Question
Chapter 10.14, Problem 111AAP
To determine
What part of the structure of polyphenylene oxide provides its relatively high strength and what part of its structure provides its molecular flexibility.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
( B ) A stress of 6.7 MPa is employed to one type of a polymer under constant strain . After 40 days at 20 ° C the stress is reduced to only 8.4 MPa . When the same polymer is heated to 40 ° C the relaxation time is 40 days . 1- Calculate the relaxation time constant for this material at 25 ° C ? 2- Estimate the stress after 50 days at 25 ° C ? 3- Estimate the stress relaxation activation energy for the same polymer .
cis-1, 2-Dimethylcyclobutane is less stable than its trans isomer, but cis-1, 3-dimethylcyclobutane is more stable than its trans isomer.Draw the most stable conformations of both, and explain.
For a given polymer, the activation energy for stress relaxation was measured to be 10 kJ/mol. If the stress relaxation time for this polymer at room
temperature is 3,600 s, what would be the relaxation time at 100 ◦C?
Chapter 10 Solutions
Foundations of Materials Science and Engineering
Ch. 10.14 - Define and differentiate polymers, plastics, and...Ch. 10.14 - (a) Describe the atomic structural arrangement of...Ch. 10.14 - What is a pendant atom or group of atoms?Ch. 10.14 - (a)What type of bonding exists within the...Ch. 10.14 - Prob. 5KCPCh. 10.14 - Prob. 6KCPCh. 10.14 - Prob. 7KCPCh. 10.14 - (a) What is the repeating chemical unit of a...Ch. 10.14 - What are the three major reactions that occur...Ch. 10.14 - Prob. 10KCP
Ch. 10.14 - (a) Why must one consider the average degree of...Ch. 10.14 - Prob. 12KCPCh. 10.14 - Write structural formulas for the mers of the...Ch. 10.14 - Prob. 14KCPCh. 10.14 - Prob. 15KCPCh. 10.14 - Prob. 16KCPCh. 10.14 - Define stepwise polymerization of linear polymers....Ch. 10.14 - What are three basic raw materials used to produce...Ch. 10.14 - Describe and illustrate the following...Ch. 10.14 - Prob. 20KCPCh. 10.14 - Prob. 21KCPCh. 10.14 - Prob. 22KCPCh. 10.14 - Prob. 23KCPCh. 10.14 - Prob. 24KCPCh. 10.14 - Prob. 25KCPCh. 10.14 - Prob. 26KCPCh. 10.14 - Prob. 27KCPCh. 10.14 - Prob. 28KCPCh. 10.14 - Prob. 29KCPCh. 10.14 - (a) Describe the compression-molding process for...Ch. 10.14 - (a) Describe the transfer-molding process for...Ch. 10.14 - Prob. 32KCPCh. 10.14 - Define an engineering thermoplastic. Why is this...Ch. 10.14 - What is the structural formula for the amide...Ch. 10.14 - (a) In the designation nylon 6,6, what does the...Ch. 10.14 - Prob. 36KCPCh. 10.14 - Prob. 37KCPCh. 10.14 - Prob. 38KCPCh. 10.14 - Prob. 39KCPCh. 10.14 - Prob. 40KCPCh. 10.14 - Prob. 41KCPCh. 10.14 - Prob. 42KCPCh. 10.14 - Prob. 43KCPCh. 10.14 - Prob. 44KCPCh. 10.14 - (a) What are the major processing methods used for...Ch. 10.14 - Prob. 46KCPCh. 10.14 - Prob. 47KCPCh. 10.14 - Prob. 48KCPCh. 10.14 - What is natural rubber mainly made of? What other...Ch. 10.14 - Prob. 50KCPCh. 10.14 - Prob. 51KCPCh. 10.14 - Prob. 52KCPCh. 10.14 - Prob. 53KCPCh. 10.14 - What is the vulcanization process for natural...Ch. 10.14 - Prob. 55KCPCh. 10.14 - Prob. 56KCPCh. 10.14 - What are the silicones? What is the general...Ch. 10.14 - Prob. 58KCPCh. 10.14 - Prob. 59KCPCh. 10.14 - Prob. 60KCPCh. 10.14 - Prob. 61KCPCh. 10.14 - Define the creep modulus of a plastic material.Ch. 10.14 - What is a craze in a glassy thermoplastic?Ch. 10.14 - Describe the structure of a craze in a...Ch. 10.14 - Prob. 65KCPCh. 10.14 - Prob. 66AAPCh. 10.14 - Prob. 67AAPCh. 10.14 - Prob. 68AAPCh. 10.14 - An injection-molding polycarbonate material has an...Ch. 10.14 - Prob. 70AAPCh. 10.14 - Prob. 71AAPCh. 10.14 - Prob. 72AAPCh. 10.14 - Prob. 73AAPCh. 10.14 - How much sulfur must be added to 70 g of butadiene...Ch. 10.14 - If 5 g of sulfur is added to 90 g of butadiene...Ch. 10.14 - Prob. 76AAPCh. 10.14 - Prob. 77AAPCh. 10.14 - Prob. 78AAPCh. 10.14 - Prob. 79AAPCh. 10.14 - Prob. 80AAPCh. 10.14 - Prob. 81AAPCh. 10.14 - Prob. 82AAPCh. 10.14 - Prob. 83AAPCh. 10.14 - A polymeric material has a relaxation time of 60...Ch. 10.14 - Prob. 85AAPCh. 10.14 - Prob. 86AAPCh. 10.14 - Prob. 87AAPCh. 10.14 - Prob. 88AAPCh. 10.14 - Prob. 89AAPCh. 10.14 - Prob. 90AAPCh. 10.14 - Prob. 91AAPCh. 10.14 - Prob. 92AAPCh. 10.14 - Prob. 93AAPCh. 10.14 - (a) What causes a polyethylene molecular chain to...Ch. 10.14 - Prob. 95AAPCh. 10.14 - Prob. 96AAPCh. 10.14 - Prob. 97AAPCh. 10.14 - Prob. 98AAPCh. 10.14 - Write the reaction for the stepwise polymerization...Ch. 10.14 - Prob. 100AAPCh. 10.14 - Prob. 101AAPCh. 10.14 - How does chain branching affect the following...Ch. 10.14 - (a) Write the general reaction for the...Ch. 10.14 - Prob. 104AAPCh. 10.14 - Prob. 105AAPCh. 10.14 - Prob. 106AAPCh. 10.14 - Prob. 107AAPCh. 10.14 - Prob. 108AAPCh. 10.14 - Prob. 109AAPCh. 10.14 - Prob. 110AAPCh. 10.14 - Prob. 111AAPCh. 10.14 - Prob. 112AAPCh. 10.14 - Prob. 113AAPCh. 10.14 - Prob. 114AAPCh. 10.14 - Prob. 115AAPCh. 10.14 - Prob. 116AAPCh. 10.14 - Prob. 117AAPCh. 10.14 - Prob. 118AAPCh. 10.14 - Prob. 119AAPCh. 10.14 - Prob. 120AAPCh. 10.14 - What are two types of reaction sites that are...Ch. 10.14 - Prob. 122AAPCh. 10.14 - Prob. 123AAPCh. 10.14 - Prob. 124AAPCh. 10.14 - Prob. 125AAPCh. 10.14 - Prob. 126AAPCh. 10.14 - How does cross-linking with sulfur affect the...Ch. 10.14 - Prob. 128AAPCh. 10.14 - Can SBR be vulcanized? Explain.Ch. 10.14 - Prob. 130AAPCh. 10.14 - Write the repeating chemical structural unit for...Ch. 10.14 - Prob. 132AAPCh. 10.14 - Prob. 133AAPCh. 10.14 - Prob. 134AAPCh. 10.14 - Prob. 135AAPCh. 10.14 - Prob. 136AAPCh. 10.14 - Prob. 137AAPCh. 10.14 - Explain how highly polar atoms bonded to the main...Ch. 10.14 - Prob. 139AAPCh. 10.14 - Prob. 140AAPCh. 10.14 - Prob. 141AAPCh. 10.14 - Prob. 142AAPCh. 10.14 - Prob. 143AAPCh. 10.14 - Prob. 144AAPCh. 10.14 - Why do cured thermoset plastics not become viscous...Ch. 10.14 - Prob. 146AAPCh. 10.14 - Prob. 147AAPCh. 10.14 - Prob. 148AAPCh. 10.14 - Prob. 149AAPCh. 10.14 - Prob. 150AAPCh. 10.14 - Prob. 151AAPCh. 10.14 - Prob. 152AAPCh. 10.14 - Prob. 153AAPCh. 10.14 - Prob. 154AAPCh. 10.14 - Prob. 155AAPCh. 10.14 - Prob. 156AAPCh. 10.14 - Prob. 157AAPCh. 10.14 - Prob. 158AAPCh. 10.14 - Prob. 159AAPCh. 10.14 - Prob. 160AAPCh. 10.14 - Prob. 161AAPCh. 10.14 - Prob. 162AAPCh. 10.14 - Prob. 163AAPCh. 10.14 - Prob. 164AAPCh. 10.14 - Prob. 165AAPCh. 10.14 - Prob. 166AAPCh. 10.14 - Prob. 167AAPCh. 10.14 - Prob. 168AAPCh. 10.14 - Prob. 169AAPCh. 10.14 - Prob. 170AAPCh. 10.14 - Prob. 171AAPCh. 10.14 - Prob. 172AAPCh. 10.14 - Prob. 173AAPCh. 10.14 - Prob. 174AAPCh. 10.14 - Prob. 175AAPCh. 10.14 - Prob. 176AAPCh. 10.14 - Prob. 178AAPCh. 10.14 - Prob. 179AAPCh. 10.14 - What are some of the advantages of epoxy thermoset...Ch. 10.14 - How are most unsaturated polyesters reinforced?Ch. 10.14 - What are some applications for reinforced...Ch. 10.14 - Prob. 183AAPCh. 10.14 - Prob. 187SEPCh. 10.14 - Prob. 188SEPCh. 10.14 - Prob. 189SEPCh. 10.14 - Prob. 190SEPCh. 10.14 - Prob. 191SEPCh. 10.14 - Prob. 192SEPCh. 10.14 - Prob. 193SEPCh. 10.14 - (a) In selecting the materials for an infant milk...Ch. 10.14 - Prob. 195SEPCh. 10.14 - Prob. 196SEPCh. 10.14 - (a) In selecting the materials for compact discs,...Ch. 10.14 - Prob. 198SEPCh. 10.14 - Prob. 199SEPCh. 10.14 - Prob. 200SEPCh. 10.14 - (a) In selecting the materials for a bungee cord,...Ch. 10.14 - Prob. 202SEPCh. 10.14 - Prob. 203SEPCh. 10.14 - In orthopedic applications related to knee and hip...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- For a given polymer, the activation energy for the stress relaxation was measured to be 59kj/mol. If the stress relaxation time for this polymer at 7 degree Celsius is 3150 seconds. What is the relaxation time at 110 degree Celsiusarrow_forwardEthylene, C2H4, and tetrafluoroethylene, C2F4, are used to make the polymers polyethylene and polytetrafluoroethylene (Teflon), respectively.(a) Draw the Lewis structures for C2H4 and C2F4, and give theideal H-C-H and F-C-F bond angles.(b) The actual H-C-H and F-C-F bond angles are 117.4° and112.4°, respectively. Explain these deviations.arrow_forwardAn unknown polymer sample was found to have the following molecular weight distribution: Molecular weight range 8,000 - 20,000 20,000 - 32,000 32,000 - 44,000 44,000 - 56,000 56,000 - 68,000 68,000 -80,000 80,000 - 92,000 0.03 Knowing that the monomer is methyl methacrylate, which of the below is the number average degree of polymerization for this polymer sample? Select one: O a. O b. DP 476 O C. DP = 338 DP = 664 O d. DP 544 O e. DP = 801 Xi 0.05 0.15 0.21 0.28 0.18 0.10 Wi 0.02 0.08 0.17 0.29 0.23 0.16 0.05arrow_forward
- We are given a sample of polypropylene with the following composition. What is the number average molecular weight? mol% of chains MW (g/mol) 35 50000 20 100000 40 500000arrow_forwardWhat monomers and polymers and give some examples of eacharrow_forwardWhich of the statements below are accurate regarding the stress-strain behavior of polymers: (This question has more than one correct answer) а. Strain softening happens in elastomers where the deformation gradually leads to a decrease in stress under constant strain rate b. As temperature is reduced, the necking behavior of plastic tensile bars completely disappears C- The slope of the stress-strain curve for totally elastic and brittle polymers is always positive d. The stress-strain curve for vulcanized elastomers has a greater slope than unvulcanized polymers throughoutarrow_forward
- Calculate the mass of each product formed when 43.82 g of diborane (B₂H₆) reacts with excess water:B₂H₆(g)+ H₂O(l)→H₃BO₃(s)+ H₂(g) [unbalanced]arrow_forwardMolecular weight data for some polymer are tabulated here. Compute (a) the number-average molecular weight, (b) the weight-average molecular weight. (c) If it is known that this material's degree of polymerization is 710, which one of the polymers listed in Table 14.3 is this polymer? Why? Molecular Weight Range g/mol 15,000-30,000 Xi Wi 0.04 0.01 30,000-45,000 0.07 0.04 45,000-60,000 0.16 0.11 60,000-75,000 0.26 0.24 75,000-90,000 0.24 0.27 90,000 105,000 0.12 0.16 105,000-120,000 0.08 0.12 120,000-135,000 0.03 0.05arrow_forwardAn unknown polymer sample was found to have the following molecular weight distribution: Molecular weight range Wi 8,000 - 20,000 0.05 0.02 20,000 – 32,000 0.15 0.08 32,000 - 44,000 0.21 0.17 44,000 – 56,000 0.28 0.29 56,000 - 68,000 0.18 0.23 68,000 - 80,000 0.10 0.16 80,000 - 92,000 0.03 0.05 Which of the following common polymers is this sample? (This question has only one correct answer)arrow_forward
- Identify reagents A and B in the following reaction scheme. This synthetic sequence was used to prepare the C16 juvenile hormone (Figure 20.6). он OH (excess) (excess) several steps several steps čo,CH3 OH OH C18 juvenile hormonearrow_forward[Materials Engineering] Bis-GMA composite resin has been widely used as the dental restorative material. Discuss the factors leading to the degradation of this biomaterial and its possible adverse effects to the host body.arrow_forwardQuestion Seven (Plastics) The data below is from a fibre reinforced plastic. Would this composite be suitable for use at 400°C? Explain your answer. Temperature (°C) 20 100 200 300 400 500 600 Plastic A Plastic B Plastic C Yield Strength (MPa) 270 350 47 Tensile Strength (MPa) 300 500 52 E (GPa) 130 3 14 115 100 95 Question Eight (Plastics) Identify the thermoplastic, the elastomer and the thermoset. 70 58 0 Young's Modulus (GPa) Elongation (%) 12 3 600arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY