Consider a Cu-30% Ag system which is cooled from 900°C to 778°C. What is the amount eutectic Alpha phase present at 778°cComposition (ats A2040801001200122002000-Liquidus1000Liquid1800Salidusa +L779 C (Tg)1600800G91.28.071.9140012006001000Solvusa80040060020040010020406080(CuComposition (wt% Ag(ATemperature ("C)Termperature ("F)

Answered: Image /qna-images/answer/4be3017a-e3e1-485a-a2f6-571ab8451f04.jpg

Consider a Cu-30% Ag system which is cooled from 900°C to 778°C. What is the amount eutectic Alpha phase present at 778°c Composition as A 40 100 2200 1200 2000 Liquidus 1000 Liquid 1800 Salidus 1600 800 779CT 8.0 71.9 (C 912 1400 (C 1200 600 Solvus 1000 800 400 600 200 400 100 20 40 60 (Cul Composit wt% Ag (Ag) wangnadua (0.) ungadue

Consider a Cu-30% Ag system which is cooled from 900°C to 778°C. What is the amount eutectic Alpha phase present at 778°c Composition as A 40 100 2200 1200 2000 Liquidus 1000 Liquid 1800 Salidus 1600 800 779CT 8.0 71.9 (C 912 1400 (C 1200 600 Solvus 1000 800 400 600 200 400 100 20 40 60 (Cul Composit wt% Ag (Ag) wangnadua (0.) ungadue

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q.4) For 30 wt% Sn- 70 wt% Pb alloy at 125 °C, (a) what phases are present? (b) What are the compositions of the phases? (c) Calculate the relative mass fraction of each phase present. Temperature (°C) 4327 C 300 200 100 (Phi 20 Solvus Solidus B 20 40 Composition lat% Sni 60 liquidus 183 C 40 Liquid E 61.9 60 Composition (wt% Sn) 80 80 100 232 C G 97.8 600 500 TEL # 400 Temperature (F) 300 200 H 100 100 (Sn)
(a) Indicate hypooeutenic, hypereutenic ranges and eutenic composition in wt%Sn. Use the phase diagram below.
Which of the following statements are true about the following phase diagram? Group of answer choices All three allotropes of iron exist at the same range of temperature and pressure. Iron vapor can exist at conditions of Earth's atmosphere. Solid iron can exist in three different crystal structures. Solid iron can exist in two different crystal structures. Liquid iron only exists at high pressure.
The lead and tin are partially dissolved in each other in solid state although they completely dissolved in liquid state. They form eutectic from solid solutions alfa (a) and beta (B) at alloying composition 62% tin and 38% lead, the eutectic forming temperature is 184°C. Alfa contained 20% tin dissolved in 80% lead at 184°C while beta consist of lead dissolved in tin at 184°C. If the 100 g of eutectic contained 45.5 g of alfa at 184°C.Knowing that the melting temperatures of lead and tin are 329°C and 232°C respectively, and the solubility of tin and lead in each other's diminished to zero at room temperature. Answer the following a) Plot the phase diagram for lead-tin system label all phases and temperature. b) What is the composition of beta at eutectic temperature. c) For 40 % lead alloy calculate the phase amount and composition at 350°C, 170°C, and Tr
Calculate the invariant reactions for Cu-Zn Reaction (eutectic eutectoid peritectic peritectoide) Temperature Transformation
Q4: For a 98 wt% Fe-2 wt% C at a temperature 700 °C, determine the following: a) The Number and types of The Phases Present. b) The Amount Of Phases Present in Grams That forms per 100 G. c)Draw The Microstructure Of Phases Present At This Point And What is The React called? d) Specify the following on Iron- Carbon Phase Diagram: (y+ L) phase, Eutectoid Reaction
At what temperature does the first liquid phase form at 90% Ni? T(°C) 1600 1500 1400 1300 1200 1100 1000, L (liquid) L+α solidus liquidus 80 100 20 40 60 80 wt% Ni
Consider Al- Cu system below. When Al-40%Cu is heated above 600°C and cooled slowly to a temperature of 545°C . Answer the following. Use the values of composition given in the phase diagram , no estimation .Each has two marks. 700 1200 600 L a + L 6 +L 548 1000 500 (CUAL) a + 6 800 400 600 300 5.65 10 20 30 32.7 40 50 52.5 (AI) Composition (wt % Cu) a. Percentage of the pro-eutectic phase present (% no decimal places) b. Composition of the pro- eutectic phase present (in %Cu one decimal place) c. What is the percentage of larger eutectic component present (% no decimal places) Temperature (°C) Temperature (°F)
1. four processes. 2. Fill out the blanks by labeling the phase regions. 3. Identify the Indicate an in- termediate compound, if any. 3. Temperature (°C) 1600 1400 1200 1000 800 600 400 1538°C 0 (Fe) -1493°C 1394°C 912°C y, Austenite 1 2 0.16 5 0,022 a, Ferrite A N 2.14 Composition (at% C) 15 10 3 1147°C L4 3 4 Composition (wt% C) 4.30 727°C Sketch the microstructure at A, label phases, figure out compositions. 20 Cementite (Fe3C). 5 6 25 6.70
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
Hi i keep getting these wrong
(a) Sketch a Pressure-Temperature phase diagram for a pure substance X where liquid X is less dense than solid X. Insert an isobar at 1 atm and an isotherm at 300 K. Clearly label all physical states, triple point, critical temperature and any normal transition temperatures.