3.The figure below shows the phase diagram for a hypoeutectoid plain carbon steel.Assume that point c is slightly above 723 °C and point d is slightly below 723 °C.i.ii.iii.Explain the structure at points a, b, c, and d on the diagram.Determine the wt% of proeutectoid ferrite at point c.Determine the wt% of eutectoid ferrite at point d.Temperature (°C)10009008007006005004000100%Fey+ a0.02a + Fe, Cb0.4723°Cy + Fe, CPearlite0.8Weight percent carbonFe₂C6.67

To find:i. The structure at points a, b, c, and d on the diagram.ii. The of proeutectoid ferrite at…

3. The figure below shows the phase diagram for a hypoeutectoid plain carbon steel. Assume that point c is slightly above 723 °C and point d is slightly below 723 °C. i. Explain the structure at points a, b, c, and d on the diagram. ii. Determine the wt% of proeutectoid ferrite at point c. iii. Determine the wt% of eutectoid ferrite at point d. Temperature (°C) 1000 900 800 y+a 0.02 700 600 500 I 400 I I 0 100% Fe a + Fe, C 0.4 a 723°C y + Fe, C Pearlite 0.8 Weight percent carbon Fe,C 6.67

3. The figure below shows the phase diagram for a hypoeutectoid plain carbon steel. Assume that point c is slightly above 723 °C and point d is slightly below 723 °C. i. Explain the structure at points a, b, c, and d on the diagram. ii. Determine the wt% of proeutectoid ferrite at point c. iii. Determine the wt% of eutectoid ferrite at point d. Temperature (°C) 1000 900 800 y+a 0.02 700 600 500 I 400 I I 0 100% Fe a + Fe, C 0.4 a 723°C y + Fe, C Pearlite 0.8 Weight percent carbon Fe,C 6.67

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

4. The figure below shows the phase diagram for a hypereutectoid plain carbon steel. Assume that point c is slightly above 723 °C and point d is slightly below 723 °C. i. Explain the structure at points a, b, c, and d on the diagram. ii. Determine the wt% of proeutectoid cementite at point c. iii. Determine the wt% of eutectoid cementite at point d. Temperature (°C) 1100 900 700 500 300 100 a + Y R 0 100% Fe 0.02 1.0 Fe, C 1.2 2.0 Fe,C Fe, C Pearlite 3.0 4.0 Weight percent carbon y+ Fe, C 723°C a + Fe, C 1 5.0 Fe,C 1 6.0 6.7
Q1 / Two metals Beryllium (Be) and Silicon (Si) have melting points 1282°C and 1414 °C respectively, are completely soluble as liquids but completely insoluble as solids . They form a eutectic at 1090°C containing 61 wt% Si -39wt% Be? Determine the following:- 1- Draw the thermal equilibrium phase diagram and identify all phases are present in diagram ,then sketches what happens in microstructure when the alloys containing , a- 10wt% Si, b-70wt%Si , solidify completely. 2- Determine the composition and the amount of each phase for the alloy which contain 15 wt% Si-85wt% Be at 1150°C If the alloy is hypoeutectic determine the amount of eutectic at 600 °C? or hypereutectic and
The following questions are based on a high carbon steel with a composition of 1,5% C and 98,5% Fe. Please refer to the Fe-Fe3C binary phase diagram in Callister and Rethwhich 1) a Name the phases present and calculate the amounts of these phases just above the eutectoid temperature b, Give the amount of austenite present at 1100°C. c. Give the amount of pro-eutectoid ferrite just above the eutectoid temperature. d. With equilibrium cooling just below the eutectoid temperature calculate the total ferrite. e. Why must the samples be quenched rapidly to obtain high hardness?
For a 70-30 Zn-Cu alloy, what would the percent of each phase be at 800°C and 500°C?
Refer to Figure 1 showing the phase diagram for the Fe-Fe3C system. Consider 1.0 kg of austenite containing 1.15 wt% C, cooled to below 727 C (1341 F). What is the proeutectoid phase? How many kilograms each of total ferrite and cementite form? How many kilograms each of pearlite and the proeutectoid phase form? Schematically sketch and label the resulting microstructure.
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
Cu-Ni phase diagram is given below. Answer the questions according to the diagram for 60% Cu- 40% Ni alloy.
For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of phase(s) present. ii. Calculate the composition(s) of the phase(s) present. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 100 (Pb) (Sn) Composition (wt % Sn) Temperature ("C) Temperature ("F)
Draw thermal equilibrium diagram for the binary alloy system (Si-Au), from the following data:- a- Silicon melts at 1414 °C, and gold melts at 1064 °C. b-Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au, and identify all phases are present in the diagram c-Determine the amount of each phase for the alloy which consist of 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
A hypo-eutectoid steel with composition of 0.5% carbon is heated to 1000°. Using the a iron-carbon phase diagram (also found in the course book, or here https://commons.wikimedia.org/wiki/File:Iron_carbon_phase_diagram.svg (Links to an external site.) (Links to an external site.)) answer the following questions. (a) What phase or phases will be present at 950°C? (b) If temperature is lowered from 950°C, at which temperature (estimate) α phase (Ferrite) will appear? (c) Use the lever rule to estimate how much (wt%) ferrite and how much austenite will exist just above 727 °C? (d) What happens to the austenite if the temperature is lowered below 727 °C? (e) Schematically sketch and label the resulting microstructure.
Copper-rich copper-beryllium alloys are precipitation hardenable. After consulting the portion of the phase diagram shown in Figure below, do the following: Composition (at% Be) 10 15 20 Liquid 1000 866°C 800 -620°C 600 a+ 400 2 3. (Cu) Composition (wt% Bo) (1) Indicate the range of compositions over which these alloys be precipitation hardened. (ii) Describe the heat-treatment procedures (in terms of temperatures) that would be used to precipitation harden an alloy having a composition of your choosing but lying within the range given for part (i). Temperature ("O
2 By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- Find the Eutectic, Eutectoid temperature of cast iron with 4.3% C 2- The microstructure of Cast iron with 3.5% C. 3- Find the melting point and microstructure of steel with 0.83% C 4- Define the temperature range for Acm temperature. 5- Find the AC3, Ac¡ temperature of steel with 0.45% C 6- The Liquid and Austinite percent with chemical composition for cast iron with 2.3% C at 1300°C