The relationship between change in resistance and strain.
Answer to Problem 6.9P
The relationship between change in resistance and strain is
Explanation of Solution
Formula Used:
Write the expression for the resistance of wire..
Here,
Write the expression for the derivative of volume in terms of length and area.
Here,
Write the expression for change in volume.
Here,
Calculation:
Differentiate equation (I) with
Rewrite equation (III) in expanded form.
For small strain, neglect
Equate equation (II) and (V).
Substitute
Substitute
Conclusion:
Thus, the relationship between change in resistance and strain is
Want to see more full solutions like this?
Chapter 6 Solutions
Materials Science And Engineering Properties
- Strain = 600 Stress = Strain = 500 Stress = 400 500 300 400 300 200 200 100 100 0.000 0.002 0.004 0.006 Strain 0.00 0.04 0.08 0.12 0.16 0.20 Strain Stress (MPa)arrow_forwardThe tension of a specimen of steel having an initial diameter of 0.507 in. was tested using a gauge length of 2 in. The following data were obtained for the elastic and plastic states. For the elastic state PAlb) 10 1000 2000 3000 4000 7000 8400 8800 9200 For the plastic state PAlb) 8800 9200 9100 13200 15200 17000 16400 14800 A/(in) 10 The reduction in the area Ris 0.0004 0.0006 0.0010 0.0013 0.0023 0.0028 0.0036 0.0089 NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part. % A, (in2) 0.1984 0.1978 0.1963 0.1924 0.1875 0.1563 0.1307 0.1077 What are the values of the yield strength, Sy and the reduction in the area? The value of the yield strength Sy is [ kpsl. 4arrow_forwardWhat is the modulus of resilience for the material with the stress-strain behavior given in the figure belowarrow_forward
- The stress–strain relation shown in Figure was obtained during the tensile test of an aluminum alloy specimen. Determine the Yield stress using an offset of 0.002 strain.arrow_forwardA brass wire of diameter d = 2.33 mm is stretched tightly between rigid supports so that the tensile force is T = 93 N (see figure). T The coefficient of thermal expansion for the wire is 19.5 x 106/°c, and the modulus of elasticity is E = 110 GPa. (a) What is the maximum permissible temperature drop (in °C) if the allowable shear stress in the wire is 60 MPa? (Enter the magnitude.) °C (b) At what temperature change (in °C) does the wire go slack? °Carrow_forwardA 5-mm-thick rectangular alloy bar is subjected to ajtensile load P by pins at A and B, as shown in the figure. The width of the bar is w = 33 mm. Strain gages bonded to the specimen measure the following strains in the longitudinal (x) and transverse (y) directions: €, =710 με and ε,--255 με (a) Determine Poisson's ratio for this specimen. (b) If the measured strains were produced by an axial load of P = 24 kN, what is the modulus of elasticity for this specimen? Answers: (a) v= (b) E= GPaarrow_forward
- The stress concentration occurs whenever there is an abrupt change in the cross-section of a component or there is any discontinuity in the material. The figure given below shows a flat plate with a hole of diameter d. The plate is fixed at one end and the other end is subjected to a tensile load of P = 41 kN due to which there is a change in length of 0.4 mm. The thickness of the plate is 11 mm. The maximum stress developed in the flat plate is 235 MPa. Take Young's modulus(E) = 210 GPa and theoretical stress concentration factor =2, Calculate the following values: i) Width of the plate (W2) in mm ii) Nominal Stress in MPa iii) Diameter of the hole (d) in mm Hole with stress concentration factor 2 35 mm W2 35 mm P 300 mm 350 mm- 250 mmarrow_forwardConsider a cylindrical metal 6 mm in diameter and 50 mm long ispulled in tension. It is known that yield strength and elastic (Young’s) Modulus of thematerial are 200 MPa and 100 GPa, respectively, and its Poisson’s Ratio is 0.3.(a) Determine whether the deformation is elastic or plastic when 6000 N is applied.(b) Calculate specimen elongation (∆l) and reduction in diameter (∆d) when 5000 N isapplied? What are the values ∆l and ∆d when the load is released?(c) If necking occurs at a load of 8850 N, determine the UTS of the metal.(d) Calculate the ductility in terms of % E.L. if the length of the specimen at fracturepoint is 56.0 mm.arrow_forwardCreep exercises You are involved in a design for high temperature alloys and have performed a rupture test of material A and B. After data analysis, you noticed that the master curve (o vs LMP) of both material A and B coincide as shown in the diagram below. Based on the rupture strength o (MPa) AtB LMP = T(C+ Int) Which material will you select if they both have same constant (CA= CB)? Which material will you select if C < C? Motivate your answer by means of a calculation.arrow_forward
- The stress concentration occurs whenever there is an abrupt change in the cross-section of a component or there is any discontinuity in the material. The figure given below shows a flat plate with a hole of diameter d. The plate is fixed at one end and the other end is subjected to a tensile load of P = 44 kN due to which there is a change in length of 0.4 mm. The thickness of the plate is 11.5 mm. The maximum stress developed in the flat plate is 228 MPa. Take Young's modulus(E) = 210 GPa and theoretical stress concentration factor =2, Calculate the following values: i) Width of the plate (W2) in mm ( ii) Nominal Stress in MPa ( iii) Diameter of the hole (d) in mmarrow_forwardThe stress-strain relationship shown in Figure P1.13 was obtained during the tensile test of an aluminum alloy specimen. Determine the following: a. Young's modulus within the linear portion b. Tangent modulus at a stress of 310 MPa c. Yield stress using an offset of 0.002 strain d. If the yield stress in part c is considered failure stress, what is the maximum working stress to be applied to this material if a factor of safety of 1.5 is used? 450 300 150 0.002 0.004 0.006 0.008 Strain, m/m FIGURE P1.13 Stress, MPaarrow_forwardThe elastic portion of the tension stress–strain diagram for an aluminum alloy is shown in the figure. The specimen used for the test has a gauge length of 2 in. and a diameter of 0.5 in. If the applied load is 10 kip, determine the new diameter of the specimen. The shear modulus is Gal = 3.8(103) ksi.arrow_forward
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning