Question
Chapter 10.14, Problem 151AAP
To determine
During the solidification of thermoplastics, how does the specific volume versus temperature plots differ for noncrystalline and partly crystalline thermoplastics.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
For a given polymer, the activation energy for stress relaxation was measured to be 10 kJ/mol. If the stress relaxation time for this polymer at room
temperature is 3,600 s, what would be the relaxation time at 100 ◦C?
sketch the generalized stress-strain curve for a semi-crystalline thermoplastic polymer.
For a given polymer, the activation energy for the stress relaxation was measured to be 59kj/mol. If the stress relaxation time for this polymer at 7 degree Celsius is 3150 seconds. What is the relaxation time at 110 degree Celsius
Chapter 10 Solutions
Foundations of Materials Science and Engineering
Ch. 10.14 - Define and differentiate polymers, plastics, and...Ch. 10.14 - (a) Describe the atomic structural arrangement of...Ch. 10.14 - What is a pendant atom or group of atoms?Ch. 10.14 - (a)What type of bonding exists within the...Ch. 10.14 - Prob. 5KCPCh. 10.14 - Prob. 6KCPCh. 10.14 - Prob. 7KCPCh. 10.14 - (a) What is the repeating chemical unit of a...Ch. 10.14 - What are the three major reactions that occur...Ch. 10.14 - Prob. 10KCP
Ch. 10.14 - (a) Why must one consider the average degree of...Ch. 10.14 - Prob. 12KCPCh. 10.14 - Write structural formulas for the mers of the...Ch. 10.14 - Prob. 14KCPCh. 10.14 - Prob. 15KCPCh. 10.14 - Prob. 16KCPCh. 10.14 - Define stepwise polymerization of linear polymers....Ch. 10.14 - What are three basic raw materials used to produce...Ch. 10.14 - Describe and illustrate the following...Ch. 10.14 - Prob. 20KCPCh. 10.14 - Prob. 21KCPCh. 10.14 - Prob. 22KCPCh. 10.14 - Prob. 23KCPCh. 10.14 - Prob. 24KCPCh. 10.14 - Prob. 25KCPCh. 10.14 - Prob. 26KCPCh. 10.14 - Prob. 27KCPCh. 10.14 - Prob. 28KCPCh. 10.14 - Prob. 29KCPCh. 10.14 - (a) Describe the compression-molding process for...Ch. 10.14 - (a) Describe the transfer-molding process for...Ch. 10.14 - Prob. 32KCPCh. 10.14 - Define an engineering thermoplastic. Why is this...Ch. 10.14 - What is the structural formula for the amide...Ch. 10.14 - (a) In the designation nylon 6,6, what does the...Ch. 10.14 - Prob. 36KCPCh. 10.14 - Prob. 37KCPCh. 10.14 - Prob. 38KCPCh. 10.14 - Prob. 39KCPCh. 10.14 - Prob. 40KCPCh. 10.14 - Prob. 41KCPCh. 10.14 - Prob. 42KCPCh. 10.14 - Prob. 43KCPCh. 10.14 - Prob. 44KCPCh. 10.14 - (a) What are the major processing methods used for...Ch. 10.14 - Prob. 46KCPCh. 10.14 - Prob. 47KCPCh. 10.14 - Prob. 48KCPCh. 10.14 - What is natural rubber mainly made of? What other...Ch. 10.14 - Prob. 50KCPCh. 10.14 - Prob. 51KCPCh. 10.14 - Prob. 52KCPCh. 10.14 - Prob. 53KCPCh. 10.14 - What is the vulcanization process for natural...Ch. 10.14 - Prob. 55KCPCh. 10.14 - Prob. 56KCPCh. 10.14 - What are the silicones? What is the general...Ch. 10.14 - Prob. 58KCPCh. 10.14 - Prob. 59KCPCh. 10.14 - Prob. 60KCPCh. 10.14 - Prob. 61KCPCh. 10.14 - Define the creep modulus of a plastic material.Ch. 10.14 - What is a craze in a glassy thermoplastic?Ch. 10.14 - Describe the structure of a craze in a...Ch. 10.14 - Prob. 65KCPCh. 10.14 - Prob. 66AAPCh. 10.14 - Prob. 67AAPCh. 10.14 - Prob. 68AAPCh. 10.14 - An injection-molding polycarbonate material has an...Ch. 10.14 - Prob. 70AAPCh. 10.14 - Prob. 71AAPCh. 10.14 - Prob. 72AAPCh. 10.14 - Prob. 73AAPCh. 10.14 - How much sulfur must be added to 70 g of butadiene...Ch. 10.14 - If 5 g of sulfur is added to 90 g of butadiene...Ch. 10.14 - Prob. 76AAPCh. 10.14 - Prob. 77AAPCh. 10.14 - Prob. 78AAPCh. 10.14 - Prob. 79AAPCh. 10.14 - Prob. 80AAPCh. 10.14 - Prob. 81AAPCh. 10.14 - Prob. 82AAPCh. 10.14 - Prob. 83AAPCh. 10.14 - A polymeric material has a relaxation time of 60...Ch. 10.14 - Prob. 85AAPCh. 10.14 - Prob. 86AAPCh. 10.14 - Prob. 87AAPCh. 10.14 - Prob. 88AAPCh. 10.14 - Prob. 89AAPCh. 10.14 - Prob. 90AAPCh. 10.14 - Prob. 91AAPCh. 10.14 - Prob. 92AAPCh. 10.14 - Prob. 93AAPCh. 10.14 - (a) What causes a polyethylene molecular chain to...Ch. 10.14 - Prob. 95AAPCh. 10.14 - Prob. 96AAPCh. 10.14 - Prob. 97AAPCh. 10.14 - Prob. 98AAPCh. 10.14 - Write the reaction for the stepwise polymerization...Ch. 10.14 - Prob. 100AAPCh. 10.14 - Prob. 101AAPCh. 10.14 - How does chain branching affect the following...Ch. 10.14 - (a) Write the general reaction for the...Ch. 10.14 - Prob. 104AAPCh. 10.14 - Prob. 105AAPCh. 10.14 - Prob. 106AAPCh. 10.14 - Prob. 107AAPCh. 10.14 - Prob. 108AAPCh. 10.14 - Prob. 109AAPCh. 10.14 - Prob. 110AAPCh. 10.14 - Prob. 111AAPCh. 10.14 - Prob. 112AAPCh. 10.14 - Prob. 113AAPCh. 10.14 - Prob. 114AAPCh. 10.14 - Prob. 115AAPCh. 10.14 - Prob. 116AAPCh. 10.14 - Prob. 117AAPCh. 10.14 - Prob. 118AAPCh. 10.14 - Prob. 119AAPCh. 10.14 - Prob. 120AAPCh. 10.14 - What are two types of reaction sites that are...Ch. 10.14 - Prob. 122AAPCh. 10.14 - Prob. 123AAPCh. 10.14 - Prob. 124AAPCh. 10.14 - Prob. 125AAPCh. 10.14 - Prob. 126AAPCh. 10.14 - How does cross-linking with sulfur affect the...Ch. 10.14 - Prob. 128AAPCh. 10.14 - Can SBR be vulcanized? Explain.Ch. 10.14 - Prob. 130AAPCh. 10.14 - Write the repeating chemical structural unit for...Ch. 10.14 - Prob. 132AAPCh. 10.14 - Prob. 133AAPCh. 10.14 - Prob. 134AAPCh. 10.14 - Prob. 135AAPCh. 10.14 - Prob. 136AAPCh. 10.14 - Prob. 137AAPCh. 10.14 - Explain how highly polar atoms bonded to the main...Ch. 10.14 - Prob. 139AAPCh. 10.14 - Prob. 140AAPCh. 10.14 - Prob. 141AAPCh. 10.14 - Prob. 142AAPCh. 10.14 - Prob. 143AAPCh. 10.14 - Prob. 144AAPCh. 10.14 - Why do cured thermoset plastics not become viscous...Ch. 10.14 - Prob. 146AAPCh. 10.14 - Prob. 147AAPCh. 10.14 - Prob. 148AAPCh. 10.14 - Prob. 149AAPCh. 10.14 - Prob. 150AAPCh. 10.14 - Prob. 151AAPCh. 10.14 - Prob. 152AAPCh. 10.14 - Prob. 153AAPCh. 10.14 - Prob. 154AAPCh. 10.14 - Prob. 155AAPCh. 10.14 - Prob. 156AAPCh. 10.14 - Prob. 157AAPCh. 10.14 - Prob. 158AAPCh. 10.14 - Prob. 159AAPCh. 10.14 - Prob. 160AAPCh. 10.14 - Prob. 161AAPCh. 10.14 - Prob. 162AAPCh. 10.14 - Prob. 163AAPCh. 10.14 - Prob. 164AAPCh. 10.14 - Prob. 165AAPCh. 10.14 - Prob. 166AAPCh. 10.14 - Prob. 167AAPCh. 10.14 - Prob. 168AAPCh. 10.14 - Prob. 169AAPCh. 10.14 - Prob. 170AAPCh. 10.14 - Prob. 171AAPCh. 10.14 - Prob. 172AAPCh. 10.14 - Prob. 173AAPCh. 10.14 - Prob. 174AAPCh. 10.14 - Prob. 175AAPCh. 10.14 - Prob. 176AAPCh. 10.14 - Prob. 178AAPCh. 10.14 - Prob. 179AAPCh. 10.14 - What are some of the advantages of epoxy thermoset...Ch. 10.14 - How are most unsaturated polyesters reinforced?Ch. 10.14 - What are some applications for reinforced...Ch. 10.14 - Prob. 183AAPCh. 10.14 - Prob. 187SEPCh. 10.14 - Prob. 188SEPCh. 10.14 - Prob. 189SEPCh. 10.14 - Prob. 190SEPCh. 10.14 - Prob. 191SEPCh. 10.14 - Prob. 192SEPCh. 10.14 - Prob. 193SEPCh. 10.14 - (a) In selecting the materials for an infant milk...Ch. 10.14 - Prob. 195SEPCh. 10.14 - Prob. 196SEPCh. 10.14 - (a) In selecting the materials for compact discs,...Ch. 10.14 - Prob. 198SEPCh. 10.14 - Prob. 199SEPCh. 10.14 - Prob. 200SEPCh. 10.14 - (a) In selecting the materials for a bungee cord,...Ch. 10.14 - Prob. 202SEPCh. 10.14 - Prob. 203SEPCh. 10.14 - In orthopedic applications related to knee and hip...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- ( B ) A stress of 6.7 MPa is employed to one type of a polymer under constant strain . After 40 days at 20 ° C the stress is reduced to only 8.4 MPa . When the same polymer is heated to 40 ° C the relaxation time is 40 days . 1- Calculate the relaxation time constant for this material at 25 ° C ? 2- Estimate the stress after 50 days at 25 ° C ? 3- Estimate the stress relaxation activation energy for the same polymer .arrow_forwardMolecular weight data for some polymer are tabulated here. Compute (a) the number-average molecular weight, (b) the weight-average molecular weight. (c) If it is known that this material's degree of polymerization is 710, which one of the polymers listed in Table 14.3 is this polymer? Why? Molecular Weight Range g/mol 15,000-30,000 Xi Wi 0.04 0.01 30,000-45,000 0.07 0.04 45,000-60,000 0.16 0.11 60,000-75,000 0.26 0.24 75,000-90,000 0.24 0.27 90,000 105,000 0.12 0.16 105,000-120,000 0.08 0.12 120,000-135,000 0.03 0.05arrow_forwardQuestion Seven (Plastics) The data below is from a fibre reinforced plastic. Would this composite be suitable for use at 400°C? Explain your answer. Temperature (°C) 20 100 200 300 400 500 600 Plastic A Plastic B Plastic C Yield Strength (MPa) 270 350 47 Tensile Strength (MPa) 300 500 52 E (GPa) 130 3 14 115 100 95 Question Eight (Plastics) Identify the thermoplastic, the elastomer and the thermoset. 70 58 0 Young's Modulus (GPa) Elongation (%) 12 3 600arrow_forward
- Explain what the following terms mean:decomposition temperature, heat distortion temperature, glass-transition temperature, and melting temperature. Why is itthat thermoplastics do not have a fixedmelting or glass-transition temperature?arrow_forwardDraw the structure of the idealized modulus-temperature for thermoplastic and thermosetscurveand mention all the transitions.arrow_forward1. Explain in 1-3 bullets how as a practicing engineer you determine the yield strength of a thermoplastic polymer from a tensile stress-strain curve. 2. Explain what is happening at the yield strength for a thermoplastic polymer from a physical standpoint in 1-3 bullets. (e.g. what are the atoms or polymer chains doing?)arrow_forward
- Why do thermoplastic polymers start to turn white as they are plastically deformed?arrow_forwardA manufacturer plant to produce a new thermoplastic product. Select a suitable processing method that can be applied А. Transfer moulding В. Rotating moulding C. Compression moulding D. Castingarrow_forwardV. Using the figure/data below, answer the following questions for polystyrene: (a) What is the specific free volume at 120°C? (b) What is the specific free volume at 80°C? ag "24 x 104 1ºc OR "55x 104 10C Spacific Volume 100°C Temperature, OCarrow_forward
- An unknown polymer sample was found to have the following molecular weight distribution: Molecular weight range 8,000 - 20,000 20,000 - 32,000 32,000 - 44,000 44,000 - 56,000 56,000 - 68,000 68,000 -80,000 80,000 - 92,000 0.03 Knowing that the monomer is methyl methacrylate, which of the below is the number average degree of polymerization for this polymer sample? Select one: O a. O b. DP 476 O C. DP = 338 DP = 664 O d. DP 544 O e. DP = 801 Xi 0.05 0.15 0.21 0.28 0.18 0.10 Wi 0.02 0.08 0.17 0.29 0.23 0.16 0.05arrow_forwardExplain the relationship between STRUCTURE/ PROPERTIES/ PROCESSING/ PERFORMANCE of a polymer which is a drawn fiber thermoplastic. You should have at least a sentence for each of these.arrow_forwardA continuous and aligned fiber-reinforced composite is to be produced consisting of 30% vol aramid fibers and 70% vol of a polycarbonate matrix. Mechanical characteristics from the test are given below. The composite is characterized by mechanical testing in both longitudinal and transverse loading. Calculate the longitudinal and transverse elastic modulus. 30% vol aramid fibers (Modulus of Elasticity - 121.68 GPa) 70% vol of a polycarbonate matrix (Modulus of Elasticity - 3.42 GPa)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Polymer Basics; Author: Tonya Coffey;https://www.youtube.com/watch?v=c5gFHpWvDXk;License: Standard youtube license