Section 26. A copper wire with length 0.5 m was subjected to a tension experiment, the wire was tensionedto 2 mm. suppose the diameter of the wire is 1mm and the poission ratio 0.24. write down thefive digits change in diameter in mm unit. *Enter your answer7.In the Brinell hardness test, if the load used 1200 kg and the ball diameter 6 mm, write down thediameter of the indentation (in mm unit) if the BHN number was 586,Enter your answer

As per policy, we can solve the first one question from multiple questions.

5. A copper wire with length 0.5 m was subjected to a tension experiment, the wire was tensioned to 2 mm. suppose the diameter of the wire is 1mm and the poission ratio 0.24. write down the five digits change in diameter in mm unit. *

5. A copper wire with length 0.5 m was subjected to a tension experiment, the wire was tensioned to 2 mm. suppose the diameter of the wire is 1mm and the poission ratio 0.24. write down the five digits change in diameter in mm unit. *

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…
7. In the Brinell hardness test, if the load used 1200 kg, and the ball diameter 6 mm, write down the diameter of the indentation (in mm unit) if the BHN number was 586. * (1 Point) Enter your answer
Question A cylindrical specimen of metal having a diameter of 12.88 mm and a gauge length of 63.50 mm is tested using a tensile testing machine. The elongation measurement are recorded in Table 3. nPlot the stress-strain curve on the graph paper provided based on data in Table 3 Based on the stress-strain curved plotted in (i): Compute the modulus of elasticity Determine the yield strength at a strain offset of 0.002. Determine the tensile strength Determine the ductility in percent elongation and percent area reduction Table 3: Load-elongation readings for a metal specimen Jadual 3: Bacaan beban pemanjangan untuk statu spesimen logam) Load (N) Elongation (mm) 1380 0.03 2780 0.06 5630 0.12 7430 0.2 8140 0.25 9870 0.64 12850 1.91 14100 3.18 14340 4.45 13830 5.72 12500 6.99 Fracture
7. In the Brinell hardness test, if the load used 1200 kg, and the ball diameter 6 mm, write down the diameter of the indentation (in mm unit) if the BHN number was 586. * Enter your answer
A tensile test was performed on a metal specimen with a diameter of 1/2 inch and a gage length (the length over which the elongation is meas- ured) of 4 inches. The data were plotted on a load-displacement graph, P vs. AL. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/AL = 1392 kips/in. What is the modulus of elasticity? BI
A sample test rod made of a ferrous material of 0.5 in. diameter was tested for tensile strength with the gauge length of 2.5 in. The following observations were recorded: Final length = 3.15 in; Final diameter = 0.275 in; Yield load = 7650 lb. and Ultimate load = 10375 lb. (a) Calculate: 1. yield stress, 2. ultimate tensile stress, 3. percentage reduction in area, and 4. percentage elongation. (b) What specific material, if any, is similar to this tested rod? Refer to AT7 and AT8. (c) This same material is then used as a tension member 55 inches long and is subjected to a maximum load of 6000 lb, repeated but not reversed. (d) Solve part (c) if the total elongation is not to exceed 0.025 in.? 1. %3D
1. Plot the engineering stress & strain diagram of an alloy having a tensile test result found in Table 1. The tensile test specimen has a diameter of 12.5mm and a gage length of 50.0mm. The given alloy is used to make a 30.0mm diameter cylinder, which is placed inside a hardened circular steel casement with a 30.01mm inner diameter. Table 1: Tensile test results of an alloy Change In Length (mm) Change In Diameter (mm) Load (kN) 0.000 0.0000 0.0000 4.364 0.0254 0.0019 -0.0057 13.092 0.0762 21.819 0.1270 0.0095 30.547 32.729 0.1778 0.7620 34.911 3.0480 30.01 mm O F Rigid Plate Cylindrical Alloy -Steel casement Figure k Section view of the steel casement encapsulating the cylindrical alloy 2. Determine the required minimum value of F such that the cylindrical alloy would touch the walls of the steel casement.
A tensile test is performed on a metal specimen, and it is found that a true plastic strain of 0.20 is produced when a true stress of 575 MPa (83,500 psi) is applied; for the same metal, the value of K in Equation 6.19 is 860 MPa (125,000 psi). Calculate the true strain that results from the application of a true stress of 600 MPa (87,000 psi). Part 1 To solve this problem, calculate the value of n using the known relationship between true stress, true strain, the strain- hardening coefficient, and K (Equation 6.19). or = Ke, What is n? n = i
diagram and determine approximately the modulus of elasticity, the yield stress, the ultimate stress, and the fracture 2.00 in. The data is listed in the table. Plot the stress-strain 8-1. A tension test was performed on a steel specimen n original diameter of 0.503 in. and gage length of PROBLEMS *84. origi the f having an for t and stress. Use a scale of 1 in. Dodraw the elastic region, using the same stress scale but a 20 ksi and 1 in. = 0.05 in./in. strain scale of 1 in.= 0.001 in./in. Load (kip) Elongation (in.) 0. 0. 0.0005 0.0015 1.50 4.60 8.00 11.00 0.0025 0.0035 0.0050 11.80 11.80 0.0080 0.0200 12.00 16.60 0.0400 0.1000 0.2800 20.00 21.50 19.50 18.50 0.4000 0.4600 Prob. 8-1
A stress-strain diagram for a tension test of an alloy steel sample is shown in the diagram below. The initial sample diameter is 0.502”, the diameter of the fractured sample is 0.412”, the original gage length is 2.00” and the final length after fracture is 2.78”. Determine/ calculate the following: (a) The stress at the proportional limit. (b) The modulus of elasticity (E). (c) The yield stress using the 0.2% offset method. (d) Theultimatetensilestrength. (e) The rupture stress. (f) The percent reduction in area. (g) The percent elongation. (h) Is the material considered ductile or brittle?
a)Draw the stress-strain curve of a ductile material such as that of a ductile steel and discuss the various regions of the curve. Explain the difference between a ductile and brittle material and the concept of ductility and its measurement. b)A machine part 10 mm thick, having the dimensions shown in the figure, is to be subjected to cyclic loading. If the maximum stress is limited to 60 MPa, determine the allowable force P. Approximate the stress concentration factors form the graph given. Where might a potential fracture occur?
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture