diagram and determine approximately the modulus ofelasticity, the yield stress, the ultimate stress, and the fracture2.00 in. The data is listed in the table. Plot the stress-strain8-1. A tension test was performed on a steel specimenn original diameter of 0.503 in. and gage length ofPROBLEMS*84.origithe fhaving anfor tandstress. Use a scale of 1 in.Dodraw the elastic region, using the same stress scale but a20 ksi and 1 in. = 0.05 in./in.strain scale of 1 in.= 0.001 in./in.Load (kip) Elongation (in.)0.0.0.00050.00151.504.608.0011.000.00250.00350.005011.8011.800.00800.020012.0016.600.04000.10000.280020.0021.5019.5018.500.40000.4600Prob. 8-1

Answered: Image /qna-images/answer/a303e3cc-c9a2-4968-98f3-c955df5017fd.jpg

strain scale of 1 in.=0.001 in./in. stress. Use a scale of 1 in. = 20 ksi and 1 in. = 0.05 in./in. diagram and determine approximately the modulus of n original diameter of 0.503 in. and gage length of tension test was performed on a steel specimen 2.00 in. The data is listed in the table. Plot the stress-strain elasticity, the yield stress, the ultimate stress, and the fracture Redraw the elastic region, using the same stress scale but a original diameter of 0.503 in. and gage length of having an 20 ksi and 1 in. 0.05 in./in. Dedraw the elastic region, using the same stress scale but a

strain scale of 1 in.=0.001 in./in. stress. Use a scale of 1 in. = 20 ksi and 1 in. = 0.05 in./in. diagram and determine approximately the modulus of n original diameter of 0.503 in. and gage length of tension test was performed on a steel specimen 2.00 in. The data is listed in the table. Plot the stress-strain elasticity, the yield stress, the ultimate stress, and the fracture Redraw the elastic region, using the same stress scale but a original diameter of 0.503 in. and gage length of having an 20 ksi and 1 in. 0.05 in./in. Dedraw the elastic region, using the same stress scale but a

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the proportional limit. Stress (ksi) 40 30- 20 10- 0- 0.0 0.0 Upper scale 0.020 0.002 22 ksi O 15 ksi E 19 ksi O 10 ksi 13 ksi Lower scale- 0.040 0.060 0.080 0.100 0.004 0.006 0.008 0.010 Strain (in./in.) 0.120 0.012
Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…
a 200mm long rod with a diameter of 50mm is loaded with a 4kN weight.the rod finale length 201.314mm and finale diameter 42mm.the load at the fracture is 2.5kN and the maximum load is 3.5kN. Calculate to third decimal and determine the folliwing 1.stress 2.strain 3.limit of proportionality 4.percentage of reduction in area 5.percentage elogation
Q2 A tensile test specimen having a diameter of (10 mm) und a page length of (S0 mm) was tested to fracture The stieisitrain curve from the tensiotn test is shown in Figure (9) The lower plat is the expanded tegion OAT and associatod with the strain valuns tiven on the lower scale Determine, 480 Lpper veile AB 241 Loser scale + The ultimaie stress, be The propotional limit, 120 e The fracture strees 4 The modulus of elasticity, OAK 0.04 0.0s 0.00 0.12 0.16 1.20 0K2 DANN 0.006 0.008 0.010 e T'he offiet yield stuen at 0.2%, Strain tmm/um) G The asial force ucting on the specireni whert t i uxtended by Figuie (3) a sans
Question A cylindrical specimen of metal having a diameter of 12.88 mm and a gauge length of 63.50 mm is tested using a tensile testing machine. The elongation measurement are recorded in Table 3. nPlot the stress-strain curve on the graph paper provided based on data in Table 3 Based on the stress-strain curved plotted in (i): Compute the modulus of elasticity Determine the yield strength at a strain offset of 0.002. Determine the tensile strength Determine the ductility in percent elongation and percent area reduction Table 3: Load-elongation readings for a metal specimen Jadual 3: Bacaan beban pemanjangan untuk statu spesimen logam) Load (N) Elongation (mm) 1380 0.03 2780 0.06 5630 0.12 7430 0.2 8140 0.25 9870 0.64 12850 1.91 14100 3.18 14340 4.45 13830 5.72 12500 6.99 Fracture
The table below shows the deformation data that resulted from applying a pure tensile load to a brass alloy rod with an initial length of 30 mm and a diameter of 10 mm. This rod was subjected to necking and beyond necking deformation. The data at fracture is shown in the last row. Applied Load (N) Length (mm) Diameter (mm) 75,100 33.8 68, 250 34.9 50,200 35.7 6.7 Solve for the TRUE STRESS/ES and TRUE STRAINS. 8.3 7.8
A tensile test specimen of 1045 hot-rolled steel having a diameter of 0.505 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the ultimate strength. Stress (ksi) 60 50- 40- 30- 20 10- 0 0 0 Upper scale O 66 ksi 28 ksi O 72 ksi O 53 ksi O 62 ksi Lower scale. 0.025 0.050 0.075 0.100 0.125 0.150 0.175 0.002 0.004 0.006 0.008 0.010 0.012 0.014 Strain (in./in.)
A bronze alloy specimen having a diameter of 12.8 mm and a gage length of 50 mm was tested to fracture. Stress and strain data obtained during the test are shown in Figure. Determine: 400 - Upper scale a. the modulus of elasticity. 320 b. the proportional limit. Lower scale c. the ultimate strength. 240 d. the yield strength (0.20% offset). 160 e. the modulus of resilience. f. the true fracture stress if the 80 final diameter of the specimen at the location of 0.100 0.005 0.300 0.015 0.200 0.400 the fracture was 10.5 mm. 0.010 0.020 g. The Poisson's ratio. Strain (mm/mm) Stress (MPa)
Example: Convert the change in length data in Table 3-2 to engineering stress and strain and plot a stress-strain curve Homework- help Table 3-2 The results of a tensile test of a 0.505 in. diameter aluminum alloy test bar, initial length (1o) = 2 in. Calculated LTO Load (Ib) Change in Length (in.) Stress (psi) Strain (in./in.) 0.000 1000 0.001 0.0005 4,993 14,978 24,963 34,948 37,445 39,442 39,941 39,691 37,944 3000 0.003 0.0015 5000 0.005 0.0025 7000 0.007 0.0035 7500 0.030 0.0150 7900 0.080 0.0400 8000 (maximum load) 0.120 0.0600 7950 0.160 0.0800 7600 (fracture) 0.205 0.1025
A tensile test specimen has a gage length = 3.0 in and diameter 0.75 in. Yielding occurs at a load of 38,000 lb. The corresponding gage length 3.01 03 in (neglect the 0.2 percent yield point). The maximum load of 54,000 lb is reached at a gage length 3.453 in. Determine the tensile strength (round to the nearest whole Ksi) 38
In a Torsion test done, the following data were collected: the radius of the specimen was 3mm and the gauge length 76.2mm. During the elastic zone: T1-0. 01N.m. 01-14.760, T2-17. 13N.m, and 02-36.910. The modulus of rigidity be equal to:
A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the true fracture stress if the final diameter of the specimen at the location of the fracture was 0.350 in. Stress (ksi) 120 Upper scale Lower scale H 0.0 0.020 0.040 0.060 0.080 0.100 0.120 0.0 0.002 0.004 0.006 0.008 0.010 0.012 Strain (in./in.) 90 60 30 0- 300 ksi O 126 ksi EA O 237 ksi O 202 ksi O 261 ksi