4. For the A-B alloy the phase diagram below, use the lever rule to find the amount of liquid and solid states and their compositionsat Temperature T. Let Cx = 25%B, C =40%B, Cy = 60 %BComplete solubility of two metalsin liquid and solid states (Ni -Cu ,Sb - Bi)TAMEMTEMaTCyABConcentration of B in Awww.substoch comTemperature

Answered: Image /qna-images/answer/c2026ee6-d76b-4181-8d6f-b9a76f1e89fe.jpg

Answered: 4. For the A-B alloy the phase diagram…

4. For the A-B alloy the phase diagram below, use the lever rule to find the amount of liquid and solid states and their compositions at Temperature T. Let Cx = 25%B, C =40%B, Cy = 60 %B

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

If 20000 g of steam is condensed in 2106 cm³ at a pressure of 6 MPa a. What is the temperature (C)? b. In what state (state) steam? c. Draw it in the form of a phase diagram that you know
Temperature (°C) 700 600 0 500 400 300 0 (AI) a 5 a+L 10 Composition (at% Cu) 10 20 a +0 L 30 Composition (wt% Cu) 20 0+ L 0 (CuAl₂) 40 30 50 1200 1000 800 600 Temperature (°F) a) For the alloy represented by the phase diagram above, what is the wt% content of eutectic if an alloy of 2.5 wt% Cu is cooled very slowly from the molten state to 300°C? b) What phases are present in 2.5 wt% Cu material if it is quenched from 550°C?
Figure 2 refers to the phase diagram for silver and tin. Label the regions (1) to (5) Temperature, 0/°C 1000 800 600 400 200 0 Liquid 2 Ag,Sn 60 a 20 40 80 Mass percentage Ag/% 100 Question 6: What will be observed when liquids of composition of 40% Ag are cooled to 200 K? When will it begin to precipitate? When will it become solid?
Referring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B. b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E. c. identify the specific name for the point denoted by F. d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur? e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form? ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting? f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…
Consider the phase diagram below. The three points A, B, and C are at concentrations of 26.4, 31.3, and 34 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300 L (liquid) 1200 20 A B C L + a C1 S liquidus L + a solidus a (solid) 50 wt% Ni a. Walpha=0.21; WL=0.33; Walpha/WL = 13.17 b. Walpha=0.09; WL=0.32; Walpha/WL = 15.00 c. Walpha=0.07; WL=0.46; Walpha/WL = 11.17 d. Walpha=0.14; WL=0.37; Walpha/WL = 9.00
An alloy consisting of completely soluble cadmium (Cd) and zinc (Zn) in the liquid state, but neither of them dissolves in each other in the solid state. the table shown below shows the solidification temperatures for various alloys of cadmium and zinc. 1. Draw the equilibrium diagram according to the information given and data in the table and indicating all important temperature and phases. 2. Find the percentage of each phases and percentage of constituents of the alloy that contain 60 % Zn and at a temperature 300 °C. 3. Find the melting point for the following alloys 20 % Cd, 80% Cd 4. Draw the internal structure, noting the phases of the following alloys A) 30 % Cd at 290 °C b) 60 % Cd at room temperature. % of Zinc in alloy Start of solidification ("C) End of solidification ("C) 0 10 14 20 30 40 50 60 321 290 266 275 293 310 328 345 70 80 90 100 362 390 401 419 266 266 266 266 266 266 266 266 266 266 266 266
Do it in your handwriting
Consider the binary alloy phase diagram shown schematically below. The left-hand side denotes phase a, and the right-hand side the phase ß. The intermediate region is a coexistence regime with both a and ß phases. The three points 1, 2 and 3 in the coexistence region are at 22.8 wt% A, 28.2 wt% A, and 33.7 wt % A respectively. If the points on the phase boundaries L and R are at 20 wt% A and 39 wt % A, respectively, what is the fraction of a phase at 1, 2 and 3? (This question has only one correct answer) T(°C) A-B binary alloy 1400 Coexistence region 3 1 2 1100 B 20 % 40 % Weight % A
I need neat and clean handwritten solution. Don't give typed solution. Correct answer will be upvoted only.do remember
A hypothetical eutectic phase diagram for metals A and B shows that cooling a liquid melt with a concentration of 50 wt% A-50 wt% B to just below 625 °C (eutectic isotherm temperature) results in simultaneous formation of alpha and beta phases. The phase diagram also shows that alpha (A rich) and beta (B rich) phases exist at left and right extremes of the phase diagram, respectively. At the eutectic isotherm temperature, the maximum solubility of B in A and A in B is 10 wt% and 5 wt%, respectively. The phase diagram does not have any intermetallic compounds. A new solid alloy is made by melting together 86 gr of a 40 wt% A-60 wt% B alloy with 136 gr of 65 wt% A-35 wt% B alloy followed by cooling the melt to 400 °C. If the new alloy is heated up from 400 °C to just below 625 °C, answer the following questions: a. Calculate the overall alloy composition. b. Determine phases present and calculate their respective masses. Calculate the masses of the primary phase, eutectic phase, and…
700 L 600 M a + L Mg, Pb 500 P 465 400 L Mg Pb 300 200 a + Mg Pb B+ Mg Pb 100 20 40 60 80 100 Mg Composition (wt% Pb) Pb Mg,Pb Using the above figure, sketch neatly the microstructure of the alloys (given in the below table) and determine the amount of each phase presented. Structure of the alloys at different compositions 田 Compositions &temperature 10%Pb,90%Mg Structure Structure Compositions &temperature 20%Pb, 80%Mg @400°C @0°C My.Pb 50%Pb,50%Mg 67%Pb, 33%Mg @0°C Mgz PB @0°C 81%Pb,19%Mg 90%Pb,10%Mg @200°C @0°C Temperature ("C)
Consider the phase diagram below. The three points A, B, and C are at concentrations of 27, 31.9, and 33.8 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300-L (liquid) 1200 20 ABC L + a C1 30 S C2 liquidus 40 L + a solidus α (solid). O a. Walpha=0.12; WL=0.41; Walpha/WL = 9.41 O b. Walpha=0.27; WL-0.26; Walpha/WL = 11.11 O c. Walpha=0.15; WL-0.26; Walpha/WL = 11.80 Od. Walpha=0.20; WL-0.31; Walpha/WL = 7.33 50 wt% Ni