Textbook Question
Chapter 3, Problem 3.45QP
A Charpy V Notch (CVN) test was performed on a steel specimen and produced the readings shown in Table P3.45. Plot the toughness-versus-temperature relation and determine the temperature transition zone between ductile and brittle behavior.
TABLE P3.45
| Temperature, C | Toughness, Joule (N.m) |
| –40 | 7 |
| 0 | 15 |
| 50 | 54 |
| 100 | 109 |
| 150 | 120 |
| 200 | 122 |
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
1.14 The stress-strain relation shown in Figure P1.14 was obtained during the ten-
sile test of an aluminum alloy specimen.
60,000
40,000
20,000
0.002
0.004
0.006
0.008
Strain, in./in.
FIGURE P1.14
Determine the following:
a. Young's modulus within the linear portion
b. Tangent modulus at a stress of 45,000 psi
c. Yield stress using an offset of 0.002 strain
d. If the yield stress in part c is considered failure stress, what is the maximum
working stress to be applied to this material if a factor of safety of 1.5 is used?
Stress, psi
In a standard tensile test, an aluminum rod of 20-mm diameter is subjected to a tension force of
P = 30 kN. Knowing that E = 70 GPa, and the change in diameter of the rod= 0.00955 mm,
determine the poissons' ratio v.
-20-mm diameter
gage length=150 mm
The (G-E) diagram obtained in the tensile test performed on a metal sample with a
diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured
on l. 16 cm gauge length were determined as follows:
B
A
B
C
Load (kgf)
4800
8400
7200
Elongation (mm)
0.192
28.8
38.4
c) Calculate the fracture work and the maximum elastic energy the metal rod can store.
d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12
tons of load with 2 times the safety of yield strength. How long does the rod extend under
this load?
Chapter 3 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 3 - What is the chemical composition of steel? What is...Ch. 3 - Why does the ironcarbon phase diagram go only to...Ch. 3 - Draw a simple ironcarbon phase diagram showing the...Ch. 3 - What is the typical maximum percent of carbon in...Ch. 3 - Calculate the amounts and compositions of phases...Ch. 3 - Briefly discuss four heat treatment methods to...Ch. 3 - Define alloy steels. Explain why alloys are added...Ch. 3 - Prob. 3.8QPCh. 3 - Specifically state the shape and size of the...Ch. 3 - What are the typical uses of structural steel?
Ch. 3 - What is the range of thicknesses of cold-formed...Ch. 3 - Why is coil steel used for cold-formed steel...Ch. 3 - If a steel with a 33 ksi yield strength is used...Ch. 3 - Why is reinforcing steel used in concrete? Discuss...Ch. 3 - What is high-performance steel? State two HPS...Ch. 3 - Name three mechanical tests used to measure...Ch. 3 - The following laboratory tests are performed on...Ch. 3 - Sketch the stress-strain behavior of steel, and...Ch. 3 - Three steel bars with a diameter of 25 mm and...Ch. 3 - Three steel bars with a diameter of 0.5 in. and...Ch. 3 - Draw a typical stressstrain relationship for steel...Ch. 3 - Getting measurements from Figure 3.18, determine...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A No. 10 steel rebar is tested in tension. By...Ch. 3 - A mild steel specimen originally 300 mm long is...Ch. 3 - A tension stress of 70 ksi was applied on a 12-in....Ch. 3 - A tensile stress is applied along the long axis of...Ch. 3 - A cylindrical steel alloy rod with a 0.5 in....Ch. 3 - A round steel alloy bar with a diameter of 0.75...Ch. 3 - A 19-mm reinforcing steel bar and a gauge length...Ch. 3 - Testing a round steel alloy bar with a diameter of...Ch. 3 - During the tension test on a steel rod within the...Ch. 3 - A grade 36 round steel bar with a diameter of 0.5...Ch. 3 - A high-yield-strength alloy steel bar with a...Ch. 3 - Estimate the cross-sectional area of a 350S125-27...Ch. 3 - An ASTM A615 grade 60 number 10 rebar with a gauge...Ch. 3 - A 32-mm rebar with a gauge length of 200 mm was...Ch. 3 - A steel pipe having a length of 3 ft. an outside...Ch. 3 - A steel pipe having a length of 1 m, an outside...Ch. 3 - A drill rod with a diameter of 10 mm is made of...Ch. 3 - A drill rod with, a diameter of 1/2 in. is made of...Ch. 3 - Prob. 3.43QPCh. 3 - An engineering technician performed a tension test...Ch. 3 - A Charpy V Notch (CVN) test was performed on a...Ch. 3 - Prob. 3.46QPCh. 3 - Prob. 3.47QPCh. 3 - How can the flaws in steel and welds be detected?...Ch. 3 - Determine the welding zone classification of A36...Ch. 3 - Briefly define steel corrosion. What are the four...Ch. 3 - Discuss the main methods used to protect steel...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.arrow_forwardAn applied torque results in a shear strain (y) of 3.75 x 103 in a solid circular steel shaft. At this strain, a portion of the shaft cross- section yields as shown in Figure 2. Determine the magnitude of the applied torque. Take G = 80 GPa and yy = 2.8125 x %3D 10-3 FIGURE 2: Plastic zone 50 mm 200 mm Elastic corearrow_forward5. A tensile test was done on a magnesium sample of original diameter and original length of 12mm 30mm respectively. The final length and diameter were 32.61mm and 11.74mm respectively. Plot the stress versus strain graph and determine: a. 0.2% proof stress b. Tensile strength c. % elongation d. % reduction e. Stress at fracture f. Modulus of Elasticity. 66 Force (N) Ext. 0.0112 0.0157 0.0199 0.0240 1.72 (mm) 177 327 462 797 1350 1720 2220 2690 2690 5.55 8.15 13.07 22.77 25.25arrow_forward
- Question 4. A tensile test is carried out on a bar of mild steel of diameter 2 cm. The bar yields under a load of 80 Kn. It reaches a maximum load of 150 kN, and breaks finally at a load of 70 kN. Estimate: a)the tensile stress at the yield point b)the ultimate tensile stress c)the average stress at the breaking point if the diameter of the fractured neck is 1 cm.arrow_forwardA 19-mm reinforcing steel bar and a gauge length of 75 mm was subjected to ten- sion, with the results shown in Table P3.27. Using a computer spreadsheet pro- gram, plot the stress-strain relationship. From the graph, determine the Young's modulus of the steel and the deformation corresponding to a 150-kN load. TABLE P3.27 Load, kN Deformation, mm 54 0.084 163 0.168 284 0.336 330 1.428 366 3.360arrow_forwardDuring a tension test, measurements for the applied load and the corresponding elongation are taken at frequent intervals. These data points are then used to: a. calculate the stress caused by the applied load at each data point. b. calculate the strain in the specimen induced by the applied load at each data point. c. plot a stress-strain diagram. d. all of the abovearrow_forward
- The following observations were made during a tensile test on a mild steel specimen 40 mm in diameter and 200 mm long. Elongation with 40 KN load (within limit of proportionality) Change in length=0.0202 mm. Determine stress and strain valuearrow_forwardQuestion 1 The ideal diameter of a steel tensile test specimen is O lin O 2 in O 1/2 in 1/4 in et Question 2 How many zones are exhibited by a typical stress- strain diagram O 3 O 5arrow_forwardA 13 mm diameter tensile specimen has 50 mm gauge length. If the load corresponding to the 0.2% offset is 6800 kg, the yield stress will be nearly 1. 31 kg/mmΒ² 2. 43 kg/mmΒ² 3. 51 kg/mmΒ² 4. 63 kg/mmΒ² Xarrow_forward
- 2.7 The following readings were recorded during a tensile test of a mild steel specimen 24 mm wide by 10 mm thick and with a gauge length of 200 mm. Force (kN) 16 32 48 64 68 72 76 79 Elongation (mm) 0,066 0,133 0,198 0,264 0,281 0,304 0,355 1,125 Force (kN) 76,8 83,7 103,8 111 112,8 108 96 Elongation (mm) 3,75 6,66 15,00 25,00 36,5 45,0 50,0 The test piece fractured at a 50-mm elongation. Plot the load-extension dia- gram using the following scales: 10 divisions on the x-axis = 5-mm exten- sion; 10 divisions on the y-axis = 10 kN. On the same graph paper and using the scale 10 divisions on x-axis = 0,5-mm extension, and 10 divisions on y-axis = 10 kN, replot the elastic portion of the graph. Using the graphs, determine the (a) modulus of elasticity for mild steel; (b) yield stress; (c) ultimate tensile stress; and (d) percentage elongation.arrow_forwardThe specimen shown is made from a 25 mm diameter cylindrical steel rod with two 38 mm outer-diameter sleeves bonded to the rod as shown. Knowing that E = 200 GPa, determine (a) the load P so that the total deformation is 0.05 mm, (b) the corresponding deformation of the central portion BC. 38 mm diameter P' 25 mm diameter B 38 mm diameter C 50 mm 75 mm 50 mmarrow_forwardI5 In a tensile test experiment of carbon steel. a standard specimen (D= 0.505 in. Gauge length=2.0 in & total length 8 in) had a 0.2% offset yield strength of 80.000 psi and engineering strain of 0.010 at the yield strength point Calculate: The load (force) at this point. The instantaneous area of the specimen at this point. c. The true stress at this point. d. The true strain at this point. e. The total length of the specimen. if the load is released at this point.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Steel Design (Activate Learning with these NEW ti...Civil EngineeringISBN:9781337094740Author:Segui, William T.Publisher:Cengage Learning
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Steel Design (Activate Learning with these NEW ti...
Civil Engineering
ISBN:9781337094740
Author:Segui, William T.
Publisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY