Question No.2 Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness I. Which metal is more ductile? Why? 900 -Metal A E 600 Metal B 300 0.00 a02 004 a.06 0.08 0.10 0.12 014 Strain, matm FIGURE P1.16 Strees, MPa

Question No.2 Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness I. Which metal is more ductile? Why? 900 -Metal A E 600 Metal B 300 0.00 a02 004 a.06 0.08 0.10 0.12 014 Strain, matm FIGURE P1.16 Strees, MPa

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.19P

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
Estimate the elastic and plastic strain at the ultimate tensile strength in the low-carbon steel specimen in Figure 6.16.
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
An aluminum alloy [E = 74 GPa; v = 0.33; a = 23.0 x 10-6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 265 mm, a cross-sectional area of A = 5300 mm², and a length of L= 4.2 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by AT = 57°C, the longitudinal normal strain in the plate is found to be 2920 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Ad. L P Answer: (a) P = i (b) Δd = i kN mm
An aluminum alloy [E = 73 GPa; v = 0.33; a= 23.0 x 10-6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 250 mm, a cross-sectional area of A = 6900 mm², and a length of L = 5.9 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by AT = 50°C, the longitudinal normal strain in the plate is found to be 2400 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Ad. L Answer: (a) P = i (b) Δd = KN mm
A steel 0.6 inch×1.2 inch steel 90 m long is subjected to a 45 KN tensile load along its lenght.If poison's ratio is 0.3 Find: A. The deformation along its lenght. B. The deformation along its thickness. C. The defirmation along uts width. D. The lateral strain.
An aluminum alloy [E = 67 GPa; ν = 0.33; α = 23.0 × 10–6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 225 mm, a cross-sectional area of A = 5100 mm2, and a length of L = 4.1 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by ΔT = 63°C, the longitudinal normal strain in the plate is found to be 2900 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Δd.
1.4-7 The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13 mm and a gage length of 50 mm (see figure for Prob. 1.4-3). At fracture, the elongation between the gage marks was 3.0 mm and the minimum diameter was 10.7 mm. Plot the conventional stress-strain curve for the steefor the steel and determine the proportional limit, modulus of elastics of elastic- ity (i.e., the slope of the initial part of the stress-strain,tress-strain curve), yield stress at 0.1% offset, ultimate stress, percent, elongation in 50 mm, and percent reduction in area. 'ess, percent area. TENSILE-TEST DATA FOR PROB. 1.4-7 Elongation (mm) 0.005 0.015 0.048 Load (kN) 5 10 30 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
Problem 4: A tensile test is carried out on a bar of a mild steel of diameter 2 cm. the bar yields under a load of 150 kN and breaks finally at a load of 70 kN. Estimate; 1-the tensile stress at the yield point 2-the ultimate tensile stress 3-the average stress at the breaking point, if the diameter of the fractured neck is 1 сm.
A bar obtained by bonding together pieces of steel (Es = 29 x 106 psi) and brass (E = 15 x 106 psi) has the cross section shown (Fig. a). Determine the maximum stress in the steel and in the brass when the bar is in pure bending with a bending moment M = 40 kip-in. 0.4 in. 3 in. Brass 0.75 in. Steel Brass 0.4 in. (a) 1) Composite bar.
A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find . The stress at elastic limit. • Young's modulus. . Percentage elongation. Percentage reduction in area. Ultimate tensile stress. .