A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the filers and the polymer are 50 X 10 psi and 0.5 x 10® psi, respectively, and the Poison's ratios of the fibers and the polvmer are 0.25 and 0.41, respectively. Calculate the following: a. modulus of elasticitv of the composite. b. percentage of load carried by the fibers c. Poison's ratio of the composite

A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the filers and the polymer are 50 X 10 psi and 0.5 x 10® psi, respectively, and the Poison's ratios of the fibers and the polvmer are 0.25 and 0.41, respectively. Calculate the following: a. modulus of elasticitv of the composite. b. percentage of load carried by the fibers c. Poison's ratio of the composite

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter12: Composite Materials

Section: Chapter Questions

Problem 12.3P

See similar textbooks

Similar questions

In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?
A fiber-reinforced polymer composite under isostrain condition consists of 35%fibers and 65% polymer by volume. The moduli of elasticity of the fibers and thepolymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of thefibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
A fiber-reinforced polymer composite under isostress condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
"A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite t Repeat under isostress condition.
"A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite" Repeat for 45% fibers by volume.
Calculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area of 300 mm2, what is the load carried by each of the fiber and the matrix phases?What is the strain sustained by each of the fiber and the matrix phases?
Q: For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 GPa and 3.66 GPa, respectively. A) If the volume fraction of fibers is 0.25, determine the moduli of elasticity of fiber and matrix phases. B) If the cross-sectional area is 200 mm? and a stress of 40 MPa is applied in this longitudinal direction, compute the magnitude of the load carried by each of the fiber and matrix phases. C) Determine the strain that is sustained by each phase when the stress in part (b) is applied.
IV- It is necessary to design a continuous and aligned glass fiber-reinforced polyester having a tensile strength of at least 1400 MPa in the longitudinal direction. The maximum possible specific gravity is 1.65. Using the following data, determine whether such a composite is possible. Justify. Assume a value of 15 MPa for the stress on the matrix when the fibers fail. Material Glass fiber Polyester Specific gravity 2.5 1.35 Tensile strength (MPa) 3500 50
For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 and 3.66 GPa (2.8x10 and 5.3x 105 psi), respectively. If the volume fraction of fibers is 0.42, determine the moduli of elasticity of fiber and matrix phases. Em- E₁= i GPa GPa
An epoxy is randomly reinforced with E-Glass fibers with 0.0012 in. diameter, 0.5 in. length, 0.5 * 106 psi ultimate tensile strength, and 7.2 ksi shear strength. Does this fiber length fully strengthen the composite? What is the minimum fiber length that would make the composite continuously reinforced?
The load-strain data obtained in a tension test of a unidirectional carbon fiber/epoxy composite are given below. The specimen dimensions are length=254 mm, width=12.7 mm and thickness is 1.4 mm. Determine the tensile modulus and Poisson ration for each fiber orientation Axial strain Load (N) Transverse strain % 自 % 0° 45° 90° 0° 45° 90° 0.05 2130 130 67 -0.012 -0.113 -0.0004 0.10 4270 255 134 -0.027 -0.021 -0.001 0.15 6400 360 204 -0.041 -0.029 -0.0014 0.20 8620 485 333 -0.054 -0.038 -0.0019 0.25 565 396 -0.048 -0.0025