(c) Using the equation d = D · t, where "d is the layer thickness, "D" is the diffusion coefficient fornitrogen and "f" is the treatment time. D=2.67 × 10-14 m²/s at 500°C, calculate the time required toreach a case depth of 30, 50 and 70 microns.

Answered: Image /qna-images/answer/45000982-50bf-4505-b39f-75d5fbe131e3.jpg

Jsing the equation d = VD · t, where "d' is the layer thickness, "D" is the diffusion coefficient for itrogen and "f" is the treatment time. D=2.67 × 10-14 m²/s at 500°C, calculate the time required to each a case depth of 30, 50 and 70 microns.

Jsing the equation d = VD · t, where "d' is the layer thickness, "D" is the diffusion coefficient for itrogen and "f" is the treatment time. D=2.67 × 10-14 m²/s at 500°C, calculate the time required to each a case depth of 30, 50 and 70 microns.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: DISCUSSION THEORY OF DISFFUSION AND THROUGLY EXPLAIN FIVE DIFFUSION QUANTITIES.ALSO EXPLAIN THE…

A: Diffusion: Diffusion is the movement of molecules along a concentration gradient from an area of…

Q: The company has recently expanded their product range to include some aluminium components. To aid…

A: Givenm=40kgT1=20oCTm=660oCLHF=387 kJ/kgC=950 J/kgK=0.950 kJ/kgK

Q: Calculate the diffusion coefficient for the interdiffusion of Zinc into Copper at 500 °C .

A: Required data from the standard table for the diffusion of zinc into copper.

Q: 1. What is diffusion? Briefly explain the difference between self-diffusion and interdiffusion.

A: Diffusion:- "Diffusion is the movement of molecules along a concentration gradient from an area of…

Q: currence of stress concentration (Kt) in a machine element.Include pictures and their equatio

Q: Raman spectroscopy uses a laser light of a single wavelength to excite a sample. (a) Describe the…

A: DISCLAIMER FOR MULTIPART FROM BARTLEBY:Since you have posted a question with multiple sub-parts, we…

Q: Ces? s- What are the factors that effect on manufacturing process of nanoparti laser ablation?

A: The manufacturing process of nanoparticles by laser oblation method is easy and unique , it can not…

Q: Consider a dispersion strengthened alloy with average interparticle spacing of L. If Nv is he number…

A: Explanation: f=43πr3Nv1=43πd23Nvd=3f2πNv13

Q: 10.3. (a) Estimate the value of P/Plat for a sphere of radius 1 nm at 300 K if the surface tension…

Q: (i) Thermal distortions and vibrations do not perturb smaller devices as much as large ones because…

A: Correct options are - (i) option A the resonant vibrations of a system are inversely proportional…

Q: he temperature trend in a multilayer material made of 2 slabs alluminum (λ1 and λ2) with air between…

A: We have to dtermine the temperture trend in the metal air sandwich

Q: In a viscoelastic material, why does tan delta peak at the glass transition temperature?

A: Glass transition temperature it is the teperature at which carbon chain in viscoelastic material…

Q: :Question 5 A. What are the conditions of diffusion ?mechanisms إجابتك B. What are the benefits of a…

Q: Assume the temperature of your skin is 32oC. If you touch a thick piece of aluminum at 75oC, what is…

A: Write the given data. Tskin=32 °CTaluminium=75 °CTconc=90 °C

Q: Sintering of ceramics is characterized by: (This question has only one correct answer) а. Extrusion…

A: given; sintering of ceramic is characterized by;

Q: why vacancy diffusion is more slow than interstitial diffusion?

A: Vacancy diffusion is slower than Interstitial diffusion. Diffusions taking place by vacancies are…

Q: What does(do) determine a diffusion coefficient (diffusivity)? (choose all) a. Concentration…

A: What does(do) determine a diffusion coefficient (diffusivity)?

Q: need these diagrams drawn neatly properly in a plain sheet of paper labelled properly

Q: Please explain crack initation and propagation during metal fatigue? Explain factors that affect…

A: Crack initation and propagation during metal fatigue The fatigue failure mechanism is characterized…

Q: Define the General Heat/Diffusion Equation ?

A: The general heat equation is a multi-dimensional equation or a three-dimensional equation. The three…

Q: A sample of poly(1,4-phenylene sulphide) (PPS) is known to have a glass transition temperature of…

A: Given:A sample of poly(1,4-phenylene sulphide) (PPS) Glass transition temperature of 89°C, A…

Q: For a steel alloy it has been determined that a carburizing heat treatment of 18 h duration at 885°C…

Q: For a steel alloy it has been determined that a carburizing heat treatment of 10-hour duration will…

A: given : x1 = 2.5mm x2 = 5mm t1 = 10 hr

Q: Briefly describe the principle and applications of the following separation operations: (i)…

A: (i) Dialysis: - Dialysis is an operation that is employed to extract additional water and toxins…

Q: In precipitation hardening, after being quenched into solution, overcooling is done and then either…

A: Precipitation Hardening: Definition: Precipitation Hardening is the heat treatment process which…

Q: What are the typical practical applications of diffusion mechanisms.

A: To explain: The applications of the diffusion mechanisms. Concept used: Diffusion mechanism:…

Q: Sodium chloride (NaCI) is a ceramic that has the following crystal structure. Given: R(Na*)= 0.098…

A: Write the formula for the ionic packing factor for NaCl. IPF=VatomsVunitcell Here, IPF is the ionic…

Q: Compare and contrast diffusion and heat. You may refer to Ficks' law, Fourier's law and/or the laws…

A: The net movement of anything (such as atoms, ions, molecules, or energy) from a location of…

Q: Estimate the thermal diffusivity of butter at 20°C.

A: Thermal diffusivity: It is defined as the ratio of heat conducted to heat storage. The conductivity…

Q: Calculate the diffusion constant,

A: GIVEN for the process at a diffusion temperature of T=1150 ⁰C D0 = 5.5 *10-5 m2/s; Qd = 148,000…

Q: THICK-WALLED PRESSURE VESSELS A steel compound cylinder is formed by shrinking a tube 400 mm outside…

A: To calculate the shrinkage allowance used during the manufacture of the compound cylinder, we can…

Q: )For the carbonization of steel at 800°C, it takes 2 hours to reach a C concentration of 0.4% at a…

A: Given DataT1=800°CD1=D2t1=2hrt2=6hrx1=100μmCx=0.4%

Q: You are examining two materials with the same density. One has a BCC crystal structure, and one has…

A: Given data:- BCC crystal structure HCP crystal structure. The same density To find:-Which crystal…

Q: ank the materials from highest to lowest of which has the best thermal shock resistance without…

A: Thermal shock resistance refers to a material's capacity to withstand quick and abrupt…

Concept explainers

Atomic diffusion in solids

In material science, diffusion can take place in solid, liquid, and gases. In solids, atomic diffusion can take place with the help of thermally activated and randomly vibrating atoms. The atomic diffusion in solids is complex and very slow in comparison to atomic diffusion in liquids and gases because the interatomic distance between the atoms is smaller in solids as compared to liquids and gases.

Question

(c) Using the equation d = D · t, where "d is the layer thickness, "D" is the diffusion coefficient for
nitrogen and "f" is the treatment time. D=2.67 × 10-14 m²/s at 500°C, calculate the time required to
reach a case depth of 30, 50 and 70 microns.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Given data

VIEW

Solution of part a

VIEW

Solution of part b and c

VIEW

Step by step

Solved in 3 steps with 3 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

A coating process using suspended particles in a liquid can attain formation of an ultrafiltration ceramic top-layer on a porous support (substrate). Which type of coating mechanisms is most probable? What is the effect of the coating time on the thickness of the coated layer? What is the effect of the pulling rate out of the liquid on the thickness of the coated layer?
In copper, what percentage of the volume change which occurs as the specimen is heated from room temperature to its melting point is due to the increased vacancy concentration, assuming that the vacancy concentration is just below the melting point (1083 oC) is 10-4. Given: Assume that the linear thermal expansion coefficient of copper is 16.5×10-6 K-1 over the whole temperature range.
Problem 4 The preexponential and activation energy for the diffusion of iron in cobalt are 1.1 x 105 m²/s and 253,300 J/mol, respectively. At what temperature will the diffusion coefficient have a value of 2.1 × 10-¹4 m²/s?
1- A large slab of steel at a uniform tempering temperature of 200°C and suddenly quenching, and it surface temperature lowered to 70°C. calculate the required time when the temperature at a depth 4.0 cm has dropped to 120°C? Given: steel [k =45 W/m°C, a=1.4x10 m²/s, c=0.46 kJ/kg]
Compare the diffusion coefficients (in cm²/s) of nitrogen in BCC and FCC iron at the allotropic transformation temperature of 912°C. Decc -153606 X Your response differs from the correct answer by more than 10%. Double check your calculations, cm²/s -1976-7 Dicc x Your response differs significantly from the correct answer. Rework your solution from the beginning and check each step carefully. cm2/s
please answer quickly
! (asap)
Problem 3. Phosphorus is diffused into a thick slice of silicon with no previous phosphorus in it at a temperature of 1100°C. If the surface concentration of the phosphorus is 1 x 10 atoms/cm and its concentration at 1 µm is 1 x 105 atoms/cm, how long must be the diffusion time? D = 3.0 x 10 cm?/s for P diffusing in Si at 1100°C.
What are the differences between Equimolar counter diffusion (EMD) and Uni molecular diffusion
If the viscosity of SCl2 gaseous molecule at 20.0 °C and 1 atm. is 132 pP. what is the viscosity of 7cz gaseous molecule in pP at the same temperature and pressure assuming both molecules having the same cross section? (MM of 35c - 35.0g mol MM of 37a - 37.0 g mol1)
Material science Engineering.
Consider a dispersion strengthened alloy with average interparticle spacing of L. If Nv is he number of particle per unit volume, d is the particle dimeter, and Vp is the volume fraction of particle, then what will be the expression for interparticle spacing in term of the particle diameter and volume fraction? rt to give answers from this point, Answers D