Textbook Question
Chapter 6, Problem 4P
A steel rotating-beam test specimen has an ultimate strength of 230 kpsi. Estimate the fatigue strength corresponding to a life of 150 kcycles of stress reversal.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Estimate the fatigue strength of a rotating-beam made of AISI 1020 HR steel
corresponding to a life of 12.5 kilocycles of stress reversal. Also, estimate the life of
the specimen corresponding to stress amplitude of 36 ksi.
A steel rotating-beam test specimen has an ultimate strength of 1600 MPa. Estimate the life of the specimenif it is tested at a completely reversed stress amplitude of 900 MPa.
2
Estimate the fatigue strength of a rotating-beam made of AISI 1035 CR steel
corresponding to a life of 10° cycles of stress reversal. Also, estimate the life of the
specimen corresponding to stress amplitude of 60 ksi.
Chapter 6 Solutions
Shigley's Mechanical Engineering Design (McGraw-Hill Series in Mechanical Engineering)
Ch. 6 - A 10-mm steel drill rod was heat-treated and...Ch. 6 - Prob. 2PCh. 6 - A steel rotating-beam test specimen has an...Ch. 6 - A steel rotating-beam test specimen has an...Ch. 6 - A steel rotating-beam test specimen has an...Ch. 6 - Repeat Prob. 6-5 with the specimen having an...Ch. 6 - A steel rotating-beam test specimen has an...Ch. 6 - Derive Eq. (6-17). Rearrange the equation to solve...Ch. 6 - For the interval 103 N 106 cycles, develop an...Ch. 6 - Estimate the endurance strength of a...
Ch. 6 - Two steels are being considered for manufacture of...Ch. 6 - A 1-in-diamctcr solid round bar has a groove...Ch. 6 - A solid square rod is cantilevered at one end. The...Ch. 6 - A rectangular bar is cut from an AISI 1020...Ch. 6 - A solid round bar with diameter of 2 in has a...Ch. 6 - The rotating shaft shown in the figure is machined...Ch. 6 - The shaft shown in the figure is machined from...Ch. 6 - Solve Prob. 6-17 except with forces F1 = 1200 lbf...Ch. 6 - Bearing reactions R1 and R2 are exerted on the...Ch. 6 - A bar of steel has the minimum properties Se = 40...Ch. 6 - Repeat Prob. 6-20 but with a steady torsional...Ch. 6 - Repeat Prob. 6-20 but with a steady torsional...Ch. 6 - Repeat Prob. 6-20 but with an alternating...Ch. 6 - A bar of steel has the minimum properties Se = 40...Ch. 6 - The cold-drawn AISI KUO steel bar shown in the...Ch. 6 - Repeat Prob. 6-25 for a load that fluctuates from...Ch. 6 - An M14 2 hex-head bolt with a nut is used to...Ch. 6 - The figure shows a formed round-wire cantilever...Ch. 6 - The figure is a drawing of a 4- by 20-mm latching...Ch. 6 - The figure shows the free-body diagram of a...Ch. 6 - Solve Prob. 6-30 except let w1 = 2.5 in. w2 = l.5...Ch. 6 - For the part in Prob. 630, recommend a fillet...Ch. 6 - Prob. 33PCh. 6 - Prob. 34PCh. 6 - A part is loaded with a combination of bending,...Ch. 6 - Repeat the requirements of Prob. 6-35 with the...Ch. 6 - 6-37 to 6-46For the problem specified in the build...Ch. 6 - 6-37 to 6-46For the problem specified in the build...Ch. 6 - 637 to 646 For the problem specified in the table,...Ch. 6 - For the problem specified in the table, build upon...Ch. 6 - 6-37 to 6-46 For the problem specified in the...Ch. 6 - 6-37 to 6-46 For the problem specified in the...Ch. 6 - 6-37 to 6-46 For the problem specified in the...Ch. 6 - Problem Number Original Problem, Page Number 637...Ch. 6 - 6-37 to 6-46 For the problem specified in the...Ch. 6 - 6-37 to 6-46 For the problem specified in the...Ch. 6 - 6-47 to 6-50 For the problem specified in the...Ch. 6 - 6-47 to 6-50 For the problem specified in the...Ch. 6 - Prob. 49PCh. 6 - Prob. 50PCh. 6 - 6-51 to 6-53 For the problem specified in the...Ch. 6 - 6-51 to 6-53 For the problem specified in the...Ch. 6 - 6-51 to 6-53 For the problem specified in the...Ch. 6 - Solve Prob. 6-17 except include a steady torque of...Ch. 6 - Solve Prob. 618 except include a steady torque of...Ch. 6 - In the figure shown, shaft A, made of AISI 1020...Ch. 6 - A schematic of a clutch-testing machine is shown....Ch. 6 - For the clutch of Prob. 657, the external load P...Ch. 6 - A flat leaf spring has fluctuating stress of max =...Ch. 6 - A rotating-beam specimen with an endurance limit...Ch. 6 - A machine part will be cycled at 350 MPa for 5...Ch. 6 - The material properties of a machine part are Sut...Ch. 6 - Repeat Prob. 662 using the Goodman criterion....
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- 2. A steel of rotating-beam test specimen has an ultimate strength of 1100Mpa. Estimate the fatigue strength of the specimen corresponding to a life of 150k cycles of stress reversal.arrow_forwardFind the equivalent stresses at Points 1 and 2 of the element with given geometry and loading conditions according to the Maximum shear stress hypothesis and the Maximum strain energy hypothesis. Shaft diameter: 20 mm, Shaft Length 120 mm, F1 = 750N, F2 = 3000N, Mb = 2400 N.mm. Steel if St37 and Safety coefficient is 2 If taken, will this stick work safely under these operating conditions? (Yield of given steel Strength 225 Mpa, Tensile strength 370 Mpa)arrow_forwardIf the ultimate strength of a steel rotating-beam test specimen was around 1600 MPa. Estimate the life of the specimen if it is tested at a completely reversed stress amplitude of 900 MPa.arrow_forward
- A steel rotating-beam test specimen has an endurance limit Se = 550 MPa and fatigue strength S= 896 MPa at 103 cycles. Estimate the fatigue strength (in MPa) corresponding to a life of 482,475 cycles of stress reversal.arrow_forwardQ2/ A steel bolt 0.005 m² in cross-section is subjected to a Static mean load of load of 200KN. What Value of Completely reversed direct fatigue load will Produce failure in 10² Cycles? Use the GERBER relationsip and assume that the Yield sureg. Strength of the steel is 400 MN/M² and the Stress required to produce. failure at 107 Cycles under Zero mean stress Condition is 300 MN/m².arrow_forwardA tensile test was conducted on a mild steel& the following data was obtained as follows. Diameter of the steel bar = 3 cm,Gauge length of the bar = 20 cm. Load at elastic limit = 250 kN . Extension at a load of 150kN = 0.21 mm . Maximum load = 380 kN . Total extension = 60 mm . Diameter of the rod at failure = 2. 25 cm Determine: (a) Young’s modulus (b) stress at elastic limit (c)the percentage of elongation (d) Percentage decrease in area.arrow_forward
- *O llAsiacell Strength of m. -> 02: A steel specimen 12mm diameter has gauge length 50mm. the steel specimen had tested via tensile test under maximum load 66KN with elongation 7.5mm, and the yield load of this specimen is 15KN with elongation 2.4mm. Calculate: 1- The engineering ultimate stress (ultimate tensile strength), and engineering strain at this point. 2- The engineering stress and strain at yield point. 3- The modulus of elasticity, and the modulus of resilience. 4- The final or fracture strain of a steel specimen, if you know that the final length of specimen after testing is 58.5mm. 5- The true stress and strain for ultimate point. Q3: The yoke-and-rod connection is subjected to a tensile force of 15 kN. Determine the average normal stress in each rod and the average shear stress in the pin A between the members. Finally, find the shear strain in pin A. Take G teef 75GPA 40 mm 15 kN, 30 mm 30 mn 15 kN 04: In figure as shown below, assume that a 35mm diameter rivet joint the…arrow_forwardQ6/ A material has a true stress -strain curve given by o=Kɛ", derive and calculate the true and engineering ultimate tensile strength of this material. (use : k=689.47kpa , n=0.5)arrow_forwardA bar of steel has the minimum properties Se = 276 MPa, Sy = 413 MPa, and Sut = 551 MPa. The bar is subjected to a steady torsional stress of 103 MPa and an alternating bending stress of 172 MPa. Find the factor of safety guarding against a static failure, and either the factor of safety guarding against a fatigue failure or the expected life of the part. For the fatigue analysis use: (a) Modified Goodman criterion. (b) Gerber criterion. (c) ASME-elliptic criterion.arrow_forward
- a rectangular stepped bar is shown. the bar is loaded in bending. determine the fatigue stress concentration factor if the ultimate stress of the material is 690 mPa. please inlcude how to calculate the notch sensitivity.arrow_forwardyields under a load of 8KN; it attains a max load of 15KN and breaks finally A tensile test is carried out on a bar of mild steel of diameter 20mm. The bar Еxample at a load of 7KN. Estimate yP (i) The tensile stress at the yield point (ii) The ultimate tensile test ii. Max loa (iii) The average stress at the breaking point if the diameter of neck is Omm.arrow_forwardFind the length of elongation of a uniform mild steel rod length of 3 m, cross-sectional area of 150 cm2 and Young's modulus of 100 GPa subjected to an axial tensile (or compressive) force F= 200 N.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY