Question
Chapter 10.14, Problem 86AAP
(a)
To determine
The relaxation time for rubber material.
(b)
To determine
The stress on rubber material after 15 days.
The stress on rubber material after 40 days.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
For a given polymer, the activation energy for the stress relaxation was measured to be 59kj/mol. If the stress relaxation time for this polymer at 7 degree Celsius is 3150 seconds. What is the relaxation time at 110 degree Celsius
Which of the statements below are accurate regarding the stress-strain behavior of polymers:
(This question has more than one correct answer)
а.
Strain softening happens in elastomers where the deformation gradually leads to a decrease in stress under constant strain
rate
b.
As temperature is reduced, the necking behavior of plastic tensile bars completely disappears
C- The slope of the stress-strain curve for totally elastic and brittle polymers is always positive
d.
The stress-strain curve for vulcanized elastomers has a greater slope than unvulcanized polymers throughout
A sample of cross-linked natural rubber (polyisoprene) is found to have a shear modulus of 100 kPa at 20˚C. Determine the force needed to stretch a 20 mm diameter by 100 mm long rod to 300 mm (stretched in the length direction). What is the diameter of this rod of natural rubber under such a load?
Chapter 10 Solutions
Foundations of Materials Science and Engineering
Ch. 10.14 - Define and differentiate polymers, plastics, and...Ch. 10.14 - (a) Describe the atomic structural arrangement of...Ch. 10.14 - What is a pendant atom or group of atoms?Ch. 10.14 - (a)What type of bonding exists within the...Ch. 10.14 - Prob. 5KCPCh. 10.14 - Prob. 6KCPCh. 10.14 - Prob. 7KCPCh. 10.14 - (a) What is the repeating chemical unit of a...Ch. 10.14 - What are the three major reactions that occur...Ch. 10.14 - Prob. 10KCP
Ch. 10.14 - (a) Why must one consider the average degree of...Ch. 10.14 - Prob. 12KCPCh. 10.14 - Write structural formulas for the mers of the...Ch. 10.14 - Prob. 14KCPCh. 10.14 - Prob. 15KCPCh. 10.14 - Prob. 16KCPCh. 10.14 - Define stepwise polymerization of linear polymers....Ch. 10.14 - What are three basic raw materials used to produce...Ch. 10.14 - Describe and illustrate the following...Ch. 10.14 - Prob. 20KCPCh. 10.14 - Prob. 21KCPCh. 10.14 - Prob. 22KCPCh. 10.14 - Prob. 23KCPCh. 10.14 - Prob. 24KCPCh. 10.14 - Prob. 25KCPCh. 10.14 - Prob. 26KCPCh. 10.14 - Prob. 27KCPCh. 10.14 - Prob. 28KCPCh. 10.14 - Prob. 29KCPCh. 10.14 - (a) Describe the compression-molding process for...Ch. 10.14 - (a) Describe the transfer-molding process for...Ch. 10.14 - Prob. 32KCPCh. 10.14 - Define an engineering thermoplastic. Why is this...Ch. 10.14 - What is the structural formula for the amide...Ch. 10.14 - (a) In the designation nylon 6,6, what does the...Ch. 10.14 - Prob. 36KCPCh. 10.14 - Prob. 37KCPCh. 10.14 - Prob. 38KCPCh. 10.14 - Prob. 39KCPCh. 10.14 - Prob. 40KCPCh. 10.14 - Prob. 41KCPCh. 10.14 - Prob. 42KCPCh. 10.14 - Prob. 43KCPCh. 10.14 - Prob. 44KCPCh. 10.14 - (a) What are the major processing methods used for...Ch. 10.14 - Prob. 46KCPCh. 10.14 - Prob. 47KCPCh. 10.14 - Prob. 48KCPCh. 10.14 - What is natural rubber mainly made of? What other...Ch. 10.14 - Prob. 50KCPCh. 10.14 - Prob. 51KCPCh. 10.14 - Prob. 52KCPCh. 10.14 - Prob. 53KCPCh. 10.14 - What is the vulcanization process for natural...Ch. 10.14 - Prob. 55KCPCh. 10.14 - Prob. 56KCPCh. 10.14 - What are the silicones? What is the general...Ch. 10.14 - Prob. 58KCPCh. 10.14 - Prob. 59KCPCh. 10.14 - Prob. 60KCPCh. 10.14 - Prob. 61KCPCh. 10.14 - Define the creep modulus of a plastic material.Ch. 10.14 - What is a craze in a glassy thermoplastic?Ch. 10.14 - Describe the structure of a craze in a...Ch. 10.14 - Prob. 65KCPCh. 10.14 - Prob. 66AAPCh. 10.14 - Prob. 67AAPCh. 10.14 - Prob. 68AAPCh. 10.14 - An injection-molding polycarbonate material has an...Ch. 10.14 - Prob. 70AAPCh. 10.14 - Prob. 71AAPCh. 10.14 - Prob. 72AAPCh. 10.14 - Prob. 73AAPCh. 10.14 - How much sulfur must be added to 70 g of butadiene...Ch. 10.14 - If 5 g of sulfur is added to 90 g of butadiene...Ch. 10.14 - Prob. 76AAPCh. 10.14 - Prob. 77AAPCh. 10.14 - Prob. 78AAPCh. 10.14 - Prob. 79AAPCh. 10.14 - Prob. 80AAPCh. 10.14 - Prob. 81AAPCh. 10.14 - Prob. 82AAPCh. 10.14 - Prob. 83AAPCh. 10.14 - A polymeric material has a relaxation time of 60...Ch. 10.14 - Prob. 85AAPCh. 10.14 - Prob. 86AAPCh. 10.14 - Prob. 87AAPCh. 10.14 - Prob. 88AAPCh. 10.14 - Prob. 89AAPCh. 10.14 - Prob. 90AAPCh. 10.14 - Prob. 91AAPCh. 10.14 - Prob. 92AAPCh. 10.14 - Prob. 93AAPCh. 10.14 - (a) What causes a polyethylene molecular chain to...Ch. 10.14 - Prob. 95AAPCh. 10.14 - Prob. 96AAPCh. 10.14 - Prob. 97AAPCh. 10.14 - Prob. 98AAPCh. 10.14 - Write the reaction for the stepwise polymerization...Ch. 10.14 - Prob. 100AAPCh. 10.14 - Prob. 101AAPCh. 10.14 - How does chain branching affect the following...Ch. 10.14 - (a) Write the general reaction for the...Ch. 10.14 - Prob. 104AAPCh. 10.14 - Prob. 105AAPCh. 10.14 - Prob. 106AAPCh. 10.14 - Prob. 107AAPCh. 10.14 - Prob. 108AAPCh. 10.14 - Prob. 109AAPCh. 10.14 - Prob. 110AAPCh. 10.14 - Prob. 111AAPCh. 10.14 - Prob. 112AAPCh. 10.14 - Prob. 113AAPCh. 10.14 - Prob. 114AAPCh. 10.14 - Prob. 115AAPCh. 10.14 - Prob. 116AAPCh. 10.14 - Prob. 117AAPCh. 10.14 - Prob. 118AAPCh. 10.14 - Prob. 119AAPCh. 10.14 - Prob. 120AAPCh. 10.14 - What are two types of reaction sites that are...Ch. 10.14 - Prob. 122AAPCh. 10.14 - Prob. 123AAPCh. 10.14 - Prob. 124AAPCh. 10.14 - Prob. 125AAPCh. 10.14 - Prob. 126AAPCh. 10.14 - How does cross-linking with sulfur affect the...Ch. 10.14 - Prob. 128AAPCh. 10.14 - Can SBR be vulcanized? Explain.Ch. 10.14 - Prob. 130AAPCh. 10.14 - Write the repeating chemical structural unit for...Ch. 10.14 - Prob. 132AAPCh. 10.14 - Prob. 133AAPCh. 10.14 - Prob. 134AAPCh. 10.14 - Prob. 135AAPCh. 10.14 - Prob. 136AAPCh. 10.14 - Prob. 137AAPCh. 10.14 - Explain how highly polar atoms bonded to the main...Ch. 10.14 - Prob. 139AAPCh. 10.14 - Prob. 140AAPCh. 10.14 - Prob. 141AAPCh. 10.14 - Prob. 142AAPCh. 10.14 - Prob. 143AAPCh. 10.14 - Prob. 144AAPCh. 10.14 - Why do cured thermoset plastics not become viscous...Ch. 10.14 - Prob. 146AAPCh. 10.14 - Prob. 147AAPCh. 10.14 - Prob. 148AAPCh. 10.14 - Prob. 149AAPCh. 10.14 - Prob. 150AAPCh. 10.14 - Prob. 151AAPCh. 10.14 - Prob. 152AAPCh. 10.14 - Prob. 153AAPCh. 10.14 - Prob. 154AAPCh. 10.14 - Prob. 155AAPCh. 10.14 - Prob. 156AAPCh. 10.14 - Prob. 157AAPCh. 10.14 - Prob. 158AAPCh. 10.14 - Prob. 159AAPCh. 10.14 - Prob. 160AAPCh. 10.14 - Prob. 161AAPCh. 10.14 - Prob. 162AAPCh. 10.14 - Prob. 163AAPCh. 10.14 - Prob. 164AAPCh. 10.14 - Prob. 165AAPCh. 10.14 - Prob. 166AAPCh. 10.14 - Prob. 167AAPCh. 10.14 - Prob. 168AAPCh. 10.14 - Prob. 169AAPCh. 10.14 - Prob. 170AAPCh. 10.14 - Prob. 171AAPCh. 10.14 - Prob. 172AAPCh. 10.14 - Prob. 173AAPCh. 10.14 - Prob. 174AAPCh. 10.14 - Prob. 175AAPCh. 10.14 - Prob. 176AAPCh. 10.14 - Prob. 178AAPCh. 10.14 - Prob. 179AAPCh. 10.14 - What are some of the advantages of epoxy thermoset...Ch. 10.14 - How are most unsaturated polyesters reinforced?Ch. 10.14 - What are some applications for reinforced...Ch. 10.14 - Prob. 183AAPCh. 10.14 - Prob. 187SEPCh. 10.14 - Prob. 188SEPCh. 10.14 - Prob. 189SEPCh. 10.14 - Prob. 190SEPCh. 10.14 - Prob. 191SEPCh. 10.14 - Prob. 192SEPCh. 10.14 - Prob. 193SEPCh. 10.14 - (a) In selecting the materials for an infant milk...Ch. 10.14 - Prob. 195SEPCh. 10.14 - Prob. 196SEPCh. 10.14 - (a) In selecting the materials for compact discs,...Ch. 10.14 - Prob. 198SEPCh. 10.14 - Prob. 199SEPCh. 10.14 - Prob. 200SEPCh. 10.14 - (a) In selecting the materials for a bungee cord,...Ch. 10.14 - Prob. 202SEPCh. 10.14 - Prob. 203SEPCh. 10.14 - In orthopedic applications related to knee and hip...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A polymer sample of height 700 cm with an area of 6 m2 supports a mass of 70 tons. Youngs modulus of the polymer sample is found to be 60 GPa. Calculate the change in height of the polymer sample, applied stress and strain.arrow_forwardA stress of 1 kPa in a polymer deceased to 0.98 kPa after six weeks. This polymer is to hold a bundle of steel rods for up to one year. If the stress is less than 1.5 kPa, the band will not hold the rods tightly. Determine the initial stress needed to hold the rods.arrow_forwardFor a given polymer, the activation energy for stress relaxation was measured to be 10 kJ/mol. If the stress relaxation time for this polymer at room temperature is 3,600 s, what would be the relaxation time at 100 ◦C?arrow_forward
- (a) Draw a qualitative engineering stress-strain curve for A Ductile polymer (i) (ii) A Metal (iii) A ceramic (Iv) (v) A glass A Natural rubber Label carefully. Rationalize your sketch for each materialarrow_forwardA panel of poly(methyl methacrylate) is bolted in the long direction only at 50°C between two other components with zero coefficients of expansion. What is the stress on the polymer at 0°C? Will the polymer break?arrow_forwardDraw the stress-strain diagram and mark the regions. How can you use stress-strain diagrams in selecting the most appropriate material for an orthopedic biomaterial?arrow_forward
- Q2/ Apolmer must not fail when tensile stress of 125 Mpa is applied .if the surfuce energy of this polymer is 0.5 j/ m and modulus of elasticity of 3 Gpa Answer the following : 1. Convert j/m to N/ m 2. Determine the allowable length of crack in ( mm) before failurearrow_forwardWhat are the differences between continuous or steady shear rheometry and oscillatory and creep measurements in determining the consistency of viscoelastic materials.arrow_forwardAt an axial load of 25 kN, a 50-mm-wide by 20-mm-thick polyimide polymer bar elongates 2.8 mm while the bar width contracts 0.29 mm. The bar is 190 mm long. At the 25-kN load, the stress in the polymer bar is less than its proportional limit. Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thickness. Answers: (a) E= (b) v= (c) Athickness= i i GPa mmarrow_forward
- Using the aid of a diagram, describe the behaviour stress vs strain of a brittle polymer. Give one example of a brittle pharmaceutical polymer and their function in table formuarrow_forwardAt an axial load of 24 kN, a 35-mm-wide by 15- mm-thick polyimide polymer bar elongates 3.0 mm while the bar width contracts 0.15 mm. The bar is 230 mm long. At the 24-kN load, the stress in the polymer bar is less than its proportional limit. Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thickness. Answers: E= = V = IN Athickness= i GPa mmarrow_forwardAn unknown polymer sample was found to have the following molecular weight distribution: Molecular weight range 8,000 - 20,000 20,000 - 32,000 32,000 - 44,000 44,000 - 56,000 56,000 -68,000 68,000 -80,000 80,000 - 92,000 Having a DP=763, which of the following common polymers is this sample? Xi 0.05 0.15 0.21 0.28 0.18 0.10 0.03 Wi 0.02 0.08 0.17 0.29 0.23 0.16 0.05 Select one: O a. Polymethylmethacrylate with a monomer molecular weight of 100.121 g/mol O b. Polystyrene with a monomer molecular weight of 104.15 g/mol Polycarbonate with a monomer molecular weight of 61.0168 g/mol O c. O d. Polyvinyl chloride with a monomer molecular weight of 62.498 g/mol Polypropylene with a monomer molecular weight of 42.08 g/mol O e.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Polymer Basics; Author: Tonya Coffey;https://www.youtube.com/watch?v=c5gFHpWvDXk;License: Standard youtube license