Foundations of Materials Science and Engineering
6th Edition
ISBN: 9781259696558
Author: SMITH
Publisher: MCG
expand_more
expand_more
format_list_bulleted
Question
Chapter 13.10, Problem 96SEP
(a)
To determine
Whether it is possible for the occurrence of a cathodic and anodic reaction in an aluminum container that is used for storing salt
(b)
To determine
The anodic and cathodic reactions.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
•You are case-hardening a tool made of BCC (α) iron in the presence of a carbonaceous material. A heat treatment at 600 oC for 100 minutes results in a carbon concentration of 0.75 wt% at a position 0.5mm below the surface. How long would it take to obtain the same concentration at the same position if the heat treatment were conducted at 900 oC?
x12/D1t1= x22/D2t2
Arrhenius equation: D=D0e^(〖-Qd〗∕RT)
Qd = Activation energy of diffusion
D0 = Pre-exponential diffusion factor
R = gas constant = 8.314 J/(mol*K)
Use the Arrhenius equation to calculate D1 and D2.
Calculate the time to satisfy the problem statement.
What is the solubility of naphthalene at 50 C in an ideal solution? The melting point of
naphthalene is 90 C and the molar heat of fusion is 3500 cal/mole.
the gas constant = 1.987 cal mol'degree
%3D
Select one:
O a. 0.55
Ob.93.3
Oc.0.27
Od.6.7
Consider de-oxidation by the addition of
ferromanganese (60 percent Mn) to molten
steel at 1600°C.The initial oxygen content is
0.04 wt%. It has to be brought down to 0.02
wt%. Calculate the quantity of
ferromanganese required per tonne of steel.
The manganese content of steel before de-
oxidation is 0.1 wt%.
(MnO) + [Fe] = [Mn] + (FeO)
Given: K Mn at 1873 K = 0.4
K Fe-Mn at 1873 K = 0.156
Assumptions: Fe and Mn form ideal solutions
Chapter 13 Solutions
Foundations of Materials Science and Engineering
Ch. 13.10 - Prob. 1KCPCh. 13.10 - Prob. 2KCPCh. 13.10 - Which is in a lower energy state: (a) elemental...Ch. 13.10 - Give several examples of environmental...Ch. 13.10 - Prob. 5KCPCh. 13.10 - Prob. 6KCPCh. 13.10 - Prob. 7KCPCh. 13.10 - What is an exchange current density? What is the...Ch. 13.10 - Prob. 9KCPCh. 13.10 - Prob. 10KCP
Ch. 13.10 - Prob. 11KCPCh. 13.10 - Prob. 12KCPCh. 13.10 - Prob. 13KCPCh. 13.10 - Prob. 14KCPCh. 13.10 - Prob. 15KCPCh. 13.10 - Prob. 16KCPCh. 13.10 - Prob. 17KCPCh. 13.10 - Prob. 18KCPCh. 13.10 - Prob. 19KCPCh. 13.10 - Describe fretting corrosion.Ch. 13.10 - What is selective leaching of an alloy? Which...Ch. 13.10 - Prob. 22KCPCh. 13.10 - Prob. 23KCPCh. 13.10 - Prob. 24KCPCh. 13.10 - Prob. 25KCPCh. 13.10 - Prob. 26KCPCh. 13.10 - Prob. 27KCPCh. 13.10 - What are Alclad alloys?Ch. 13.10 - Prob. 29AAPCh. 13.10 - Prob. 30AAPCh. 13.10 - Prob. 31AAPCh. 13.10 - Prob. 32AAPCh. 13.10 - Prob. 33AAPCh. 13.10 - The emf of a standard Ni-Cd galvanic cell is...Ch. 13.10 - What is the emf with respect to the standard...Ch. 13.10 - Prob. 36AAPCh. 13.10 - Prob. 37AAPCh. 13.10 - Prob. 38AAPCh. 13.10 - Prob. 39AAPCh. 13.10 - Prob. 40AAPCh. 13.10 - Prob. 41AAPCh. 13.10 - Prob. 42AAPCh. 13.10 - Prob. 43AAPCh. 13.10 - Prob. 44AAPCh. 13.10 - Prob. 45AAPCh. 13.10 - Prob. 46AAPCh. 13.10 - Prob. 47AAPCh. 13.10 - Prob. 48AAPCh. 13.10 - Prob. 49AAPCh. 13.10 - Prob. 50AAPCh. 13.10 - Prob. 51AAPCh. 13.10 - Prob. 52AAPCh. 13.10 - Prob. 53AAPCh. 13.10 - Prob. 54AAPCh. 13.10 - A galvanized (zinc-coaled) steel sheet is found to...Ch. 13.10 - Prob. 56AAPCh. 13.10 - Prob. 57AAPCh. 13.10 - Prob. 58AAPCh. 13.10 - Prob. 59AAPCh. 13.10 - Prob. 60AAPCh. 13.10 - Prob. 61AAPCh. 13.10 - Prob. 62AAPCh. 13.10 - Prob. 63AAPCh. 13.10 - Prob. 64AAPCh. 13.10 - Prob. 65AAPCh. 13.10 - Prob. 66AAPCh. 13.10 - Prob. 67AAPCh. 13.10 - Prob. 68AAPCh. 13.10 - Prob. 69AAPCh. 13.10 - Prob. 70AAPCh. 13.10 - Prob. 71AAPCh. 13.10 - Prob. 72AAPCh. 13.10 - Prob. 73AAPCh. 13.10 - Prob. 74AAPCh. 13.10 - Prob. 75AAPCh. 13.10 - Prob. 76SEPCh. 13.10 - Prob. 77SEPCh. 13.10 - Prob. 78SEPCh. 13.10 - Prob. 79SEPCh. 13.10 - Prob. 80SEPCh. 13.10 - Prob. 81SEPCh. 13.10 - Prob. 82SEPCh. 13.10 - Prob. 83SEPCh. 13.10 - Prob. 84SEPCh. 13.10 - Corrosion is observed at the root of threads on...Ch. 13.10 - Prob. 86SEPCh. 13.10 - Prob. 87SEPCh. 13.10 - Prob. 88SEPCh. 13.10 - Prob. 89SEPCh. 13.10 - Prob. 90SEPCh. 13.10 - Prob. 91SEPCh. 13.10 - Prob. 92SEPCh. 13.10 - Prob. 93SEPCh. 13.10 - Prob. 94SEPCh. 13.10 - Prob. 95SEPCh. 13.10 - Prob. 96SEPCh. 13.10 - Prob. 97SEPCh. 13.10 - Prob. 98SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Problem 3 An FCC iron-carbon alloy initially containing 0.35 wt% C is exposed to an oxygen-rich and virtually carbon- free atmosphere at 1400 K (1127 °C). Under these circumstances the carbon diffuses from the alloy and reacts at the surface with the oxygen in the atmosphere; that is, the carbon concentration at the surface position is maintained essentially at 0 wt% C. (This process of carbon depletion is termed decarburization.) At what position will the carbon concentration be 0.15 wt% after a 10-h treatment? The value of D at 1400 K is 6.9 x 10¹¹ m²/s.arrow_forwardAn FCC iron-carbon alloy initially containing 0.10 wt% C is carburized at an elevated temperature and in an atmosphere in which the surface carbon concentration is maintained at 1.10 wt%. If the treatment is conducted at 1050 °C, how long should the treatment be performed to reach a 0.30 wt% of carbon concentration at a position 4.2 mm below the surface?arrow_forwardProblem 2 Determine the carburizing time necessary to achieve a carbon concentration of 0.45 wt% at a position 2 mm into an iron-carbon alloy that initially contains 0.20 wt% C. The surface concentration is to be maintained at 1.30 wt% C, and the treatment is to be conducted at 1000 °C. Use the diffusion data for y-Fe in Table 5.2.arrow_forward
- In a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the total and partial phases? Given:Eutectoid temperature=723°C; Eutectoid concentration=0.76% C; Limit concentration of ferrite=0.022%; Limiting concentration of cementite: 6.7%.arrow_forwardA 1020 steel contains 0.20% carbon is carburized by a source that maintains a surface carbon content 0f 2.0% C. It is desired to produce a 0.80 wt% C concentration 0.1 cm below the steel surface after a 4-hour treatment. At what temperature should the carburization be carried out? R = 8.314 J/mol•K; DO = 2.3x10-5 m2 /s; Qd=148,000 J/mol erf(z) erf(z) erf(z) 0.55 0.5633 1.3 0.9340 0.025 0.05 0.0282 0.60 0.6039 1.4 0.9523 0.0564 0.65 0.6420 1.5 0.9661 0.10 0.1125 0.70 0.6778 1.6 0.9763 0.15 0.1680 0.75 0.7112 1.7 0.9838 0.20 0.25 0.30 0.2227 0.80 0.7421 1.8 0.9891 0.2763 0.85 0.7707 1.9 0.9928 0.3286 0.90 0.7970 2.0 0.9953 0.35 0.3794 0.95 0.8209 2.2 0.9981 0.40 0.4284 1.0 0.8427 2.4 0.9993 0.45 0.4755 1.1 0.8802 2.6 0.9998 0.50 0.5205 1.2 0.9103 2.8 0.9999arrow_forwardDetermine the following 1. Determine what substance has a great strength? Calculate and demonstrate. 2. Determine the substance that has greater resilience? Calculate and demonstrate. 3. Determine which one of the samples have stronger molecular bonds? Give a brief explanation of your response. Draw diagrams as necessary.arrow_forward
- Temperature zones, A, B, C and D, for a range of heat-treatment processes for carbonsteel are shown in Figure 2 below. Identify and explain the heat-treatment processrepresented by the zonesarrow_forwardA mixture of 1.0 mol of hexane and 1.0 mol of nitrobenzene was prepared at 290 K. Calculate the amount of hexane present in each phase at 290 K by using the phase diagram given below. (nala = nglp) T/K P= 1 290 P= 2 273 0.17 ㅇ 0.2 0:65 0.8 0.6 0.4 1 x(C;H14)arrow_forwardA student performing this lab experiment receives his unknown solution that may contain ( Ba, Ca, and Mg). And begins to conduct tests to identify 2+ 2+ 2+ the cations present in the unknown solution. Based on the following observation 1) When the unknown solution was treated with K,Cro4, no precipitate was formed. 2) The resulting solution from step 1 was basified with 6M NH, before the addition of aqueous K,C,0, which forms a white precipitate. 3) To the resulting solution from step 2, was treated with ammonia and of Na,HPO,· A white precipitate 4 was formed after heating the solution for 10 minutes at 60°C. Which cations were present in the student's unknown solution? Select one or more: 2+ Ва 2+ Mg 2+ Саarrow_forward
- In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.arrow_forwardWhat do you mean copolymers and give two examplesarrow_forwardA. What is the maximum solid solubility of Cu in Ag? At what temperature? Write the Ag-Cu eutectic reaction, indicating the reactant and product phase(s), and the temperature and the composition (as wt% Cu) at which the reaction takes place.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Extent of Reaction; Author: LearnChemE;https://www.youtube.com/watch?v=__stMf3OLP4;License: Standard Youtube License