Question
Chapter 5, Problem 5.4P
(a)
To determine
The temperature when the first solid start to form and the chemical composition of it.
(b)
To determine
The phases present at
(c)
To determine
The temperature at which entire alloy become solid at slow cooling and the chemical composition of solid.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A magnesium-lead alloy of mass 6.4 kg consists of a solid a phase that has a composition just slightly below the solubility limit
at 300°C (570°F). The magnesium-lead phase diagram is shown in Animated Figure 9.20.
(a) What mass of lead is in the alloy?
i
kg
(b) If the alloy is heated to 400°C (750°F), how much more lead may be dissolved in the a phase without exceeding the
solubility limit of this phase?
kg
For alloys of two hypothetical metals A and B, there exist an a, A-rich phase and a ß, B-rich phase.
From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine
the composition of the phase boundary (or solubility limit) for the following:
Fraction Fraction
Alloy Composition
a Phase
B Phase
60 wt% A - 40 wt% B
0.59
0.41
30 wt% A - 70 wt% B
0.13
0.87
(a) a phase
wt% A
(b) B phase
wt% A
A steel alloy is known to contain 93.8 wt% Fe, 6.0 wt% Ni, and 0.2 wt% C. Assume that there are no alterations in the positions
of other phase boundaries with the addition of Ni.
(a) What is the approximate eutectoid temperature of this alloy?
i
°C
(b) What is the proeutectoid phase when this alloy is cooled to a temperature just below the eutectoid?
(c) Compute the relative amounts of the proeutectoid phase and pearlite.
i
Wp
i
Chapter 5 Solutions
Materials Science And Engineering Properties
Ch. 5 - Prob. 1CQCh. 5 - Prob. 2CQCh. 5 - Prob. 3CQCh. 5 - Prob. 4CQCh. 5 - Prob. 5CQCh. 5 - Prob. 6CQCh. 5 - Prob. 7CQCh. 5 - Prob. 8CQCh. 5 - Prob. 9CQCh. 5 - Prob. 10CQ
Ch. 5 - Prob. 11CQCh. 5 - Prob. 12CQCh. 5 - Prob. 13CQCh. 5 - Prob. 14CQCh. 5 - Prob. 15CQCh. 5 - Prob. 16CQCh. 5 - Prob. 17CQCh. 5 - Prob. 18CQCh. 5 - Prob. 19CQCh. 5 - Prob. 20CQCh. 5 - Prob. 21CQCh. 5 - Prob. 22CQCh. 5 - Prob. 23CQCh. 5 - Prob. 24CQCh. 5 - Prob. 25CQCh. 5 - Prob. 26CQCh. 5 - Prob. 27CQCh. 5 - Prob. 28CQCh. 5 - Prob. 29CQCh. 5 - Prob. 30CQCh. 5 - Prob. 31CQCh. 5 - Prob. 32CQCh. 5 - Prob. 33CQCh. 5 - Prob. 34CQCh. 5 - Prob. 35CQCh. 5 - Prob. 36CQCh. 5 - Prob. 1ETSQCh. 5 - Prob. 2ETSQCh. 5 - Prob. 3ETSQCh. 5 - Prob. 4ETSQCh. 5 - Prob. 5ETSQCh. 5 - Prob. 6ETSQCh. 5 - Prob. 7ETSQCh. 5 - Prob. 8ETSQCh. 5 - Prob. 9ETSQCh. 5 - Prob. 10ETSQCh. 5 - Prob. 11ETSQCh. 5 - Prob. 12ETSQCh. 5 - Prob. 1DRQCh. 5 - Prob. 2DRQCh. 5 - Prob. 3DRQCh. 5 - Prob. 5.1PCh. 5 - Prob. 5.2PCh. 5 - Prob. 5.3PCh. 5 - Prob. 5.4PCh. 5 - Prob. 5.5PCh. 5 - Prob. 5.6PCh. 5 - Prob. 5.7PCh. 5 - Prob. 5.8PCh. 5 - Prob. 5.9PCh. 5 - Prob. 5.10PCh. 5 - Prob. 5.11PCh. 5 - Prob. 5.12PCh. 5 - Prob. 5.13PCh. 5 - Prob. 5.14PCh. 5 - Prob. 5.15PCh. 5 - Prob. 5.16PCh. 5 - Prob. 5.17PCh. 5 - Prob. 5.18PCh. 5 - Prob. 5.19P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- 1. A 65 wt% Ni -35 wt% Cu alloy is heated to a temperature within the a + liquid phase region. If the composition of the a phase is 70 wt % Ni, determine i. The temperature of the alloy ii. The composition of the liquid phase iii. The mass fraction of both phases Composition (at% Ni) 20 40 60 80 100 1600 H 2800 1500 Liquid 1453°C 2600 1400 Solidus line Liquidus line 2400 1300 a +L 1200 2200 1100 A 2000 1085°C 1000 20 40 60 80 100 (Cu) Composition (wt% Ni) (Ni) Temperature (°C) Temperature (F)arrow_forward2. In a copper-nickel system as shown in figure, an alloy composition of 35 wt% Ni was cooled down from the temperature of 1300°C. Sketch the expected microstructures at the point a, b, c, d and e and briefly describe the development of these microstructures in the equilibrium cooling. L. L (35 Ni) 1300 L (32 Ni) a (46 Ni) a(43 Ni) L (24 Ni) d 1200 1100 20 30 40 50 Composition (wt% Ni) Temperature (°C))arrow_forwardMetal X has an atomic weight of 43.1 g/mol, theoretical density of 6.40 g/cm^3, and atomic radius of 122 pm. Determine whether the crystal structure of Metal X is BCC, FCC, or simple cubic. Provide your complete solution.arrow_forward
arrow_back_ios
arrow_forward_ios
Recommended textbooks for you
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning