Question
Chapter 5, Problem 5.19Q
To determine
The explanation for the promoting low superheat equiaxed grains over columnar grains.
The explanation for equiaxed grains becomes finer as the pouring temperature decreases.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
For a sand casting a steel rectangular plate with dimensions 80mm x 120mm x 20mm. Calculate shrinkage and draft allowance. And draw the designed pattern. Assume shrinkage of material as 0.1% for 12 inch, pattern material is wood and assume suitable draft angles
For sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical
riser has to be designed. The height of the riser is equal to its diameter. The total solidification
time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification
time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter
(in mm) of the riser is ____
2. In the casting of steel under certain mould conditions, the mould constant in Chvorinov's rule is
known to be 4.0 min/cm?, based on previous experience. The casting is a flat plate whose length is
25 cm, width is 8 cm, and thickness is 2.5 cm. Exponent n is taken to have a value of 2. Determine
how long it will take for the casting to solidify.
Chapter 5 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
Ch. 5 - Prob. 5.1QCh. 5 - Prob. 5.2QCh. 5 - Prob. 5.3QCh. 5 - Prob. 5.4QCh. 5 - Prob. 5.5QCh. 5 - Prob. 5.6QCh. 5 - Prob. 5.7QCh. 5 - Prob. 5.8QCh. 5 - Prob. 5.9QCh. 5 - Prob. 5.10Q
Ch. 5 - Prob. 5.11QCh. 5 - Prob. 5.12QCh. 5 - Prob. 5.13QCh. 5 - Prob. 5.14QCh. 5 - Prob. 5.15QCh. 5 - Prob. 5.16QCh. 5 - Prob. 5.17QCh. 5 - Prob. 5.18QCh. 5 - Prob. 5.19QCh. 5 - Prob. 5.20QCh. 5 - Prob. 5.21QCh. 5 - Prob. 5.22QCh. 5 - Prob. 5.23QCh. 5 - Prob. 5.24QCh. 5 - Prob. 5.25QCh. 5 - Prob. 5.26QCh. 5 - Prob. 5.27QCh. 5 - Prob. 5.28QCh. 5 - Prob. 5.29QCh. 5 - Prob. 5.30QCh. 5 - Prob. 5.31QCh. 5 - Prob. 5.32QCh. 5 - Prob. 5.33QCh. 5 - Prob. 5.34QCh. 5 - Prob. 5.35QCh. 5 - Prob. 5.36QCh. 5 - Prob. 5.37QCh. 5 - Prob. 5.38QCh. 5 - Prob. 5.39QCh. 5 - Prob. 5.40QCh. 5 - Prob. 5.41QCh. 5 - Prob. 5.42QCh. 5 - Prob. 5.43QCh. 5 - Prob. 5.44QCh. 5 - Prob. 5.45QCh. 5 - Prob. 5.46QCh. 5 - Prob. 5.47QCh. 5 - Prob. 5.48QCh. 5 - Prob. 5.49QCh. 5 - Prob. 5.50QCh. 5 - Prob. 5.51QCh. 5 - Prob. 5.52QCh. 5 - Prob. 5.53QCh. 5 - Prob. 5.54QCh. 5 - Prob. 5.55QCh. 5 - Prob. 5.56QCh. 5 - Prob. 5.57QCh. 5 - Prob. 5.58QCh. 5 - Prob. 5.59QCh. 5 - Prob. 5.60QCh. 5 - Prob. 5.61PCh. 5 - Prob. 5.62PCh. 5 - Prob. 5.63PCh. 5 - Prob. 5.64PCh. 5 - Prob. 5.65PCh. 5 - Prob. 5.66PCh. 5 - Prob. 5.67PCh. 5 - Prob. 5.68PCh. 5 - Prob. 5.69PCh. 5 - Prob. 5.70PCh. 5 - Prob. 5.71PCh. 5 - Prob. 5.72PCh. 5 - Prob. 5.73PCh. 5 - Prob. 5.74PCh. 5 - Prob. 5.75PCh. 5 - Prob. 5.76PCh. 5 - Prob. 5.77PCh. 5 - Prob. 5.78PCh. 5 - Prob. 5.79PCh. 5 - Prob. 5.80PCh. 5 - Prob. 5.81PCh. 5 - Prob. 5.82PCh. 5 - Prob. 5.83PCh. 5 - Prob. 5.84PCh. 5 - Prob. 5.85PCh. 5 - Prob. 5.86PCh. 5 - Prob. 5.87PCh. 5 - Prob. 5.88PCh. 5 - Prob. 5.89PCh. 5 - Prob. 5.90PCh. 5 - Prob. 5.91PCh. 5 - Prob. 5.92PCh. 5 - Prob. 5.93DCh. 5 - Prob. 5.94DCh. 5 - Prob. 5.95DCh. 5 - Prob. 5.96DCh. 5 - Prob. 5.97DCh. 5 - Prob. 5.98DCh. 5 - Prob. 5.99DCh. 5 - Prob. 5.100DCh. 5 - Prob. 5.101DCh. 5 - Prob. 5.102DCh. 5 - Prob. 5.103DCh. 5 - Prob. 5.104DCh. 5 - Prob. 5.105DCh. 5 - Prob. 5.106DCh. 5 - Prob. 5.107DCh. 5 - Prob. 5.108DCh. 5 - Prob. 5.109DCh. 5 - Prob. 5.110DCh. 5 - Prob. 5.111DCh. 5 - Prob. 5.112DCh. 5 - Prob. 5.113DCh. 5 - Prob. 5.114DCh. 5 - Prob. 5.115D
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A mould having dimensions 100 mm x 90 mm x 20 mm is filled with molten metal through a gate with height h and CS area A, the mould filling time is t1. The height is now quadrupled and the crosssectional area is halved. The corresponding filling time is t2 . What is the ratio t2/t1 ?arrow_forwardIn sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is placed inside the mould cavity. The densities of core material and lead are 1600 kg/m³ and 11300 kg/m³ respectively. The net force (in N) that tends to lift he core during pouring of molten metal will be. . . . .arrow_forwardEX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTS = 2.0 min.arrow_forward
- (b) In casting experiments performed using a certain alloy and type of sand mould, for which n can be approximately taken as 2, it took 155 sec for a cube-shaped casting to solidify. The cube was 50 mm per side. (i) Determine the value of the mould constant in Chvorinov's rule. (ii) When the same alloy and mould type are used to make a cylindrical casting of diameter 30 mm, what is the maximum length of the cylinder if the maximum solidification time is limited to 1 minute?arrow_forwarda riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.arrow_forwardWhen designing patterns for casting, patternmakers use special rulers that automatically incorporate solid shrinkage allowances into their designs. For example, a 12-in. patternmaker’s ruler is longer than 1 foot. How long should a patternmaker’s ruler be for making patterns for (a) aluminum castings and (b) high-manganese steel?arrow_forward
- Explain the open and closed mold forging processes with figures. Draw the force-stroke diagram in closed mold forging. Comment on the diagram.arrow_forwardA slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.arrow_forward(1) In sand casting, the volumetric size of the pattern is: (a) bigger than, (b) the same as, or (c) smaller than the cast part (2) Machining processes include which of the following (two correct answers): (a) casting, (b) drilling, (c) extrusion, (d) forging, (e) shaping, (f), and painting? (3) Aluminum sections used for making metal doors and windows are made by which process: (a) Rolling, (b) welding, (c) extrusion, (d) turning. (4) The average flow stress is the flow stress multiplied by which of the following factors: (a) n, (b) (1-n), (c) 1/n, or (d) 1/(1+n), where n is the strain hardening exponent? (5) The strength of a brazed joint is typically (a) equal to, (b) stronger than, or (c) weaker than soldered joint? (6) Thread cutting operation is normally performed on which one of the following machine tools: (a) drill press, (b) lathe, (c) milling machine, (d) planer, or (e shaper?arrow_forward
- Calculate the size of a cylindrical riser (Height and diameter equal ) necessary to feed slab casting 45 * 45 * 25 cm with a side riser , casting poured horizontally in to the mould.Use caine's equation and take constants in caine equation as a= 0.18; b = 0.05 and c= 1.0.arrow_forwardDetermine the time required to fill the mold cavity along with the riser as shown in the following figure. A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.arrow_forward1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 min.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license