For the equilibrium silver-copper system, if you were at a temperature of 779 °C and a composition of 60 wt% Cu, what fraction of the system would be in the a phase? Your answer should be in the form of a percentage (a value 0-100). °C 1084.$ 1000 961.93 900 a +L B+L 800 780 91.2 80 71.9 700 600 a+B 500 400 Cu 10 20 30 40 50 60 70 80 90 Ag Weight Percent Silver

For the equilibrium silver-copper system, if you were at a temperature of 779 °C and a composition of 60 wt% Cu, what fraction of the system would be in the a phase? Your answer should be in the form of a percentage (a value 0-100). °C 1084.$ 1000 961.93 900 a +L B+L 800 780 91.2 80 71.9 700 600 a+B 500 400 Cu 10 20 30 40 50 60 70 80 90 Ag Weight Percent Silver

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Consider Al- Cu system below. When Al-40%Cu is heated above 600°C and cooled slowly to a temperature of 545°C . Answer the following. Use the values of composition given in the phase diagram , no estimation .Each has two marks. 700 1200 600 L a + L 6 +L 548 1000 500 (CUAL) a + 6 800 400 600 300 5.65 10 20 30 32.7 40 50 52.5 (AI) Composition (wt % Cu) a. Percentage of the pro-eutectic phase present (% no decimal places) b. Composition of the pro- eutectic phase present (in %Cu one decimal place) c. What is the percentage of larger eutectic component present (% no decimal places) Temperature (°C) Temperature (°F)
Consider a Cu-30% Ag system which is cooled from 900°C to 778°C. What is the amount eutectic Alpha phase present at 778°c Composition (ats A 20 40 80 100 1200 12200 2000 -Liquidus 1000 Liquid 1800 Salidus a +L 779 C (Tg) 1600 800 G 91.2 8.0 71.9 1400 1200 600 1000 Solvus a 800 400 600 200 400 100 20 40 60 80 (Cu Composition (wt% Ag (A Temperature ("C) Termperature ("F)
The Pb-Sn phase diagram is given: What is the Primary phase for a Pb-75%Sn alloy and what is the amount of Eutectic mixture at 100°C for this alloy? Composition (at% Sn) 20 40 60 80 100 327°C H600 300 Liquid 500 232°C a + L 200 B + L 1400 183°C 18.3 61.9 97.8 B00 100 a + B 200 H100 20 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Temperature (°C) Temperature (°F)
Consider 1 kg of tin-bismuth alloy (Sn-Bi) containing 40 wt% Bi. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 138 "C (just below the eutectic temperature). How many kilograms of phase B form? 300 271°C 232°C 200 Bi + L В +L 139 C 21 100 Bi - В + Bi 13°C vate Windows 100gs to activate Windows (Bi) 20 40 60 80 (Sn) 6:37 PM A 4) ENG 57 B. Temperature (°C)
Figure 1 shows the phase diagram of platinum-silver (Pt-Ag) at equilibrium. Determine the phases present, composition, and amount of each phase at 1100 °C and 60 wt.% Ag. Alloy 1 Alloy 2 1800 1600 Liquid O 1400 L+a a 1186°C 1200 L+B 1000 800 a + B B 600 42.4 10 20 30 40 50 60 70 80 90 100% 100% Weight percent silver Ag Pt Figure 1 Temperature (°C)
The phase diagram of the alloy Copper – Silver is shown in the figure below. Composition (at% Ag) 20 100 2200 40 60 80 1200 2000 A -Liquidus 1000 Liquid 1800 -Solidus F a +L 779°C (Tg). 1600 B+L 9 800 E B G 91.2 (Cog 8.0 71.9 1400 1200 600 1000 Solvus a +B 800 400 C 600 H 200 0 60 400 100 20 40 80 (Cu) Composition (wt% Ag) (Ag) (a) Cite the phases that are present and the phase compositions for the following alloys: 1) 5 wt% Cu – 95 wt% Ag at 900 °C 2) 50 wt% Cu – 50 wt% Ag at 1000°C 3) 30 wt% Cu – 70 wt% Ag at 900 °C 4) 20 wt% Cu - 80 wt% Ag at 600 °C 5) 40 wt% Cu – 60 wt% Ag at 600 °C (b) Determine the eutectic temperature and eutectic composition. (c) What is the maximum solubility of silver in copper and at which temperature? Temperature ("C) Temperature ("F)
iii) For a 68 wt% Zn-32 wt% Cu alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 1000°C, 760°C, 600°C and 400°C. Label all phases and indicate their approximate compositions. Comportion a In 20 40 60 100 1200 |2200 H2000 Liquid 1000 - 1800 デ+ダ H1600 J400 E 1200 600 400 『+キ 600 200 400 40 60 Conpositon tet% Zro
7. Consider 1.5 kg of a 99.6 wt% Fe-0.4 wt% C steel that is cooled to a temperature just below the eutectoid. (a) How many kilograms of ferrite (a) form? (b) How many kilograms of cementite (Fe;C) form? Include your tie line in the solution. 1600| L 1400 T(°C) 1200 (austenite) y+L 1148°C L+Fe;C 1000 Y + Fe;C 800 727°C 600 a + Fe;C 400 1 2 4 6 6.7 C, wt% C Fe;C (cementite)
An alloy system consists of two metals A&B which are soluble in each other in all proportions in the liquid state, but completely insoluble in the solid state. The melting point of metal A is 425°C and B is 375°C. The lowest melting point (Eutectic) is 230°C at 40%B. Choose the correct answers for the following sentences: the phases present in the equilibrium diagram are: OL& A & B O A & B O A&L B& L
An alloy system consists of two metals A&B which are soluble in each other in all proportions in the liquid state, but completely insoluble in the solid state. The melting point of metal A is 425°C and B is 375°C. The lowest melting point (Eutectic) is 230°C at 40%B. For a 30 wt% A alloy at 300°C, the phases weight are O 0.4 kg B and 0.6 kg Liquid O 0.21 kg A and 0.789 kg Liquid 0.35 kg B and 0.65 kg Liquid 0.82 kg A and 0.18 kg Liquid
A 45 wt% Pb-55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high- temperature microstructure is preserved. This microstructure is found to consist of the a phase and Mg2Pb, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Use Animated Figure. °℃
Presume that we have 100 grams of an alloy with overall chemical composition of90 wt. pct. tin and 10 wt. pct. lead. The alloy (in the liquid state) is cooled atnear-equilibrium conditions.Determine the following:At slightly below 183oC, what are the following: (parts a-h at a temperature below 183C please!)