Question
Chapter 7, Problem 7.7P
To determine
The tensile strength and elastic modulus of alloy.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A batch of casted mild steel has a modulus of elasticity of 200 GPa and a yield strength of 250 MPa. Calculate for its modulus of resilience. After cold working the steel, the yield strength increases to 310 MPa. Calculate for the percent reduction in the average grain diameter given σo = 70 MPa and k = 0.74.
Task (3)
you are asked to perform tensile test on specimens of two different materials (A and B) and you obtained the
stress-strain diagram of the two specimens as shown in Figure 2:
400
350
300
250
Material A
200
150
100
50
0.02
0.04
0.06
0.08
0.1
0.12
0.14
0.16
0.18
Strain (mm/mm)
50
Material B
30
20
10
0.02
0.04
0.06
0.08
0.1
Strain (mm/mm)
Figure 2: Tensile Test Analysis
Stress (MPa)
Stress (MPa)
(b) (i)
A tensile test specimen made from 0.4% C steel has a circular cross section of diameter
d mm and a gauge length of 25 mm. When a load of 4500 N is applied during the test, the
gauge length of the specimen extends to 25.02 mm.
If the Young's Modulus of the steel is 199 GPa, calculate the diameter of the
tensile test specimen used.
4
Chapter 7 Solutions
Materials Science And Engineering Properties
Ch. 7 - Prob. 1CQCh. 7 - Prob. 2CQCh. 7 - Prob. 3CQCh. 7 - Prob. 4CQCh. 7 - Prob. 5CQCh. 7 - Prob. 6CQCh. 7 - Prob. 7CQCh. 7 - Prob. 8CQCh. 7 - Prob. 9CQCh. 7 - Prob. 10CQ
Ch. 7 - Prob. 11CQCh. 7 - Prob. 12CQCh. 7 - Prob. 13CQCh. 7 - Prob. 14CQCh. 7 - Prob. 15CQCh. 7 - Prob. 16CQCh. 7 - Prob. 17CQCh. 7 - Prob. 18CQCh. 7 - Prob. 19CQCh. 7 - Prob. 20CQCh. 7 - Prob. 21CQCh. 7 - Prob. 22CQCh. 7 - Prob. 23CQCh. 7 - Prob. 24CQCh. 7 - Prob. 25CQCh. 7 - Prob. 26CQCh. 7 - Prob. 27CQCh. 7 - Prob. 28CQCh. 7 - Prob. 29CQCh. 7 - Prob. 30CQCh. 7 - Prob. 31CQCh. 7 - Prob. 32CQCh. 7 - Prob. 33CQCh. 7 - Prob. 34CQCh. 7 - Prob. 35CQCh. 7 - Prob. 36CQCh. 7 - Prob. 37CQCh. 7 - Prob. 38CQCh. 7 - Prob. 39CQCh. 7 - Prob. 40CQCh. 7 - Prob. 41CQCh. 7 - Prob. 42CQCh. 7 - Prob. 43CQCh. 7 - Prob. 44CQCh. 7 - Prob. 45CQCh. 7 - Prob. 46CQCh. 7 - Prob. 47CQCh. 7 - Prob. 48CQCh. 7 - Prob. 49CQCh. 7 - Prob. 50CQCh. 7 - Prob. 51CQCh. 7 - Prob. 52CQCh. 7 - Prob. 1DRQCh. 7 - Prob. 2DRQCh. 7 - Prob. 3DRQCh. 7 - Prob. 4DRQCh. 7 - Prob. 5DRQCh. 7 - Prob. 6DRQCh. 7 - Prob. 7DRQCh. 7 - Prob. 8DRQCh. 7 - Prob. 1ETSQCh. 7 - Prob. 2ETSQCh. 7 - Prob. 3ETSQCh. 7 - Prob. 4ETSQCh. 7 - Prob. 5ETSQCh. 7 - Prob. 6ETSQCh. 7 - Prob. 7ETSQCh. 7 - Prob. 8ETSQCh. 7 - Prob. 9ETSQCh. 7 - Prob. 7.1PCh. 7 - Prob. 7.2PCh. 7 - Prob. 7.3PCh. 7 - Prob. 7.4PCh. 7 - Prob. 7.5PCh. 7 - Prob. 7.6PCh. 7 - Prob. 7.7PCh. 7 - Prob. 7.8PCh. 7 - Prob. 7.9PCh. 7 - Prob. 7.10PCh. 7 - Prob. 7.11PCh. 7 - Prob. 7.13P
Knowledge Booster
Similar questions
- i need quickly please please please Which of these cast iron would allow the greatest amount of plastic deformation before fracture . Nodular cast iron Grey cast iron White cast iron None of them can be worked. If the diameter of steel specimen stretched by tension load is doubled , then it’s tensile strength will be Halved Remain unaffected Doubled Become four times Temperature is proportional with Percent of elongation Tensile strength Modulus of elasticity All above The tensile strength of a steel specimen that have a 182 HB , equals to 490 MPa 910 MPa 627 MPa Not given…arrow_forwardQuestion-5 The following engineering stress-strain data were obtained from the tensile test for a 0.2% plain carbon steel. (a) Plot the engineering stress-strain curve for these data. (b) Determine the 0.2 percent offset yield stress for this steel. (c) Determine the tensile elastic modulus of this steel. (d) Determine the ultimate tensile strength of the alloy. (e) Determine the percent elongation at fracture. Engineering stress (ksi) 0 30 55 60 68 72 74 75 Engineering strain (in./in.) 0 0.001 0.002 0.005 0.01 0.02 0.04 0.06 Engineering stress (ksi) 76 75 73 69 65 56 51 Engineering strain (in./in.) 0.08 0.10 0.12 0.14 0.16 0.18 (Fracture) 0.19 Question-6 A 20-cm-long rod with a diameter of 0.250 cm is loaded with a 5000 N weight. If the diameter decreases to 0.210 cm, determine (a) the engineering stress and strain at this load and (b) the true stress and strain at this load.arrow_forwardQ3: A cylindrical specimen of steel having an original diameter of (12.8mm) is tensile tested to fracture and found to have engineering fracture strength of (450MP ). If its cross-sectional diameter at fracture is (10.7mm), determine: (1) the ductility in terms of percent reduction in area and (2) the true stress at fracture.arrow_forward
- A structural component in the shape of a flat plate 24.3 mm thick is to be fabricated from a metal alloy for which the yield strength and plane strain fracture toughness values are 533 MPa and 22.0 MPa-m1/2, respectively. For this particular geometry, the value of Y is 1.3. Assuming a design stress of 0.4 times the yield strength, calculate the critical length of a surface flaw. What formulas do i use ? And how do i use them?arrow_forwardA nondestructive testing program for a component made of 1040 steel can ensure that no flaws greater than 1 mm will exist. Will this inspection program be effective in preventing fast fracture? The steel of interest has a fracture toughness of Klc =120 MPa √m, a tensile modulus of E=207 GPa, a yield strength = 290 MPa, and an ultimate tensile strength of 520 MPa.arrow_forwardAn aluminum alloy rod with 10 mm diameter was subjected to a 5-kN tensile load. After the load was applied, the diameter was measured and found to be 9.997 mm. If the yield strength is 139 MPa, calculate the Poisson’s ratio of the material.arrow_forward
- The stress-strain tests were carried out on five different metals (A, B, C, D and E) and the results are shown in the figure below. Select the metal for given properties. Stress L ii. iii. iv. V. vi. B Strain Property Highest resistance to plastic strain Lowest stiffness Highest ductility Highest brittleness Highest tensile strength Lowest fracture strength Metal (A, B, C, D or E) Narrow_forwardWhat are the two major considerations for avoiding brittle fracture in ceramics?arrow_forwardA mild steel specimen with an original length of 300 mm long is acted on with a tensile stress of 500 MPa. If the deformation is entirely elastic, compute the resultant elongation? The modulus of elasticity of mild steel is 200 GPa.arrow_forward
- Is it possible to conduct a valid plane strain fracture toughness test for a CrMoV steel alloy under the following conditions: KIC = 53 MPa√m , σys = 620 MPa, W = 6 cm, and plate thickness B = 2.5 cm?arrow_forwardThe aluminum (E=15x10^10psi, α=11.6x10^-6/°F) shell is fully bonded to the brass (E=10.6x10^6psi, α=12.9x10^-6/°F) sore, and the assembly is unstressed at a temperature of 78°F. Considering only axial deformations, determine the stress when the temperature reaches 180°F (a) in the brass core (b) in the aluminum shellarrow_forwardTwo previously undeformed cylindrical specimens of an alloy are to be strain hardened by reducing their cross-sectional areas (while maintaining their circular cross sections). For one specimen, the initial and deformed radii are 15?? and 12??, respectively. The second specimen, with an initial radius of 11??, must have the same deformed hardness as the first specimen. Compute the second specimen’s radius after deformation.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning