Calculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area of 300 mm2, what is the load carried by each of the fiber and the matrix phases?What is the strain sustained by each of the fiber and the matrix phases?

Calculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area of 300 mm2, what is the load carried by each of the fiber and the matrix phases?What is the strain sustained by each of the fiber and the matrix phases?

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter12: Composite Materials

Section: Chapter Questions

Problem 12.3P

See similar textbooks

Similar questions

In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?
IV- It is necessary to design a continuous and aligned glass fiber-reinforced polyester having a tensile strength of at least 1400 MPa in the longitudinal direction. The maximum possible specific gravity is 1.65. Using the following data, determine whether such a composite is possible. Justify. Assume a value of 15 MPa for the stress on the matrix when the fibers fail. Material Glass fiber Polyester Specific gravity 2.5 1.35 Tensile strength (MPa) 3500 50
A fiber-reinforced polymer composite under isostress condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
Determine the maximum moment of inertia of the composite figure shown below, in mm^4.
The load-strain data obtained in a tension test of a unidirectional carbon fiber/epoxy composite are given below. The specimen dimensions are length=254 mm, width=12.7 mm and thickness is 1.4 mm. Determine the tensile modulus and Poisson ration for each fiber orientation Axial strain Load (N) Transverse strain % 自 % 0° 45° 90° 0° 45° 90° 0.05 2130 130 67 -0.012 -0.113 -0.0004 0.10 4270 255 134 -0.027 -0.021 -0.001 0.15 6400 360 204 -0.041 -0.029 -0.0014 0.20 8620 485 333 -0.054 -0.038 -0.0019 0.25 565 396 -0.048 -0.0025
A fiber-reinforced polymer composite under isostrain condition consists of 35%fibers and 65% polymer by volume. The moduli of elasticity of the fibers and thepolymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of thefibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
Determine the y-bar centroid of the composite figure shown. Where: y = 20mm and x = 10 mm
The composite bar is stress-free before the axial loads P, and P, are applied. Assuming that the walls are rigid, calculate the stress (MPa) in each material if P1 = 150 kN and P2 = 90 kN Aluminum A = 900 mm A = 2000 mm A = 1200 mm? E = 70 GPa | E= 200 GPa Steel Bronze E = 83 GPa P1 500 mm 250 mm' 350 mm
The composite bar is initially stress-free. Calculate the stress in each material and indicate tension or compression if the temperature has increased to 25°C. Consider that the walls are unyielding and suitably braced to prevent buckling. Use 2 decimal places.
Determine the x-bar centroid of the composite figure shown. Where r=49 mm
For the composite area shown, calculate the moment of inertia about X and Y axes
A 1500 mm long composite bar consists of aluminum and steel as shown. The cross-sectional area of the aluminum bar is twice that of the steel bar. If the assembly is exposed to an axial tensile load of 250 kN, determine the lengths of each of the components if the elongation of the aluminum is the same with that of the steel. The modulus of elasticity of steel E = 200 GPa and for the aluminum is one-third of the steel.