Textbook Question
Chapter 7.10, Problem 33AAP
Refer to Problem 7.31: Compute the final critical surface crack length if the fatigue life must be a minimum of 7.0 × 105 cycles. Assume the initial maximum edge surface crack length of 1.80 mm and a maximum tensile stress of 160 MPa. Assume m = 1.8 and A = 7.5 × 10−13 in MPa and meter units. Assume Y = 1.25.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Problem 4. A large flat plate is subjected to constant-amplitude uniaxial cyclic tensile and compressive stresses. Compute the final critical surface crack length if the fatigue life must be a minimum of 7.0 x 10^5 cycles. Assume the initial maximum edge surface crack length of 1.80 mm and a maximum tensile stress of 160 MPa. Assume m = 1.8 and A = 7.5 x 10^-13 in MPa and meter units. Assume Y = 1.25.
2. Another cylindrical component is madeof Enfennering ceramic Al203
but with different
dimensions. Here, l=30 cm and the diameter is 4 cm. Assume the same Weibull modulus of 9.
Calculate the level of the tensile strength for the following probability of failures:
a. Pr (V) = 0.1
b. Pr (Vo) = 0.01
c. What is the survival probability and the failure probability of this component if a stress of
200 MPa is applied?
For a large plate, the geometry factor, f, is 1.03. Suppose a steel casting alloy has a critical fracture toughness of 78,886 psi*in1/2. The steel will be exposed to a stress of 40,295 psi during service. Calculate the minimum size of an edge crack that will grow. Repeat the calculation for Al2O3 with a fracture toughness of 1,600 psi*in1/2. How many times larger is the minimum size edge crack in the steel versus the alumina?
Chapter 7 Solutions
Foundations of Materials Science and Engineering
Ch. 7.10 - What are the characteristics of the surface of a...Ch. 7.10 - Prob. 2KCPCh. 7.10 - Prob. 3KCPCh. 7.10 - Prob. 4KCPCh. 7.10 - Prob. 5KCPCh. 7.10 - Prob. 6KCPCh. 7.10 - Prob. 7KCPCh. 7.10 - Prob. 8KCPCh. 7.10 - Prob. 9KCPCh. 7.10 - How does the carbon content of a plain-carbon...
Ch. 7.10 - Describe a metal fatigue failure.Ch. 7.10 - What two distinct types of surface areas are...Ch. 7.10 - Prob. 13KCPCh. 7.10 - Prob. 14KCPCh. 7.10 - Prob. 15KCPCh. 7.10 - Describe the four basic structural changes that...Ch. 7.10 - Describe the four major factors that affect the...Ch. 7.10 - Prob. 18KCPCh. 7.10 - Prob. 19KCPCh. 7.10 - Prob. 20KCPCh. 7.10 - Prob. 21KCPCh. 7.10 - Determine the critical crack length for a through...Ch. 7.10 - Determine the critical crack length for a through...Ch. 7.10 - The critical stress intensity (KIC) for a material...Ch. 7.10 - What is the largest size (in mm) of internal...Ch. 7.10 - A Ti-6Al-4V alloy plate contains an internal...Ch. 7.10 - Using the equation KIC=fa, plot the fracture...Ch. 7.10 - (a) Determine the critical crack length (mm) for a...Ch. 7.10 - A fatigue test is made with a maximum stress of 25...Ch. 7.10 - A fatigue test is made with a mean stress of...Ch. 7.10 - A large, flat plate is subjected to...Ch. 7.10 - Prob. 32AAPCh. 7.10 - Refer to Problem 7.31: Compute the final critical...Ch. 7.10 - Prob. 34AAPCh. 7.10 - Prob. 35AAPCh. 7.10 - Equiaxed MAR-M 247 alloy (Fig. 7.31) is used to...Ch. 7.10 - Prob. 37AAPCh. 7.10 - If DS CM 247 LC alloy (middle graph of Fig. 7.31)...Ch. 7.10 - Prob. 39AAPCh. 7.10 - Prob. 40AAPCh. 7.10 - Prob. 41SEPCh. 7.10 - Prob. 42SEPCh. 7.10 - A Charpy V-notch specimen is tested by the...Ch. 7.10 - Prob. 44SEPCh. 7.10 - Prob. 45SEPCh. 7.10 - Prob. 46SEPCh. 7.10 - Prob. 47SEPCh. 7.10 - Prob. 48SEPCh. 7.10 - Prob. 49SEPCh. 7.10 - Prob. 50SEPCh. 7.10 - While driving your car, a small pebble hits your...Ch. 7.10 - Prob. 52SEPCh. 7.10 - Prob. 53SEPCh. 7.10 - Prob. 54SEPCh. 7.10 - Prob. 56SEPCh. 7.10 - Prob. 57SEPCh. 7.10 - Prob. 58SEPCh. 7.10 - Prob. 59SEPCh. 7.10 - The components in Figure P7.60 are high-strength...
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
The spring of k and unstretched length 1.5R is attached to the disk at a radial distance of 0.75R from the cent...
Engineering Mechanics: Statics
What parts are included in the vehicle chassis?
Automotive Technology: Principles, Diagnosis, And Service (6th Edition) (halderman Automotive Series)
A biological fluid moves at a flow rate of m=0.02kg/s through a coiled, thin-walled, 5-mm-diameter tube submerg...
Fundamentals of Heat and Mass Transfer
What types of polymers are most commonly blow molded?
Degarmo's Materials And Processes In Manufacturing
A pipe flowing light oil has a manometer attached, as shown in Fig, P1.52. What is the absolute pressure in pip...
Fundamentals Of Thermodynamics
Determine the velocity of block D if end A of the rope is pulled down with a speed of vA = 3 m/s.
Engineering Mechanics: Dynamics (14th Edition)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Some aluminum aircraft components have a KIc = 35 MPa(m)1/2. It has been determined that failure occurs at a stress of 250 MPa when the critical internal crack length is 2 mm. Will this component achieve failure at a stress of 325 MPa when the critical internal crack length is 1.1 mm?arrow_forwardASAParrow_forwardQuestion 2 A machine component is made of Aluminium alloy having an ultimate tensile stress Ou = 350MPa, a fracture toughness Kic= 40 MPa√m and a geometry factor Y=1.12. The component is subject to cyclic tensile stress of 200 MPa and cyclic compressive stress of 70 MPa. Before the operation, using an ultrasonic non-destructive testing technique, it was found that there is an edge crack of length 2mm. The crack growth C(AK)m, where is in m/cycle, AK ΔσΥ νπα , C ~ 2.2×10-12 da rate is given by da dN dN and m=3.2. Find the critical crack length. = =arrow_forward
- An Al2O3 part contains both internal cracks with a maximum length of 0.075 mm, and external cracks with a maximum length of 0.05 mm. At what applied stress will the internal cracks begin to propagate? At what applied stress will the external cracks begin to propagate? The fracture toughness KIC = 1.76 MPa x m1/2, Y=1.arrow_forwardWhat is the magnitude of the maximum stress that exists at the tip of an internal crack having a radius of curvature of 1.9 x 10" mm and a crack length of 3.8 x 10 mm when a tensile stress of 140 MPa is applied? 4. 5. A ceramic matrix composite contains internal flaws as large as 0.001 cm in length. The plane strain fracture toughness of the composite is 45 and the tensile strength is 550 MPa. Will the flaw cause the composite to fail before the tensile strength is reached? Assume that Y 1 A cylindrical rod 500 mm long, having a diameter of 12.7 mm, is to be subjected to a tensile load. If the rod is to experience neither plastic deformation nor an elongation of more than 1.3 mm. when the applied load is 29,000 N, which of the four met ls or alloys listed below are possible cardidates? Justify your choice(s). Materia! Modulus of Yield Tensiie Strength (MPa) Elasticity(GPa) Strength(MPa) Aluminium alloy 70 255 420 Brass alloy 100 345 420 Сopper 110 210arrow_forwardHelp me pleasearrow_forward
- 2- In a 2024 aluminum alloy, a skin crack of length 4mm was detected. For the first evaluation of the fatigue strength, the area of the crack can be considered as a very wide plate. The system is subjected to a constant amplitude fatigue loading from 0 to 100 MPa. Evaluate the number of cycles for the crack to grow to a length of 10 mm. The alloy obeys the following fatigue crack growth rule:{ da/dN=2.5x10-12. (AK) },with da/dN in m/cycle and AK in MPa.(m)1/2 , AK = Ao (na)1/2..arrow_forwardA large flat plate is subjected to constant-amplitude uniaxial cyclic tensile and compressive stresses of 120 and 35MPa, respectively. If before testing the largest surface crack is 1.00 mm and the plain-strain fracture toughness of the plate is 35 MPa vm, estimate the fatigue life of the plate in cycles to failure. For the plate, m = 3.5 and A=5.0 x 10-12 in MPa and meter units. Assume Y = 1.3.arrow_forwardThe fluctuating stresses listed in the table are found at a critical location of a component made of steel with Se = 40 ksi, Sy = 80 ksi, Sut = 110 ksi and f= 0.87. These stresses are applied on the part within 10 s. What is the accumulative damage of this part? What is the life of the part in hours if this stress pattern continues to repeat for the remained of the part's life? Use Goodman criterion and Miner's rule in your solution. Loading order |Omin o max |Number of cycles -20 30 -10 50 1 3. -30 30 1arrow_forward
- According to Griffith's theory for brittle fracture, the stress required to propagate a crack is: (This question has more than one correct answer) 0.5 a. Proportional to a' where 2a is the crack length b. More than the ideal fracture stress -0.5 c. Proportional to a d. Less than the ideal fracture stress e. Proportional to the surface energy y0.5 f. Proportional to the surface energy yarrow_forwardA specimen of a steel alloy with a plane strain fracture toughness of 22.1 MPavm. The largest surface crack is 0.6 mm long? Assume that the parameter Y has a value of 0.5. What is the critical stress in MPa. Write your answer with 2 decimal places. Answer: 0 dºvo vo (0) 00 00, GMarrow_forward1. For the stress-strain curve shown below, please estimate the properties indicated. (a) Fracture Strain Please do your work on a separate sheet of paper, and put your answers in the boxes on the right. Be sure to include the proper symbol and units. Stress Strain 70 60 50 Stress (ksi) 240 30 20 10 70 0 0.000 60 50 Stress (ksi) 40 20 10 KULL 0 0.000 0.010 0.050 0.100 Strain (in/in) Stress Strain 0.020 0.030 Strain (in/in) 0.040 0.150 0.050 (b) Ultimate Tensile Stress (c) Fracture Stress (d) Proportional Limit (e) Elastic Modulus (1) Yield Stress (g) Tensile Toughness (Modulus of Toughness) (h) Modulus of Resiliencearrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Stresses Due to Fluctuating Loads Introduction - Design Against Fluctuating Loads - Machine Design 1; Author: Ekeeda;https://www.youtube.com/watch?v=3FBmQXfP_eE;License: Standard Youtube License