh. 11.3 - Prob. 8PCh. 11.3 - Using E = 29 106 psi, determine (a) the strain...Ch. 11.3 - Using E = 200 GPa, determine (a) the strain energy...
Ch. 11.3 - A 30-in. length of aluminum pipe of...Ch. 11.3 - A single 6-mm-diameter steel pin B is used to...Ch. 11.3 - Prob. 13PCh. 11.3 - Prob. 14PCh. 11.3 - The assembly ABC is made of a steel for which E =...Ch. 11.3 - Show by integration that the strain energy of the...Ch. 11.3 - Prob. 17PCh. 11.3 - Prob. 18PCh. 11.3 - Prob. 19PCh. 11.3 - 11.18 through 11.21 In the truss shown, all...Ch. 11.3 - Prob. 21PCh. 11.3 - Each member of the truss shown is made of aluminum...Ch. 11.3 - Each member of the truss shown is made of aluminum...Ch. 11.3 - 11.24 through 11.27 Taking into account only the...Ch. 11.3 - Prob. 25PCh. 11.3 - 11.24 through 11.27 Taking into account only the...Ch. 11.3 - 11.24 through 11.27 Taking into account only the...Ch. 11.3 - Prob. 28PCh. 11.3 - Prob. 29PCh. 11.3 - Prob. 30PCh. 11.3 - 11.30 and 11.31 Using E = 200 GPa, determine the...Ch. 11.3 - Assuming that the prismatic beam AB has a...Ch. 11.3 - Prob. 33PCh. 11.3 - The design specifications for the steel shaft AB...Ch. 11.3 - Show by integration that the strain energy in the...Ch. 11.3 - The state of stress shown occurs in a machine...Ch. 11.3 - Prob. 37PCh. 11.3 - The state of stress shown occurs in a machine...Ch. 11.3 - Prob. 39PCh. 11.3 - Prob. 40PCh. 11.3 - Prob. 41PCh. 11.5 - A 5-kg collar D moves along the uniform rod AB and...Ch. 11.5 - The 18-lb cylindrical block E has a horizontal...Ch. 11.5 - The cylindrical block E has a speed v0 =16 ft/s...Ch. 11.5 - Prob. 45PCh. 11.5 - Prob. 46PCh. 11.5 - The 48-kg collar G is released from rest in the...Ch. 11.5 - Prob. 48PCh. 11.5 - Prob. 49PCh. 11.5 - Prob. 50PCh. 11.5 - Prob. 51PCh. 11.5 - The 2-kg block D is dropped from the position...Ch. 11.5 - The 10-kg block D is dropped from a height h = 450...Ch. 11.5 - Prob. 54PCh. 11.5 - A 160-lb diver jumps from a height of 20 in. onto...Ch. 11.5 - Prob. 56PCh. 11.5 - A block of weight W is dropped from a height h...Ch. 11.5 - 11.58 and 11.59 Using the method of work and...Ch. 11.5 - 11.58 and 11.59 Using the method of work and...Ch. 11.5 - 11.60 and 11.61 Using the method of work and...Ch. 11.5 - 11.60 and 11.61 Using the method of work and...Ch. 11.5 - 11.62 and 11.63 Using the method of work and...Ch. 11.5 - 11.62 and 11.63 Using the method of work and...Ch. 11.5 - Using the method of work and energy, determine the...Ch. 11.5 - Using the method of work and energy, determine the...Ch. 11.5 - The 20-mm diameter steel rod BC is attached to the...Ch. 11.5 - Torques of the same magnitude T are applied to the...Ch. 11.5 - Prob. 68PCh. 11.5 - The 20-mm-diameter steel rod CD is welded to the...Ch. 11.5 - The thin-walled hollow cylindrical member AB has a...Ch. 11.5 - 11.71 and 11.72 Each member of the truss shown has...Ch. 11.5 - 11.71 and 11.72 Each member of the truss shown has...Ch. 11.5 - Each member of the truss shown is made of steel...Ch. 11.5 - Each member of the truss shown is made of steel....Ch. 11.5 - Each member of the truss shown is made of steel...Ch. 11.5 - The steel rod BC has a 24-mm diameter and the...Ch. 11.9 - 11.77 and 11.78 Using the information in Appendix...Ch. 11.9 - 11.77 and 11.78 Using the information in Appendix...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.79 through 11.82 For the beam and loading...Ch. 11.9 - 11.83 through 11.85 For the prismatic beam shown,...Ch. 11.9 - 11.83 through 11.85 For the prismatic beam shown,...Ch. 11.9 - 11.83 through 11.85 For the prismatic beam shown,...Ch. 11.9 - 11.86 through 11.88 For the prismatic beam shown,...Ch. 11.9 - 11.86 through 11.88 For the prismatic beam shown,...Ch. 11.9 - 11.86 through 11.88 For the prismatic beam shown,...Ch. 11.9 - For the prismatic beam shown, determine the slope...Ch. 11.9 - For the prismatic beam shown, determine the slope...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - 11.93 and 11.94 For the beam and loading shown,...Ch. 11.9 - 11.93 and 11.94 For the beam and loading shown,...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - Prob. 97PCh. 11.9 - For the beam and loading shown, determine the...Ch. 11.9 - 11.99 and 11.100 For the truss and loading shown,...Ch. 11.9 - 11.99 and 11.100 For the truss and loading shown,...Ch. 11.9 - 11.101 and 11.102 Each member of the truss shown...Ch. 11.9 - 11.101 and 11.102 Each member of the truss shown...Ch. 11.9 - 11.103 and 11.104 Each member of the truss shown...Ch. 11.9 - 11.103 and 11 104 Each member of the truss shown...Ch. 11.9 - A uniform rod of flexural rigidity EI is bent and...Ch. 11.9 - For the uniform rod and loading shown and using...Ch. 11.9 - For the beam and loading shown and using...Ch. 11.9 - Two rods AB and BC of the same flexural rigidity...Ch. 11.9 - Three rods, each of the same flexural rigidity EI,...Ch. 11.9 - Three rods, each of the same flexural rigidity EI,...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - 11.111 through 11.115 Determine the reaction at...Ch. 11.9 - For the uniform beam and loading shown, determine...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.117 through 11.120 Three members of the same...Ch. 11.9 - 11.121 and 11.122 Knowing that the eight members...Ch. 11.9 - 11.121 and 11.122 Knowing that the eight members...Ch. 11 - Rod AB is made of a steel for which the yield...Ch. 11 - Each member of the truss shown is made of steel...Ch. 11 - The ship at A has just started to drill for oil on...Ch. 11 - Collar D is released from rest in the position...Ch. 11 - Each member of the truss shown is made of steel...Ch. 11 - A block of weight W is placed in contact with a...Ch. 11 - Two solid steel shafts are connected by the gears...Ch. 11 - A 160-lb diver jumps from a height of 20 in. onto...Ch. 11 - For the prismatic beam shown, determine the slope...Ch. 11 - A disk of radius a has been welded to end B of the...Ch. 11 - A uniform rod of flexural rigidity EI is bent and...Ch. 11 - The steel bar ABC has a square cross section of...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A tensile-testing apparatus is to be constructed that must withstand a maximum load of 293516 N. The design calls for two cylindrical support posts, each of which is to support half of the maximum load; the minimum yield and tensile strengths of this alloy are 343 MPa and 565 MPa or 82,000 psi respectively.what is required diameter? Take factor of safety is 2.3arrow_forwardPlease provide detailed solution, thank you. τA = ? psi τB = ? psiarrow_forwardWhich steel presents the maximum modulus of resilience UR? UR = 1/2 × ((Sy^2)/E) AISI 4142 AISI 1095 and AISI 1020 AISI 1020 They are all the samearrow_forward
- Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.arrow_forwardBar DE is steel (E = 29,000 ksi, oYield = 36 ksi) and has a cross-section area of 0.25 in2. Bar BC is brass (E = 15,000 ksi, oYield = 30 ksi) and has a cross-sectional area of 0.30 in2. Bar ABDF can be considered rigid. Both the steel and brass bars are deformable. The weight of the bars can be assumed negligible in comparison to the forces they are supporting. Find the axial stress in the steel and brass bars and the deflection at point A. Not to Scale E 16 in 8 in UMU VOVE 2 in 4 in 4 in D 5.4 kipsarrow_forwardThe blue bar is made from steel with the following mechanical properties: Young's Modulus, E = 17x10° psi; Poisson's Ratio v = 0.31. The bar has a circular cross-section with diameter d= 0.50 in. being the length of each side. 557 lb 557 Ib 60 in. - Determine the following under the action of the axial load (assume elastic behavior): a. The bar's axial deformation, ô, in in.: b. The average axial or longitudinal strain, ELong: c. The change in the bar's diameter, in in.:arrow_forward
- Lo=80 mm, Copper Alloy C93200 (bearing bronze), T1=20 C, T2=75 C. dL=?, Lf=? Copper Alloy C93200 (bearing bronze) is Coefficient of Thermal Expansion : 10-6 (°C)-1 is 18.0 Coefficient of Thermal Expansion : 10-6 (°F)-1 is 10.0arrow_forwardThe figure below shows the tensile engineering stress-strain behavior for a steel alloy. (a) What is the modulus of elasticity? (b) What is the yield strength at a strain offset of 0.002? (c) What is the tensile strength? Stress (MPa) 600 500 400 300 200 100 T I 0.00 Stress (MPa) 0.04 500 400 300 200 100 0.000 0.08 0.002 Strain 0.004 Strain 0.12 I 0.006 0.16 0.20 In the previous problem, A load of 85,000 N (19,100 lbf) is applied to a cylindrical specimen of the steel alloy that has a cross-sectional diameter of 15 mm (0.59 in.). (a) Will the specimen experience elastic and/or plastic deformation? Why? (b) If the original specimen length is 250 mm (10 in.), how much will it increase in length when this load is applied?arrow_forwardA tensile test was conducted on a mild steel& the following data was obtained as follows. Diameter of the steel bar = 3 cm,Gauge length of the bar = 20 cm. Load at elastic limit = 250 kN . Extension at a load of 150kN = 0.21 mm . Maximum load = 380 kN . Total extension = 60 mm . Diameter of the rod at failure = 2. 25 cm Determine: (a) Young’s modulus (b) stress at elastic limit (c)the percentage of elongation (d) Percentage decrease in area.arrow_forward
- 1. An 8.0-mm (0.31-in.-) diameter cylindrical rod fabricated from a red brass alloy (Figure 8.34) is subjected to reversed tension-compression loading cycling along it’s axis. If the maximum tensile and compressive loads are +7500 N (1700lbf) -7500 N (-1700 lbf), respectively, determine it’s fatigue life. Assume that the stress plotted in Figure 8.34 is stress amplitude. 2. Consider an 18-8 Mo stainless (Figure 8.35) that is exposed to a temperature 500C (773K). What is maximum allowable stress level for a rupture lifetime of 5 years? 20years? Please state the given. Thanks a lot…arrow_forwardThe shear stress-strain diagram for an alloy is shown in the figure below (Figure 1). Take ✓ = 0.3 Figure 7 (ksi) и Ty 50 0.004 y (rad) < 1 of 2 Part A If a bolt having a diameter of 0.27 in. is made of this material and used in the lap joint, determine the modulus of elasticity E. (Figure 2) Express your answer to three significant figures and include appropriate units. E 3.25x10 ksi Submit ✓ Correct Part B Previous Answers Determine the force P required to cause the material to yield. Express your answer to three significant figures and include appropriate units. P= 5.73 X Incorrect Enter your Provide Feedback μA Submit Previou Answers Request Answer ksi ? Wronarrow_forwardThank you for answering this question. Please you specify each step as soon as possible. Good Luck! Thank You. Find the maximum biaxial stress,ox= -20, oy= -30, o > 0, that one can apply to a 60° lamina of glass/epoxy. Use maximum stress theory. Strength values of glass/epoxy: (01Jult = 1062 MPa, (01Jult= 610 MPa, (02")ut = 30 MPa, (02)ult = 118 MPa, (T12)ult = 72 MPaarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Relationship Between Elastic Constants and Connecting Equations; Author: Engineers Academy;https://www.youtube.com/watch?v=whW5PnM7Pug;License: Standard Youtube License