EX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTs = 2.0 min. %3D

EX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTs = 2.0 min. %3D

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.
(9,00 Puanlar) 36 - A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 25 cm, width = 15 cm, and thickness = 2,5 cm. If the total solidification time of the casting itself is known to be 4,5 min, determine the diameter of the riser so that it will take 2596 longer for the riser to solidify. Riser volume: V-(nD³/6 (D=diameter) Riser area: A-TD2 Casting volume: V-L-W-t (L-Length, W=width, t=thickness)
1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 min.
(9,00 Puanlar) A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with 8- length 50 cm, width = 35 cm, and thickness = 4 cm. If the total solidification time of the casting itself is known to be 7,5 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify. %3D Riser volume: V3(TD3)/6(D%3Ddiameter) Riser area: A=TD2 Casting volume: V-L-Wt (L-Length, W=width, t-thickness) a) 8,41 cm b) O 7,34 cm c) 6.62 cm 11,46 cm Boş bırak KÖnceki 8/43 Sonraki> Каpat
A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.
4- A spherical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 20 cm  10 cm  2.0 cm. Previous observation have indicated that the total solidification time (TTS) for this casting = 3.5 min. determine the diameter of the riser so that it will take 25% longer for the riser to solidify
A vertical true centrifugal casting process is used to produce bushings that are 200 mm long and 200 mm in outside diameter. If the rotational speed during solidification is 500 rev/min, determine the inside diameter at the top of the bushing if the inside diameter at the bottom is 150 mm? Ans. Dt = 167.98 mm.
Determine the time required to fill the mold cavity along with the riser as shown in the following figure. A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.
flו. 3D) امتحان شهري.pdf 1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 2. A mold sprue is 180 mm long, the cross-sectional area at its base is 2.4 cm?. The sprue feeds a horizontal runner leading into a mold cavity whose volume is 1600 cm?. Determine, volume rate of flow and time to fill the mold.
A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser to solidify. %3D %3!
For sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical riser has to be designed. The height of the riser is equal to its diameter. The total solidification time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter (in mm) of the riser is ____
In sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is placed inside the mould cavity. The densities of core material and lead are 1600 kg/m3 and 11300 kg/m³ respectively. The net force (in N) that tends to lift he core during pouring of molten metal will be