The total tensile proportional limit stress.
Answer to Problem 6.11P
The tensile proportional limit stress is
Explanation of Solution
Given:
The critical shear stress of niobium is
The temperature is
Formula Used:
Write the expression for the angle between normal to
Here,
Write the expression for the angle between
Here,
Write the expression for relation between resolved shear stress and tensile proportional limit stress.
Here,
Calculation:
Substitute
Substitute
Substitute
Further simplify the above,
Conclusion:
Thus, the tensile proportional limit stress is
Want to see more full solutions like this?
Chapter 6 Solutions
Materials Science And Engineering Properties
- A metal sample on a tension in the test ,296MPa , a tensile true strain 0.08, and true stress 356 MPa when the strain is 0.27. Determine the strength coefficient and strain hardening exponent in the flow curve equation.arrow_forwardAt an axial load of 22 kN, a 15-mm-thick x 35-mm-wide polyimide polymer bar elongates 4.2 mm while the bar width contracts 0.25 mm. The bar is 215-mm long. At the 22-kN load, the stress in the polymer bar is less than its proportional limit. Determine Poisson's ratio. O 0.366 O 0.336 EBA O 0.473 O 0.229 O 0.427arrow_forwardAt an axial load of 22 kN, a 15-mm-thick × 50-mm-wide polyimide polymer bar elongates 5.7 mm while the bar width contracts 0.15 mm. The bar is 245-mm long. At the 22-kN load, the stress in the polymer bar is less than its proportional limit. Determine Poisson’s ratio.arrow_forward
- At an axial load of 20 kN, a 35-mm-wide by 10-mm-thick polyimide polymer bar elongates 2.7 mm while the bar width contracts 0.15 mm. The bar is 240 mm long. At the 20-kN load, the stress in the polymer bar is less than its proportional limit.Determine(a) the modulus of elasticity.(b) Poisson’s ratio.(c) the change in the bar thickness.arrow_forwardAt an axial load of 25 kN, a 50-mm-wide by 15-mm-thick polyimide polymer bar elongates 3.1 mm while the bar width contracts 0.26 mm. The bar is 220 mm long. At the 25-kN load, the stress in the polymer bar is less than its proportional limit Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thickness. Answers: (a) E- (b) v- (c) Audness GPa mmarrow_forward(a) Illustrate a typical stress-strain curve for brittle and ductile materials.arrow_forward
- At an axial load of 22 kN, a 45-mm-wide by 15-mm-thick polyimide polymer bar elongates 2.8 mm while the bar width contracts 0.25 mm. The bar is 190 mm long. At the 22-kN load, the stress in the polymer bar is less than its proportional limit. Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thicknessarrow_forward2- What is the largest size (mm) internal through crack that a thick plate of aluminium alloy 7075-T651 can support at an applied stress of (a) three-quarters of the yield strength and (b) one-half of the yield strength? Assume Y = 1. for 7075-T651, KỊC = 24.2 MPa ym and oYS = 495 MPa.arrow_forwardAn aluminum alloy [E = 67 GPa; ν = 0.33; α = 23.0 × 10–6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 225 mm, a cross-sectional area of A = 5100 mm2, and a length of L = 4.1 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by ΔT = 63°C, the longitudinal normal strain in the plate is found to be 2900 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Δd.arrow_forward
- 1) Please indicate in the stress-strain diagram given below the stress levels that can cause creep. 2) The effect of an increase in service temperature or applied stress is to shift the 3) Dislocation density . In Region number (...) while creep deformation is increasing at an increasing rate. 4) Dislocation density is remains constant in Region number (.) while the creep rate is increasing. 5) For some applications the amount of creep in Region number (.) is taken as the design criteria.arrow_forwardConsider a metal single crystal oriented such that the normal to the slip plane and the slip direction are at angles of 43.1° and 47.9°, respectively, with the tensile axis. If the critical resolved shear stress is 20.7 MPa, will an applied stress of 45 MPa cause the single crystal to yield or slip? If not, what stress will be necessary?arrow_forwardIn a brittle material, the ultimate stress is equal to the breaking stress. A True B Falsearrow_forward
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning