Question
Chapter 11, Problem 11.21QP
To determine
The modulus of elasticity of the carbon-epoxy composite under isostress condition and the percentage of load carried by the carbon fibers.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Calculate the modulus of elasticity of carbon–epoxy composite under isostrain condition if the composite consists of 40% carbon fibers and 60% epoxy by volume. Also, calculate the percentage of load carried by the carbon fibers.The moduli of elasticity of the carbon fibers and the epoxy are 350 and 3.5 GPa, respectively. Repeat under isostress condition.
A fiber-reinforced polymer composite under isostress condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
"A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite" Repeat for 45% fibers by volume.
Chapter 11 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 11 - Prob. 11.1QPCh. 11 - Prob. 11.2QPCh. 11 - Prob. 11.3QPCh. 11 - Prob. 11.4QPCh. 11 - Prob. 11.5QPCh. 11 - Prob. 11.6QPCh. 11 - Prob. 11.7QPCh. 11 - Prob. 11.8QPCh. 11 - Prob. 11.9QPCh. 11 - What are the functions of aggregate used in...
Ch. 11 - Prob. 11.11QPCh. 11 - Prob. 11.12QPCh. 11 - What are the benefits of adding dispersed steel...Ch. 11 - Getting measurements from Figure 11.20, determine...Ch. 11 - Three 6 in. 12 in. concrete cylinders with...Ch. 11 - Prob. 11.16QPCh. 11 - Prob. 11.17QPCh. 11 - Prob. 11.18QPCh. 11 - Prob. 11.19QPCh. 11 - Prob. 11.20QPCh. 11 - Prob. 11.21QPCh. 11 - Prob. 11.22QPCh. 11 - Prob. 11.23QPCh. 11 - Prob. 11.24QPCh. 11 - Prob. 11.25QPCh. 11 - Prob. 11.26QPCh. 11 - Prob. 11.27QPCh. 11 - Prob. 11.28QPCh. 11 - Prob. 11.29QPCh. 11 - Prob. 11.30QPCh. 11 - A circular FRP composite rod with continuous and...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?arrow_forward"A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite t Repeat under isostress condition.arrow_forwardCalculate the modulus of elasticity of carbon–epoxy composite under isostrain condition if the composite consists of 40% carbon fibers and 60% epoxy by volume. Also, calculate the percentage of load carried by the carbon fibers.The moduli of elasticity of the carbon fibers and the epoxy are 350 and 3.5 GPa, respectively. Repeat for 35% carbon fibers by volume.arrow_forward
- A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the filers and the polymer are 50 X 10 psi and 0.5 x 10® psi, respectively, and the Poison's ratios of the fibers and the polvmer are 0.25 and 0.41, respectively. Calculate the following: a. modulus of elasticitv of the composite. b. percentage of load carried by the fibers c. Poison's ratio of the compositearrow_forwardA fiber-reinforced polymer composite under isostrain condition consists of 35%fibers and 65% polymer by volume. The moduli of elasticity of the fibers and thepolymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of thefibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the compositearrow_forwardCalculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area of 300 mm2, what is the load carried by each of the fiber and the matrix phases?What is the strain sustained by each of the fiber and the matrix phases?arrow_forward
- Compute the components of the centroid Of the composite area shown. X = ÿ 11 y 60 mm 60 mm xarrow_forwardQ6) How does moisture impact tension and compression strength in composites?arrow_forwardIV- It is necessary to design a continuous and aligned glass fiber-reinforced polyester having a tensile strength of at least 1400 MPa in the longitudinal direction. The maximum possible specific gravity is 1.65. Using the following data, determine whether such a composite is possible. Justify. Assume a value of 15 MPa for the stress on the matrix when the fibers fail. Material Glass fiber Polyester Specific gravity 2.5 1.35 Tensile strength (MPa) 3500 50arrow_forward
- Q: For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 GPa and 3.66 GPa, respectively. A) If the volume fraction of fibers is 0.25, determine the moduli of elasticity of fiber and matrix phases. B) If the cross-sectional area is 200 mm? and a stress of 40 MPa is applied in this longitudinal direction, compute the magnitude of the load carried by each of the fiber and matrix phases. C) Determine the strain that is sustained by each phase when the stress in part (b) is applied.arrow_forwardCalculate the modulus of elasticity of carbon–epoxy composite under isostrain condition if the composite consists of 40% carbon fibers and 60% epoxy by volume. Also, calculate the percentage of load carried by the carbon fibers. The moduli of elasticity of the carbon fibers and the epoxy are 350 and 3.5 GPa, respectively.arrow_forwardCalculate the modulus of elasticity of carbon–epoxy composite under isostrain condition if the composite consists of 40% carbon fibers and 60% epoxy by volume. Also, calculate the percentage of load carried by the carbon fibers.The moduli of elasticity of the carbon fibers and the epoxy are 350 and 3.5 GPa, respectively.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning