Question
Chapter 11, Problem 11.29QP
(a)
To determine
The modulus of elasticity of the composite in the longitudinal and transverse directions.
(b)
To determine
The load carried by the each of the fibers and matrix.
(c)
To determine
The strain sustained by each of the phases.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A FRP composite includes 47% continuous and aligned Aramid fibers by volume. The moduli of elasticity of the Aramid fibers and the epoxy resin matrix are 19 * 106 psi and 0.6 * 106 psi, respectively.a. Compute the modulus of elasticity of the composite in the longitudinal and transverse directions.b. If the composite cross-sectional area is 0.5 in.2 and a stress of 12 ksi is applied in the longitudinal direction, compute the load carried by the fibers and the matrix.c. Determine the strain sustained by each of the phases when stress in part(b) is applied.
A FRP composite includes 40% continuous and aligned Aramid fibers by vol-ume. The moduli of elasticity of the Aramid fibers and the epoxy resin matrix are 130 and 3.9 GPa, respectively.
a. Compute the modulus of elasticity of the composite in the longitudinal and transverse directions.
b. If the composite cross-sectional area is 150 mm' and a stress of 40 MPa is applied in the longitudinal direction, compute the load carried by the fibers and the matrix.
c. Determine the strain sustained by each of the phases when stress in part
(b) is applied.
An FRP composite includes 40% continuous and aligned Aramid fibers byvolume. The moduli of elasticity of the Aramid fibers and the epoxy resinmatrix are 130 and 3.9 GPa, respectively.a. Compute the modulus of elasticity of the composite in the longitudinaland transverse directions.b. If the composite cross-sectional area is 150 mm2 and a stress of 40 MPais applied in the longitudinal direction, compute the load carried by thefibers and the matrix.c. Determine the strain sustained by each of the phases when stress in part(b) is applied.
Chapter 11 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 11 - Prob. 11.1QPCh. 11 - Prob. 11.2QPCh. 11 - Prob. 11.3QPCh. 11 - Prob. 11.4QPCh. 11 - Prob. 11.5QPCh. 11 - Prob. 11.6QPCh. 11 - Prob. 11.7QPCh. 11 - Prob. 11.8QPCh. 11 - Prob. 11.9QPCh. 11 - What are the functions of aggregate used in...
Ch. 11 - Prob. 11.11QPCh. 11 - Prob. 11.12QPCh. 11 - What are the benefits of adding dispersed steel...Ch. 11 - Getting measurements from Figure 11.20, determine...Ch. 11 - Three 6 in. 12 in. concrete cylinders with...Ch. 11 - Prob. 11.16QPCh. 11 - Prob. 11.17QPCh. 11 - Prob. 11.18QPCh. 11 - Prob. 11.19QPCh. 11 - Prob. 11.20QPCh. 11 - Prob. 11.21QPCh. 11 - Prob. 11.22QPCh. 11 - Prob. 11.23QPCh. 11 - Prob. 11.24QPCh. 11 - Prob. 11.25QPCh. 11 - Prob. 11.26QPCh. 11 - Prob. 11.27QPCh. 11 - Prob. 11.28QPCh. 11 - Prob. 11.29QPCh. 11 - Prob. 11.30QPCh. 11 - A circular FRP composite rod with continuous and...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?arrow_forwardQ: For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 GPa and 3.66 GPa, respectively. A) If the volume fraction of fibers is 0.25, determine the moduli of elasticity of fiber and matrix phases. B) If the cross-sectional area is 200 mm? and a stress of 40 MPa is applied in this longitudinal direction, compute the magnitude of the load carried by each of the fiber and matrix phases. C) Determine the strain that is sustained by each phase when the stress in part (b) is applied.arrow_forwardFor a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 and 3.66 GPa (2.8x10 and 5.3x 105 psi), respectively. If the volume fraction of fibers is 0.42, determine the moduli of elasticity of fiber and matrix phases. Em- E₁= i GPa GPaarrow_forward
- IV- It is necessary to design a continuous and aligned glass fiber-reinforced polyester having a tensile strength of at least 1400 MPa in the longitudinal direction. The maximum possible specific gravity is 1.65. Using the following data, determine whether such a composite is possible. Justify. Assume a value of 15 MPa for the stress on the matrix when the fibers fail. Material Glass fiber Polyester Specific gravity 2.5 1.35 Tensile strength (MPa) 3500 50arrow_forwardA fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the filers and the polymer are 50 X 10 psi and 0.5 x 10® psi, respectively, and the Poison's ratios of the fibers and the polvmer are 0.25 and 0.41, respectively. Calculate the following: a. modulus of elasticitv of the composite. b. percentage of load carried by the fibers c. Poison's ratio of the compositearrow_forwardDetermine the x-bar centroid of the composite figure shown. Where r=42 mmShow your solutionarrow_forward
- A fiber-reinforced polymer composite under isostrain condition consists of 35%fibers and 65% polymer by volume. The moduli of elasticity of the fibers and thepolymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of thefibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the compositearrow_forwardConsider a 40 % V¢ SiC whisker-reinforced aluminum composite. Ef = 400 GPa, Em = 70 GPa, and (l/d) = 20. Compute the longitudinal elastic mod- %3D ulus of this composite if all the whiskers are aligned in the longitudinal direction. Use Halpin-Tsai-Kardos equations. Take = 2(1ld).arrow_forwardA fiber-reinforced polymer composite under isostress condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the compositearrow_forward
- Compare the desired properties of the matrix and the fiber phases of the fiber reinforced composite.arrow_forwardQ2: A composite component consists of a glass fiber and an epoxy matrix. The glass fiber weight fraction is triple of the epoxy weight fraction. Use the given properties of epoxy and glass to determine: 1. The composite axial modulus, transverse modulus, major Poisson's ratio, and in- plane shear modulus. 2. If the total load is 24 kN and the applied stress is 60 MPa in this axial direction, compute the cross-sectional area of the composite and the magnitude of the load carried by each of the fiber and matrix phases. Given: Glass p, 2.5 g/cm³. Ey-E 80 GPa. v 0.2, G 38 GPa epoxy Pm-1.2 g/cm', E-, E- 3.5 GPa, vy= 0.3, G= 1.35 GPaarrow_forwardDetermine the total area of the composite figur e . (mm^2)Determine the x coordinate of the centroid of composite figure. (mm)Determine the y coordinate of the centroid of composite figure. (mm)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning