Hide blocksIron (II) oxide (FeO) is a ceramic that has the same crystal structure as NaCl.Given:R(Fe2)=0.087 nm and R(0²)-0.132Calculate the lonic Packing Factor (IPF) of FeO?Select one:O a. 0.12Ob.0.41Oc. 0.21O d. 0.74Oe. 0.14O£.0.47O g. 0.59O h.0.5110:14 PM15-Apr-2021

Given:radius of Fe2+=0.087 nmradius of O2-=0.132 nmPacking factor=(number of cation*volume of…

Answered: Iron (II) oxide (FeO) is a ceramic that…

Iron (II) oxide (FeO) is a ceramic that has the same crystal structure as NaCl. Given: R(Fe2)= 0.087 nm and R(O?)-0.132 Calculate the lonic Packing Factor (IPF) of FeO? Na

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: The fraction of lattice points occupied by vacancies in solid magnesium at 660°C is 103. Compute the…

Q: Two processes are used to produce polycrystalline Al2O3. In the first process the grain size is 10…

A: given data; ⇒for first process grain size(L1)=10μm⇒for second process grain size(L2)=25μm⇒ASTM grain…

Q: What are the Miller indices for the plane drawn in the sketch below? Select one: O a (000) Ob.110)…

Q: ketch the lattice planes in cubic crystal using Miller indices for (-200), (-1-20) and (302) planes

Q: what microstructure is this ASTM A128 material

A: ASTM A128 is a standard specification for high manganese steel casting. High manganese steel is a…

Q: what are the properties of

Q: Iron sulfide (FeS) may form a crystal structure that consists of an HCP arrangement of S² ions. (a)…

A: (a) The iron (Fe2+) ions will occupy octahedral interstitial sites in the HCP arrangement of S² ions…

Q: Calculate the number of Frenkel defects per cubic meter in zinc oxide at 939°C. The energy for…

Q: CFRP and GFRP are examples of hybrid materials. Body diagonal in BCC structure has Miller indices…

A: Yes, CFRP and GFRP are the hybrid materials. Yes, The BCC structure has miller indices of [111] No,…

Q: 4. Calculate the fraction of vacant lattice sites for pure copper at 1080°C. The value of the…

A: Temperature T = 1080 C = 1080+273 = 1353 K

Q: The only alkali metal halides that do not adopt the NaCl structure are CsCl, CsBr, and CsI, formed…

A: The size of Cs+ ion is greater than the Na+ion size. The coordination number of Cs ion is 8 while…

Q: Consider the ReO3 unit cell shown below, with a = 3.74 Å and ∆ Hsub = 626 kj/mol (a) What is the…

A: Solution: Given Data: a=3.74 Ao∆Hsub=626 kJ/mol To Find: (a) What is the Bravais lattice and…

Q: Identify the Atomic Packing Factor (APF) for Body-Centered Cubic (BCC).

A: Given Structure BCC We have to find atomic packing factor of BCC

Q: Determine the Miller Indices of Direction C and D in an HCP crystal.

Q: Chemistry Consider FCC copper. If bond energy per atom is 5.62 × 10-19 J, and its atomic radius is…

A: Given that, Bond energy per atom, ε=5.62×10-19 J,Atomic radius, r=0.128 nm, a=22ra=22×0.128a=0.362…

Q: Factors influence crystal structure for ionic materials What factors influence crystal…

A: a)Electrostatic attraction binds ions into ionic crystals. Their configuration depends on the size…

Q: Calculate the surface density of the lattice atoms that lie on the (100) plane of an FCC crystal???…

A: Find the surface density for FCC Plane(100)

Q: The unit cell for Cr2O3 has hexagonal symmetry with lattice parameters a = 0.4961 nm and c = 1.360…

A: To findCalculate its atomic packing factor.Givenlattice parameter, density of material, Ionic radii…

Q: APF for FCC and HCP are the same.

A: APF = fraction of volume occupied by hard Spheres = (Sum of atomic volumes)/(Volume of cell) = 0.74…

Q: Beryllium with a crystalline structure HCP lattice constant c / a = 1.568 and the radius of the atom…

A: Unit cell: The unit cell is the smallest part of the lattice which repeats multiple times to form a…

Q: Vanadium (V) has a BCC crystal structure. The atomic radius is R = 0.132 nm and the atomic mass is M…

Q: 1.- Calculate the number of iron atoms in a-1000-kg-of-iron. 2.- Calculate the volume in a cubic…

A: (1) From the given table, write the atomic mass of iron. Atomic mass=55.847 g/mol

Q: Determine the spacing between dislocations in a low angle tilt boundary in iridium ( FCC) when the…

A: Data given- a = 3.84 A° Irridum ( FCC structure ) angle of tilts i) 2° ii) 4°

Q: 1. Show that the atomic packing factor for HCP is 0.74. 2. Calculate the radius of Palladium atom…

A: given; (1) atomic packing factor for HCP? (2) radius of palladium(r)=?density(ρ)=12g/cm3atomic…

Q: Consider two hypothetical metallic crystal structures A and B. A has an fcc and B a bcc lattice…

Q: P.3 The diffusivity of manganese atoms in the FCC iron lattice is 1.50 x 10-14 m²/s at 1300°C and…

Q: Can ceramic and polymeric materials contain dislocations

A: Ceramic: It is an non-organic and non-metallic solid compounds which is shaped and then heated to…

Q: It is the structure of metals wherein atoms are located at each corners and centers of all cube…

A: GIVEN DATA- A MCQ GIVEN OF MATERIAL SCIENCE SUBJECT WE HAVE TO TELL WHICH TYPE OF CUBIC STRUCTURE…

Q: Illustrate the difference between crystalline structure and amorphous structure using an example

A: Crystalline structure: The structure in which atoms , molecules or ions are arranged in well ordered…

Q: Molybdenum has a BCC crystal structure, an atomic radius of 0.1363 nm, and an atomic weight of 95.94…

Q: What are the three types of lattice structures?

A: The three types of lattice structure are BCC, FCC, HCP

Q: su uct Question-5 How many atoms per unit cell are there in the HCP crystal structure (give…

Q: Determine the Miller Index of plane of the given plane in an HCP crystal? (1070) → (10 – 10 ) ►…

A: find the miller index of green plane For Given HCP cystal

Q: e crystal structure and drive mic packing factor (APF) for

A: It's given in next step

Q: Niobium has a BCC crystal structure, an atomic radius of 0.143 nm and an atomic weight of 92.91…

Q: Explain the number of atoms, coordination number of a FCC cubic structure with a neat diagram.

A: Find the no of atoms and coordination number for face centred cube .

Q: Platinum (Pt) has the FCC crystal structure, an atomic radius of 0.1387 nm, and an atomic weight of…

Q: 3.29 The unit cell for Al₂O3 has hexagonal symme- try with lattice parameters a = 0.4759 nm and c =…

A: Lattice parameter Avogadro Number Atomic mass of aluminium Atomic mass of oxygen Ionic radius of…

Q: Question 2. HfO2 has the CaF2 crystal structure. Calculate the density of HfO2 in kg/m³ if the ionic…

Q: Calculate the planar densities of Li+1 and Cl-1 ions on the (111) plane for LiCl, which has the NaCl…

A: Given, LiCl has NaCl type structure. So at 4 corners we have Li+ atoms and at remaining 4 corners we…

Q: (a) Why is the carbon concentration in austenite (y-Fe) higher than in ferrite (a-Fe)? (b) Determine…

A: To find: (a) To explain why is the carbon concentration in austenite γ-Fe higher than in ferrite…

Q: What is "Tin Disease"? The crystal Structure of Zinc (Zn) is Hexagonal Closed Packed (HCP). Show…

A: Explanation: Tin disease is the process of allotropic transformation of tin from white tin to gray…

Concept explainers

The Space Lattice and Unit Cells

Every matter consists of atoms, molecules, and ions. If these atoms, molecules, and ions (micro-particles) are represented in a three-dimensional space-occupying certain specific points in space, then these arrangements are termed as space lattices and the specific points which are being occupied by atoms, molecules and ions are termed as lattice points. The atoms, molecules, and ions at the lattice points are generally grouped in a regular fashion and repeat periodically at the three-dimensional space.

Question

Hide blocks
Iron (II) oxide (FeO) is a ceramic that has the same crystal structure as NaCl.
Given:
R(Fe2)=0.087 nm and R(0²)-0.132
Calculate the lonic Packing Factor (IPF) of FeO?
Select one:
O a. 0.12
Ob.0.41
Oc. 0.21
O d. 0.74
Oe. 0.14
O£.0.47
O g. 0.59
O h.0.51
10:14 PM
15-Apr-2021

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Principal Metallic Crystal Structures and Crystal Structure Analysis

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Vanadium (V) has a BCC crystal structure. The atomic radius is R = 0.132 nm and the atomic mass is M = 50.94 g/mole. What is the density of Vanadium in g/mm3? Given: Avogadro’s Number NA = 0.6023 × 1024 (atoms/mole) Select one: a. 1.5 b. 0.021 c. 0.011 d. 0.0087 e. 0.00597
Molybdenum, a BCC metal has an atomic radius of 0.136 nm. (a) Calculate the d-spacing for the (211) plane.
Calculate the number of vacancies per cubic meter in iron at 855°C. The energy of vacancy formation is 1.08 eV/atom. Futhermore, the density & atomic weight are 7.65g/cm3 & 55.85 g/mol respectively.
The spacing of adjacent atoms in a NaCl crystal is 0.282 nm, and the masses of the atoms are 3.82*10-26 kg (Na) and 5.89*10-26 kg (CI). Use this information to calculate the density of NaCl. p= kg/m³
a. Molybdenum at 20°C has Body Centered Cubic (BCC) crystal structure with an atomic radius, R of 0.140 nm. Draw the BCC crystal, identify the relationship between atomic radius, R and lattice constant, a. Calculate the atomic packing factor (APF) for Molybdenum at 20°C. b. What is grain boundary and state the importance of grain boundaries
1. Is there a difference in packing (coordination number) between these two types (FCC and HCP) of structures? 2. Look at the two structures. A small difference in arrangement of atoms causes a dramatic difference in the properties of FCC ductile metals and HCP brittle metals. Can you see it? Try to draw the differences (You can draw the 3-layers separately):
Calculate the density in g / cm3 of a metal with a structure fcc molecular mass of 100g / mol and an atomic radius of 0.145nm
3. Give the Miller indices of the planes that are perpendicular to the those planes having Miller indices: 0 to ±3. Please at least give four different solutions plane. Limit your planes to
Calculate the number of vacancies per m 3 for gold at 900 C. The energy for vacancyformation is 0.86 eV/atom.
please answer quickly
What is the coordination number for atoms in the HCP structure? How does this compare to the coordination number for FCC? How would you expect HCP and FCC to compare in terms of APF? Which would be greater? (or would they be the same?)
please answer quickly