Textbook Question
Chapter 8.4, Problem 1P
A tension test was performed on a steel specimen having an original diameter of 0.503 in. and gage length of 2.00 in. The data is listed in the table. Plot the stress–strain diagram and determine approximately the modulus of elasticity, the yield stress, the ultimate stress, and the fracture stress. Use a scale of 1 in. = 20 ksi and 1 in. = 0.05 in./in. Redraw the elastic region, using the same stress scale but a strain scale of 1 in. = 0.001 in./in.
Load (kip) | Elongation (in.) |
0 | 0 |
1.50 | 0.0005 |
4.00 | 0.0015 |
8.00 | 0.0025 |
11.00 | 0.0035 |
11.80 | 0.0050 |
11.80 | 0.0080 |
12.00 | 0.0200 |
16.60 | 0.0400 |
20.00 | 0.1000 |
21.50 | 0.2800 |
19.50 | 0.4000 |
18.50 | 0.4600 |
Prob. 8–1
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
diagram and determine approximately the modulus of
elasticity, the yield stress, the ultimate stress, and the fracture
2.00 in. The data is listed in the table. Plot the stress-strain
8-1. A tension test was performed on a steel specimen
n original diameter of 0.503 in. and gage length of
PROBLEMS
*84.
origi
the f
having an
for t
and
stress. Use a scale of 1 in.
Dodraw the elastic region, using the same stress scale but a
20 ksi and 1 in. = 0.05 in./in.
strain scale of 1 in.= 0.001 in./in.
Load (kip) Elongation (in.)
0.
0.
0.0005
0.0015
1.50
4.60
8.00
11.00
0.0025
0.0035
0.0050
11.80
11.80
0.0080
0.0200
12.00
16.60
0.0400
0.1000
0.2800
20.00
21.50
19.50
18.50
0.4000
0.4600
Prob. 8-1
The principal plane stresses and associated strains in a
35 ksi, 02 = 15 ksi,
plane at a point are 01
1
€1 = 1.02(10-3), 2 = 0.180(10-³).
▼
Determine the modulus of elasticity.
Express your answer using three significant figures and include the appropriate units.
E=
Submit
Part B
V=
μA
Value
Request Answer
Submit
Determine the Poisson's ratio.
Express your answer using three significant figures.
ΠΑΠΙ ΑΣΦ | Η
VE
Units
Request Answer
?
vec
POSSIA
space
?
A tensile test specimen has a gage length = 3.0 in and
diameter 0.75 in. Yielding occurs at a load of 38,000 lb. The
corresponding gage length = 3.0103 in (neglect the 0.2 percent
yield point). The maximum load of 54,000 lb is reached at a gage
length = 3.453 in. Determine the modulus of elasticity (neglect
the 0.2% offset, and round to the nearest whole Msi).
37
Chapter 8 Solutions
Statics and Mechanics of Materials (5th Edition)
Ch. 8.4 - Define a homogeneous material.Ch. 8.4 - Prob. 2FPCh. 8.4 - Prob. 3FPCh. 8.4 - Prob. 4FPCh. 8.4 - Prob. 5FPCh. 8.4 - As the temperature increases the modulus of...Ch. 8.4 - Prob. 7FPCh. 8.4 - Prob. 8FPCh. 8.4 - Prob. 9FPCh. 8.4 - Prob. 10FP
Ch. 8.4 - The material for the 50-mm-long specimen has the...Ch. 8.4 - If the elongation of wire BC is 0.2 mm after the...Ch. 8.4 - A tension test was performed on a steel specimen...Ch. 8.4 - Data taken from a stressstrain test for a ceramic...Ch. 8.4 - Data taken from a stressstrain test for a ceramic...Ch. 8.4 - Prob. 4PCh. 8.4 - The stress-strain diagram for a steel alloy having...Ch. 8.4 - Prob. 6PCh. 8.4 - The rigid beam is supported by a pin at C and an...Ch. 8.4 - The rigid beam is supported by a pin at C and an...Ch. 8.4 - Prob. 9PCh. 8.4 - The stressstrain diagram for an aluminum alloy...Ch. 8.4 - The stressstrain diagram for an aluminum alloy...Ch. 8.4 - Prob. 12PCh. 8.4 - A bar having a length of 5 in. and cross-sectional...Ch. 8.4 - The rigid pipe is supported by a pin at A and an...Ch. 8.4 - The rigid pipe is supported by a pin at A and an...Ch. 8.4 - Prob. 16PCh. 8.4 - The rigid beam is supported by a pin at C and an...Ch. 8.4 - Prob. 18PCh. 8.4 - Prob. 19PCh. 8.6 - A 100 mm long rod has a diameter of 15 mm. If an...Ch. 8.6 - A solid circular rod that is 600 mm long and 20 mm...Ch. 8.6 - Prob. 15FPCh. 8.6 - Prob. 16FPCh. 8.6 - The acrylic plastic rod is 200 mm long and 15 mm...Ch. 8.6 - The plug has a diameter of 30 mm and fits within a...Ch. 8.6 - The elastic portion of the stress-strain diagram...Ch. 8.6 - The elastic portion of the stress-strain diagram...Ch. 8.6 - The brake pads for a bicycle tire arc made of...Ch. 8.6 - The lap joint is connected together using a 1.25...Ch. 8.6 - The lap joint is connected together using a 1.25...Ch. 8.6 - Prob. 27PCh. 8.6 - The shear stress-strain diagram for an alloy is...Ch. 8.6 - Prob. 29PCh. 8 - The elastic portion of the tension stress-strain...Ch. 8 - Prob. 2RPCh. 8 - Prob. 3RPCh. 8 - Prob. 4RPCh. 8 - Prob. 5RPCh. 8 - Prob. 6RPCh. 8 - The stress-strain diagram for polyethylene, which...Ch. 8 - The pipe with two rigid caps attached to its ends...Ch. 8 - Prob. 9RPCh. 8 - Prob. 10RP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- The steel bolt and anchor assembly is used to reinforce the roof of a passageway in an underground coal mine. In installation, the bolt is tensioned to 5,500 lb. Calculate the stress, strain, and extension of the bolt with length I= 39 in. if it is formed from 1045 steel alloy. Coal seam Passageway in. Roof line (Express your answer using three significant figures.) |ksi (Express your answer using two significant figures.) |×10-4 (Express your answer using whole numbers.) mils AL = %3Darrow_forwardTensile test specimens are extracted from the "X" and "y" directions of a rolled sheet of metal. "x" is the rolling direction, "y" is transverse to the rolling direction, and "z" is in the thickness direction. Both specimens were pulled to a longitudinal strain = 0.15 strain. For the sample in the x-direction, the width strain was measured to be ew= -0.0923 at that instant. For the sample in the y-direction, the width strain was measured to be gw=-0.1000 at that instant. The yield strength of the x-direction specimen was 50 kpsi and the yield strength of the y-direction specimen was 52 kpsi. Determine the strain ratio for the x direction tensile test specimen. Determine the strain ratio for the y-direction tensile test specimen. Determine the expected yield strength in the z-direction. Give your answer in units of kpsi (just the number). If the sheet is plastically deformed in equal biaxial tension (a, = 0, to the point where & = 0.15, calculate the strain, 6, that would be expected.arrow_forwardNatural rubber is tested in tension to a maximum extension ratio of λ = 3. The Mooney-Rivlin constants for this material are found to be C1 = 0.069 MPa and C2 = 0.125 MPa. Plot the corresponding uniaxial stress vs. extension ratio behavior over the tested range. Derive an expression for the slope of the function, then determine the secant and tangent moduli at 100% strain.arrow_forward
- A tension test was performed on a specimen having an original diameter of 12.5 mm and a gage length of 50mm. The data are listed in the table below: Complete the following: Plot the stress-strain curve. Label the y-axis every 50 MPa, and the x-axis every 0.05 mm/mm. Plot the linear portion of the stress-strain curve (first 5 points). Label the y-axis every 50 MPa, and the x-axis every 0.001 mm/mm. Determine the approximate Modulus of Elasticity Determine the approximate Ultimate Stress Determine the approximate Fracture Stress Determine the approximate Modulus of Resilience Determine the approximate Modulus of Toughness Other Requirements: Provide an example hand-written calculation showing how you calculated one point on the curve. Remember to properly label your plots and provide axis labels with units. Hand sketched plots will not be accepted. Use Excel or similar software.arrow_forwardA tensile test specimen has a gage length = 3.0 in and diameter 0.75 in. Yielding occurs at a load of 38,000 lb. The corresponding gage length 3.01 03 in (neglect the 0.2 percent yield point). The maximum load of 54,000 lb is reached at a gage length 3.453 in. Determine the tensile strength (round to the nearest whole Ksi) 38arrow_forwardShown is the stress-strain curve developed from the tension test of a metal alloy bar. The specimen used to develop the stress-strain curve has a round cross-section with a diameter of d = 7 mm and a gauge length of L = 370 mm. Determine the load that must be applied to the specimen to stress the specimen to it's 0.2% offset yield. Express your answer in kN to the nearest whole kN. Your written solution must also include the length of the specimen when stressed to the 0.2% offset yield stress. σ (MPa) 700 600 500 400 300 200 100 0 0.02 0.04 0.06 0.08 0.10 0.002 0.004 0.006 0.008 0.010 € (mm/mm) P darrow_forward
- Determine the elastic modulus and the yield strength for the material having the stress-strain curve shown. Use the 0.2% offset method. 1600 1400 1200 E 1000 800 600 400 200 0.5 1 1.5 2 Strain, percent Elastic modulus: (Express your answer in whole numbers.) E = ksi Yield strength: (Express your answer using three significant figures.) Sy = ksi Stress, psiarrow_forwardThe elastic portion of the tension stress–strain diagram for an aluminum alloy is shown in the figure. The specimen used for the test has a gage length of 2 in. and a diameter of 0.5 in. If the applied load is 10 kip, determine the new diameter of the specimen. The shear modulus is Gal = 3.811032 ksi.arrow_forwardA tensile test specimen of 1045 hot-rolled steel having a diameter of 0.505 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the modulus of elasticity. Stress (ksi) 240 200 160- 120- 80 40- 0+ 0 0 Upper scale O 79100 ksi E O 94000 ksi O 86700 ksi O 63200 ksi O 51900 ksi Lower scale. 0.025 0.050 0.075 0.100 0.125 0.150 0.175 0.002 0.004 0.006 0.008 0.010 0.012 0.014 Strain (in./in.)arrow_forward
- Electrical strain gauges were applied to a notched specimen to determine the stresses in the notch. The results were ex = 0.0019 and ey = -0.00072. Find ox and ay if the material is carbon steel.arrow_forwardFind the strain proportions (ɛ1:E2:E3) that existed in a forming process where O3= 0. Also specify two conditions that can be used the stresses are 01 02=01/3 , to describe the deformation process.arrow_forward8-2. Data taken from a stress-strain test for a ceramic are given in the table. The curve is linear between the origin and the first point. Plot the diagram, and determine the modulus of elasticity and the modulus of resilience. o (MPa) e (mm/mm) 232.4 318.5 0.0006 0.0010 345.8 0.0014 0.0018 360.5 373.8 0.0022arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY