4.The figure below shows the phase diagram for a hypereutectoid plain carbon steel.Assume that point c is slightly above 723 °C and point d is slightly below 723 °C.i.Explain the structure at points a, b, c, and d on the diagram.ii. Determine the wt% of proeutectoid cementite at point c.iii. Determine the wt% of eutectoid cementite at point d.Temperature (°C)1100900700500300100a+YR0100%Fe0.021.0Fe, C1.22.0Fe,CFe, CPearlite3.04.0Weight percent carbony+ Fe, C723°Ca + Fe, C15.0Fe,C16.0 6.7

To find:i. The structure at points a, b, c, and d on the diagram.ii. The of proeutectoid ferrite at…

4. The figure below shows the phase diagram for a hypereutectoid plain carbon steel. Assume that point c is slightly above 723 °C and point d is slightly below 723 °C. i. Explain the structure at points a, b, c, and d on the diagram. Determine the wt% of proeutectoid cementite at point c. iii. Determine the wt% of eutectoid cementite at point d. ii. Temperature (°C) 1100 900 700 500 300 100 0 100% Fe 0.02 1.0 Fe,C 1.2 2.0 Fe, C Fe, C Pearlite 3.0 4.0 Weight percent carbon y + Fe, C 723°C a + Fe, C 5.0 Fe,C 6.0 6.7

4. The figure below shows the phase diagram for a hypereutectoid plain carbon steel. Assume that point c is slightly above 723 °C and point d is slightly below 723 °C. i. Explain the structure at points a, b, c, and d on the diagram. Determine the wt% of proeutectoid cementite at point c. iii. Determine the wt% of eutectoid cementite at point d. ii. Temperature (°C) 1100 900 700 500 300 100 0 100% Fe 0.02 1.0 Fe,C 1.2 2.0 Fe, C Fe, C Pearlite 3.0 4.0 Weight percent carbon y + Fe, C 723°C a + Fe, C 5.0 Fe,C 6.0 6.7

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

For a 70-30 Zn-Cu alloy, what would the percent of each phase be at 800°C and 500°C?
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
Answer the following questions using the phase diagram of iron and iron carbide below:For a 99.70 wt% Fe–0.30 wt% C alloy at a temperature of 600oC, determine the following:a. The fractions of total ferrite and cementite phases b. The fractions of the pro eutectoid ferrite and pearlite
What is a peritectic phase diagram? Draw a typical equilibrium diagram for a eutectic type of system with limited solid solubility and explain its important features.
The iron-carbon phase diagram is usually shown for a metastable system. What does this mean, and why do we use the phase diagram for the metastable system?
I need the answer as soon as possible
Temperature C For the phase diagram shown calculate the amount of austenite present at the point P 1600 8+ liquid 1400 Liquid 1200 Fe,C+ liquid Y. 1000 y+Fe,C 800 a + Fe,C Fe,C- 600 2. 4. 6. C /wt%
When alloys A, B, and C are gently cooled from 1000 o C in the following temperature ranges, sketch their microstructures. (equilibrium cooling). List every phase present in the microstructures. Comment on the constituent phases of the resulting alloy and its mechanical characteristics. Please keep it brief.
Question 7: The illustration shows the iron-carbon phase diagram. 1600 1400 1200 1000 800 600 400 1538°C 0 (Fe) 1493°C 1394°C 912°C 7. Austenite 0.76 0.022 a, Ferrite Y+L 2.14 Composition (at%C) 15 10 1147 C a+FezC Y+FeyC 4 3 Composition (wt% C) 727 C Cementite (FeyC). 2500 2000 1500 1000 6.70 Temperature (°F) e) Describe the changes in phase compositions of a carbon steel with a carbon content of 1 % (weight-%) from 1500°C down to 727°C with the help of the attached phase diagram and appropriate equations/reactions.
The Iron-Carbon system: Phase Diagram 1. You heat treated a 1045 steel plate by heating it to 900°C and slowly cooling it to 725 °C, which is below the eutectoid temperature. What phases are present at 725°C? What are the compositions of each phase at 725°C? What are the weight fractions of each phase at 725°C? What microconstituents are present at 725°C? What are the compositions of each microconstituent at 725°C? What are the weight fractions of each microconstituent at 725°C?
Q4: For a 98 wt% Fe-2 wt% C at a temperature 700 °C, determine the following: a) The Number and types of The Phases Present. b) The Amount Of Phases Present in Grams That forms per 100 G. c)Draw The Microstructure Of Phases Present At This Point And What is The React called? d) Specify the following on Iron- Carbon Phase Diagram: (y+ L) phase, Eutectoid Reaction
Need all the three parts in neat and clean handwritten solution. Remember this for an upvote. BEST OF LUCK