Question
Chapter 31, Problem 23QLP
To determine
List the process parameters that you think will affectthe weld strength of a friction weld, and explain why youthink those parameters are important.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
An arc welding is performed to join two metal pieces. After the welding process, the product is subjected to fatigue test. Discuss which part of the weld joint will have high potential to experience fatigue failure.
Provide a reasonable explanation for the following observation: a welded component made of Al 6061-T6 alloy is routinely found to deform plastically first in the region adjacent to the weld joint despite the fact that the stress is nominally the same everywhere in the component. What solution would you propose to fix this problem, assuming that the weld joint cannot be eliminated from the design?
Two 3.5 mm thick metal (Um = 9.5 J/mm?)
sheets are being joined using resistance spot welding. To achieve
required strength, it is desired to form a weld nugget that is 5.5 mm in
diameter and 4.0 mm thick. The weld duration will be set at 0.3 sec. If
the electrical resistance between the surfaces is 140 microohms, and
only onethird of the electrical energy generated will be used to form the
weld nugget determine the current.
Chapter 31 Solutions
Manufacturing Engineering & Technology
Ch. 31 - Explain what is meant by solid-state welding.Ch. 31 - What is cold welding? Why is it so called?Ch. 31 - What is (a) a ferrule, (b) filled gold, and (c) a...Ch. 31 - What are faying surfaces in solid-state welding...Ch. 31 - What is the basic principle of (a) ultrasonic...Ch. 31 - Explain how the heat is generated in the...Ch. 31 - Prob. 7RQCh. 31 - Describe the principle of resistance-welding...Ch. 31 - Prob. 9RQCh. 31 - What type of products are suitable for stud...
Ch. 31 - Prob. 11RQCh. 31 - Prob. 12RQCh. 31 - Prob. 13RQCh. 31 - Describe how high-frequency butt welding operates.Ch. 31 - What materials are typically used in...Ch. 31 - Make a list of processes in this chapter,...Ch. 31 - Prob. 17QLPCh. 31 - Explain the reasons why the processes described in...Ch. 31 - Explain the similarities and differences between...Ch. 31 - Describe your observations concerning Figs....Ch. 31 - Would you be concerned about the size of weld...Ch. 31 - What advantages does friction welding have over...Ch. 31 - Prob. 23QLPCh. 31 - Prob. 24QLPCh. 31 - Discuss the factors that influence the strength of...Ch. 31 - What are the sources of heat for the...Ch. 31 - Can the roll-bonding process be applied to a...Ch. 31 - Prob. 28QLPCh. 31 - List and explain the factors involved in the...Ch. 31 - Give some of the reasons that spot welding is...Ch. 31 - Prob. 31QLPCh. 31 - Prob. 32QLPCh. 31 - Prob. 33QLPCh. 31 - Prob. 34QLPCh. 31 - Prob. 35QLPCh. 31 - Prob. 36QLPCh. 31 - Prob. 37QLPCh. 31 - Prob. 38QLPCh. 31 - Which processes in this chapter are not affected...Ch. 31 - Consider the situation where two round...Ch. 31 - Prob. 41QLPCh. 31 - The energy required in ultrasonic welding is found...Ch. 31 - Prob. 43QTPCh. 31 - Prob. 44QTPCh. 31 - Prob. 45QTPCh. 31 - Prob. 46SDPCh. 31 - Explain how you would fabricate the structures...Ch. 31 - Prob. 48SDPCh. 31 - Prob. 49SDPCh. 31 - Prob. 50SDPCh. 31 - Prob. 51SDPCh. 31 - Prob. 52SDPCh. 31 - Prob. 53SDPCh. 31 - Describe the methods you would use for removing...Ch. 31 - Prob. 55SDPCh. 31 - Prob. 56SDPCh. 31 - Inspect the sheet-metal body of an automobile,...Ch. 31 - Prob. 59SDPCh. 31 - Prob. 60SDPCh. 31 - Sketch the microstructure you would expect if a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- It has been reported that gas–tungsten arc welds of aluminum made in the overhead position (assumed lap weld joint) tend to have a significantly higher porosity level than those made in the flat position: Explain why Sketch the general view of the overhead position Indicate where the (most probable) location of the porosityarrow_forwardTwo 1.2 mm thick flat copper sheets are being spot welded using a current of 6000A and a current flow time of 0.18 s. The electrodes are 5 mm in diameter. Estimate the generated in the weld zone. Take effective resistance as 150 ohm. also calculate temperature rise assuming that the heat generated is confined to the volume ogf materials directly between two electrodes and temperature is uniformly distributed.arrow_forwardA gas metal arc welding test is performed to determine the value of melting factor f₂ for a certain metal and operation. The welding voltage = 25 volts, current = 125 amps, and heat transfer factor is assumed to be = 0.90, a typical value for GMAW. The rate at which the filler metal is added to the weld is 0.50 in³ per minute, and measurements indicate that the final weld bead consists of 57% filler metal and 43% base metal. The unit melting energy for the metal is known to be 75 Btu/in³. (a) Find the melting factor. (b) What is the travel speed if the cross-sectional area of the weld bead = 0.05 in²?arrow_forward
- What are some of the problems that oxygen can cause in welds?arrow_forwardExplain the mechanism of heat generation in Resistance spot welding. Explain the Force (current) vs time diagram.arrow_forwardCalculate the heat input during the arc welding process, if the voltage is 33 volts, current is 115 amperes, the length of the weld is 88mm and the time to complete the weld 34 secs.arrow_forward
- A circular electrode of 190 mm diameter is used for carrying out seam welding at 5 welds per cm on a mild steel tube of thickness 1.5 mm. The duration of the welding cycle is given as On - 4 cycles, Off- 3 cycles. The power supply is at 50 Hz. Calculate work speed, welds per minutę, RPM, and energy requirement assuming effective resistance between an electrode as 100u ohm.arrow_forwardTwo 1.2 mm thick sheets of steel are joined by double-sided spot welding using a current of 6000A and current flow time of t = 0.15 sec. The electrodes are 3 mm in diameter and the weld spot thickness is approximately one third of the total thickness of the metal sheets. Assuming that the effective resistance in this operation is 200 micro resistance, estimate the heat generated and its distribution in the weld zone. (Take density of steel = 8600 Kg/m3 and its latent heat capacity, L =1400 J/g)arrow_forwardA 40 mm diameter solid shaft is to be welded to a flat plate and is required to carry a torque of 2000 Nm. If fillet joint is used foe welding what will be the minimum size of the weld when working shear stress is 76 MPa.arrow_forward
- Two 1.2 mm thick flat copper sheets are being spot welded using a current of 6000 A and a current flow time of 0.18 s. The electrodes are 5 mm in diameter. Estimate the heat generated in the weld zone. Take effective resistance as 150 µΩ. Also calculate temperature rise assuming that the heat generated is confined to the volume of material directly between the two electrodes and temperature is uniformly distributed.arrow_forward(b) A resistance welding is performed to join two 2-mm thick stainless steel sheets with ten 6-mm diameter spot welds produced concurrently. The resulted weld nugget each has average 3 mm in thickness. Calculate the required welding current and energy consumption for the welding if ten seconds are needed for the whole welding operation. Given that the applied voltage is 10 V. Provide 00 TWO important assumptions in your calculation.arrow_forwardA GTAW operation is performed on low carbon steel, whose unit melting energy is 10.3 J/mm3. The welding voltage is 22 volts and the current is 135 amps. The heat transfer factor is 0.7 and the melting factor is 0.65. If filler metal wire of 3.5 mm diameter is added to the operation, the final weld bead is composed of 60% volume of filler and 40% volume base metal. If the travel speed in the operation is 5 mm/sec, determine (a) cross-sectional area of the weld bead, and (b) the feed rate (mm/sec) at which the filler wire must be supplied.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
Metal Joining Process-Welding, Brazing and Soldering; Author: Toc H Kochi;https://www.youtube.com/watch?v=PPT5_fDSzGY;License: Standard YouTube License, CC-BY