(b) In casting experiments performed using a certain alloy and type of sand mould, for which n can be approximately taken as 2, it took 155 sec for a cube-shaped casting to solidify. The cube was 50 mm per side. (i) Determine the value of the mould constant in Chvorinov's rule. (ii) When the same alloy and mould type are used to make a cylindrical casting of diameter 30 mm, what is the maximum length of the cylinder if the maximum solidification time is limited to 1 minute?

(b) In casting experiments performed using a certain alloy and type of sand mould, for which n can be approximately taken as 2, it took 155 sec for a cube-shaped casting to solidify. The cube was 50 mm per side. (i) Determine the value of the mould constant in Chvorinov's rule. (ii) When the same alloy and mould type are used to make a cylindrical casting of diameter 30 mm, what is the maximum length of the cylinder if the maximum solidification time is limited to 1 minute?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Manufacturing Processes
2. In the casting of steel under certain mould conditions, the mould constant in Chvorinov's rule is known to be 4.0 min/cm?, based on previous experience. The casting is a flat plate whose length is 25 cm, width is 8 cm, and thickness is 2.5 cm. Exponent n is taken to have a value of 2. Determine how long it will take for the casting to solidify.
Only answer question 4
flו. 3D) امتحان شهري.pdf 1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 2. A mold sprue is 180 mm long, the cross-sectional area at its base is 2.4 cm?. The sprue feeds a horizontal runner leading into a mold cavity whose volume is 1600 cm?. Determine, volume rate of flow and time to fill the mold.
For sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical riser has to be designed. The height of the riser is equal to its diameter. The total solidification time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter (in mm) of the riser is ____
In casting experiments performed during a certain alloy and type of sand mould it took 155 second for a cube shaped casting to solidify. The cube was 50 mm on a side. (i) Determine the value of the mould constant in Chvorinov's Rule. (ii) If the same alloy and mould type were used, find the total solidification time for cylindrical casting in which the diameter D = 30 mm and length L = 50 mm. %3D
Parvinbhai
A cast iron part with a square cross section is sand casted. Its length 14 in and the sides of the square cross section-2.5 in. If the mold constant in Chvorinov's rule - 3.6 min/in², how long, in minutes, will it take the casting to solidify?
a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.
Answer this broadly.
EX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTS = 2.0 min.
A disk-shaped part is cast out of aluminium with a diameter of 630 mm and a thickness of 16 mm. If the mold constant is 2.2 sec/mm2 in Chvorinov's rule, how long will it take the casting to solidify?